Preparation and characterization of SiO2/ZrO2/Ag multicoated microspheres

A new type of multicoated silica/zirconia/silver (SiO₂/ZrO₂/Ag) core-shell composite microspheres is synthesized in this paper. In the process, ZrO₂-decorated silica (SiO₂/ZrO₂) core-shell composites were firstly fabricated by the modification of zirconia on silica microspheres through the hydrolysis of zirconium precursor. Subsequently, on SiO₂/ZrO₂ composite cores, silver nanoparticles were introduced via ultrasonic irradiation and acted as “Ag seeds” for the formation of integrate silver shell by further reduction of silver ions using formaldehyde as reducer. The resulting samples were characterized by transmission electron microscopy, X-ray diffraction, Fourier-transform infrared, energy-dispersive X-ray, and UV-vis spectroscopy, indicating that zirconia and silver layers were successfully coated on the surfaces of silica microspheres.     

Preparation of sol-gel ZrO2-SiO2 highly reflective multilayer films and laser-induced damage threshold characteristic

Sol-gel (ZrO₂/SiO₂)¹² ZrO₂ films were prepared by spin coating method. The reflectivity spectrum of the films was measured with a Lambda 900 spectrometer. In order to investigate laser-induced damage threshold (LIDT) characteristic of highly reflective films, one-layer ZrO₂ and SiO₂ films, two-layer ZrO₂/SiO₂ and SiO₂/ZrO₂ films were also prepared by spin coating method. LIDT of each film was measured. Damage morphology after laser irradiation was characterized by optical microscopy (Nikon E600K). The experimental results showed that the reflectivity of (ZrO₂/SiO₂)¹² ZrO₂ film at 1064 nm and 355 nm wavelength is 99.7%. The LIDT results decreases as the number of layer of films increases. All the films have similar damage morphology. The experimental results are explained by the different temperature profiles of the films.     

Fabrication and characterization of Au/SiO2 nanocomposite films grown by radio-frequency cosputtering

Au/SiO₂ nanocomposite films were prepared on Si wafers by cosputtering of SiO₂ and gold wires. Au/Si atomic ratios in Au/SiO₂ nanocomposite films were varied from 0.53 to 0.92 by controlling the length of gold wire to study the evolution of the crystallization of gold, the size of Au/SiO₂ nanocomposite particles, and the optical properties of as-deposited Au/SiO₂ nanocomposite films. An X-ray photoelectron spectroscopy reveals that Au exists as a metallic phase in the bulk of SiO₂ matrix. Dome-shaped Au/SiO₂ nanocomposite particles and both Au (1 1 1) and (2 0 0) planes were observed in a field-emission scanning electron microscopy and X-ray diffraction studies respectively. With an ultraviolet-visible, absorption peaks of Au/SiO₂ nanocomposite films were observed at 525 nm.     

Stability of La2O3 and GeO2 passivated Ge surfaces during ALD of ZrO2 high-k dielectric

La₂O₃ grown by atomic layer deposition (ALD) and thermally grown GeO₂ are used to establish effective electrical surface passivations on n-type (1 0 0)-Ge substrates for high-k ZrO₂ dielectrics, grown by ALD at 250 °C substrate temperature. The electrical characterization of MOS capacitors indicates an impact of the Ge-surface passivation on the interfacial trap density and the frequency dependent capacitance in the inversion regime. Lower interface trap densities can be obtained for GeO₂ based passivation even though a chemical decomposition of the oxidation states occur during the ALD of ZrO₂. As a consequence the formation of a ZrGeO_x compound inside the ZrO₂ matrix and a decline of the interfacial GeO₂ are observed. The La₂O₃ passivation provides a stable amorphous lanthanum germanate phase at the Ge interface but also traces of Zr germanate are indicated by X-ray-Photoelectron-Spectroscopy and Transmission-Electron-Microscopy.     

Electroluminescence from Si／SiO2 films deposited on p—Si substrates

The structure of Au/Si/SiO₂/p-Si has been fabricated using the magnetron sputtering technique. It has a very good rectifying behaviour. Visible electroluminescence (EL) has been observed from the Au/Si/SiO₂/p-Si structure at a forward bias of 5V or larger. A broad band with one peak around 650－660 nm appears in all the EL spectra of the structure. The effects of the thickness of the Si layer in the Si/SiO₂ films and of the input electrical power on EL spectra are studied systematically.     

The effect of Si surface nitridation on the interfacial structure and electrical properties of (La2O3)0.5(SiO2)0.5 high-k gate dielectric films

Thermal stability, interfacial structures and electrical properties of amorphous (La₂O₃)_0.5(SiO₂)_0.5 (LSO) films deposited by using pulsed laser deposition (PLD) on Si (1 0 0) and NH₃ nitrided Si (1 0 0) substrates were comparatively investigated. The LSO films keep the amorphous state up to a high annealing temperature of 900 °C. HRTEM observations and XPS analyses showed that the surface nitridation of silicon wafer using NH₃ can result in the formation of the passivation layer, which effectively suppresses the excessive growth of the interfacial layer between LSO film and silicon wafer after high-temperature annealing process. The Pt/LSO/nitrided Si capacitors annealed at high temperature exhibit smaller CET and EOT, a less flatband voltage shift, a negligible hysteresis loop, a smaller equivalent dielectric charge density, and a much lower gate leakage current density as compared with that of the Pt/LSO/Si capacitors without Si surface nitridation.     

Long lasting phosphorescent properties of Ti doped ZrO2

A novel long-lasting afterglow phosphor ZrO₂:Ti is prepared by the conventional solid-stated method and their luminescent properties are investigated. A bluish white strong and broad emissive band, which is attributed to originate from the recombination of electrons trapped by F⁺ centers and the holes created in Valence band, is observed under 254 nm UV irradiation. The identical color long afterglow, which lasts about 1 h, is found in the ZrO₂:Ti phosphor after removing the 254 nm UV light. The mechanism of the long lasting phosphorescence (LLP) has been discussed based on the thermoluminescence (TL) results. The replacement of Zr by Ti produces more anion vacancies, resulting in the enhanced photoluminescence (PL) and LLP of ZrO₂:Ti sample. These results indicate that ZrO₂:Ti phosphor has potential promising applications.     

Characterization of ZrO2-promoted Cu/ZnO/nano-Al2O3 methanol steam reforming catalysts

Three Cu/ZnO/ZrO₂/Al₂O₃ methanol reforming catalysts were investigated using X-ray photoelectron spectroscopy (XPS). The catalysts which contained ZrO₂ from a monoclinic nanoparticle ZrO₂ precursor exhibit both a higher activity toward the methanol steam reforming reaction and a lower CO production rate compared to catalysts composed of an XRD-amorphous ZrO₂ produced by impregnation using a Zr(NO₃)₂ precursor. The presence of a monoclinic phase appears to result in an increased charge transfer between the Zr and Cu species, as evidenced by a relatively electron-rich ZrO₂ phase and a partially oxidized Cu species on reduced catalysts. This electron deficient Cu species is more reactive toward the methanol reforming reaction and partially suppresses CO formation through the reverse water gas shift or methanol decomposition reactions.     

Stabilization of a very high-k crystalline ZrO2 phase by post deposition annealing of atomic layer deposited ZrO2/La2O3 dielectrics on germanium

The impact of the ZrO₂/La₂O₃ film thickness ratio and the post deposition annealing in the temperature range between 400 °C and 600 °C on the electrical properties of ultrathin ZrO₂/La₂O₃ high-k dielectrics grown by atomic layer deposition on (1 0 0) germanium is investigated. As-deposited stacks have a relative dielectric constant of 24 which is increased to a value of 35 after annealing at 500 °C due to the stabilization of tetragonal/cubic ZrO₂ phases. This effect depends on the absolute thickness of ZrO₂ within the dielectric stack and is limited due to possible interfacial reactions at the oxide/Ge interface. We show that adequate processing leads to very high-k dielectrics with EOT values below 1 nm, leakage current densities in the range of 0.01 A/cm², and interface trap densities in the range of 2-5 × 10¹² eV⁻¹ cm⁻².     

Annealing effects on the optical and structural properties of Al2O3/SiO2 films as UV antireflection coatings on 4H-SiC substrates

Al₂O₃/SiO₂ films have been prepared by electron-beam evaporation as ultraviolet (UV) antireflection coatings on 4H-SiC substrates and annealed at different temperatures. The films were characterized by reflection spectra, ellipsometer system, atomic force microscopy (AFM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), respectively. As the annealing temperature increased, the minimum reflectance of the films moved to the shorter wavelength for the variation of refractive indices and the reduction of film thicknesses. The surface grains appeared to get larger in size and the root mean square (RMS) roughness of the annealed films increased with the annealing temperature but was less than that of the as-deposited. The Al₂O₃/SiO₂ films maintained amorphous in microstructure with the increase of the temperature. Meanwhile, the transition and diffusion in film component were found in XPS measurement. These results provided the important references for Al₂O₃/SiO₂ films annealed at reasonable temperatures and prepared as fine antireflection coatings on 4H-SiC-based UV optoelectronic devices.     

Preparation and characterization of amine-functionalized SiO2/TiO2 films for formaldehyde degradation

This paper investigated the gaseous formaldehyde degradation by the amine-functionalized SiO₂/TiO₂ photocatalytic films for improving indoor air quality. The films were synthesized via the co-condensation reaction of methyltrimethoxysilane (MTMOS) and 3-aminopropyltrimethoxysilane (APTMS). The physicochemical properties of prepared photocatalysts were characterized with N₂ adsorption/desorption isotherms measurement, X-ray diffraction (XRD) and Fourier Transform Infrared spectroscopy (FT/IR). The effect of amine-functional groups and the ratio of MTMOS/APTMS precursors on the formaldehyde adsorption and photocatalytic degradation were investigated. The results showed that the formaldehyde adsorption and photocatalytic degradation of the APTMS-functionalized SiO₂/TiO₂ film was higher than that of SiO₂/TiO₂ film due to the surface adsorption on amine sites and the relatively high of the specific surface area of the APTMS-functionalized SiO₂/TiO₂ film (15 times higher than SiO₂/TiO₂). The enhancement of the formaldehyde degradation of the film can be attributed to the synergetic effect of adsorption and subsequent photocatalytic decomposition. The repeatability of photocatalytic film was also tested and the degradation efficiency was 91.0% of initial efficiency after seven cycles.     

Electron beam-physical vapor deposition of SiC/SiO2 high emissivity thin film

When heated by high-energy electron beam (EB), SiC can decompose into C and Si vapor. Subsequently, Si vapor reacts with metal oxide thin film on substrate surface and formats dense SiO₂ thin film at high substrate temperature. By means of the two reactions, SiC/SiO₂ composite thin film was prepared on the pre-oxidized 316 stainless steel (SS) substrate by electron beam-physical vapor deposition (EB-PVD) only using β-SiC target at 1000 °C. The thin film was examined by energy dispersive spectroscopy (EDS), grazing incidence X-ray asymmetry diffraction (GIAXD), scanning electron microscopy (SEM), atomic force microscopy (AFM), backscattered electron image (BSE), electron probe microanalysis (EPMA), X-ray photoelectron spectroscopy (XPS) and Fourier transformed infra-red (FT-IR) spectroscopy. The analysis results show that the thin film is mainly composed of imperfect nano-crystalline phases of 3C-SiC and SiO₂, especially, SiO₂ phase is nearly amorphous. Moreover, the smooth and dense thin film surface consists of nano-sized particles, and the interface between SiC/SiO₂ composite thin film and SS substrate is perfect. At last, the emissivity of SS substrate is improved by the SiC/SiO₂ composite thin film.     

Effect of UV lamp irradiation during oxidation of Zr/Pt/Si structure on electrical properties of Pt/ZrO2/Pt/Si structure

Metal-insulator-metal (MIM) capacitors were fabricated using ZrO₂ films and the effects of structural and native defects of the ZrO₂ films on the electrical and dielectric properties were investigated. For preparing ZrO₂ films, Zr films were deposited on Pt/Si substrates by ion beam deposition (IBD) system with/without substrate bias voltages and oxidized at 200 °C for 60 min under 0.1 MPa O₂ atmosphere with/without UV light irradiation (λ = 193 nm, Deep UV lamp). The ZrO₂(∼12 nm) films on Pt(∼100 nm)/Si were characterized by X-ray diffraction pattern (XRD), field emission scanning electron microscopy (FE-SEM) and high-resolution transmission electron microscopy (HRTEM), capacitance-voltage (C-V) and current-voltage (I-V) measurements were carried out on MIM structures. ZrO₂ films, fabricated by oxidizing the Zr film deposited with substrate bias voltage under UV light irradiation, show the highest capacitance (784 pF) and the lowest leakage current density. The active oxygen species formed by UV irradiation are considered to play an important role in the reduction of the leakage current density, because they can reduce the density of oxygen vacancies.     

ZrO2／SiO2多层膜中膜厚组合周期数及基底材料对残余应力的影响

ZrO₂／SiO₂多层膜由相同沉积条件下的电子束蒸发方法制备而成， 通过改变多层膜中高(ZrO₂)、低(SiO₂)折射率材料膜厚组合周期数的方法，研究了沉积 在熔石英和BK7玻璃 基底上多层膜中残余应力的变化. 用ZYGO光学干涉仪测量了基底镀膜前后曲率半径的变化， 并确定了薄膜中的残余应力. 结果发现，该多层膜中的残余应力为压应力，随着薄膜中膜厚 组合周期数的增加，压应力值逐渐减小. 而且在相同条件下，石英基底上所沉积多层膜中的 压应力值要小于BK7玻璃基底上所沉积多层膜中的压应力值. 用x射线衍射技术测量分析了膜 厚组合周期数不同的ZrO₂／SiO₂多层膜微结构，发现随着周期数增 加，多层膜的结晶程 度增强. 同时多层膜的微结构应变表现出了与所测应力不一致的变化趋势，这主要是由多层 膜中，膜层界面之间复杂的相互作用引起的. 关键词： 2／SiO₂多层膜')" href="#">ZrO₂／SiO₂多层膜 残余应力 膜厚组合周期数     

Coupling between Ge-nanocrystals and defects in SiO2

Room temperature photoluminescence (PL) at around 600 nm from magnetron-sputtered SiO₂ films co-doped with Ge is reported. The PL signal is observed in pure SiO₂, however, its intensity increases significantly in the presence of Ge-nanocrystals (Ge-nc). The PL intensity has been optimized by varying the temperature of heat treatment, type of gas during heat treatment, concentration of Ge in the SiO₂ films, and gas pressure during deposition. Maximum intensity occurs when Ge-nc of around 3.5 nm are present in large concentration in SiO₂ layers deposited at fairly high gas pressure. Based on time resolved PL, and PL measurements after α-particle irradiation or H passivation, we attribute the origin of the PL to a defect in SiO₂ (probably an O deficiency) that is excited through an energy transfer from Ge-nc. There is no direct PL from the Ge-nc; however, there is a strong coupling between excitons created in the Ge-nc and the SiO₂ defect.     

Influence of ZrO2 in HfO2 on reflectance of HfO2/SiO2 multilayer at 248 nm prepared by electron-beam evaporation

Influence of ZrO₂ in HfO₂ on the reflectance of HfO₂/SiO₂ multilayer at 248 nm was investigated. Two kinds of HfO₂ with different ZrO₂ content were chosen as high refractive index material and the same kind of SiO₂ as low refractive index material to prepare the mirrors by electron-beam evaporation. The impurities in two kinds of HfO₂ starting coating materials and in their corresponding single layer thin films were determined through glow discharge mass spectrum (GDMS) technology and secondary ion mass spectrometry (SIMS) equipment, respectively. It showed that between the two kinds of HfO₂, either the bulk materials or their corresponding films, the difference of ZrO₂ was much larger than that of the other impurities such as Ti and Fe. It is the Zr element that affects the property of thin films. Both in theoretical and in experimental, the mirror prepared with the HfO₂ starting material containing more Zr content has a lower reflectance. Because the extinction coefficient of zirconia is relatively high in UV region, it can be treated as one kind of absorbing defects to influence the optical property of the mirrors.     

Intrinsic defect related luminescence in ZrO2

The studies of ZrO₂ and yttrium stabilized ZrO₂ nanocrystals luminescence as well as yttrium stabilized single crystal luminescence and induced absorption showed that the intrinsic defects are responsible for luminescence at room temperature. These defects form a quasi-continuum of states in ZrO₂ band gap and are the origin of the luminescence spectrum dependence on the excitation energy. Luminescence centers are oxygen vacancies related but not the vacancies themselves. At room temperature, in ZrO₂, deep traps for electrons and holes exist. The oxygen vacancies are proposed to be the traps for electrons.     

SiO2的赝晶化及AlN/SiO2纳米多层膜的超硬效应

采用反应磁控溅射法制备了一系列不同SiO₂层厚度的AlN/SiO₂纳米多层膜，利用X射线衍射仪、高分辨透射电子显微镜和微力学探针表征了多层膜的微结构和力学性能，研究了SiO₂层在多层膜中的晶化现象及其对多层膜生长方式及力学性能的影响. 结果表明，由于受AlN六方晶体结构的模板作用，溅射条件下以非晶态存在的SiO₂层在其厚度小于0.6 nm时被强制晶化为与AlN相同的六方结构赝晶体并与AlN形成共格外延生长. 由于不同模量的两调制层存在晶格错配度，多层膜中产生了拉、压交变的应力场，使得多层膜产生硬度升高的超硬效应. SiO₂随层厚的进一步增加又转变为以非晶态生长，多层膜的外延生长结构受到破坏，其硬度也随之降低. 关键词： 2纳米多层膜')" href="#">AlN/SiO₂纳米多层膜 赝晶化 应力场 超硬效应     

High-temperature oxidation behavior of SiO2 protective layer deposited on IN738LC superalloy by combustion CVD (CCVD)

A SiO₂ protective coating was deposited on an IN738LC alloy using CCVD. The physical properties of a SiO₂ protective layer are influenced by the amount of tetraethyl orthosilicate (TEOS, C₈H₂₀O₄Si). Therefore, the SiO₂ protective coating was deposited using different TEOS concentrations and deposition times to optimize the conditions. The deposited coating layer was confirmed to be a SiO₂ layer by SEM, EDX, and ESCA analyses. The oxidation resistance of the alloy was evaluated by thermo gravimetric analysis. The oxidation resistance of the SiO₂ protective coating was highest when the coating was processed at a TEOS concentration of 0.05 mol/l, which is the highest concentration of source material used. The surface roughness of the SiO₂ protective layer also increased with increasing TEOS concentration. The surface roughness of the coating had little effect on the oxidation resistance for a film thickness of approximately 1 μm.     

Preparation and characterization of novel Pd/SiO2 and Ca-Pd/SiO2 egg-shell catalysts with porous hollow silica

Novel egg-shell structured monometallic Pd/SiO₂ and bimetallic Ca-Pd/SiO₂ catalysts were prepared by an impregnation method using porous hollow silica (PHS) as the support and PdCl₂ and Ca(NO₃)₂·4H₂O as the precursors. It was found from transmission electron microscope (TEM), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) that Pd was loaded on PHS with a particle size of 5-12 nm in Pd/SiO₂ samples and the Pd particle size in Ca-Pd/SiO₂ was smaller than that in Pd/SiO₂ since Ca could prevent Pd particles from aggregating. X-ray photoelectron spectroscopy (XPS) analyses exhibited that Pd 3d_5/2 binding energies of Pd/SiO₂ and Ca-Pd/SiO₂ were 0.2 and 0.9 eV lower than that of bulk Pd, respectively, as a result of the shift of the electron cloud from Pd to oxygen in Pd/SiO₂ and to both oxygen and Ca in Ca-Pd/SiO₂. The activity of Ca-Pd/SiO₂ egg-shell catalyst for CO hydrogenation and the selectivity to methanol, with a value of 36.50 mmol_CO mol⁻¹_Pd s⁻¹ and 100%, respectively, were much higher than those of the catalysts prepared with traditional silica gel as the support, owing to the porous core-shell structure of the PHS support.