电荷补偿对Ba2ZnGe2O7：Bi3+荧光粉发光性质的影响

采用高温固相法制备了2个系列的荧光粉样品：Ba_2-xZnGe₂O₇：xBi³⁺（系列Ⅰ）和Ba_1.994-yK_yZnGe₂O₇：0.006Bi³⁺（系列Ⅱ）。X射线衍射（XRD）测试结果表明,少量Bi³⁺、K⁺的掺杂不会明显改变材料的物相结构。样品的荧光光谱测试结果表明,虽然2个系列样品的发光光谱都随组成成分变化有少量变化,但发光颜色基本上均为黄绿色。在358 nm的激发下,荧光粉的发射光谱呈现一个峰值在500 nm的宽发射带,归属于³P₁→¹S₀能级跃迁。在500 nm监测下,荧光粉的最强激发峰位于358 nm,归属于¹S₀→³P₁能级跃迁,此外还有一个位于320 nm的肩峰归属于O^2--Bi³⁺电荷转移带。系列Ⅰ样品的光谱数据结果指出,Bi³⁺的最佳掺杂量x为0.006。在该基质中,Bi³⁺掺杂取代Ba²⁺属于不等价取代,会在晶格中产生Ba²⁺空位或间隙O^2-,对材料的发光强度产生负面影响。对此,采用K⁺与Bi³⁺协同掺杂起到电荷补偿的作用,填补Ba²⁺空位或捕获间隙O^2-缺陷。空位被填补或间隙被捕获均减少了晶格畸变,从而使发光强度明显提高。系列Ⅱ样品的光谱数据表明,完全电荷补偿的荧光粉样品相比于没有掺K⁺的样品,其发光强度提高了约2.5倍。     

白光LED用Sr0.955Al2Si2-xTixO8：Eu2+荧光粉的晶体结构和光谱特性

由高温固相反应制得Sr_0.955Al₂Si_2-xTi_xO₈：Eu²⁺（x=0~1.0）系列试样,研究了Ti⁴⁺置换Si⁴⁺对其晶体结构和光谱特性的影响。Ti⁴⁺以类质同相替代Si⁴⁺进入晶体晶格中,形成了连续固溶体,其晶胞参数a,b,c,β和晶胞体积V随Ti⁴⁺置换量呈线性递增。Ti⁴⁺置换Si⁴⁺对晶胞参数c的影响显著,b其次,a最小。荧光激发谱为宽带,位于230~400nm,由267nm、305nm、350nm和375nm 4个峰拟合成,表观峰值位于351nm;随着Ti⁴⁺置换量的增加,半高宽（FWHM）从105nm减小到93nm。发射光谱位于380~600nm,表观峰值位于407nm,可由406nm和441nm两峰拟合而成并且随Ti⁴⁺置换量增加线性红移,Ti⁴⁺进入晶格对长波长发射中心影响较少;Ti⁴⁺置换量为1.0时,表观发射峰位从407nm红移至417nm;利用试样荧光光谱和VanUitert经验公式,得出SrAl₂Si₂O₈：Eu²⁺中Sr²⁺的配位数为9。随着Ti⁴⁺置换量Si⁴⁺进入基质晶格,造成Eu-O距离变小,使得Eu²⁺所处的晶体场强度增强,发光中心Eu²⁺的5d能级分裂增大,造成Eu²⁺最低发射能级重心下移,两拟合谱峰峰位均呈线性红移。     

Cr3+掺杂Ca4HfGe3O12宽带近红外荧光粉的发光特性及应用

近红外荧光粉在生物活体成像领域展现出重要的应用前景。但活体成像用近红外荧光粉存在种类匮乏、耐温性差等瓶颈问题。采用固相法合成了宽带近红外Ca₄HfGe₃O₁₂∶ xCr³⁺(0≤x≤0.09)荧光粉。X射线衍射和能谱分析的结果表明Cr³⁺离子成功进入Ca₄HfGe₃O₁₂晶格。在469 nm蓝光激发下,Ca₄HfGe₃O₁₂∶xCr³⁺荧光粉发射出690~1 200 nm的宽带近红外光,峰值波长为825 nm (⁴T₂-⁴A₂),半高宽达到141 nm,Cr³⁺掺杂最佳浓度为0.03。依据激发光谱峰形和寿命衰减行为,证实Cr³⁺仅占据基质中一种阳离子格位。Ca₄HfGe₃O₁₂∶0.03Cr³⁺荧光粉的荧光量子效率为33.63%,该荧光粉发射光谱在400 K下的积分面积为室温下的60.5%,表明该样品具有优良的热稳定性。采用自制近红外荧光粉转换器件照射人手掌和滤波片遮挡的水果,观察到清晰地静脉血管和遮挡水果的轮廓。     

CaSb2O6:Bi3+,Eu3+荧光粉的制备和发光性质

采用共沉淀法及1 200 ℃后续煅烧4 h,成功制备了CaSb₂O₆:Bi³⁺,Eu³⁺荧光粉,并对其结构及发光性能进行了研究。所制备荧光粉颗粒为六边形类圆饼状,平均尺寸在100~600 nm之间。对CaSb₂O₆:Bi³⁺,Eu³⁺发光的机理分析表明,Bi³⁺对Eu³⁺的发光存在高效的敏化与能量传递。当Bi³⁺和Eu³⁺的掺杂浓度分别为0.5%和8%,Eu³⁺位于580 nm(⁵D₀→⁷F₀ )处的荧光发射显著增强,Bi³⁺,Eu³⁺共掺样品的荧光强度是CaSb₂O₆:Eu³⁺的10倍左右。调节Bi³⁺/Eu³⁺离子掺杂比,色坐标呈现了从蓝、白光到红光的变化,表明该荧光粉可分别作为蓝或红色荧光粉使用,甚至可实现从蓝、白光到红光的自由调控,这为白光LED荧光粉的发展提供了参考。     

Li4SrCa (SiO4)2:Eu3+红色荧光粉的合成及其发光性能

采用硅酸盐作为基质材料,通过高温固相法合成了Li₄SrCa（SiO₄）₂：Eu³⁺红色荧光粉。通过X射线粉末衍射、X射线光电子能谱、透射电镜和荧光光谱,对所得样品的物相、形貌及其发光性能进行了表征分析。结果表明,掺入Eu³⁺后,Li₄SrCa（SiO₄）₂的晶体结构并没有发生改变。在393 nm光激发下,荧光粉的荧光光谱中693 nm处发射峰强度最强。以693 nm作为监测波长,荧光激发峰分别为361 nm（⁷F₀→⁵D₄）、375 nm（⁷F₀→⁵G₃）、413 nm（⁷F₀→⁵D₃）、393 nm（⁷F₀→⁵L₆）和464 nm（⁷F₀→⁵D₂）,即样品对近紫外和蓝光有较好的吸收。利用发射光谱研究了Eu³⁺掺杂浓度（物质的量分数）对荧光粉发光强度的影响。当Eu³⁺的掺杂浓度x=0.10时,样品发射强度最强,发射红光,其色坐标为（0.637 5,0.353 7）。通过Dexter强度与浓度关系分析了浓度猝灭机制。     

双钙钛矿型Ca2Gd1-xTaO6：xTb3+绿色荧光粉的合成与荧光性质

通过高温固相法合成了双钙钛矿型Ca₂Gd_1-xTaO₆：xTb³⁺（CGTO：xTb³⁺）绿色荧光粉。采用X射线衍射、扫描电镜、荧光光谱、荧光衰减曲线、量子效率（η）测试分别表征了CGTO： xTb³⁺荧光粉的物相、形貌和荧光性质。在紫外光激发下,CGTO： xTb³⁺荧光粉实现了较强的绿光发射,绿光为Tb³⁺离子的⁵D₄-⁷F₅跃迁。通过变温发射光谱研究发现CGTO：0.15Tb³⁺荧光粉的热猝灭活化能为0.181 9 eV。在255 nm的激发下,最佳Tb³⁺掺杂浓度的CGTO：0.15Tb³⁺荧光粉的量子效率为32.32%。     

固溶体结构对Ca2-xSrxZn4Ti15O36∶Pr3+发光性质的影响

Ca_2-xSr_xZn₄Ti₁₅O₃₆∶Pr red long decay phosphor was synthesized by high temperature solid state reaction. Photoluminescence property and crystalline and unit cell parameters of the orthorhombic were investigated by fluorescence spectrophotometer and by powder X-ray diffraction, respectively. The emission intensity at 618 nm changes sharply when the concentration of Sr²⁺ (x) is less than 0.1 and the emission intensity reaches the maximum when x is equal to 0.007. There is an obviously broad excitation band at 270 nm when x is equal to 0.003 and it disappears gradually when x is over 0.01. The unit cell a parameter of Ca_2-xSr_xZn₄Ti₁₅O₃₆∶Pr decreases while c parameter increases with the increases of the concentration of the doped Sr²⁺. When x is over 0.1 the value of the unit cell parameters a and c become stable. TL peaks of Ca₂Zn₄Ti₁₅O₃₆∶Pr, Ca_1.993Sr_0.007Zn₄Ti₁₅O₃₆∶0.002Pr³⁺, 0.002Na⁺, are located at 62 ℃, 88 ℃, respectively, which indicates that there are deeper traps in Ca_1.993Sr_0.007Zn₄Ti₁₅O₃₆∶0.002Pr³⁺, 0.002Na⁺.     

Sm3+掺杂Ba0.85Ca0.15Ti0.90Zr0.10O3无铅多功能铁电陶瓷的储能和光致发光性能

通过高温固相反应法制备了Ba_0.85Ca_0.15Ti_0.90Zr_0.10O₃∶xSm³⁺(BCTZ∶xSm³⁺,x=0.0%、0.2%、0.4%、0.6%、0.8%、1.0%,物质的量分数)陶瓷,系统研究了其微观形貌、铁电性能、储能性能和光致发光性能。研究表明,Sm³⁺掺入后,陶瓷平均晶粒大小明显下降,致密度显著提高。所有陶瓷均表现出典型的铁电性。BCTZ∶xSm³⁺陶瓷放电储能密度得到了极大的提高,BCTZ∶1.0% Sm³⁺陶瓷放电储能密度较纯BCTZ陶瓷可提高约49.0%。此外,在408 nm光的激发下,BCTZ∶xSm³⁺陶瓷在596 nm左右表现出强烈的橙红色发光,且发光强度相对可调性可达449%。     

Tm3+/Er3+/Ho3+共掺SiO2-Bi2O3-AlF3-BaF2玻璃发光性能

采用高温熔融法制备了Tm³⁺/Er³⁺/Ho³⁺共掺的铋硅酸盐50SiO₂-40Bi₂O₃-5AlF₃-5BaF₂玻璃。研究了在808 nm激光器（Laser Diode）激发下Tm³⁺/Er³⁺/Ho³⁺共掺的铋硅酸盐在2 060 nm处的发光性能,同时测试及分析了该铋硅酸盐玻璃的差热特性、吸收光谱及荧光光谱。根据吸收光谱以及Judd-Oflet理论,计算了Ho³⁺的Judd-Oflet强度参数Ω_t（t=2,4,6）以及Tm³⁺/Er³⁺/Ho³⁺相应的吸收截面。铋硅酸盐玻璃中,Tm₂O₃、Er₂O₃和Ho2O3掺杂浓度分别为0.75%、1.0%和0.5%时,2 060 nm处Ho³⁺∶⁵I₇→⁵I₈发射峰强度达到最大。对Tm³⁺/Er³⁺/Ho³⁺ 3种离子的光谱性质和离子间可能存在的能量传递也做了分析。Ho³⁺在1 953 nm处的最大吸收截面σ_abs为9.08×10^-21 cm²,在2 060 nm处的最大发射截面σem为11.68×10^-21 cm²,辐射寿命τ_mea为2.75 ms,具有良好的增益效应σ_emτ（3.212×10^-20 cm^-2·ms）。     

绿色荧光粉Ca3Y2Si3O12:Tb3+,Ce3+的制备及发光特性

采用高温固相法合成了绿色荧光粉Ca₃Y₂Si₃O₁₂:Tb³⁺。XRD检测结果显示,荧光粉主晶相为Ca₃Y₂Si₃O₁₂,属单斜晶系。荧光光谱分析表明:Ca₃Y₂Si₃O₁₂:Tb³⁺硅酸盐荧光粉可以被370nm的近紫外光激发,发射绿光,主发射峰位于490nm(⁵D₄→⁷F₆),544nm(⁵D₄→⁷F₅),585nm(⁵D₄→⁷F₄)和621nm(⁵D₄→⁷F₃)。用544nm最强峰监测,得到主激发峰位于370nm的激发光谱,此光谱覆盖了300~450nm的波长范围。研究了煅烧条件、掺杂浓度及Ce³⁺共掺杂对荧光粉发光性能的影响:在1400℃下经二次煅烧6h得到的样品的发光性能最佳,Tb³⁺离子的最佳掺杂浓度为20mol%,Ce³⁺离子共掺杂能够提高荧光粉的发光强度,其最佳掺杂量为4mol%,说明存在Ce³⁺→Tb³⁺的能量传递。     

Syntheses, crystal structures and Raman spectra of Ba(BF4)(PF6), Ba(BF4)(AsF6) and Ba2(BF4)2(AsF6)(H3F4); the first examples of metal salts containing simultaneously tetrahedral BF4 and octahedral AF6 anions

In the system BaF₂/BF₃/PF₅/anhydrous hydrogen fluoride (aHF) a compound Ba(BF₄)(PF₆) was isolated and characterized by Raman spectroscopy and X-ray diffraction on the single crystal. Ba(BF₄)(PF₆) crystallizes in a hexagonal space group with a=10.2251(4) Å, c=6.1535(4) Å, V=557.17(5) Å³ at 200 K, and Z=3. Both crystallographically independent Ba atoms possess coordination polyhedra in the shape of tri-capped trigonal prisms, which include F atoms from BF₄⁻ and PF₆⁻ anions. In the analogous system with AsF₅ instead of PF₅ the compound Ba(BF₄)(AsF₆) was isolated and characterized. It crystallizes in an orthorhombic Pnma space group with a=10.415(2) Å, b=6.325(3) Å, c=11.8297(17) Å, V=779.3(4) Å³ at 200 K, and Z=4. The coordination around Ba atom is in the shape of slightly distorted tri-capped trigonal prism which includes five F atoms from AsF₆⁻ and four F atoms from BF₄⁻ anions. When the system BaF₂/BF₃/AsF₅/aHF is made basic with an extra addition of BaF₂, the compound Ba₂(BF₄)₂(AsF₆)(H₃F₄) was obtained. It crystallizes in a hexagonal P6₃/mmc space group with a=6.8709(9) Å, c=17.327(8) Å, V=708.4(4) Å³ at 200 K, and Z=2. The barium environment in the shape of tetra-capped distorted trigonal prism involves 10 F atoms from four BF₄⁻, three AsF₆⁻ and three H₃F₄⁻ anions. All F atoms, except the central atom in H₃F₄ moiety, act as μ₂-bridges yielding a complex 3-D structural network.     

Ca2+-Mg2+-Zn2+体系在水溶性聚磷酸铵溶液中螯合规律的研究

近年来,水溶性聚磷酸铵在液体肥料和复合肥料的领域受到了广泛的关注,并在发达国家中得到了大面积的推广及应用。在pH值为5.5~8.0、温度为278.15 K~323.15 K的条件下,本文采用滴定法研究Ca_²⁺-Mg_²⁺-Zn_²⁺体系在聚磷酸铵溶液中的螯合规律。实验结果表明：相同质量分数的聚磷酸铵溶液对金属离子的螯合量会随着体系中Ca_²⁺、Mg_²⁺、Zn_²⁺的摩尔浓度的变化而变化;随着温度的升高而逐渐降低;随着pH的增加而逐渐增加;随着聚合度的升高而逐渐增加。采用傅里叶红外光谱对聚磷酸铵和A₁B₃C₃体系的螯合物进行表征。     

复合催化剂上CO2加氢合成C2烃类

介绍了由CO₂+H₂合成C2⁺烃的几种复合催化剂体系的研究进展，比较和评价了复合催化剂体系的活性和选择性及对C2⁺烃类生成的影响。着重于复合催化剂体系对C4⁺烃的生成及产物分布的影响并简述反应机理。     

氨基酸-BrO-3-Mn2+-H2SO4-丙酮体系的振荡反应

This paper, Using potentiometric method, first reports the oscillating behavior of five amino acids (L-methionine, L-cystine, L-tryptophan, L-serine, L-tyrosine) in a new oscillating system of amino acid-BrO_3~--Mn~(2+)-H_2SO_4-acetone. The effect of many factors on oscillation have been investigated. According to Arrhenius equation, the apparent activation energy of the oscillatary induction period and oscillation period of five oscillating systems are obtained within temperature range of 20～37 ℃.     

La7O6(BO3)(PO4)2:Eu3+/Tb3+荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La₇O₆（BO₃）（PO₄）₂：Eu³⁺材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为⁵D₀→⁷F₂特征能级跃迁,Eu³⁺的最优掺杂浓度为0.08,对应的CIE坐标为（0.610 2,0.382 3）;La₇O₆（BO₃）（PO₄）₂：Tb³⁺材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb³⁺的⁵D₄→⁷F₅能级跃迁,Tb³⁺离子的最优掺杂浓度为0.15,对应的CIE坐标为（0.317 7,0.535 2）。此外,对2种材料的变温光谱分析发现Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂荧光材料均具有良好的热稳定性。     

PO43-掺杂Bi2O2CO3/Bi0的制备及其可见光催化性能

构建氧空位以及附着金属单质Bi(Bi⁰)是增强半导体材料光吸收性能、促进半导体光生载流子分离的有效方法。通过简单的共沉淀法及氢气热还原成功制备了PO₄^3-掺杂Bi₂O₂CO₃附着Bi⁰(Bi-P-BOC)的可见光催化剂,并对其在可见光下催化降解氧氟沙星(OFX)的性能及机理进行了研究。材料表征结果表明BOC随着PO₄^3-的均匀掺杂,可见光吸收能力增强,表面缺陷增多,比表面积增大。而随着氢气热还原,BOC表面形成 Bi⁰的同时也原位构建了大量的氧空位。可见光催化性能测试表明,Bi-P-BOC可以在180 min内降解约85%的OFX,降解速率为0.013 0 min^-1,是BOC降解速率的8倍。Bi-P-BOC光催化降解机理表明其具有更好的可见光吸收能力,Bi⁰以及氧空位的存在促进了光生载流子的分离,h+是其光催化降解过程中的主要的活性氧物种(ROS),此外,¹O₂和·O₂^-也对降解有一定贡献。     

PO43-掺杂Bi2O2CO3/Bi0的制备及其可见光催化性能

构建氧空位以及附着金属单质Bi(Bi⁰)是增强半导体材料光吸收性能、促进半导体光生载流子分离的有效方法。通过简单的共沉淀法及氢气热还原成功制备了PO₄^3-掺杂Bi₂O₂CO₃附着Bi⁰(Bi-P-BOC)的可见光催化剂,并对其在可见光下催化降解氧氟沙星(OFX)的性能及机理进行了研究。材料表征结果表明BOC随着PO₄^3-的均匀掺杂,可见光吸收能力增强,表面缺陷增多,比表面积增大。而随着氢气热还原,BOC表面形成Bi⁰的同时也原位构建了大量的氧空位。可见光催化性能测试表明,Bi-P-BOC可以在180 min内降解约85%的OFX,降解速率为0.013 0 min^-1,是BOC降解速率的8倍。Bi-P-BOC光催化降解机理表明其具有更好的可见光吸收能力,Bi⁰以及氧空位的存在促进了光生载流子的分离,h⁺是其...     

Ce3+,Tb3+,Eu3+共掺杂Sr2MgSi2O7体系的白色发光和能量传递机理

通过正交试验,采用高温固相法制备了Sr2-x-y-zMgSi2O7∶xCe3+,yTb3+,zEu3+系列样品.使用X射线衍射仪和荧光光谱仪表征了样品的物相和发光性质,并讨论了Ce3+-Tb3+-Eu3+共掺杂Sr2MgSi2O7体系中的能量传递过程.实验结果表明,在327 nm波长激发下,所合成荧光粉的发射峰主要位于387 nm(蓝紫)、542nm(绿)和611 nm(红)处;分别以387,542和611 nm为监控波长,所得激发光谱显示荧光粉在327 nm处有最好的激发.在327 nm光激发下,系列样品发光进入白光区.最优化的荧光粉为Sr1.91MgSi2O7∶0.01Ce3+,0.05Tb3+,0.03Eu3+,其色坐标为(0.337,0.313),是一种潜在的发光二极管(LED)用白色荧光粉.     

Ho3+/Yb3+共掺ZnO-Al2O3-GeO2-SiO2玻璃陶瓷的制备和上转换发光性质

综合ZnO-Al₂O₃-SiO₂系和锗酸盐玻璃陶瓷的优点,采用熔融-晶化法首次制备了Ho³⁺/Yb³⁺共掺以ZnAl₂O₄为主晶相的ZnO-Al₂O₃-GeO₂-SiO₂系玻璃陶瓷。因[GeO₄]四面体和[SiO₄]四面体都是玻璃网络形成体,讨论了GeO₂取代SiO₂对玻璃陶瓷样品硬度及发光性能的影响,最终确定GeO₂的取代量为10.55%（w/w）时,玻璃陶瓷综合性能最佳。在980 nm泵浦光的激发下,发现强的绿色（546 nm）和弱的红色（650 nm）上转换发光,并研究了不同Ho³⁺/Yb³⁺掺杂比对样品上转换发光的影响,最终结果表明当Ho³⁺/Yb³⁺掺杂比为1：11（n/n）时样品荧光强度最强,在绿色上转换发光材料方面具有潜在的应用。     

IR and Raman spectra of two layered aluminium phosphates Co(en)3Al3P4O16 · 3H2O and [NH4]3[Co(NH3)6]3[Al2(PO4)4]2 · 2H2O

The FT IR and FT Raman spectra of Co(en)₃Al₃P₄O₁₆ · 3H₂O (compound I) and [NH₄]₃[Co(NH₃)₆]₃[Al₂(PO₄)₄]₂ · 2H₂O (compound II) are recorded and analysed based on the vibrations of Co(en)₃³⁺, Co(NH₃)₆³⁺, NH₄⁺, Al---O---P, PO₃, PO₂ and H₂O. The observed splitting of bands indicate that the site symmetry and correlation field effects are appreciable in both the compounds. In compound I, the overtone of CH₂ deformation Fermi resonates with its symmetric stretching vibration. The NH₄ ion in compound II is not free to rotate in the crystalline lattice. Hydrogen bonding of different groups is also discussed.