L-半胱氨酸改性Fe3O4纳米粒子的水热合成及其应用

以L-半胱氨酸为表面改性剂与粒径调节剂,采用水热法制备具有良好分散稳定性的磁性Fe₃O₄纳米粒子。通过透射电镜（TEM）、扫描电镜（SEM）、X射线衍射仪（XRD）、比磁饱和强度测定仪（VSM）等对产物进行表征,研究L-半胱氨酸对磁性Fe₃O₄纳米粒子的形貌、粒径分布、晶型结构、分散稳定性等的影响,理论推导了L-半胱氨酸改性后的Fe₃O₄纳米粒子（L-Fe₃O₄纳米粒子）的生成机制,将该材料作为载体吸附金种后探讨其在催化对硝基苯酚方面的应用。结果表明：沉降22 h时,调节pH值为7.0制备的Fe₃O₄纳米粒子的沉降高度大约是L-Fe₃O₄纳米粒子的6.5倍;吸附金种后的L-Fe₃O₄纳米粒子催化效率大约是未改性Fe₃O₄纳米粒子的5倍。L-半胱氨酸有效的改善了Fe₃O₄纳米粒子与分散介质之间的相容性,保护并改善了纳米粒子的分散稳定性,在污水处理等方面有潜在的应用。     

Electrocatalytic activity of starch/Fe3O4/zeolite bionanocomposite for oxygen reduction reaction

The present work demonstrated an eco-friendly and facile method for the preparation of starch/Fe₃O₄/zeolite-bionanocomposite (BNC) at moderate temperature. Zeolite and starch were used as solid support and stabilizer, respectively. The analysis of UV–vis showed the appearance of surface plasmon resonance. From PXRD analysis, the incorporation of magnetite nanoparticles (NPs) in zeolite substrate results in reducing of intensities and broadening of the zeolite peaks of BNC. The TEM analysis showed the formation of highly distributed Fe₃O₄-NPs with an average diameter and standard deviation of 9.24 ± 3.57 nm. The FESEM and EDX analyses imply that Fe₃O₄-NPs were homogeneously formed on the surface of the zeolite substrate. VSM analysis illustrated the as prepared BNC possessed magnetic behaviour with a saturation magnetization and coercivity of 1.84 emu g⁻¹ and 17.76 G, respectively. The prepared BNC showed potential applicability in energy as low-cost electrode material. The BNC was used as a non-precious catalyst for oxygen reduction reaction (ORR) in the alkaline medium. The presence of starch and zeolite promoted long term stability up to 1000 cycles and avoid the dissolution and agglomeration of iron oxide. The ORR commences at the onset potential of 0 V follows by the two successive reduction peaks at −0.48 V and −1.00 V.     

柠檬酸根辅助多元醇法制备直径和磁性可控的Fe_3O_4亚微球

以柠檬酸三钠作辅助剂,用多元醇溶剂热还原法制备了纳米晶粒和微球直径可控的、单分散的超顺磁Fe3O4亚微球.发现与铁原子有强亲和力的柠檬酸根能有效吸附在还原产生的初始Fe3O4纳米粒子表面,阻碍其晶粒生长和影响其静电排斥力的大小,从而能在较大范围内调控最终产物Fe3O4亚微球的直径和饱和磁化强度.改变柠檬酸根或铁盐浓度不但可以调控初始Fe3O4纳米粒子的粒径,而且可以在220-550nm范围内调控单分散Fe3O4亚微球的直径,从而得到粒径均一的超顺磁Fe3O4亚微球.     

纳米Fe2O3和Fe3O4的制备及其催化高氯酸铵热分解性能的研究——一个仪器分析综合实验

介绍一个仪器分析综合实验——纳米Fe_2O_3和Fe_3O_4的制备及其催化高氯酸铵热分解性能的研究。采用水热法合成纳米Fe_3O_4,进而煅烧得到纳米Fe_2O_3。使用X射线粉末衍射(XRD)对制得的样品结构进行表征,通过透射电镜(TEM)可以发现其为球形颗粒,粒径在10–20 nm范围内。将制得的纳米Fe_2O_3和纳米Fe_3O_4按不同比例加入高氯酸铵(AP)中,通过对混合物进行热分析(TG-DSC),发现纳米Fe_2O_3和纳米Fe_3O_4可以明显促进AP的分解,且Fe_2O_3的催化效果优于Fe_3O_4的催化效果,并对催化机理进行了简单讨论。通过该实验,可以让学生学习水热反应的方法,掌握利用XRD、热分析等多种手段对化合物结构及性能进行表征的技能。     

磁性纳米复合物的制备及对铜离子(Ⅱ)的传感检测

采用化学共沉淀法合成硅包覆的磁性纳米粒子Fe_3O_4@SiO_2,进一步通过六亚甲基二异氰酸酯将吡哆酰肼分子(Pyh)接枝到Fe_3O_4@SiO_2表面,制得功能化的磁性纳米复合物(Fe_3O_4@SiO_2-Pyh)。通过傅里叶变换红外光谱、透射电子显微镜、X射线衍射等技术手段对其结构、形貌和磁性能进行了表征。Fe_3O_4@SiO_2-Pyh粒子具有规则的核壳结构,粒径分布在50~55 nm,壳层厚度约为15 nm。Fe_3O_4@SiO_2-Pyh结构中含有酰腙类活性基团—CO—NH—N=CH—,能与Cu~(2+)形成稳定的配合物,在此基础上采用紫外可见吸收光谱特性建立了测定Cu~(2+)的分析方法,线性范围为3.4×10~(-7)~4.5×10~(-6)mol/L,检出限为1.03×10~(-7)mol/L。此外,利用Fe_3O_4@SiO_2-Pyh良好的磁响应,通过外部磁场能够有效地除去水中过量的铜离子,在环境领域具有潜在的应用价值。     

A highly selective magnetic sensor with functionalized Fe/Fe3O4 nanoparticles for detection of Pb2+

A magnetic sensor for detection of Pb~(2+) has been developed based on Fe/Fe_3O_4 nanoparticles modified by3-(3,4-dihydroxyphenyl)propionic acid(DHCA). The carboxyl groups of DHCA have a strong affinity to coordination behavior of Pb~(2+) thus inducing the transformation of Fe/Fe_3O_4 nanoparticles from a dispersed to an aggregated state with a corresponding decrease, then increase in transverse relaxation time(T_2) of the surrounding water protons. Upon addition of the different concentrations of Pb~(2+) to an aq. solution of DHCA functionalized Fe/Fe_3O_4 nanoparticles(DHCA-Fe/Fe_3O_4 NPs)([Fe] = 90 mmol/L), the change of T_2 values display a good linear relationship with the concentration of Pb~(2+) from 40 μmol/L to 100 μmol/L and from 130 μmol/L to 200 μmol/L, respectively. Owing to the especially strong interaction between DHCA and Pb~(2+), DHCA-Fe/Fe_3O_4 NPs exhibited a high selectivity over other metal ions.     

Magnetic CuO nanoparticles supported on graphene oxide as an efficient catalyst for A3-coupling synthesis of propargylamines

Magnetically separable CuO nanoparticles supported on graphene oxide (Fe₃O₄ NPs/GO-CuO NPs) is synthesized and characterized for the preparation of propargylamines in EtOH, at 90℃. Fe₃O₄ NPs/GO-CuO NPs is found to be an efficient catalyst for the A³-coupling of aldehydes, amines, and alkynes through C-H activation. Both aromatic and aliphatic aldehydes and alkynes are combined with secondary amines to provide a wide range of propargylamines in moderate to excellent yields.     

Preparation of Functionalized Fe3O4@SiO2 Magnetic Nanoparticles for Monoclonal Antibody Purification

Magnetic Fe₃O₄@SiO₂ nanoparticles with superparamagnetic properties were prepared via a reverse mi-croemulsion method at room temperature. The as-prepared samples were characterized by transmission electron mi-croscopy(TEM), X-ray diffractometry(XRD), and vibrating sample magnetometry(VSM). The Fe₃O₄@SiO₂ nanoparticles were modified by (3-aminopropyl)triethoxysilane(APTES) and subsequently activated by glutaraldehyde(Glu). Protein A was successfully immobilized covalently onto the Glu activated Fe₃O₄@SiO₂ nanoparticles. The adsorption capacity of the nanoparticles was determined on an ultraviolet spectrophotometer(UV) and approximately up to 203 mg/g of protein A could be uniformly immobilized onto the modified Fe₃O₄@SiO₂ magnetic beads. The core-shell of the Fe₃O₄@SiO₂ magnetic beads decorated with protein A showed a good binding capacity for the chime-ric anti-EGFR monoclonal antibody(anti-EGFR mAb). The purity of the anti-EGFR mAb was analyzed by virtue of HPLC. The protein A immobilized affinity beads provided a purity of about 95.4%.     

表面分子印迹磁性纳米粒子的制备及其血红蛋白传感应用

以Fe₃O₄磁性纳米粒子为载体、多巴胺（DA）为功能单体、血红蛋白（Hb）为模板分子,用氯铂酸氧化DA生成聚多巴胺（PDA）,同时氯铂酸还原为铂纳米粒子（PtNPs）,与Hb一起负载于Fe₃O₄纳米粒子表面,洗脱Hb后合成了表面分子印迹磁性纳米粒子（印迹Fe₃O₄/PDA-PtNPs）. 将印迹Fe₃O₄/PDA-PtNPs修饰于磁性玻碳基底表面,制得印迹Fe₃O₄/PDA-PtNPs修饰电极. 实验结果表明,印迹Fe₃O₄/PDA-PtNPs具有良好的水溶性,粒径分布均匀,生成的PtNPs具有良好的导电性和刚性. 用印迹Fe₃O₄/PDA-PtNPs构建的传感器对Hb具有良好的识别性,在0.14 ~ 2.7 μg·mL^-1 Hb浓度范围与交流阻抗变化值呈良好的线性关系,检出限（S/N=3）为0.05 μg·mL^-1.     

磁性印迹纳米粒子固定血红蛋白修饰磁性电极构建过氧化氢传感器

采用表面印迹技术,以磁性二氧化硅纳米粒子（Fe₃O₄@SiO₂ NPs）作为载体、血红蛋白（Hb）为模板分子、正硅酸乙酯（TEOS）为印迹聚合物单体,制备了Hb印迹Fe₃O₄@SiO₂的磁性印迹纳米粒子（MMIPs NPs）. MMIPs NPs具有磁性内核和血红蛋白印迹壳层的核壳结构,可以富集并固定Hb. 使用壳聚糖将MMIPs NPs固定于磁性电极表面,构建血红蛋白类酶生物传感器,研究了Hb对过氧化氢（H₂O₂）的催化活性. MMIPS NPS相比于磁性非印迹纳米粒子（MNIPS NPS）,催化电流增加了14.3%. 采用磁性电极,MMIPS NPS、Hb和O₂的顺磁性使得该类酶生物传感器对H₂O₂的催化电流增加了60.0%. 血红蛋白类酶生物传感器电流响应与H₂O₂浓度在25 ~ 200 μmol·L^-1间呈线性关系,检出限为3 μmol·L^-1（S/N=3）,表明该类酶传感器对H₂O₂具有良好的催化性能.     

Iron Oxide Nanoparticles: Biosynthesis,Magnetic Behavior,Cytotoxic Effect

Iron oxide nanoparticles have attracted much attention because of their superparamagnetic properties and their potential applications in many fields such as magnetic storage devices, catalysis, sensors, superparamagnetic relaxometry (SPMR), and high-sensitivity biomolecule magnetic resonance imaging (MRI) for medical diagnosis and therapeutics. In this study, iron oxide nanoparticles (Fe₂O₃ NPs) have been synthesized using a taranjabin (camelthorn or persian manna) aqueous solution. The synthesized Fe₂O₃ NPs were identified through powder X-ray diffraction (PXRD), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), field energy scanning electron microscopy (FESEM), transmission electron microscopy (TEM), energy-dispersive spectroscopy (EDX), vibrating-sample magnetometer (VSM) and Raman technics. The results show that the nanoparticles have a hexagonal structure with 20 to 60 nm in size. The cytotoxic effect of the synthesized nanoparticles has been tested upon application against lung cancer cell (A549) lines. It was found that there is no cytotoxic activity at lower concentrations of 200 μg/mL. The ability of the synthesized nanoparticles for lead removal in wastewaters was tested. Results show that highest concentration of adsorbent (50 mg/L) has maximum removal efficiency (96.73 %). So, synthesized Fe₂O₃ NPs can be a good candidate to use as heavy metals cleaner from contaminated waters.     

基于MIL-100(Fe)的磁性纳米碳材料的制备及其在内源性肽富集中的应用

以Fe₃O₄为核，采用层层自组装的方法合成核壳型Fe₃O₄@MIL-100（Fe）磁性纳米材料，经高温煅烧得到具有较大孔径（17.78 nm）、高含碳量（6.79%）的磁性纳米材料Fe₃O₄@MC。将该材料用于多肽的富集，并通过基质辅助激光解吸电离飞行时间质谱仪（MALDI-TOF MS）进行鉴定。Fe₃O₄@MC材料从牛血清白蛋白（BSA）酶解液中富集得到33条肽段，且具有较高的选择性（BSA酶解液与BSA的质量比为1：400），用于人血清中内源性肽段的分离富集也取得了较好的效果。     

Effective Removal of Tetracycline by Using Biochar Supported Fe3O4 as a UV-Fenton Catalyst

Novel Fe3O4-decorate hierarchical porous carbon skeleton derived from maize straw(Fe3O4@MSC)was synthesized by a facile co-precipitation process and a calcination process,which was developed as a UV assisted heterogeneous Fenton-like catalyst.The as-synthesized catalysts were characterized via X-ray powder diffraction(XRD), scanning electron microscope(SEM),transmission electron microscope(TEM),Brunauer-Emmet-Teller(BET)and vibrating sample magnetometer(VSM)at room temperature.The morphology and structure analysis revealed that the as-prepared Fe3O4@MSC retained the original pore morphology of the maize straw material.The non-uniform poly- hedral Fe3O4 grew on the whole surface of the MSC,which reduced the aggragation of Fe3O4 and provided more active sites to strengthen the UV-assisted Fenton-like reaction.As a result,the tetracycline(TC)degradation efficiency after 40 min reaction and total organic carbon(TOC)removal efficiency after 2 h reaction of Fe3O4@MSC catalyzing UV-Fenton system reached 99.2%and 72.1%,respectively,which were more substantial than those of Fe3O4@MSC/H2O2(31.5%and 2%),UV/H2O2 system(68%and 23.4%)and UV/Fe3O4/H2O2(80% and 37.5%).The electron spin resonance(ESR)results showed that the ·OH played an important role in the catalytic reaction.A possible degradation pathway of TC was proposed on the basis of the identified intermediates.Overall,the UV assisted heterogeneous Fenton-like process in Fe3O4@MSC improved the cycle of Fe^3+/Fe^2+ and activated the interfacial catalytic site,which eventually realized the enhancement of degradation and mineralization to tetracycline.     

基于介孔Fe3O4@mSiO2@Cu2+磁性纳米粒子的固相萃取-高效液相色谱法测定水中微囊藻毒素

通过水热合成和常温合成的方法制备了介孔Fe₃O₄@mSiO₂@Cu²⁺磁性复合纳米粒子(NPs),其具有均匀的尺寸大小、良好的磁性能和特异的选择性。本研究将合成的NPs用作磁性固相萃取(MSPE)介质,结合高效液相色谱(HPLC)发展了一种测定水样品中痕量微囊藻毒素MC-LR的方法。在优化MSPE和HPLC条件后,该方法在0.1~15 μg/L范围内呈现良好的线性,线性相关系数(r)为0.9994,检出限为0.025 μg/L,定量限为0.082 μg/L。进一步将该方法用于水样中痕量藻毒素分析,结果发现回收率达到78%。这一结果表明:制得的磁性纳米粒子具有良好的萃取性能,可有效用于水样中痕量藻毒素的测定。     

Fast synthesis of dopamine-coated Fe3O4 nanoparticles through ligand-exchange method

A fast approach was described for the synthesis of water-dispersible monodisperse dopamine-coated Fe₃O₄ nanoparticles（DA-Fe₃O₄） with uniform size and shape via ligand-exchange of oleic acid on Fe₃O₄ using only 2 min.The prepared DA-Fe₃O₄ nanoparticles were characterized by transmission electron microscopy,Fourier transform infrared spectrometry,and vibrating sample magnetometer.The results indicated that the resulting DA-Fe₃O₄ nanoparticles had an average diameter of about 19.2 nm. The magnetic saturation value of the prepared DA-Fe₃O₄ nanoparticles was determined to be 72.87 emu/g,which indicating a well-established superparamagnetic property.     

Application of response surface methodology for optimization of Orange Ⅱ removal by heterogeneous Fenton-like process using Fe_3O_4nanoparticles

In this study, Fe3O4nanoparticles（Fe3O4NPs） were successfully prepared via oxidation–precipitation method and characterized by scanning electron microscopy（SEM）, X-ray diffraction（XRD） and Fourier transform infrared spectroscopy（FT-IR）. The characterization results indicated that Fe3O4 NPs with regular crystal structure and a narrow of diameters had been synthesized successfully and had high purity. A series of experiments were carried out to investigate the degradation of Orange II by the obtained heterogeneous Fe3O4 catalysts in the presence of H2O2. The response surface methodology（RSM） based on Box–Behnken design（BBD） was employed to design and optimize individual and interactive effects of the four main independent parameters（catalyst loading, initial p H, reaction temperature and H2O2concentration） on decolorization efficiency of Orange II. A significant quadratic model（p-value 〈0.0001, R2= 0.9369） was derived using analysis of variance（ANOVA）. Optimum conditions were catalyst loading of 1.5 g/L, initial p H of 2.7, reaction temperature of 42 8C and H2O2 concentration of 22 mmol/L, respectively. The predicted decolorization rate under the optimum conditions as determined by the proposed model was 99.55%. Confirmatory tests were carried out and the decolorization rate of 99.49% was observed under the optimum conditions, which agreed well with the model prediction.     

Magnetic responsive polymer nanofiber composites for easy collecting chemical spills

We describe a simple method to prepare magnetic responsive polydivinylbenzene(PDVB)nanofiber composites by precipitated cationic living polymerization in the present of oleic acid capped Fe3O4 nanoparticles(NPs).The Fe3O4 NPs are encapsulated with the PDVB forming dendrites,from which thin nanofibers are grown in the tip-growth mode.The thin nanofibers are interwoven with the thick nanofibers forming robust composite network.The composites are magnetic responsive and highly efficient to gel almost all chemicals.Separation of the gelled chemicals from water becomes easier with a magnet.The performance is promising for magnetic collection of chemical spills.     

Nanosized Pd assembled on superparamagnetic core–shell microspheres:Synthesis,characterization and recyclable catalytic properties for the Heck reaction

A series of magnetically recyclable Pd/Fe3O4@g-Al2O3 catalysts were synthesized using the superparamagnetic Fe3O4@g-Al2O3core–shell microspheres as the supporter and nano-Pd particles assembled on g-Al2O3 shell as the active catalytic component.The structure of the catalysts was characterized by X-ray diffraction(XRD),transmission electron microscopy(TEM),N2adsorption–desorption and vibrating sample magnetometer(VSM).The catalytic activity and the recyclability properties of the catalysts for the Heck coupling reaction with aryl bromides and the olefins were investigated.The results show that the microspheres of the magnetic Pd/Fe3O4@g-Al2O3 catalysts were about 400 nm and the nano-Pd particles assembled on g-Al2O3 shell were about 3–4 nm in size.The saturation magnetization(MS) of the magnetic catalysts was sufficiently high to allow magnetic separations.In the Heck coupling reactions,the magnetic Pd/Fe3O4@g-Al2O3 catalysts exhibited good catalytic activity and recyclability.With Pd/Fe3O4@g-Al2O3(0.021 mol%) catalyst,the bromobenzene conversion and product yield reached about 96.8% and 91.2%,respectively,at 120 8C and in 14 h.After being recycled for six times,the conversion of bromobenzene and the recovery of the catalyst were about80% and 90%,respectively.The nano-Pd particles were kept well dispersed in the used Pd/Fe3O4@g-Al2O3 catalysts.     

磁性荧光双功能复合纳米粒子Fe3O4@SiO2@ZrO2:Tb3+的合成和表征

通过原位反应合成法成功合成了一种新型水溶性的磁性荧光复合纳米粒子Fe₃O₄@SiO₂@ZrO₂:Tb³⁺,并通过扫描电子显微镜(SEM)、X射线粉末衍射仪(XRD)、红外光谱仪(FT-IR)、磁性测试仪和荧光(PL)光谱对其形貌、尺寸、相组成、磁性和荧光性能进行了表征。 结果表明,核(Fe₃O₄@SiO₂)壳(ZrO₂:Tb³⁺)结构组成的磁性荧光复合纳米粒子具有超顺磁性,其饱和磁化强度达到36 emu/g,并且在494 nm(⁵D₄→⁷F₆)、549 nm(⁵D₄→⁷F₅)、587 nm(⁵D₄→⁷F₄)和625 nm(⁵D₄→⁷F₃)处具有4个Tb³⁺特有的荧光发射光谱带峰值。 磁性荧光双功能的复合纳米粒子在生物医学领域具有潜在的应用价值。     

原位限域合成介孔碳负载四氧化三铁纳米颗粒

利用废弃蟹壳做模板制备的具有均一孔道结构的介孔碳材料做载体,在孔道内限域原位合成四氧化三铁氧化物纳米颗粒。 通过扫描电子显微镜(SEM)、透射电子显微镜(TEM)和X射线衍射(XRD)表征了材料的结构和性能。 结果表明,孔道结构呈整体式结构,孔直径在40~50 nm,长50~200 μm。 纳米颗粒为四氧化三铁,粒径在10 nm左右,尺寸单分散性好,可均匀分散在介孔孔道内。 该方法工艺路线简单,绿色环保。