Surface modifications of ultra-thin gold films by swift heavy ion irradiation

Gold films of thickness 10 and 20 nm grown on float glass substrate by thermal evaporation technique were irradiated with 107 MeV Ag⁸⁺ and 58 MeV Ni⁵⁺ ions at different fluences and characterized by Grazing Incidence X-ray Diffraction (GIXRD) and Atomic Force Microscopy (AFM). The pristine films were continuous and no island structures were found even at these small thicknesses. The surface roughness estimated from AFM data did not show either monotonic increase or decrease with ion fluences. Instead, it increased at low fluences and decreased at high fluences for 20 nm thick film. In the 10 nm film roughness first increased with ion fluence, then decreased and again increased at higher fluences. The pattern of variation, however, was identical for Ni and Ag beams. Both the beams led to the formation of cracks on the film surface at intermediate fluences. The observed ion-irradiation induced thickness dependent topographic modification is explained by the spatial confinement of the energy deposited by ions in the reduced dimension of the films.     

125 MeV Si ion irradiation of calcium phosphate thin film coated by rf-magnetron sputtering technique

Titanium substrate was coated with hydroxyapatite by radiofrequency magnetron sputtering (rf-magnetron sputtering) technique and subjected to swift heavy ion (SHI) irradiation of 125 MeV with Si⁹⁺ at fluences of 1 × 10¹⁰, 1 × 10¹¹ and 1 × 10¹² ions/cm². The glancing incidence X-ray diffraction (GIXRD) analysis confirmed the HAp phase of the irradiated film. There was a considerable decrease in crystallinity and particle size after irradiation. In addition, DRS-UV reflectance spectra revealed a decrease in optical band gap (E_g) from 5.2 to 4.6 eV. Wettability of biocompatible materials plays an important role in biological cells proliferation for tissue engineering, drug delivery, gene transfer and bone growth. HAp thin films irradiated with 1 × 10¹¹ ions/cm² fluence showed significant increase in wettability. While the SHI irradiated samples exhibited enhanced bioactivity, there was no significant variation in cell viability. Surface roughness, pores and average particle size were analyzed by atomic force microscopy (AFM).     

Effect of 160 MeV Ni ion irradiation on PbS quantum dots

PbS quantum dots of average size 10 nm are encapsulated in a matrix (polyvinyl alcohol (PVA)) following chemical route. They are irradiated with 160 MeV Ni¹²⁺ ion beam with fluences 10¹²-10¹³ ions/cm². Red shift in the absorption response in the optical absorption spectra reveal size enhancement of the quantum dots after irradiation and was confirmed by transmission electron microscopy (TEM). Photoluminescence (PL) study was carried out with excitation wavelength 325 nm on both unirradiated and irradiated samples at different fluences and fluence-dependent surface states and excitonic emission is observed in the PL study. The Huang-Rhys coupling constant decreases significantly after swift heavy ion (SHI) irradiation and shows a decreasing trend with increase in ion fluence.     

Evolution of surface morphology of NiO thin films under swift heavy ion irradiation

NiO nanoparticle thin films grown on Si substrates were irradiated by 107 MeV Ag⁸⁺ ions. The films were characterized by glancing angle X-ray diffraction and atomic force microscopy. Ag ion irradiation was found to influence the shape and size of the nanoparticles. The pristine NiO film consisted of uniform size (∼100 nm along major axis and ∼55 nm along minor axis) elliptical particles, which changed to also of uniform size (∼63 nm) circular shape particles on irradiation at a fluence of 3 × 10¹³ ions cm⁻². Comparison of XRD line width analysis and AFM data revealed that the particles in the pristine films are single crystalline, which turn to polycrystalline on irradiation with 107 MeV Ag ions.     

SHI induced silicide formation and surface morphology at Co/Si system

Ion beam mixing is a useful technique to produce modifications at the surface and interface of the solid material. In the present work, ion beam induced modifications at Co/Si interface using 120 MeV Au-ion irradiation has been studied at ion fluences in the range of 10¹² to 10¹⁴ ions/cm² by secondary ion mass spectroscopy (SIMS) technique and calculated mixing efficiency at the interface. Silicide formation has been discussed on the basis of swift heavy ion (SHI) irradiation induced effects. Surface morphology and roughness of irradiated system with fluence 5 × 10¹³ and 1 × 10¹⁴ ions/cm² is studied by scanning tunneling microscopy (STM). Roughness of the surface shows marks of melting process and confirms the appearance of some pinholes in the reacted Co/Si system. Comparative study was also undertaken on annealed sample at 300 °C and then irradiated at a dose 1 × 10¹⁴ ions/cm².     

Structural phase diagram for ZnS nanocrystalline thin films under swift heavy ion irradiation

The synthesis of nanocrystalline ZnS thin films by pulsed laser deposition and their modification by swift heavy ions are presented. The irradiations with 150 MeV Ni ions at fluences of 1×10¹¹, 1×10¹² and 1×10¹³ ions/cm² have been used for these studies. Irradiation results in structural phase transformation and bandgap modification of these films are investigated by using X-ray diffraction and UV-visible absorption measurements, respectively. Since stoichiometry changes induced by irradiation can contribute to the modification of these properties, elastic recoil detection analysis has been performed on pristine and 150 MeV Ni ions irradiated ZnS thin films using a 120 MeV Ag ion beam. The stoichiometry of the films has been found to be similar for pristine and ion irradiated samples. A structural phase diagram based on thermal and pressure spikes has been constructed to explain the structural phase transformation.     

Ripple topography on thin ZnO films by grazing and oblique incidence ion sputtering

We have investigated the formation and growth of nano sized ripple topography on ZnO thin films by 10 keV O¹⁺ bombardment at impact angles of 80° and 60°, varying the ion fluence from 5 × 10¹⁶ to 1 × 10¹⁸ ions/cm². At 80° the ripples are oriented along the ion beam direction whereas at 60° it is perpendicular to the ion beam direction. The developed ion induced structures are characterized by atomic force microscopy (AFM) and the alignment, variation of rms roughness, wavelength and correlation length of the structures are discussed with the existing model and basic concept of ion surface interaction.     

Luminescence studies on swift heavy ion irradiated nanocrystalline aluminum oxide

Pellets of nanocrystalline aluminum oxide synthesized by a combustion technique are irradiated with 120 MeV Au⁹⁺ ions for fluence in the range 5×10¹¹-1×10¹³ ions cm⁻². Two photoluminescence (PL) emissions, a prominent one with peak at ∼525 nm and a shoulder at ∼465 nm are observed in heat treated and Au⁹⁺ ion irradiated aluminum oxide. The 525 nm emission is attributed to F₂²⁺-centers. The PL intensity at 525 nm is found to increase with increase in ion fluence up to 1×10¹² ions cm⁻² and decreases beyond this fluence. Thermoluminescence (TL) of heat-treated and swift heavy ion (SHI) irradiated aluminum oxide gives a strong and broad TL glow with peak at ∼610 K along with a weak shoulder at 500 K. The TL intensity is found to increase with Au⁹⁺ ion fluence up to 1×10¹³ ions cm⁻² and decreases beyond this fluence.     

Effect of 100 MeV Ni ion irradiation on MOCVD grown n-GaN

Metal-organic chemical vapor deposition (MOCVD) grown n-type Gallium nitride (GaN) has been irradiated with 100 MeV Ni⁹⁺ ions at room temperature. Atomic force microscopy (AFM) images show the nano-clusters' formation upon irradiation and the irradiated GaN surface roughness increases with the increasing ion fluences. High-resolution X-ray diffraction (HR-XRD) analysis reveals the formation of Ga₂O₃ due to the interface mixing of GaN/Al₂O₃ upon irradiation. FWHM values of GaN (0 0 0 2) increases due to the lattice disorder. Photoluminescence studies show reduced band edge emission and yellow luminescence (YL) intensity with the increasing ion fluences. Change in the band gap energy between 3.38 and 3.04 eV was measured by UV-visible optical absorption spectrum on increasing the ion fluences.     

Effect of swift heavy ion irradiation on photoluminescence properties of ZnO/PMMA nanocomposite films

We report a study on the SHI induced modifications on structural and optical properties of ZnO/PMMA nanocomposite films. The ZnO nanoparticles were synthesized by the chemical route using 2-mercaptoethanol as a capping agent. The structure of ZnO nanoparticles was confirmed by XRD, SEM and TEM. These ZnO nanoparticles were dispersed in the PMMA matrix to form ZnO/PMMA nanocomposite films by the solution cast method. These ZnO/PMMA nanocomposite films were then irradiated by swift heavy ion irradiation (Ni⁸⁺ ion beam, 100 MeV) at a fluence of 1×10¹¹ ions/cm². The nanocomposite films were then characterized by XRD, UV-vis absorption spectroscopy and photoluminescence spectroscopy. As revealed from the absorption spectra, absorption edge is not changed by the irradiation but the optical absorption is increased. Enhanced green luminescence at about 527 nm and a less intense blue emission peak around 460 nm were observed after irradiation with respect to the pristine ZnO/PMMA nanocomposite film.     

Effect of swift heavy ion irradiation on dilute Fe-doped Sb0.95Se0.05 magnetic semiconductor

A thin film of dilute Fe (0.008)-doped Sb_0.95Se_0.05 alloy was grown on silicon substrate using the thermal evaporation technique. This film was irradiated with swift heavy ions (SHIs) Ag⁺¹⁵ having 200?MeV energy at ion fluences of 1?×?10¹² and 5?×?10¹² ions per cm², respectively. The thickness of the thin film was ～500?nm. We study the effect of irradiation on structural, electrical, surface morphology and magnetic properties of this film using grazing angle XRD (GAXRD), DC resistivity, atomic force microscopy (AFM) and magnetic force microscopy (MFM), respectively. GAXRD suggests that no significant change is observed in this system due to SHI irradiation. The average crystallite size increases with fluence, whereas the AFM image shows the rms roughness decreases due to irradiation with respect to the un-irradiated thin film. The MFM image shows that the magnetic interaction in irradiated film decreases due to the irradiation effect. Although the un-irradiated sample shows metal to semiconducting transition, but after irradiation with fluence of 5?×?10¹² ions per cm², the sharpness of the metal to semiconducting phase transition is observed to increase dramatically at ～300?K. This characteristic of the thin film makes it a promising candidate for an electrical switching device after irradiation.     

Defects induced magnetic transition in Co doped ZnS thin films: Effects of swift heavy ion irradiations

The effect of swift heavy ions (SHI) on magnetic ordering in ZnS thin films with Co ions substituted on Zn sites is investigated. The materials have been synthesized by pulsed laser deposition on substrates held at 600 °C for obtaining films with wurtzite crystal structure and it showed ferromagnetic ordering up to room temperature with a paramagnetic component. 120 MeV Ag ions have been used at different fluences of 1×10¹¹ ions/cm² and 1×10¹² ions/cm² for SHI induced modifications. The long range correlation between paramagnetic spins on Co ions was destroyed by irradiation and the material became purely paramagnetic. The effect is ascribed to the formation of cylindrical ion tracks due to the thermal spikes resulting from electron–phonon coupling.     

Structural modifications of diamond like carbon films induced by MeV nitrogen ion irradiation

Diamond-like carbon (DLC) films were deposited on Si(1 0 0) substrates using plasma deposition technique. The deposited films were irradiated using 2 MeV N⁺ ions at fluences of 1×10¹⁴, 1×10¹⁵ and 5×10¹⁵ ions/cm². Samples have been characterized by using Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and high-resolution transmission electron microscopy (HRTEM). Analysis of Raman spectra shows a gradual shift of both D and G band peaks towards higher frequencies along with an increase of the intensity ratio, I(D)/I(G), with increasing ion fluence in irradiation. These results are consistent with an increase of sp² bonding. XPS results also show a monotonic increase of sp²/sp³ hybridization ratio with increasing ion fluence. Plan view TEM images show the formation of clusters in the irradiated DLC films. HRTEM micrographs from the samples irradiated at a fluence of 5×10¹⁵ ions/cm² show the lattice image with an average interplanar spacing of 0.34 nm, revealing that the clusters are graphite clusters. The crystallographic planes in these clusters are somewhat distorted compared to the perfect graphite structure.     

Engineering of hydrophilic and plasmonic properties of Ag thin film by atom beam irradiation

Hydrophilic Ag nanostructures were synthesized by physical vapour deposition of 5 nm Ag thin films followed by irradiation with 1.5 keV Ar atoms. Optical absorbance measurements show a characteristic surface plasmon resonance absorption band in visible region. A blue-shift in absorbance from 532 to 450 nm is observed with increasing fluence from 1 × 10¹⁶ to 3 × 10¹⁶ atoms/cm². Atomic force microscopy was performed for the pristine and irradiated samples to study the surface morphology. The atom beam irradiation induced sputtering and surface diffusion lead to the formation of plasmonic surface. Rutherford backscattering spectroscopy of the pristine and irradiated film indicates that metal content in the film decreases with ion fluence, which is attributed to the sputtering of Ag by Ar atoms. The contact angle measurement demonstrates the possibility of engineering the hydrophilicity by atom beam irradiation.     

Surface modifications by swift heavy-ion irradiation of indium phosphide

InP (001) samples were irradiated with 200 MeV Au ions at different fluences. The surface nanotopographical changes due to increasing fluence of swift heavy ions were observed by Atomic Force Microscopy (AFM), where the onset of a large increase in surface roughness for fluences sufficient to cause complete surface amorphization was observed. Transmission Electron Microscopy (TEM) was used to observe bulk-ion tracks that formed in InP, and high resolution TEM (HRTEM) revealed that single-ion tracks might not be amorphous in nature. Surface-ion tracks were observed by AFM in the form of ill-defined pits (hollows) of ~12 nm in diameter (width). In addition, Rutherford backscattering was utilized to follow the formation of disorder to amorphization in the irradiated material. The interpretation of the large increase in surface roughness with the onset of amorphization can be attributed to the plastic phenomena induced by the change of states from crystalline to amorphous by ion irradiation. The text was submitted by the authors in English.     

The effects of xenon ion irradiation on the photoluminesce behavior of poly(p-cresolformaldeyde)/diazonaphtoquinone thin films

In the present paper, we investigate the origin of photoluminescence (PL) and the changes in the optical properties: refractive index and absorption coefficient, in poly(p-cresolformaldeyde) and diazonaphtoquinone thin films irradiated with Xe ions. Films 400 nm thick have been irradiated with 800 keV Xe²⁺ ions in a fluence range from 10¹³ to 6 × 10¹⁵ Xe cm⁻². The structural modifications were followed by the techniques of nuclear reaction analysis, elastic recoil detection analysis, Rutherford backscattering, Fourier transform infrared and Raman spectroscopies. The PL behavior was characterised with 488 nm excitation wavelength. The pristine films show emission with maxima of the main bands located at 635, 720 and 830 nm. For fluences up to 10¹⁴ Xe cm⁻², the photoluminescence intensity increases with the irradiation fluence. The chain mobility lowering, characterized by the crosslinked structure, explains this behavior in organic systems. Other possible contribution for increasing of PL intensity, at these fluences, is the presence of oxygen trapped in the polymer chains by the dangling bonds. At intermediate and higher fluences, the photoluminescence starts to decrease. At fluences higher than 10¹⁴ Xe cm⁻², irreversible changes of the organic structure occur and they are characterized by large losses of oxygen and hydrogen, transforming the material into amorphous carbon films. The loss of photoluminescent behavior is associated with the light absorption characteristics of the amorphous carbon structure. This conclusion is supported by the observed increase of the refractive indexes and absorption coefficients, obtained in the infrared region, as well as by the Raman results. Also, the effect of irradiation modifying the refractive index in the infrared region suggests the application of these films as waveguide in this region of wavelength.     

Swift heavy ion irradiation induced modification of BiFeO3 thin films prepared by sol-gel method

We report the preparation of multiferroic BiFeO₃ thin films on ITO coated glass substrates through sol-gel spin coating method followed by thermal annealing and their modification by swift heavy ion (SHI) irradiation. X-ray diffraction and Raman spectroscopy studies revealed amorphous nature of the as deposited films. Rhombohedral crystalline phase of BiFeO₃ evolved on annealing the films at 550°C. Both XRD and Raman studies indicated that SHI irradiation by 200 MeV Au ions result in fragmentation of particles and progressive amorphization with increasing irradiation fluence. The average crystallite size estimated from the XRD line width decreased from 38 nm in pristine sample annealed at 550°C to 29 nm on irradiating these films by 200 MeV Au ions at 1 × 10¹¹ ions cm⁻². Complete amorphization of the rhombohedral BiFeO₃ phase occurs at a fluence of 1 × 10¹² ions.cm⁻². Irradiation by another ion (200 MeV Ag) had the similar effect. For both the ions, the electronic energy loss exceeds the threshold electronic energy loss for creation of amorphized latent tracks in BiFeO₃.     

Study of optical band gap, carbonaceous clusters and structuring in CR-39 and PET polymers irradiated by 100 MeV O ions

Commercially purchased CR-39 and PET polymers were irradiated by 100 MeV O⁷⁺ ions of varying fluences, ranging from 1×10¹¹ to 1×10¹³ ions/cm². The effects of swift heavy ions (SHI) on the structural, optical and chemical properties of CR-39 and PET polymers were studied using X-ray diffraction (XRD), UV-visible spectroscopy and Fourier transform infrared (FTIR) spectroscopy. The XRD patterns of CR-39 show that the intensity of the peak decreases with increasing ion fluence, which indicates that the semicrystalline structure of polymer changes to amorphous with increasing fluences. The XRD patterns of PET show a slight increase in the intensity of the peaks, indicating an increase in the crystallinity. The UV-visible spectra show the shift in the absorbance edge towards the higher wavelength, indicating the change in band gap. Band gap in PET and CR-39 found to be decrease from 3.87 to 2.91 and 5.3-3.5 eV, respectively. The cluster size also shows a variation in the carbon atoms per cluster that varies from 42 to 96 in CR-39 and from 78 to 139 in PET. The FTIR spectra show an overall reduction in intensity of the typical bands, indicating the degradation of polymers after irradiation.     

Impact of 100 MeV Au on the surface of relaxed Si0.5Ge0.5 alloy films studied by atomic force microscopy

We demonstrate a gradual surface modification process of relaxed Si_0.5Ge_0.5 alloy films by 100 MeV Au beam with fluence varying between 5 × 10¹⁰ and 1 × 10¹² ions/cm² at 80 K by means of atomic force microscopy (AFM). Presence of Ge quantum dots (QDs) was found in the virgin sample. The disappearance of the QDs were noticed when the samples were irradiated with a fluence of 5 × 10¹⁰ ions/cm². Craters were found developing at a fluence of 1 × 10¹¹ ions/cm². Apart from the evolution of the craters, blisters were also detected at a fluence of 1 × 10¹² ions/cm². Variation of the average root mean square value of the surface roughness as a function of fluence was examined.     

Ag implantation-induced modification of Ni–Ti shape memory alloy thin films

Nanocrystalline thin films of Ni–Ti shape memory alloy are deposited on an Si substrate by the DC-magnetron co-sputtering technique and 120?keV Ag ions are implanted at different fluences. The thickness and composition of the pristine films are determined by Rutherford Backscattering Spectrometry (RBS). X-Ray diffraction (XRD), atomic force microscopy (AFM) and four-point probe resistivity methods have been used to study the structural, morphological and electrical transport properties. XRD analysis has revealed the existence of martensitic and austenite phases in the pristine film and also evidenced the structural changes in Ag-implanted Ni–Ti films at different fluences. AFM studies have revealed that surface roughness and grain size of Ni–Ti films have decreased with an increase in ion fluence. The modifications in the mechanical behaviour of implanted Ni–Ti films w.r.t pristine film is determined by using a Nano-indentation tester at room temperature. Higher hardness and the ratio of higher hardness (H) to elastic modulus (E_r) are observed for the film implanted at an optimized fluence of 9?×?10¹⁵ ions/cm². This improvement in mechanical behaviour could be understood in terms of grain refinement and dislocation induced by the Ag ion implantation in the Ni–Ti thin films.