固溶体结构对Ca2-xSrxZn4Ti15O36∶Pr3+发光性质的影响

Ca_2-xSr_xZn₄Ti₁₅O₃₆∶Pr red long decay phosphor was synthesized by high temperature solid state reaction. Photoluminescence property and crystalline and unit cell parameters of the orthorhombic were investigated by fluorescence spectrophotometer and by powder X-ray diffraction, respectively. The emission intensity at 618 nm changes sharply when the concentration of Sr²⁺ (x) is less than 0.1 and the emission intensity reaches the maximum when x is equal to 0.007. There is an obviously broad excitation band at 270 nm when x is equal to 0.003 and it disappears gradually when x is over 0.01. The unit cell a parameter of Ca_2-xSr_xZn₄Ti₁₅O₃₆∶Pr decreases while c parameter increases with the increases of the concentration of the doped Sr²⁺. When x is over 0.1 the value of the unit cell parameters a and c become stable. TL peaks of Ca₂Zn₄Ti₁₅O₃₆∶Pr, Ca_1.993Sr_0.007Zn₄Ti₁₅O₃₆∶0.002Pr³⁺, 0.002Na⁺, are located at 62 ℃, 88 ℃, respectively, which indicates that there are deeper traps in Ca_1.993Sr_0.007Zn₄Ti₁₅O₃₆∶0.002Pr³⁺, 0.002Na⁺.

Effects of Solid Solution Structures on Luminescence of Ca2-xSrxTi15O36:Pr3+