Half Ca-doped LaMnO3 films on (0 0 1) SLAO and STO substrate studied by magnetization and transport measurements

In this study, La_0.5Ca_0.5MnO₃ (LCMO) films, at the boundary between ferromagnetic metallic and charge-ordered antiferromagnetic insulator according to the bulk phase diagram, were epitaxially grown on (0 0 1) SrTiO₃ (STO) and SrLaAlO₄ (SLAO) substrates by pulsed laser deposition technique. The films were analyzed by X-ray diffraction, magnetization and magnetoresistance measurements. A considerably higher magnetization was measured for 290-nm-thick film on SLAO substrate compared to the film on STO substrate, although both films have the same chemical composition, thickness and epitaxial orientation. The film on SLAO shows a metal-insulator (MI) transition, which occurs at higher temperatures with increasing applied magnetic field, whereas only insulating behavior was observed for the 290-nm-thick film on STO except for the highest applied magnetic field (7 T). In addition, transport measurements were performed and analyzed by Mott's variable range hopping (VRH) model to correlate the resistivity of the films with the Jahn-Teller strain (ε_J−T) in the structure.     

Alloy formation of Co/Ni/Pt(1 1 1)

The initial growth and alloy formation of ultrathin Co films deposited on 1 ML Ni/Pt(1 1 1) were investigated by Auger electron spectroscopy (AES), low energy electron diffraction (LEED), and ultraviolet photoelectron spectroscopy (UPS). A sequence of samples of d_Co Co/1 ML Ni/Pt(1 1 1) (d_Co = 1, 2, and 3 ML) were prepared at room temperature, and then heated up to investigate the diffusion process. The Co and Ni atoms intermix at lower annealing temperature, and Co-Ni intermixing layer diffuses into the Pt substrate to form Ni-Co-Pt alloys at higher annealing temperature. The diffusion temperatures are Co coverage dependent. The evolution of UPS with annealing temperatures also shows the formation of surface alloys. Some interesting LEED patterns of 1 ML Co/1 ML Ni/Pt(1 1 1) show the formation of ordered alloys at different annealing temperature ranges. Further studies in the Curie temperature and concentration analysis, show that the ordered alloys corresponding to different LEED patterns are Ni_xCo_1−xPt and Ni_xCo_1−xPt₃. The relationship between the interface structure and magnetic properties was investigated.     

Thermal stability study of palladium and cobalt Schottky contacts on n-Ge (1 0 0) and defects introduced during contacts fabrication and annealing process

Palladium (Pd) and cobalt (Co) Schottky barrier diodes were fabricated on n-Ge (1 0 0). The Pd-Schottky contacts were deposited by resistive evaporation while the Co-contacts were deposited by resistive evaporation and electron beam deposition. Current-voltage (I-V), capacitance-voltage (C-V) and deep level transient spectroscopy (DLTS) measurements were performed on as-deposited and annealed samples. Electrical properties of Pd and Co samples annealed between 30 and 600 °C indicate the formation of one phase of palladium germanide and two phases of cobalt germanide. No defects were observed for the resistively evaporated as-deposited Pd-and Co-Schottky contacts. A hole trap at 0.33 eV above the valence band was observed on the Pd-Schottky contacts after annealing at 300 °C. An electron trap at 0.37 eV below the conduction band and a hole trap at 0.29 eV above the valence band was observed on as-deposited Co-electron beam deposited Schottky contacts. Rutherford back scattering (RBS) technique was also used to characterise the Co-Ge, for as-deposited and annealed samples.     

Seedlayer interface enhanced magnetic anisotropy in CoPt (0 0 0 2)-textured films

The effects of interface roughness of Ta seedlayer on the structural and magnetic properties of Co₇₂Pt₂₈(20 nm)/Ru(30 nm)/Pt(2 nm)/Ta(5 nm)/glass were investigated. Uniaxial perpendicular magnetic anisotropy (8.6×10⁶ ergs/cc), coercivity (5.5 kOe) and nucleation field (−2.8 kOe) in the Co₇₂Pt₂₈ thin film sputter-deposited on relatively smooth surface of Ta seedlayer were achieved. The results showed that relatively smoother interface roughness of Ta seedlayer improved the CoPt/Ru (0 0 0 2) texture and magnetic properties.     

Perpendicular magnetic anisotropy of ultrathin FeCo alloy films on Pd(0 0 1) surface: First principles study

Using the full potential linearized augmented plane wave (FLAPW) method, thickness dependent magnetic anisotropy of ultrathin FeCo alloy films in the range of 1 monolayer (ML) to 5 ML coverage on Pd(0 0 1) surface has been explored. We have found that the FeCo alloy films have close to half metallic state and well-known surface enhancement in thin film magnetism is observed in Fe atom, whereas the Co has rather stable magnetic moment. However, the largest magnetic moment in Fe and Co is found at 1 ML thickness. Interestingly, it has been observed that the interface magnetic moments of Fe and Co are almost the same as those of surface elements. The similar trend exists in orbital magnetic moment. This indicates that the strong hybridization between interface FeCo alloy and Pd gives rise to the large magnetic moment. Theoretically calculated magnetic anisotropy shows that the 1 ML FeCo alloy has in-plane magnetization, but the spin reorientation transition (SRT) from in-plane to perpendicular magnetization is observed above 2 ML thickness with huge magnetic anisotropy energy. The maximum magnetic anisotropy energy for perpendicular magnetization is as large as 0.3 meV/atom at 3 ML film thickness with saturation magnetization of . Besides, the calculated X-ray magnetic circular dichroism (XMCD) has been presented.     

CoPt alloy grown on the WSe2(0 0 0 1) van der Waals surface

The structural and magnetic properties of 3-nm-thick CoPt alloys grown on WSe₂(0 0 0 1) at various temperature are investigated. Deposition at room temperature leads to the formation of a chemically disordered fcc CoPt alloy with [1 1 1] orientation. Growth at elevated temperatures induces L1₀ chemical order starting at 470 K accompanied with an increase in grain size and a change in grain morphology. As a consequence of the [1 1 1] growth direction, the CoPt grains can adopt one of the three possible variants of the L1₀ phase with tetragonal c-axis tilted from the normal to the film plane direction at 54°. The average long-range order parameter is found to be 0.35(±0.05) and does not change with the increase in the deposition temperature from 570 to 730 K. This behavior might be related to Se segregation towards the growing facets and surface disorder effects promoted by a high surface-to-volume ratio. Magnetic studies reveal a superparamagnetic behavior for the films grown at 570 and 730 K in agreement with the film morphology and degree of chemical order. The measurements at 10 K reveal the orientation of the easy axis of the magnetization lying basically in the film plane.     

Kinetic stabilization of Fe film on GaAs(1 0 0): An in situ X-ray reflectivity study

We study the growth of Fe films on GaAs(1 0 0) at a low temperature, 140 K, by in situ X-ray reflectivity (XRR) using synchrotron radiation. The XRR curves are well modeled by a single Fe layer on GaAs both at the growth temperature and after annealed at the room temperature. We found that the surface became progressively rougher during the growth with the growth exponent, β_S = 0.43 ± 0.14. The observed β_S is attributed to the restricted interlayer diffusion at the low growth temperature. The change of the interface width during growth was minimal. When the Fe film was annealed to room temperature, the surface smoothed, keeping the interface width almost unchanged. The confinement of the interface derives from that the diffusion of Ga and As proceeds via the inefficient bulk diffusion, and the overlying Fe film is kinetically stabilized.     

Photoemission study of cobalt interaction with the oxidized Si(1 0 0)2 × 1 surface

The interaction of cobalt atoms with an oxidized Si(1 0 0)2 × 1 surface was studied by photoelectron spectroscopy with synchrotron radiation at room and elevated temperatures. The SiO_x layer grown in situ on the crystal surface was ∼0.3 nm thick, and the amount of deposited cobalt was varied within eight atomic layers. It was found that Co atoms could penetrate under the SiO_x layer even at room temperature in the initial growth. As the Co amount increased, a ternary Co-O-Si phase was formed at the interface, followed by a Co-Si solid solution. Silicide synthesis associated with the decomposition of these phases started under the SiO_x layer at ∼250 °C, producing cobalt disilicide with a stable CaF₂-type of structure.     

Magneto-optical study of slanted Co nanowires embedded in CeO2/SrTiO3(0 0 1)

Sequential pulsed laser deposition of CoO and CeO₂ at 650 °C under vacuum leads to the formation of a slanted Co nanowires assembly embedded in CeO₂/SrTiO₃(0 0 1) epilayers. High temperature magneto-optical Faraday measurements were performed, which revealed a Faraday ellipticity of 1.3° at a wavelength of 450 nm for 300 nm thick samples and which allowed to access the magnetic properties. From the analysis of the coercivity dependence on temperature, it is shown that the magnetic anisotropy of the slanted Co nanowires is dominated by shape anisotropy and that their magnetization reversal is localized.     

Crystallization of amorphous Co2MnSi thin film

Amorphous Co₂MnSi thin film was deposited using radio-frequency sputtering. The amorphous film crystallized into a single-phased L2₁ structure at 500 °C, which was highly disordered. The structure was meta-stable as the crystallized film decomposed upon further heating. Increasing the annealing temperature to 600 °C precipitated fcc Co together with Co₂MnSi. Magnetic measurements showed that the as-deposited amorphous film was paramagnetic, exhibiting a spin glass state below 44 K. The phase transition at 500 °C produced a ferromagnetic Co₂MnSi thin film whose saturation magnetic moment was considerably lower than reported values due to the disordered structure of the crystallized film.     

Oxidation of epitaxial Y(0 0 0 1) films

We have investigated the oxidation behavior of MBE grown epitaxial Y(0 0 0 1)/Nb(1 1 0) films on sapphire substrates at elevated temperatures under atmospheric conditions with a combination of experimental methods. At room temperature X-ray diffraction (XRD) reveals the formation of a 25 Å thick YO_xH_x layer at the surface, while simultaneously oxide growth proceeds along defect lines normal to the film plane, resulting in the formation of a single crystalline cubic Y₂O₃ (2 2 2) phase. Furthermore, nuclear resonance analysis (NRA) reveals that hydrogen penetrates into the sample and transforms the entire Y film into the hydride YH₂ phase. Additional annealing in air leads to further oxidation radially out from the already existing oxide channels. Finally material transport during oxidation results in the formation of conically shaped oxide precipitations at the surface above the oxide channels as observed by atomic force microscopy (AFM).     

Magnetoresistance of magnetite thin films grown by pulsed laser deposition on GaAs(1 0 0) and Al2O3(0 0 0 1)

Magnetotransport properties of magnetite thin films deposited on gallium arsenide and sapphire substrates at growth temperatures between 473 and 673 K are presented. The films were grown by UV pulsed laser ablation in reactive atmospheres of O₂ and Ar, at working pressure of 8 × 10⁻² Pa. Film stoichiometry was determined in the range from Fe_2.95O₄ to Fe_2.97O₄. Randomly oriented polycrystalline thin films were grown on GaAs(1 0 0) while for the Al₂O₃(0 0 0 1) substrates the films developed a (1 1 1) preferred orientation. Interfacial Fe³⁺ diffusion was found for both substrates affecting the magnetic behaviour. The temperature dependence of the resistance and magnetoresistance of the films were measured for fields up to 6 T. Negative magnetoresistance values of ∼5% at room temperature and ∼10% at 90 K were obtained for the as-deposited magnetite films either on GaAs(1 0 0) or Al₂O₃(0 0 0 1).     

Perpendicular magnetic anisotropy of V/Co(0 0 1)

Based on the full-potential linearized augmented plane wave (FLAPW) calculations, various magnetic properties of ultra thin face centered cubic (fcc) Co(0 0 1) film and V adsorbed systems on Co(0 0 1) surface are explored. It was found that the V film grown on fcc Co(0 0 1) surface has large induced magnetic moment and the direction of magnetization is antiparallel to that of Co atom in the submonolayer coverage. Very interestingly, we found that the surface alloy and 0.5 ML adsorbed V/Co(0 0 1) systems have perpendicular magnetocrystalline anisotropy and the magnitude of anisotropy energy in 0.5 ML V on fcc Co(0 0 1) surface is greatly larger than that of surface alloy, while we observed in-plane magnetization in pure fcc Co(0 0 1) film. It was found that the spin-orbit interaction through spin-flip process cannot be ignored, therefore the simple relation with orbital anisotropy is not applicable in the interpretation of magnetocrystalline anisotropy.     

Magnetic,structural and electrical properties of ordered and disordered Co50Fe50 films

Co₅₀Fe₅₀ films with thickness varying from 100 to 500 Å were deposited on a glass substrate by sputtering process, respectively. Two kinds of CoFe films were studied: one was the as-deposited film, and the other the annealed film. The annealing procedure was to keep the films at 400 °C for 5 h in a vacuum of 5×10⁻⁶ mbar. From the X-ray study, we find that the as-deposited film prefers the CoFe(1 1 0) orientation. Moreover, the body-centered cubic (bcc) CoFe(1 1 0) line is split into two peaks: one corresponding to the ordered body-centered tetragonal (bct) phase, and the other, the disordered bcc phase. After annealing, the peak intensity of the ordered bct phase becomes much stronger, while that of the disordered bcc phase disappears. The annealing has also caused the ordered CoFe(2 0 0) line to appear. When the amount of the ordered bct phase in Co₅₀Fe₅₀ is increased, the saturation magnetization (M_s) and coercivity (H_c) become larger, but the electrical resistivity (ρ) decreases. From the temperature coefficient of resistance (TCR) measurement, we learn that the bct grains in the CoFe film start to grow at temperature 82 °C.     

Four-fold magnetic anisotropy in a Co film on MgO(0 0 1)

The development of devices based on magnetic tunnel junctions has raised new interests on the structural and magnetic properties of the interface Co/MgO. In this context, we have grown ultrathin Co films (≤30 Å) by molecular-beam epitaxy on MgO(0 0 1) substrates kept at different temperatures (T_S). Their structural and magnetic properties were correlated and discussed in the context of distinct magnetic anisotropies for Co phases reported in the literature. The sample characterization has been done by reflection high energy electron diffraction, magneto-optical Kerr effect and ferromagnetic resonance. The main focus of the work is on a sample deposited at T_S=25 °C, as its particular way of growth has enabled a bct Co structure to settle on the substrate, where it is not normally obtained without specific seed layers. This sample presented the best crystallinity, softer magnetic properties and a four-fold in-plane magnetic anisotropy with Co〈1 1 0〉 easy directions. Concerning the samples prepared at T_S=200 and 500° C, they show fcc and polycrystalline structures, respectively and more intricate magnetic anisotropy patterns.     

Early stages of interface formation of C60 on GaAs(1 0 0)

We present a detailed investigation of the electronic properties of C₆₀ grown on GaAs(1 0 0) substrates, as a function of the fullerene coverage, from the very early stages of interface formation up to the development of a bulk-like fullerene film. We monitor the chemical interactions and the energy levels alignment by means of X-rays, ultraviolet and inverse photoemission spectroscopies. The two latter techniques allow to investigate the electronic structure close to the Fermi level. Energy levels alignment at the interfaces of C₆₀ with p-doped and GaAs(1 0 0) are obtained and discussed.     

High temperature annealing effect on structural and magnetic properties of Ti/Ni multilayers

High temperature annealing effect on structural and magnetic properties of Ti/Ni multilayer (ML) up to 600 °C have been studied and reported in this paper. Ti/Ni multilayer samples having constant layer thicknesses of 50 Å each are deposited on float glass and Si(1 1 1) substrates using electron-beam evaporation technique under ultra-high vacuum (UHV) conditions at room temperatures. The micro-structural parameters and their evolution with temperature for as-deposited as well as annealed multilayer samples up to 600 °C in a step of 100 °C for 1 h are determined by using X-ray diffraction (XRD) and grazing incidence X-ray reflectivity techniques. The X-ray diffraction pattern recorded at 300 °C annealed multilayer sample shows interesting structural transformation (from crystalline to amorphous) because of the solid-state reaction (SSR) and subsequent re-crystallization at higher temperatures of annealing, particularly at ≥400 °C due to the formation of TiNi₃ and Ti₂Ni alloy phases. Sample quality and surface morphology are examined by using atomic force microscopy (AFM) technique for both as-deposited as well as annealed multilayer samples. In addition to this, a temperature dependent dc resistivity measurement is also used to study the structural transformation and subsequent alloy phase formation due to annealing treatment. The corresponding magnetization behavior of multilayer samples after each stage of annealing has been investigated by using Magneto-Optical Kerr Effect (MOKE) technique and results are interpreted in terms of observed micro-structural changes.     

First principles studies of Fe/Co superlattices and multilayers with bcc (0 0 1) and (1 1 0) orientations

The layer resolved magnetic moments and magnetic anisotropy energy of Fe/Co superlattices and multilayers with bcc (0 0 1) and (1 1 0) orientations obtained from first principles simulations are reported here. The magnetic moment of Fe atoms are found to depend on the geometry, coordination number and proximity to Co atoms, whereas that of Co remains almost constant in the superlattices and multilayers. Mixing of atoms at the interface resulted in enhanced Fe magnetic moment while that of Co is unaffected. The magnetic anisotropy energy in superlattices and multilayers are found to be larger than the corresponding values of bulk counterparts. Calculated easy axis of magnetization is in the plane for all superlattice compositions considered in the study, while that in multilayers, changes with crystalline orientation and thickness of Co layers.     

Structural, magnetic and electronic transport properties of MnxGe1−x/Ge(0 0 1) films grown by MBE at 350 °C

We report on the structural, magnetic and electronic transport properties of thin Mn_xGe_1−x films grown at 350 °C. Isolated Mn₅Ge₃ nanoclusters, about 100 nm in size, were formed at the top surface of the film, dominating the magnetic properties of the whole film. Electronic transport properties show Mn doping effect indicating the presence of substitutional Mn ions dispersed in the Ge host, contributing to the formation of a Mn_xGe_1−x diluted phase. Electrical behaviour indicates a saturation effect with the raise of the nominal Mn concentration in the film, above x ≅ 0.03.