Electrodeposition and magnetic properties of Ni nanowire arrays on anodic aluminum oxide/Ti/Si substrate

Ni nanowire arrays with different diameters have now been extended to directly fabricate in porous anodic alumina oxide (AAO) templates on Ti/Si substrate by direct current (DC) electrodeposition. An aluminum film is firstly sputter-deposited on a silicon substrate coated with a 300 nm Ti film. AAO/Ti/Si substrate is synthesized by a two-step electrochemical anodization of the aluminum film on the Ti/Si substrate and then used as template to grow Ni nanowire arrays with different diameters. The coercivity and the squareness in parallel direction of Ni nanowires with about 10 nm diameters are 664 Oe and 0.90, respectively. The Ni nanowire arrays fabricated on AAO/Ti/Si substrates should lead to practical applications in ultrahigh-density magnetic storage devices because of the excellent properties.     

Magnetic optical bifunctional CoPt_3/Co multilayered nanowire arrays

CoPt3/Co multilayered nanowire(NW) arrays are synthesized by pulsed electrodeposition into nanoporous anodic aluminum oxide(AAO) templates. The electrochemistry deposition parameters are determined by cyclic voltammetry to realize the well control of the ratio of Co to Pt and the length of every segment. The x-ray diffraction(XRD) patterns show that both Co and CoPt3 NWs exhibit face-centered cubic( fcc) structures. In the UV-visible absorption spectra,CoPt3/Co NW arrays show a red-shift with respect to pure CoPt3 NWs. Compared with the pure Co nanowire arrays, the CoPt3/Co multilayered nanowire arrays show a weak shape anisotropy and well-modulated magnetic properties. CoPt3/Co multilayered nanowires are highly encouraging that new families of bimetallic nanosystems may be developed to meet the needs of nanomaterials in emerging multifunctional nanotechnologies.     

Magnetic nanowires fabricated by anodic aluminum oxide template—a brief review

Anodic aluminum oxide(AAO) with highly ordered nanoscale pores which are monodisperse and mutually parallel can be produced through a self-organized electrochemical process.Subsequent deposition of materials into the nanopores produces AAO embedded nanowire arrays.Whilst the templates can be further removed to obtain free individual nanowires,the embedded nanowires form an interesting nanocomposite structure.Recent research activities on the fabrication and characteriza-tion of AAO template based magnetic n...     

Control of magnetic anisotropy of Co nanowires

Cobalt nanowires were fabricated by DC electrodeposition onto anodic aluminium oxide (AAO) templates. The effects of AAO pore diameter, current density, pH, annealing and deposition under external magnetic fields on the structure and magnetic properties of the nanowire arrays were studied. It is found that the smaller pore size produces high crystallinity, resulting in improved magnetic performance at low current density. The pH can transform fcc-Co phase to hcp-Co phase, with the easy axis along the nanowire axis switched over to the perpendicular direction. Annealing demonstrates excellent thermal stability of the magnetic nanowire arrays at high temperature. The application of external magnetic field during deposition influences the growth habit of the nanowires, leading to the change in the magnetic properties.     

Synthesis and magnetic properties of ordered barium ferrite nanowire arrays in AAO template

BaFe₁₂O₁₉ nanowire arrays having single magnetic domain size (≤460 nm) in anodic aluminum oxide (AAO) templates were prepared by sol-gel and self-propagating high-temperature synthesis techniques. The diameter of the nanowire arrays is approximately 70 nm and the length is about 2-4 μm. The specimens were characterized using X-ray diffraction, vibrating sample magnetometer, field emission scan electron microscope, atomic force microscopy and microwave vector network analyzer. The magnetic properties of BaFe₁₂O₁₉ nanowire arrays embedded in AAO templates were measured by VSM with a field up to 1274 KA/m at room temperature. The results indicate that the nanowire arrays exhibit large saturation magnetization and high coercivity in the range of 6000 Oe and an obvious magnetic anisotropy with the easy magnetizing axis along the length of the nanowire arrays, probably due to the shape anisotropy and magneto-crystalline anisotropy. Finally the microwave absorption properties of the nanowires were discussed.     

Synthesis and magnetic properties of spinel CoFe2O4 nanowire arrays

Spinel CoFe₂O₄ nanowire arrays were synthesized in nanopores of anodic aluminum oxide (AAO) template using aqueous solution of cobalt and iron nitrates as precursor. The precursor was filled into the nanopores by vacuum impregnation. After heat treatment, it transformed to spinel CoFe₂O₄ nanowires. The structure, morphology and magnetic properties of the sample were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). The results indicate that the nanowire arrays are compact. And the individual nanowires have a high aspect ratio, which are about 80 nm in diameter and 10 μm in length. The nanowires are polycrystalline spinel phase. Magnetic measurements indicate that the nanowire arrays are nearly magnetic isotropic. The reason is briefly discussed. Moreover, the temperature dependence of the coercive force of the nanowire arrays was studied.     

Fabrication and structural properties of LaFeO3 nanowires by an ethanol–ammonia-based sol–gel template route

Highly ordered LaFeO₃ nanowire arrays of composite oxides were synthesized within porous anodic aluminum oxide (AAO) templates by an ethanol–ammonia-based sol–gel route. The results of scanning electron microscopy and transmission electron microscopy revealed that the obtained LaFeO₃ nanowires had a uniform length and diameter, which were determined by the thickness and the pore diameter of the applied AAO template. Energy-dispersive X-ray spectroscopy demonstrated that the stoichiometric LaFeO₃ was formed. Furthermore, the results of X-ray diffraction and selected-area electron diffraction indicated that the LaFeO₃ nanowires had a perovskite-type crystalline structure. It is expected that the novel and effective technique presented in this article would also be appropriate for the preparation of nanowires of other mono-component or multi-component oxides. PACS 61.66.Fn; 61.46.+w; 81.20.Fw     

Growth and magnetic properties of single crystalline Ni nanowire arrays prepared by pulse DC electrodeposition

Highly textured Ni nanowire arrays were fabricated into anodic aluminum oxide(AAO) templates by pulse DC electrodeposition.The applied voltage and pH value of electrolytes were found strongly affecting the microstructure and magnetic properties of Ni nanowire arrays.Low applied potential and pH value both prefer to form polycrystalline fcc Ni nanowires.Increasing the applied potential or pH value favors the Ni [220] texture and even eventually forms the [220] oriented single crystal Ni wires,while exorbitan...     

Fabrication and optical properties of platinum nanowire arrays on anodic aluminium oxide templates

Arrays of Pt nanowires, fabricated by electrodepositing Pt metal into nanoporous anodic aluminium oxide (AAO) templates, exhibit a preferable optical absorption band in the ultraviolet-visible (UV-VIS) spectra and present a blueshift as the wire aspect ratio increases or its radius decreases. This type of optical property of Pt nanowire/porous alumina composites has been theoretically explored using Maxwell－Garnett (MG) effective medium theory. The MG theory, however, is only applicable to nanowires with an infinitesimally small radius relative to the wavelength of an incident light. The nanowire radius is controlled by the pore radius of the host alumina, which depends on anodizing conditions such as the selected electrolyte, anodizing time, temperature and voltage. The nanowire aspect ratios depend on the amount of Pt deposited into the nanopores of AAO films. The optical absorption properties of the arrays of Pt nanowires with diameters of 24, 55 and 90 nm have been investigated by the UV-VIS spectra, which show that the extinction maximum (λ_max) shifts to shorter wavelength side as the wire aspect ratio increases or its radius decreases. The results are qualitatively consistent with those calculated based on the MG theory.     

Electroless synthesis of large scale Co-Zn-P nanowire arrays and the magnetic behaviour

Co-Zn-P nanowire arrays have been synthesized by electroless deposition in an anodic alumina membrane (AAM). The images of Co-Zn-P nanowire arrays and single nanowires are obtained by both scanning electron microscope (SEM) and transmission electron microscope (TEM), respectively. Selected area electron diffraction (SAED), X-ray diffraction (XRD) and energy dispersive spectra (EDS) are employed to study the morphology and chemical composition of the nanowires. The results indicate that Co-Zn-P nanowire arrays are amorphous in structure. The hysteresis loops characterized by a vibrating sample magnetometer (VSM) show that the easily magnetized direction of Co-Zn-P nanowire arrays is parallel to the nanowire arrays and that there exhibits clearly a magnetic anisotropy as a result of the shape anisotropy.     

铋纳米线中电导的温度依赖性

采用电沉积的方法在多孔氧化铝模板中合成了直径为30 nm且沿着[0112]方向生长的单晶铋纳米线,测量了纳米线电导随着温度78～320 K变化的关系曲线. 结果发现,其半金属半导体转变的温度为230 K,且纳米线的电导有很强的温度依赖性.     

Synthesis and characteristics of Co100−xSnx nanowire arrays

Co_100?xSn_x alloy nanowires were fabricated by electrodeposition of Co²⁺ and Sn²⁺ into anodic aluminum oxide (AAO) templates. X-ray diffraction results indicate that the crystal structures of the nanowires changed from polycrystal to amorphism, and then to polycrystal again with the increase of Sn content in the nanowires. Transmission electron microscopy result shows that the nanowires are about 50 nm in diameter and the aspect ratio is approximately 75. The magnetic response of the arrays was measured using vibrating sample magnetometry at room temperature. The results show that the coercivity and squareness with the magnetic field along the nanowire arrays decrease with the increase of the Sn content. Nanowires exhibit obviously uniaxial magnetic anisotropy, and the easy magnetizing axis is parallel to the nanowires owing to the large shape anisotropy.     

Growth mechanism studies of ZnO nanowire arrays via hydrothermal method

Well-controlled ZnO nanowire arrays have been synthesized using the hydrothermal method, a low temperature and low cost synthesis method. The process consists of two steps: the ZnO buffer layer deposition on the substrate by spin-coating and the growth of the ZnO nanowire array on the seed layer. We demonstrated that the microstructure and the morphology of the ZnO nanowire arrays can be significantly influenced by the main parameters of the hydrothermal method, such as pH value of the aqueous solution, growth time, and solution temperature during the ZnO nanowire growth. Scanning electron microscopy observations showed that the well oriented and homogeneous ZnO nanowire arrays can be obtained with the optimized synthesis parameters. Both x-ray diffraction spectra and high-resolution transmission electron microscopy (HRTEM) observations revealed a preferred orientation of ZnO nanowires toward the c-axis of the hexagonal Wurtzite structure, and HRTEM images also showed an excellent monocrystallinity of the as-grown ZnO nanowires. For a deposition temperature of 90 °C, two growth stages have been identified during the growth process with the rates of 10 and 3 nm/min, respectively, at the beginning and the end of the nanowire growth. The ZnO nanowires obtained with the optimized growth parameters owning a high aspect ratio about 20. We noticed that the starting temperature of seed layer can seriously influence the nanowire growth morphology; two possible growth mechanisms have been proposed for the seed layer dipped in the solution at room temperature and at a high temperature, respectively.     

Fabrication of Anodic Aluminum Oxide Templates with Small Interpore Distances

The influence of the electropolishing and anodization voltage on surface morphology has been carefully studied for fabrication of ordered anodic aluminum oxide （AAO） templates. In accordance with that in the anodization experiment, the size of small patterns on the foil surface formed from the electropolishing treatment increases with voltage. Using a combined method of small-voltage eleetropolishing and anodization, we have fabricated well ordered templates with much smaller interpore distances compared with that under normal-voltage fabrication conditions. The Ni nanowire arrays with two small diameters are eleetrodeposited through the above templates, exhibiting different magnetic properties. This also helps us to clarify the inner structure of this kind of templates.     

Synthesis of ordered ZnO nanowire arrays from aqueous solution using AAO template

In this paper we report a simple method that enables the easy fabrication of ordered ZnO nanowire arrays using Anodic Aluminium Oxide (AAO) template. We have used a vacuum injection technique to fill solution into the pores of an AAO template. The AAO template has been fabricated by a two-step anodization process using 0.3 M oxalic acid (H₂C₂O₄) solution under a constant voltage of 40 V. The AAO template formed through this process has been detached from Al substrate via an anodic voltage pulse using perchloric acid (HClO₄) solution (70%). The nanowires of ZnO have been synthesized by injecting the saturated Zn(NO₃)₂ solution into the pores of the detached AAO template using a vacuum pump. The ZnO nanowires synthesized by this technique have been found dense & continuous with uniform diameter throughout the length of the wire. The structural characteristics of AAO template and ZnO nanowires have been studied by Field Emission Scanning Electron Microscope (FESEM), Atomic force microscope (AFM) and Transmission Electron Microscope (TEM).     

Fabrication and magnetic properties of Fe3O4 nanowire arrays in different diameters

Fe₃O₄ nanowire arrays with different diameters of D=50, 100, 150 and 200 nm were prepared in anodic aluminum oxide (AAO) templates by an electrodeposition method followed by heat-treating processes. A vibrating sample magnetometer (VSM) and a Quantum Design SQUID MPMS magnetometer were used to investigate the magnetic properties. At room temperature the nanowire arrays change from superparamagnetism to ferromagnetism as the diameter increases from 50 to 200 nm. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization measurements show that the blocking temperature T_B increases with the diameter of nanowire. The ZFC curves of D=50 nm nanowire arrays under different applied fields (H) were measured and a power relationship between T_B and H were found. The temperature dependence of coercivity below T_B was also investigated. Mössbauer spectra and micromagnetic simulation were used to study the micro-magnetic structure of nanowire arrays and the static distribution of magnetic moments of D=200 nm nanowire arrays was investigated. The unique magnetic behaviors were interpreted by the competition of the demagnetization energy of quasi-one-dimensional nanostructures and the magnetocrystalline anisotropy energy of particles in nanowires.     

Template synthesis of single-crystal Cu nanowire arrays by electrodeposition

Cu nanowire arrays have been synthesized using potentiostatic electrodeposition within the confined nanochannels of a porous anodic alumina membrane. The Cu nanowire arrays and the individual nanowires have been characterized using SEM, TEM, SAED, HREM and XRD. Investigation results reveal that the Cu nanowire arrays having high wire packing densities are highly ordered over large areas. The individual Cu nanowires (diameter ∼60 nm) were single-crystal and found to be dense and continuous with uniform diameters throughout their entire length. An optimum ECD condition (at lower overpotentials) for the synthesis of single-crystal Cu nanowires was also discussed. Received: 19 April 2001 / Accepted: 28 April 2001 / Published online: 20 June 2001     

Fabrication of CoFe_2O_4 ferrite nanowire arrays in porous silicon template and their local magnetic properties

CoFe_2O_4 ferrite nanowire arrays are fabricated in porous silicon templates. The porous silicon templates are prepared via metal-assisted chemical etching with gold(Au) nanoparticles as the catalyst. Subsequently, CoFe_2O_4 ferrite nanowires are successfully synthesized into porous silicon templates by the sol–gel method. The magnetic hysteresis loop of nanowire array shows an isotropic feature of magnetic properties. The coercivity and squareness ratio(M_r/M_s) of ensemble nanowires are found to be 630 Oe(1 Oe = 79.5775 A·m~(-1) and 0.4 respectively. However, the first-order reversal curve(FORC) is adopted to reveal the probability density function of local magnetostatic properties(i.e., interwire interaction field and coercivity). The FORC diagram shows an obvious distribution feature for interaction field and coercivity. The local coercivity with a value of about 1000 Oe is found to have the highest probability.     

Diameter-dependent electrical transport properties of bismuth nanowire arrays

Single-crystalline bismuth nanowire arrays with different diameters were fabricated within porous anodic alumina membranes with the same pore size using the pulsed electro-deposition technique. X-ray diffraction measurements show that the as-synthesized nanowires have a highly preferential orientation. Scanning electron microscopy, transmission electron microscopy and high-resolution transmission electron microscopy analyses indicate that bismuth nanowire arrays are high filling, ordered and single-crystalline. Electrical resistance measurements show that the bismuth nanowires have a metal-semiconductor transition when the diameters decrease from 90 to 50 nm, and the resistance behaviors are explained on the basis of the quantum confinement effect and Matthiessen’s rule.     

NiFe2O4纳米线阵列的制备与磁性

在氧化铝模板的纳米孔洞中, 用电化学的方法沉积铁镍合金纳米线，经过550℃30h氧化处理 , 成功制备出 NiFe2O4纳米线阵列. 分别用扫描电子显微镜 (SEM) 、透射电 子显微镜 (TEM) 、x射线衍射仪 (XRD) 和振动样品磁场计 (VSM) 对样品的形貌、晶体结构 和磁学性质进行了表征测试. SEM和TEM观察结果显示氧化铝模板的孔洞分布均匀，孔心距约 为110nm; 纳米线的直径约为70nm. XRD显示纳米线阵列的物相结构为NiFe2O4; VSM测试结果表明，NiFe2O4纳米线阵列膜的易磁化方向垂直于膜面. 当垂直 磁化时磁滞回线的矩形比约为05，矫顽力为41×103A/m，比氧化处理前的铁镍合金 纳米线阵列都有显著提高. 关键词： 纳米线 Ni Fe2O4 矫顽力