基于应变能的复杂应力场低周疲劳分析

塑性应变能使材料微观组织结构发生不可逆变化,从而引起等效宏观应力,该应力随循环加载而增大．假定材料疲劳源处破坏是由最大拉应力引起的,最大等效宏观应力与外加应力叠加达到材料本征断裂应力时形成微裂纹．微裂纹引起上述两部分应力变化,继续加载直至宏观裂纹出现,从而得到材料的疲劳寿命．本文所建立的多轴疲劳寿命公式包含材料参数、拉应力以及塑性应变能等,以上数据可通过单轴疲劳数据和有限元方法获得．通过对SM45C材料的计算验证,表明该模型对多轴随机应变加载低周疲劳寿命,具有良好的预测结果．     

Q345低周疲劳性能与疲劳寿命预测分析

本文对结构用钢Q345的低周疲劳性能进行了试验研究。试验在常温下岛津电液伺服疲劳试验机上进行,采用轴向应变控制方法,恒定应变速率为0.005s-1,应变比为-1。试验结果表明,初始阶段,Q345在高应变幅值(0.6%)循环作用下出现循环硬化效应,而在低应变幅值(0.6%)作用下出现循环软化效应;随着加载应变幅的增加,硬化和软化率呈直线上升趋势。Q345疲劳裂纹萌生阶段占其整个寿命的60%以上,其裂纹萌生寿命与应变幅存在幂函数关系。根据Coffin-Manson公式得到了Q345的应变-寿命关系公式;采用能量预测法得到了材料的塑性应变能与疲劳寿命的关系表达式。上述结果对钢结构的设计、评估具有重要的工程应用参考价值。     

An experimental approach to low-cycle fatigue damage based on thermodynamic entropy

This paper presents an experimental approach to fatigue damage in metals based on thermodynamic theory of irreversible process. Fatigue damage is an irreversible progression of cyclic plastic strain energy that reaches its critical value at the onset of fracture. In this work, irreversible cyclic plastic energy in terms of entropy generation is utilized to experimentally determine the degradation of different specimens subjected to low cyclic bending, tension-compression, and torsional fatigue. Experimental results show that the cyclic energy dissipation in the form of thermodynamic entropy can be effectively utilized to determine the fatigue damage evolution. An experimental relation between entropy generation and damage variable is developed.     

A new distortion energy-based equivalent stress for multiaxial fatigue life prediction

A new equivalent stress amplitude expression has been developed for the assessment of fatigue life in components under multiaxial loading. The expression was generated by incorporating non-linear/plastic stress–strain relation into a mechanical energy calculation, and then applying the calculation to the distortion energy theory for a cyclic loading case. Therefore, the new uniaxial equivalent stress expression determines an appropriate stress amplitude value for multiaxial cyclic loading. The purpose of the equivalent stress value is to determine multiaxial fatigue failure using an energy-based fatigue life prediction criterion. The governing understanding behind the criterion states that the physical damage quantity for failure is equal to the accumulated strain energy in a monotonic fracture, which is also equal to the accumulated strain energy during fatigue failure. Using the new equivalent stress amplitude expression and the energy-based life prediction method, a comparison is made between prediction results and multiaxial empirical data. The multiaxial data was acquired by a vibration-based biaxial bending fatigue test and a torsion fatigue test with an assumed axial misalignment. The results of the comparison provide encouragement regarding the capability of the newly developed equivalent stress amplitude expression for fatigue life prediction.     

Plastic Strain Energy Model for Rock Salt Under Fatigue Loading

The fatigue test for rock salt is conducted to investigate the effects of stress amplitude, loading frequency and loading rate on the plastic strain energy, from which the evaluation rule of the plastic strain energy is analyzed, which is divided into three stages: cyclic hardening,saturation and cyclic softening. The total accumulated plastic strain energy only depends on the mechanical behavior of rock salt, but is immune to the loading conditions. A novel model for fatigue life prediction is proposed based on the invariance of the total plastic dissipation energy and the stability of the plastic energy per cycle.     

基于电能耗散的金属材料疲劳损伤测量

根据电磁学原理，提出了基于电能耗散的疲劳损伤定义，指出其较能反映金属材料疲劳损伤的特征。获得了用电阻变化测量疲劳损伤的公式，应用计及疲劳极限和循环应力幅影响的非线性累积疲劳损伤模型，给出了金属材料疲劳损伤的剩余寿命预测公式。通过正火45^#碳钢的旋转弯曲疲劳试验，验证了本文提出的剩余寿命预测公式的可靠性，和韧性耗散测量疲劳损伤相比较；说明了用电阻测量疲劳损伤的合理性。     

一种考虑非比例附加损伤的多轴低周疲劳模型

在实际工作环境中,机械结构往往承受着多轴非比例循环载荷.相比多轴比例循环加载,多轴非比例循环加载由于产生了附加强化现象,造成机械结构疲劳寿命下降.通过分析薄壁圆筒管件在非比例加载工况下应力应变变化规律和发生破坏位置,本文基于临界面法提出一种考虑多轴非比例附加损伤的疲劳模型.该模型将最大剪切应变幅平面作为临界面,提出一个新的附加强化因子,结合临界面上切应变幅和正应变幅组成新的多轴疲劳损伤参量.此参量不仅考虑了非比例加载下临界面上正应变幅和切应变幅对材料造成的疲劳损伤,还考虑到应变路径的变化和材料非比例加载敏感特性对材料疲劳寿命的影响.考虑到实际情况下模型所需材料附加强化系数有时难以获得的情况,给出了材料附加强化系数的有关近似计算公式.只需要材料基本力学参数便可得到材料附加强化系数,方便工程实际应用.采用8种材料的多轴疲劳寿命数据对提出的新模型进行检验,结果表明所提出的新模型与传统多轴疲劳模型相比预测寿命精度更高.      

Fatigue life predictions by integrating EVICD fatigue damage model and an advanced cyclic plasticity theory

An event independent cumulative damage (EVICD) fatigue prediction model was previously developed for the fatigue damage prediction under general multiaxial stress state and loading conditions. The model takes the plastic strain energy as the major contributor to the fatigue damage. The application of the EVICD model does not require a cycle counting method for general random loading. In the current effort, derivations were made to explicitly and directly relate the material constants in the fatigue model to the parameters in the Manson–Coffin equations and the cyclic stress–strain curve of the material. In addition, an advanced cyclic plasticity theory was implemented for the determination of the detailed stress–strain response that was required as the input for the EVICD fatigue model. Three metallic materials were used to demonstrate the capability of the modified fatigue model for the predictions of fatigue lives under different loading conditions. The results show that the fatigue model can provide fatigue life predictions in close agreement with the experimental observations.     

An Energy Based Fatigue Life Prediction Framework for In-Service Structural Components

An energy based fatigue life prediction framework has been developed for calculation of remaining fatigue life of in service gas turbine materials. The purpose of the life prediction framework is to account aging effect caused by cyclic loadings on fatigue strength of gas turbine engines structural components which are usually designed for very long life. Previous studies indicate the total strain energy dissipated during a monotonic fracture process and a cyclic process is a material property that can be determined by measuring the area underneath the monotonic true stress-strain curve and the sum of the area within each hysteresis loop in the cyclic process, respectively. The energy-based fatigue life prediction framework consists of the following entities: (1) development of a testing procedure to achieve plastic energy dissipation per life cycle and (2) incorporation of an energy-based fatigue life calculation scheme to determine the remaining fatigue life of in-service gas turbine materials. The accuracy of the remaining fatigue life prediction method was verified by comparison between model approximation and experimental results of Aluminum 6061-T6. The comparison shows promising agreement, thus validating the capability of the framework to produce accurate fatigue life prediction.     

Analysis of Strain Energy Behavior Throughout a Fatigue Process

The dissipation of strain energy density per cycle was analyzed to understand its trend through a fatigue process. The motivation behind this analysis is to improve a fatigue life prediction method, which is based on a strain energy and failure correlation. The correlation states that the same amount of strain energy is dissipated during both monotonic fracture and cyclic fatigue. This means the summation of strain energy density per cycle is equal to the total strain energy density dissipated monotonically. In order to validate this understanding, the strain energy density per cycle was analyzed at several alternating stress levels for fatigue life of Aluminum 6061-T6 (Al 6061-T6) between 10³ and 10⁵ cycles. The analysis includes the following: Alternating between high and low operating frequencies (50x magnitude difference), interruption of cyclic load during testing, and idle/zero-loading intervals of 20–40 minutes in-between cyclic loading sequences. All experimental results show a consistent trend of cyclic softening as the loading cycles approach failure; however, due to an inefficient curve fit procedure of the stress-dependent strain equation at low alternating stresses onto the experimental stress-strain data, a new approach for calculating the strain energy density per cycle is explored and shows promising results.     

镍基单晶合金多轴非比例加载低周疲劳研究

基于正交设计, 分别在680℃和850℃下进行DD3镍基单晶合金薄壁圆管试样([001]取向)拉/扭非比例加载低周疲劳试验, 研究等效应变范围、应变路径角、拉/扭载荷相位角、循环特性和温度诸因素对镍基单晶合金多轴低周疲劳寿命的影响作用. 疲劳试验数据的极差分析表明, 应变路径角、拉/扭载荷相位角和等效应变范围是影响疲劳寿命的主要因素. 将菱形应变加载路径区分为比例加载段和非比例加载段, 提出了表征非比例加载效应的等效应变参量, 并通过引入单晶应变三轴性因子反映拉/扭应变路径角对多轴疲劳寿命的影响. 用考虑非比例加载效应的等效应变范围和单晶应变三轴性因子构造循环塑性应变能损伤参量, 进行多元线性回归分析, 疲劳寿命回归模型与试验寿命具有很好的相关性, 所有试验数据都落在2.0倍的偏差分布带之内.      

孔边循环应变与疲劳循环次数相关性实验研究

材料的应变疲劳寿命与裂端的塑性应变有关。研究孔边循环应变与疲劳循环次数的相关性,对于研究材料损伤及微裂纹的产生,预防宏观裂纹的产生及扩展具有十分重要的意义。所以本文对有限宽板中心带孔试件进行了拉伸疲劳试验,用以研究这种相关性。在疲劳试验前首先进行逐级的加、卸载缓慢循环实验,同时利用数字图像相关技术测量孔周的位移场,进而求出孔边应变。在疲劳试验过程中,每当疲劳循环1500次就停机,进行同样的缓慢循环实验,并测量出孔周的位移场及孔边应变。实验研究中获得了一些很重要的结果。     

New approach based on continuum damage mechanics with simple parameter identification to fretting fatigue life prediction

A new continuum damage mechanics model for fretting fatigue life prediction is established. In this model, the damage evolution rate is described by two kinds of quantities. One is associated with the cyclic stress characteristics obtained by the finite element(FE) analysis, and the other is associated with the material fatigue property identified from the fatigue test data of standard specimens. The wear is modeled by the energy wear law to simulate the contact geometry evolution. A two-dimensional(2D) plane strain FE implementation of the damage mechanics model and the energy wear model is presented in the platform of ABAQUS to simulate the evolutions of the fatigue damage and the wear scar. The effect of the specimen thickness is also investigated. The predicted results of the crack initiation site and the fretting fatigue life agree well with available experimental data. Comparisons are made with the critical plane SmithWatson-Topper(SWT) method.     

Uniaxial ratcheting and fatigue failure of tempered 42CrMo steel: Damage evolution and damage-coupled visco-plastic constitutive model

Uniaxial ratcheting and fatigue failure of tempered 42CrMo steel were observed by the tests under the uniaxial stress-controlled cyclic loading with non-zero mean stress [G.Z. Kang, Y.J. Liu, Mater. Sci. Eng. A 472 (2008) 258–268]. Based on the obtained experimental results, the evolution features of whole-life ratcheting behavior and low-cycle fatigue (LCF) damage of the material were discussed first. Then, in the framework of unified visco-plasticity and continuum damage mechanics, a damage-coupled visco-plastic cyclic constitutive model was proposed to simulate the whole-life ratcheting and predict the fatigue failure life of the material presented in the uniaxial stress cycling with non-zero mean stress. In the proposed model, the damage was divided into two parts, i.e., elastic damage and plastic damage, which were described by the evolution equations with the same form but different constants, since the maximum applied stresses in most of loading cases were lower than the nominal yielding strength of the material. The ratcheting of the material was still described by employing a nonlinear kinematic hardening rule based on the Abdel-Karim–Ohno combined kinematic hardening model [M. Abdel Karim, N. Ohno, Int. J. Plast. 16 (2000) 225–240] but extended by considering the effect of damage. The maximum strain criterion combined with an elastic damage threshold was employed to determine the failure life of the material caused by two different failure modes, i.e., fatigue failure (caused by low-cycle fatigue due to plastic shakedown) and ductile failure (caused by large ratcheting strain). The simulated whole-life ratcheting behavior and predicted failure life of tempered 42CrMo steel are in a fairly good agreement with the experimental ones.     

考虑非比例附加损伤的多轴低周疲劳寿命模型

基于临界面法, 提出了一种能够反映非比例疲劳寿命锐减现象的多轴低周疲劳寿命模型. 与传统临界面模型只考虑附加强化效果不同, 新的模型在疲劳损伤参量中引入新定义的非比例附加损伤系数, 能综合考虑非比例加载条件下附加强化和载荷路径两种因素对疲劳寿命减少的影响, 并且分别以最大切应变和最大损伤平面作为临界面来构建疲劳损伤参量, 反映了临界面的选取对模型预测结果的重要影响. 从已发表文献中选用8 种材料的多轴疲劳试验结果进行验证, 新模型能同时适用于比例和非比例加载, 并且具有很好的寿命预测精度和材料适用性.      

扭转预应变对35CrMo钢低周疲劳性能的影响

自行设计了疲劳和扭转两用的试样,通过对试件预扭转不同的角度,系统研究35CrMo钢在不同扭转预应变下的低周疲劳性能,分析了扭转预应变后35CrMo钢的循环硬化软化特性、滞后回线、塑性应变能及循环弹性模量的变化规律,并对疲劳断口进行扫描电镜分析。结果表明:4种预扭转处理过的试件均表现出明显的循环软化行为,且循环软化规律及衰减的程度基本相同;循环应力范围及疲劳寿命随着预扭转角的增大而降低;应力应变滞后回线中加卸载曲线间的宽度随着预扭转角的增大而减小;塑性应变能都随着循环次数的增大而增加,且随着预扭转角的增大其增大速率下降;循环弹性模量都随着循环次数的增加而逐渐降低,且随着预扭转角的增大其衰减趋势减缓。     

复杂应力状态镍基单晶合金低周疲劳损伤模型

根据连续介质损伤力学理论,采用应变能释放率作为热力学广义力描述正交异性材料的疲劳损伤过程,引入取向函数考虑镍基单晶合金晶体取向对疲劳损伤的非线性影响,提出了一个各向异性疲劳损伤模型。应用多元线性回归分析方法,拟合疲劳试验数据可确定模型参数。从应变能释放率的应变空间表达式出发,导出了含有3个弹性常数的单晶合金应变三轴性因子,它既反映了材料性能的晶体取向相关性,又反映了正应力和剪应力的相互作用,并可退化为各向同性材料的应变三轴性因子。利用该模型对CMSX-2镍基单晶合金在应力控制对称循环拉-扭载荷作用下的低周疲劳寿命进行预测,预测值与试验值吻合的相当好,试验所得数据均落在2.2倍偏差的分布带内。     

高温合金材料循环相关热机械疲劳寿命预测

在变温非线性运动强化规律所描述的高温合金材料热机械寿命应力－应变循环特性的基础上，讨论了应变控制的循环相关热机械疲劳寿命预测技术，所建模型采用了由应变以密度表示的损伤参数，并且引入了温度损伤系数，考虑了温度变化范围以及温度循环和应变循环相位关系对疲劳寿命的影响，在确定模型的一些参数，采用等温力学试验和疲劳试验的数据，为了把等温疲劳研究成果推广到变温疲劳分析领域，开辟了新的途径。     

考虑塑性应变记忆恢复的循环棘轮本构模型研究

在统一粘塑性循环本构理论框架下,以Ohno-Abdel-Karim非线性随动硬化模型为基础,建立了一个循环本构模型。模型通过引入塑性应变幅值记忆效应,并在塑性应变记忆项中加入恢复系数,提高了对循环硬化材料单轴棘轮行为的预言能力。将模型应用于316L不锈钢单轴棘轮行为的描述中,模拟不同平均应力、应力幅值下的棘轮应变,均与实验数据吻合较好,证明本文改进的本构模型能合理地描述循环硬化材料的单轴棘轮行为。