Deposition and characterization of binary Al2O3/SiO2 coating layers on the surfaces of rutile TiO2 and the pigmentary properties

Binary Al₂O₃/SiO₂-coated rutile TiO₂ composites were prepared by a liquid-phase deposition method starting from Na₂SiO₃·9H₂O and NaAlO₂. The chemical structure and morphology of binary Al₂O₃/SiO₂ coating layers were investigated by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, TG-DSC, Zeta potential, powder X-ray diffraction, and transmission electron microscopy techniques. Binary Al₂O₃/SiO₂ coating layers both in amorphous phase were formed at TiO₂ surfaces. The silica coating layers were anchored at TiO₂ surfaces via Si-O-Ti bonds and the alumina coating layers were probably anchored at the SiO₂-coated TiO₂ surfaces via Al-O-Si bonds. The formation of continuous and dense binary Al₂O₃/SiO₂ coating layers depended on the pH value of reaction solution and the alumina loading. The binary Al₂O₃/SiO₂-coated TiO₂ composites had a high dispersibility in water. The whiteness and brightness of the binary Al₂O₃/SiO₂-coated TiO₂ composites were higher than those of the naked rutile TiO₂ and the SiO₂-coated TiO₂ samples. The relative light scattering index was found to depend on the composition of coating layers.     

Effects of coating parameters on the morphology of SiO2-coated TiO2 and the pigmentary properties

SiO₂-coated TiO₂ powders were prepared by the chemical deposition method starting from rutile TiO₂ and Na₂SiO₃. The SiO₂-coated TiO₂ powders were characterized by X-ray photoelectron spectroscopy, Zeta-potential analysis, Fourier transform infrared spectroscopy, and transmission electron microscopy. The evolution of island-like and uniform coating layers was found to depend upon the ratio of Na₂SiO₃ to TiO₂, reaction temperature, and pH. The whiteness and brightness of the SiO₂-coated TiO₂ powders increased in response to an increase in the SiO₂ loading, but there was a maximum value among the light scattering indexes. The SiO₂-coated TiO₂ powders possessed more negative Zeta potentials than the naked TiO₂. The dispersibility of the SiO₂-coated TiO₂ powders with the continuous and uniform SiO₂ coating layers was higher than that of the naked TiO₂ and the SiO₂-coated TiO₂ powders with the island-like SiO₂ coating layers.     

A facile synthesis of monodisperse CoFe2O4/SiO2 nanoparticles

Aminated-CoFe₂O₄/SiO₂ magnetic nanoparticles (NPs) were prepared from primary silica particles using modified StÖber method. By optimizing the preparation conditions, monodisperse CoFe₂O₄/SiO₂ NPs with high amino groups’ density were obtained, which is necessary for enzyme immobilization. TEM confirm that the sample is a core/shell structure. These aminated-CoFe₂O₄/SiO₂ NPs have narrow size distributions with a mean size of about 60 nm. Moreover, the aminated-CoFe₂O₄/SiO₂ NPs can be easily dispersed in aqueous medium. The experimental results also show that the NPs have superparamagnetism, indicating that the aminated-CoFe₂O₄/SiO₂ NPs can be used as an effective carrier for the enzyme immobilization.     

Preparation and characterization of SiO2/ZrO2/Ag multicoated microspheres

A new type of multicoated silica/zirconia/silver (SiO₂/ZrO₂/Ag) core-shell composite microspheres is synthesized in this paper. In the process, ZrO₂-decorated silica (SiO₂/ZrO₂) core-shell composites were firstly fabricated by the modification of zirconia on silica microspheres through the hydrolysis of zirconium precursor. Subsequently, on SiO₂/ZrO₂ composite cores, silver nanoparticles were introduced via ultrasonic irradiation and acted as “Ag seeds” for the formation of integrate silver shell by further reduction of silver ions using formaldehyde as reducer. The resulting samples were characterized by transmission electron microscopy, X-ray diffraction, Fourier-transform infrared, energy-dispersive X-ray, and UV-vis spectroscopy, indicating that zirconia and silver layers were successfully coated on the surfaces of silica microspheres.     

Core/shell structured ZnO/SiO2 nanoparticles: Preparation, characterization and photocatalytic property

ZnO nanoparticles were prepared by a simple chemical synthesis route. Subsequently, SiO₂ layers were successfully coated onto the surface of ZnO nanoparticles to modify the photocatalytic activity in acidic or alkaline solutions. The obtained particles were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), transmission electron microscopy (TEM), energy dispersive spectrometry (EDS) and zeta potential. It was found that ultrafine core/shell structured ZnO/SiO₂ nanoparticles were successfully obtained. The photocatalytic performance of ZnO/SiO₂ core/shell structured nanoparticles in Rhodamine B aqueous solution at varied pH value were also investigated. Compared with uncoated ZnO nanoparticles, core/shell structured ZnO/SiO₂ nanoparticles with thinner SiO₂ shell possess improved stability and relatively better photocatalytic activity in acidic or alkaline solutions, which would broaden its potential application in pollutant treatment.     

XPS investigation of diffusion of two-layer ZrO2/SiO2 and SiO2/ZrO2 sol–gel films

Two-layer ZrO₂/SiO₂ and SiO₂/ZrO₂ films were deposited on K9 glass substrates by sol–gel dip coating method. X-ray photoelectron spectroscopy (XPS) technique was used to investigate the diffusion of ZrO₂/SiO₂ and SiO₂/ZrO₂ films. To explain the difference of diffusion between ZrO₂/SiO₂ and SiO₂/ZrO₂ films, porous ratio and surface morphology of monolayer SiO₂ and ZrO₂ films were analyzed by using ellipsometry and atomic force microscopy (AFM). We found that for the ZrO₂/SiO₂ films there was a diffusion layer with a certain thickness and the atomic concentrations of Si and Zr changed rapidly; for the SiO₂/ZrO₂ films, the atomic concentrations of Si and Zr changed relatively slowly, and the ZrO₂ layer had diffused through the entire SiO₂ layer. The difference of diffusion between ZrO₂/SiO₂ and SiO₂/ZrO₂ films was influenced by the microstructure of SiO₂ and ZrO₂.     

Silica-based composite and mixed-oxide nanoparticles from atmospheric pressure flame synthesis

Binary TiO₂/SiO₂ and SnO₂/SiO₂ nanoparticles have been synthesized by feeding evaporated precursor mixtures into an atmospheric pressure diffusion flame. Particles with controlled Si:Ti and Si:Sn ratios were produced at various flow rates of oxygen and the resulting powders were characterized by BET (Brunauer–Emmett–Teller) surface area analysis, XRD, TEM and Raman spectroscopy. In the Si–O–Ti system, mixed oxide composite particles exhibiting anatase segregation formed when the Si:Ti ratio exceeded 9.8:1, while at lower concentrations only mixed oxide single phase particles were found. Arrangement of the species and phases within the particles correspond to an intermediate equilibrium state at elevated temperature. This can be explained by rapid quenching of the particles in the flame and is in accordance with liquid phase solubility data of Ti in SiO₂. In contrast, only composite particles formed in the Sn–O–Si system, with SnO₂ nanoparticles predominantly found adhering to the surface of SiO₂ substrate nanoparticles. Differences in the arrangement of phases and constituents within the particles were observed at constant precursor mixture concentration and the size of the resultant segregated phase was influenced by varying the flow rate of the oxidant. The above effect is due to the variation of the residence time and quenching rate experienced by the binary oxide nanoparticles when varying the oxygen flow rate and shows the flexibility of diffusion flame aerosol reactors.     

Effect of combination of noble metals and metal oxide supports on catalytic reduction of NO by H2

We investigated the effects of combination of noble metals M (Rh, Pd, Ir, Pt) and metal oxide supports S (Al₂O₃, SiO₂, ZrO₂, CeO₂) on the NO + H₂ reaction using planar catalysts with M/S two layered thin films on Si substrate. In this study, NO reduction ability per metal atom were evaluated with a specially designed apparatus employing pulse valves for the injection of reactant molecules onto catalysts and a time-of-flight mass spectrometer to measure multiple transient products: NH₃, N₂ and N₂O simultaneously as well as with an atomic force microscopy to observe the surface area of metal particles. The catalytic performances of Rh and Ir catalysts were hardly affected by a choice of a metal oxide support, while Pd and Pt catalysts showed different catalytic activity and selectivity depending on the metal oxide supports. This assortment is consistent with ability to dissociate NO depending on metals without the effect of any support materials. There, the metals to the left of Rh and Ir on the periodic table favor dissociation of NO and those to the right of Pd and Pt tend to show molecular adsorption of NO. Therefore, the catalytic property of noble metals could be assorted into two groups, i.e. Rh and Ir group whose own property would mainly dominate the catalytic performance, and Pd and Pt group whose interaction with metal oxides supports would clearly contribute to the reaction of NO with H₂. NO reduction activity of Pd and Pt was found to be promoted above that of Rh and Ir, provided that Pd and Pt were supported by CeO₂ and ZrO₂.     

Preparation of sol-gel ZrO2-SiO2 highly reflective multilayer films and laser-induced damage threshold characteristic

Sol-gel (ZrO₂/SiO₂)¹² ZrO₂ films were prepared by spin coating method. The reflectivity spectrum of the films was measured with a Lambda 900 spectrometer. In order to investigate laser-induced damage threshold (LIDT) characteristic of highly reflective films, one-layer ZrO₂ and SiO₂ films, two-layer ZrO₂/SiO₂ and SiO₂/ZrO₂ films were also prepared by spin coating method. LIDT of each film was measured. Damage morphology after laser irradiation was characterized by optical microscopy (Nikon E600K). The experimental results showed that the reflectivity of (ZrO₂/SiO₂)¹² ZrO₂ film at 1064 nm and 355 nm wavelength is 99.7%. The LIDT results decreases as the number of layer of films increases. All the films have similar damage morphology. The experimental results are explained by the different temperature profiles of the films.     

Degradation of Y2SiO5:Ce phosphor powders

The degradation of the cathodoluminescence (CL) intensity of cerium-doped yttrium silicate (Y₂SiO₅:Ce) phosphor powders was investigated for possible application in low voltage field emission displays (FEDs). Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS) and CL spectroscopy were used to monitor changes in the surface chemical composition and luminous efficiency of commercially available Y₂SiO₅:Ce phosphor powders. The degradation of the CL intensity for the powders is consistent with a well-known electron-stimulated surface chemical reaction (ESSCR) model. It was shown with XPS and CL that the electron stimulated reaction led to the formation of a luminescent silicon dioxide (SiO₂) layer on the surface of the Y₂SiO₅:Ce phosphor powder. XPS also indicated that the Ce concentration in the surface layer increased during the degradation process and the formation of CeO₂ and CeH₃ were also part of the degradation process. The CL intensity first decreased until about 300 C cm⁻² and then increased due to an extra peak arising at a wavelength of 650 nm.     

Preparation and characterization of size-controlled CeO2 nanoparticles coated with SiO2

CeO₂@SiO₂ (core@shell) nanoparticles were prepared by means of chemical precipitation technique. Results from X-ray diffraction, transmission electron microscopy (TEM), and Zeta-potential analyses provide strong microscopic and spectroscopic evidences to prove that CeO₂ particles have been encapsulated inside amorphous SiO₂ shell. As revealed from TEM investigations, the average grain size of CeO₂@SiO₂ is significantly smaller than that of uncoated CeO₂ nanoparticles prepared under the same conditions, indicating it is an effective method to restrict the grain enlargement of nanocrystalline CeO₂ by coating a thin layer of SiO₂ at elevated temperatures. The CeO₂@SiO₂ nanoparticles display a similar surface electric character behavior to that of SiO₂, and its dispersibility in water is improved.     

Spherical Zn2SiO4:Eu@SiO2 phosphor particles in core-shell structure: Synthesis and characterization

Spherical SiO₂ particles have been coated with Zn₂SiO₄:Eu³⁺ phosphor layers by a Pechini sol-gel process. The microstructure and luminescent properties of the obtained Zn₂SiO₄:Eu³⁺@SiO₂ particles were well characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, and lifetime. The results demonstrate that the Zn₂SiO₄:Eu³⁺@SiO₂ particles, which have regular and uniform spherical morphology, emitted an intensive red light emission at 613 nm under excitation at 395 nm. Besides, the effects of the Eu³⁺ concentration, annealing temperature and charge compensators of Li⁺ ions on the PL emission intensities were investigated in detail.     

Spectroscopic studies of interfacial structures of CeO2-TiO2 mixed oxides

We have investigated the geometric and electronic structures of the cerium oxide (CeO₂)-titanium dioxide (TiO₂) mixed oxides with various Ce/TiO₂ weight ratios prepared by the sol-gel method in detail by means of X-ray diffraction (XRD), high-resolution X-ray photoelectron spectroscopy (XPS), Raman spectroscopy excited by 325 and 514.5 nm lasers, and scanning electron microscope (SEM). Existence of cerium effectively inhibits the phase transition of TiO₂ from the anatase phase to the rutile phase. XRD peaks of TiO₂ anatase attenuate continuously with the increasing amount of CeO₂ in the mixed oxide, but the XRD peaks of cubic CeO₂ appear only after the weight ratio of Ce/TiO₂ reaches 0.50. The average crystalline sizes of TiO₂ anatase and cubic CeO₂ in CeO₂-TiO₂ mixed oxides are smaller than those in the corresponding individual TiO₂ anatase and cubic CeO₂. Raman spectroscopy excited by the 514.5 nm laser detects CeO₂ after the weight ratio of Ce/TiO₂ reaches 0.70 whereas Raman spectroscopy excited by the 325 nm laser detects CeO₂ after the weight ratio of Ce/TiO₂ reaches 0.90. XPS results demonstrate that Ti exists in the form of Ti⁴⁺ in the CeO₂-TiO₂ mixed oxide. Ce is completely in the form of Ce³⁺ in the mixed oxides with a 0.05 weight ratio of Ce/TiO₂. With the increasing weight ratio of Ce/TiO₂, Ce⁴⁺ dominates. On basis of these results, we proposed that CeO₂ initially nucleates at the defects (oxygen vacancies) within TiO₂ anatase, forming an interface bridged with oxygen between CeO₂ and TiO₂ anatase. At the interface, Ce species cannot substitute Ti⁴⁺ in the lattice of TiO₂ anatase whereas Ti⁴⁺ can substitute Ce⁴⁺ in the lattice of cubic CeO₂. The decreasing concentration of oxygen vacancies, the Ti-O-Ce interface, and the decreasing average crystalline size of TiO₂ anatase act to inhibit the phase transformation of TiO₂ anatase. With the increasing amounts of CeO₂, the CeO₂ clusters continuously grow and form cubic CeO₂ nanocrystals. Spectroscopic results strongly demonstrate that the surface region of CeO₂-TiO₂ mixed oxide is enriched with TiO₂.     

Synthesis and Characterization of Monodispersed SiO2@Y3Al5O12:Er3+ Core-Shell Particles

Submicron core-shell structure particles SiO₂@Y₃Al₅O₁₂:Er³⁺, which silica spherical particles was coated with an yttrium aluminum garnet (Y₃Al₅O₁₂) layer doped with Er³⁺, were prepared by the modified Pechini-Type sol-gel method for the first time. The structure and morphology of samples were detected by the X-ray powder diffraction (XRD) measurement, field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM), respectively. The results indicate that well-crystallized garnet nanocrystallines were formed on the surface of the silica particles. The luminescent spectra in near infrared and visible region of the core-shell structured SiO₂@Y₃Al₅O₁₂:Er³⁺ powders were also investigated and compared with those of the pure Y₃Al₅O₁₂:Er³⁺ and the Er³⁺ doped silicate glass. The results show that mono-dispersed SiO₂@Y₃Al₅O₁₂:Er³⁺ core-shell spherical particles with the near infrared, red and green luminescent emissions under the excitation of 980 nm laser diode have been successfully synthesized.     

Nanometric core-shell-shell γ-Fe2O3/SiO2/TiO2 particles

The preparation of core-shell-shell γ-Fe₂O₃/SiO₂/TiO₂ nanoparticles of few tens nanometers is performed by successively coating onto magnetic nanoparticles a SiO₂ layer and a TiO₂ layer, using sol–gel methods. The thickness of the two layers and the aggregation state of the particles can be controlled by the experimental conditions used for the two coatings. These composite nanoparticles may find application as magnetic photocatalysts, since they are characterized by their small diameters which allow a good accessibility to the TiO₂ shell. Electronic supplementary material  The online version of this article (doi:) contains supplementary material, which is available to authorized users.     

Size-Dependent HCl Generation of PVC/SiO2 Micro- and Nanocomposites

In this study HCl generation of polyvinyl (chloride) (PVC)/SiO₂ composites during its combustion was investigated. SiO₂ with different particle sizes were used as HCl absorbers and their HCl uptake ability results were compared to that of CaCO₃. It was found that the amount of released HCl gas during PVC combustion decreased in the presence of SiO₂. The HCl uptake ability of SiO₂ improved with decreasing of its particle size. Although thermogravimetric analysis (TGA) results showed that SiO₂ particles decreased the first thermal degradation temperature (T _onset) of PVC by initiating dehydrochlorination of PVC at lower temperatures, SiO₂ particles had more effective HCl uptaking ability than that of CaCO₃. Scanning electron microscopy (SEM) micrographs showed that some aggregates whose size was less than 100 nm were formed when Si-25 nm was used as filler. When SiO₂ with micron size was added to PVC as filler, more uniform and better distribution of the SiO₂ on the surface was observed.     

In situ Radical Copolymerization in Presence of Surface‐Modified TiO2 Nanoparticles: Influence of a Double Modification on Properties of Unsaturated Polyester (UP) Nanocomposites

In the preparation of nanocomposites, there is competition between the dispersion of nanoparticles and the formation of agglomerates. In this study, radical copolymerization of ethyl acrylate and methyl methacrylate initiated by 2,2‐azobis (isobutyro) nitrile (AIBN) was performed, in the presence of titanium oxide (TiO₂) nanoparticles modified in a new approach; a good dispersion of the nanoparticles in the unsaturated polyester (UP) matrix was obtained. The TiO₂ nanoparticles were exposed to 3‐(methacryloxy) propyl trimethoxy silane as the coupling agent. The presence of coupling agent‐grafted TiO₂ nanoparticles in the copolymerization process resulted in the formation of a polymeric layer on the surface of the TiO₂ nanoparticles (doubly modified‐TiO₂). The grafting of coupling agent molecules and consequently copolymer macromolecular chains onto the surface of TiO₂ nanoparticles was investigated using Fourier transform infrared (FTIR) analysis. It found that the formation of an acrylate layer on the surface of nanoparticles was successful. Then, unsaturated polyester (UP)/TiO₂ nanocomposites were prepared. The morphology was studied using transmission electron microscopy (TEM). Mechanical properties and ultraviolet visible (UV/VIS) spectroscopy of various samples, including the doubly modified‐TiO₂ nanoparticles, with different nanoparticle inclusions and the unmodified‐TiO₂ nanoparticles, were also investigated. The results showed the doubly modified‐TiO₂ nanoparticles, compared to those of unmodified‐TiO₂, had better nanoparticle dispersion causing improvement in the mechanical properties and UV shielding.     

Preparation and characterization of novel Pd/SiO2 and Ca-Pd/SiO2 egg-shell catalysts with porous hollow silica

Novel egg-shell structured monometallic Pd/SiO₂ and bimetallic Ca-Pd/SiO₂ catalysts were prepared by an impregnation method using porous hollow silica (PHS) as the support and PdCl₂ and Ca(NO₃)₂·4H₂O as the precursors. It was found from transmission electron microscope (TEM), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) that Pd was loaded on PHS with a particle size of 5-12 nm in Pd/SiO₂ samples and the Pd particle size in Ca-Pd/SiO₂ was smaller than that in Pd/SiO₂ since Ca could prevent Pd particles from aggregating. X-ray photoelectron spectroscopy (XPS) analyses exhibited that Pd 3d_5/2 binding energies of Pd/SiO₂ and Ca-Pd/SiO₂ were 0.2 and 0.9 eV lower than that of bulk Pd, respectively, as a result of the shift of the electron cloud from Pd to oxygen in Pd/SiO₂ and to both oxygen and Ca in Ca-Pd/SiO₂. The activity of Ca-Pd/SiO₂ egg-shell catalyst for CO hydrogenation and the selectivity to methanol, with a value of 36.50 mmol_CO mol⁻¹_Pd s⁻¹ and 100%, respectively, were much higher than those of the catalysts prepared with traditional silica gel as the support, owing to the porous core-shell structure of the PHS support.     

Immobilization of glucose oxidase using CoFe2O4/SiO2 nanoparticles as carrier

Aminated-CoFe₂O₄/SiO₂ magnetic nanoparticles (NPs) were prepared from primary silica particles using modified StÖber method. Glucose oxidase (GOD) was immobilized on CoFe₂O₄/SiO₂ NPs via cross-linking with glutaraldehyde (GA). The optimal immobilization condition was achieved with 1% (v/v) GA, cross-linking time of 3 h, solution pH of 7.0 and 0.4 mg GOD (in 3.0 mg carrier). The immobilized GOD showed maximal catalytic activity at pH 6.5 and 40 °C. After immobilization, the GOD exhibited improved thermal, storage and operation stability. The immobilized GOD still maintained 80% of its initial activity after the incubation at 50 °C for 25 min, whereas free enzyme had only 20% of initial activity after the same incubation. After kept at 4 °C for 28 days, the immobilized and free enzyme retained 87% and 40% of initial activity, respectively. The immobilized GOD maintained approximately 57% of initial activity after reused 7 times. The K_M (Michaelis-Menten constant) values for immobilized GOD and free GOD were 14.6 mM and 27.1 mM, respectively.     

Immobilization of metalloporphyrins on P(4VP-co-St)/SiO2 by the quaternarization reaction

Poly(4vinylpyridine-co-styrene) (P(4VP-co-St)) was grafted on silica gel particles in the manner of “grafting from”, and the grafting particle P(4VP-co-St)/SiO₂ was gained. The chloromethylation reaction for the tetraphenylporphyrin (TPP) was performed using a chloromethylation reagent, 1,4-bis(chloromethyoxy)butane which was uncarcinogenic, and the tetra-chloromethylphenyl-porphyrin (TMCPP) was prepared. Then, the quaternization reaction between the benzyl chloride groups on TMCPP and pyridine groups of the grafted P(4VP-co-St) macromolecules occurred and the bonding of TMCPP on the particles P(4VP-co-St)/SiO₂ was realized, resulting in the functional composite-type particles TMCPP-P(4VP-co-St)/SiO₂. Subsequently, the metallation of the bonded particles TMCPP-P(4VP-co-St)/SiO₂ was carried out via the coordination reaction between TMCPP-P(4VP-co-St)/SiO₂ and metal salt, resulting in the supported metalloporphyrin (MP) catalysts MP-P(4VP-co-St)/SiO₂. The supported catalysts were characterized by UV-Vis spectra. The effects of various factors on the bonding process of TMCPP on P(4VP-co-St)/SiO₂ were studied in detail. In addition, the catalytic activity of the supported catalysts MP-P(4VP-co-St)/SiO₂ have been studied in oxidation process of ethyl benzene with molecular oxygen to acetophenone without the use of sacrificial co-reductant. The experimental results showed that the tetra-chloromethylphenyl-porphyrin (TMCPP) could be successfully bonded onto the P(4VP-co-St)/SiO₂ surfaces by means of the quaternization reaction between TMCPP and the pyridine groups on grafted P(4VP-co-St) macromolecules. The supported catalysts MP-P(4VP-co-St)/SiO₂ exhibited the fine catalytic activity. Moreover, the supported cobalt porphyrin was more active than the supported iron and manganese porphyrins.