表面活性剂含量对全息聚合物分散液晶光栅电光特性的影响

研究了含表面活性剂Actyflon-G04的全息聚合物分散液晶透射光栅的表面形貌和电光特性,通过理论分析得出驱动电压和膜的锚定能及表面自由能的关系.实验结果表明,在Actyflon-G04含量为4wt%-8wt%时光栅相分离程度高,相界面平滑,聚合物层的致密度增加.光栅的衍射效率达到96%,接近理想值.实现了在提高光栅衍射效率的同时降低驱动电压,使光栅的电光特性得到改善.     

纳米银掺杂的高效率全息聚合物分散液晶光栅制备

报道了一种基于掺杂纳米银聚合物分散液晶(PDLC)材料的高衍射率全息电控光栅的制备及特性。通过在原有聚合物分散液晶材料体系中添加适量的纳米银颗粒以制备体全息光栅,实验研究了掺杂不同质量比的纳米银颗粒对全息聚合物分散液晶(H-PDLC)体光栅的衍射效率、驱动阈值电压、响应时间的影响。实验结果表明,通过掺杂纳米银材料,能够优化聚合物和液晶两相分离结构,使聚合物与液晶分离更加彻底,显著提高H-PDLC体光栅的一级衍射效率,同时能改善体光栅的电光特性,缩短响应时间。初步分析表明,由于纳米银颗粒的表面等离子体效应和体系折射率匹配的优化改善了H-PDLC光栅的特性。     

表面垂直取向对HPDLC光栅特性的影响

为了提高聚合物/液晶（HPDLC）光栅的衍射效率并改善光栅的表面形貌,研究了表面垂直取向处理对HPDLC光栅的影响。首先,研究了表面垂直处理对液晶分子的取向作用,发现垂直取向层对液晶的锚定作用随着盒厚的增加而逐渐减弱,取向层的作用范围大概在3 m ~5 m之间;其次,对相分离程度进行了实验表征,结果表明,随着液晶盒厚度的增加,相分离开始的时间越来越快,并且分离程度也越来越彻底。最后,讨论了表面垂直取向对HPDLC光栅衍射效率的影响,随着盒厚的增加,相分离出来的液晶微滴形成连续的区域,光栅的衍射效率逐渐升高,当盒厚增加到一定程度,其衍射效率和无取向处理的光栅接近。当盒厚过大时,垂直取向处理对HPDLC光栅散射损失并没有太大的改善,只有当盒厚适中（12 m）时,光栅的衍射效率最高,散射损失最小。     

电控聚合物分散液晶变焦全息透镜制作

介绍了相位型全息聚合物分散液晶(PDLC)材料全息透镜,在电场作用下液晶微滴折射率逐渐与聚合物折射率匹配,实现透镜电控变焦。研究了微米尺寸和纳米尺寸液晶微滴聚合物分散液晶材料配方特性和微观结构。采用优化纳米尺寸材料配方制作5~6μm聚合物分散液晶盒,采用离轴式平面波和球面波干涉全息写入光路,成功制作电控变焦聚合物分散液晶全息透镜样品。该透镜样品焦距为20 mm,能够正一级衍射放大成像。实现“0”,“1”变焦的驱动电压阈值为60 V。并进一步提出了基于聚合物分散液晶电控变焦元件集成叠加技术实现电控变焦光学成像系统的技术思路。     

聚合物分散液晶光栅的制备实验

把夹预聚物分散液晶的玻璃用菲林掩膜遮盖,在紫外灯下进行弱准直光曝光,使液晶和聚合物产生相分离,形成聚合物分散液晶光栅。并采用偏光显微镜对光栅的形貌进行检测,利用激光笔对光栅的电光特性进行测定,证明衍射效率具有电场可调谐性。实验方法简单易操作,现象明显,在光栅常数较大时可以明显看到衍射效果,对液晶物理专业基础实验的教学具有参考意义。     

双重复合式液晶/聚合物电调谐光栅的制备

采用一次性全息曝光的方法同时在样品上制备了周期分别为1μm和4μm,衍射效率电场可调的双重复合式液晶/聚合物光栅.使用He-Ne激光器对复合光栅的衍射特性进行了实验研究,发现光栅存在两个1级衍射极强峰.对峰值衍射效率的测定结果表明,周期1μm的光栅衍射效率为90%,周期4μm的光栅,60%.结合耦合波理论计算了周期1μm和4μm光栅的衍射效率理论值,分别为92.57%和63.68%.实验结果与理论值符合得非常好.对电光特性的测试表明该复合光栅内的两套子光栅的驱动电压V₉₀关键词： 光栅 液晶     

NVP在全息聚合物分散液晶光栅中的反应动力学研究

为了提高全息聚合物分散液晶(简称HPDIC)光栅的衍射效率并得到良好的光栅表面形貌,在制备光栅的反应体系中添加了具有吡咯烷酮结构的单官能度小分子NVP,并进一步阐述了NVP对HPDLC光栅在反应动力学方面的影响.分析表明,NVP的添加显著增加了预聚单体的聚合速率,并且能使原本被困在聚合物网络当中的双键继续发生反应,从而大大提高了反应体系的双键转化率;另外,NVP的添加使得光栅的相分离更加彻底,在获得良好的表面形貌的同时也增大了光栅的折射率调制度,从而提高了HPDLC光栅的衍射效率.总之,在添加了NVP之后,体系的聚合速率和预聚单体的反应度都大大提高,从而使得光栅的表面形貌和衍射效率也得到较大的改善和提高,衍射效率提高到96.36%.     

基于聚合物分散液晶全息光栅的可调增益均衡器

从理论和实验两方面分析研究了聚合物分散液晶全息光栅在632.8 nm光波的入射下的衍射谱特性和电压可调特性，实验结果与耦合波理论的计算结果具有很好的一致性，从实验上验证了用耦合波理论来描述聚合物分散液晶全息光栅的衍射特性是恰当的.并且提出了利用聚合物分散液晶全息光栅对掺饵光纤放大器增益谱进行平坦化的方法，利用聚合物分散液晶全息光栅的电压可调特性可实现动态增益均衡.运用该方法，可使掺饵光纤放大器在C波段1530~1560 nm内，温度在0℃~65℃范围内变化，掺饵光纤放大器自发辐射谱的不平坦度从3.3 dB降到0.2 dBp－p（峰-峰值）.     

一次曝光法制备二维电调谐聚合物液晶光栅

采用四光束一次曝光法制备了二维电调谐聚合物分散液晶光栅,实验表明该方法制备的二维光栅具有非常好的电光特性,其衍射图样为空间点阵且衍射效率可以通过电场进行调节;偏光显微镜和原子力显微镜表明光栅中的液晶和聚合物在二维空间上呈周期性分布.同时利用二维衍射模型对二维光栅的电光特性进行了理论模拟,得到理论模拟的结果与实验结果相吻合.     

一次曝光法制备二维电调谐聚合物液晶光栅

采用四光束一次曝光法制备了二维电调谐聚合物分散液晶光栅,实验表明该方法制备的二维光栅具有非常好的电光特性,其衍射图样为空间点阵且衍射效率可以通过电场进行调节|偏光显微镜和原子力显微镜表明光栅中的液晶和聚合物在二维空间上呈周期性分布.同时利用二维衍射模型对二维光栅的电光特性进行了理论模拟,得到理论模拟的结果与实验结果相吻合.     

Biodegradable Holographic Polymer-Dispersed Liquid Crystal

The a-D-glucose was chemically modified with an allyl isocyanate (MG) and introduced into the polymer matrix for holographic polymer-dispersed liquid crystal (HPDLC), and the effects were studied in terms of morphology, grating formulation dynamics and electro-optical and biodegradable properties. Phase separation and diffraction efficiency increased at low content of (MG ≤ 4 wt%), while a rapid increase in crosslink density entrapped the LC droplets within the polymer to give poor phase separation, small droplet size, and low diffraction efficiency at high content. The HPDLC film was driven only with the addition of MG due to the increased droplet size with a minimum driving voltage of 18 V at 6.0 wt% MG. With the addition and an increasing amount of MG, the biodegradation of the composite film in a buffer solution was significantly increased in proportion to its amount.     

High dielectric anisotropy compound doped transmission gratings of HPDLC

Effects of high dielectric anisotropy compound (MLC) and oligomer molecular weight on the grating formation and electro-optical properties of transmission holographic polymer dispersed liquid crystal (HPDLC) have been studied. Addition of MLC reduced the response time and switching voltage with the increased formulation viscosity which introduced a sequence of phenomenon, i.e. slow diffusion, polymerization, phase separation, grating formation, and droplet coalescence giving small droplet size and enhanced diffraction efficiency of the film. Apparently, increase in oligomer molecular weight gave effects similar to those of increasing MLC content since both variables control droplet coalescence through different mechanisms.     

全息聚合物弥散液晶器件电光特性的研究

研究了全息聚合物弥散液晶(HPDLC)器件的电光特性，研究了添加不同表面活性剂对聚合物界面对液晶的锚定能的影响机理，寻求到了低工作电压的实现方法. 分析了聚合物基体与液晶折射率不匹配性对器件对比度的影响，测量了HPDLC器件的响应时间和弛豫时间，得到了平均100μs的快速响应. 关键词： 全息聚合物弥散液晶 电光特性 表面活性剂 对比度 响应时间     

基于液晶/聚合物光栅的高转化效率有机半导体激光器

采用有机半导体发光材料聚[2-甲氧基-5-(2-乙基己氧基)-1,4-苯乙炔]作为增益介质,低官能度光敏单体制备的液晶/聚合物光栅作为外部反馈谐振腔,制备出参数可独立控制的分离式结构的有机半导体激光器.液晶/聚合物光栅中液晶分子的取向影响光栅折射率调制量,从而影响光栅的反馈能力,最终影响激光器出射激光的性能.通过研究发现决定液晶分子取向的主要有两种与光栅周期有关的作用力,利用这一原理制备不同周期的光栅,光栅周期小于450 nm时,相分离出的液晶分子取向由光栅矢量方向变为光栅沟槽方向,此时光栅的折射率调制量增加,光反馈能力增强.采用周期为395 nm的液晶/聚合物光栅制备二级布拉格散射的有机半导体激光器,相较于大周期光栅(593 nm)制备的激光器,激光阈值由0.70μJ/pulse降低至0.18μJ/pulse,转化效率由2.5%提高到6.4%,且出射激光垂直于基板表面发射,有利于后续的处理及应用.     

Orientational holographic gratings observed in nematics aligned by carbon nanotube film

In this paper, we present a novel type of nematic liquid crystal cell with carbon nanotube film deposited by electrophoresis as the alignment layer. Self-diffraction was observed without applying a dc voltage across the cell under low intensity optical irradiation of a few milliwatts at 488 nm. The first-order diffraction efficiency increased and the response time of the grating decreased with the applied dc voltage increasing up to the dynamic scattering threshold voltage at 4 V (the corresponding dc electric field was 0.2 V/μm). A diffraction efficiency of ∼20%, the grating formation time of 0.5 s and an effective refractive index change coefficient of 0.14 cm²/W were obtained at 3.7 V with a writing beam intensity of 33 mW/cm². These observed phenomena were attributed to the photoactive charge layer formed at the interface of the carbon nanotube film and the liquid crystal film. PACS 42.65.Hw; 42.70.Df; 42.70.Nq; 42.40.Eq     

全息聚合物弥散液晶材料衍射特性的优化

研究了影响全息聚合物弥散液晶(HPDLC)衍射效率的主要因素，分析了衍射效率与聚合物单体的选择、曝光强度、曝光时间、液晶含量及温度的依赖关系，从而找到最佳条件，使衍射特性得到优化.目前测得的最大衍射效率为802%.实验中还研究了扫描电镜(SEM)观察下HPDLC的表面形貌.     

基于丙烯酸酯的全息聚合物分散液晶光栅的动力学理论研究

采用一维无限长模型分析法对全息聚合物分散液晶(HPDLC)做了动力学方面的研究，给出了相关的扩散动力学方程和聚合动力学方程,并与折射率调制度Δn相结合获得了光栅衍射效率的表达式，对HPDLC光栅性能的改善提供了理论上的指导.