臭氧化法表面改性聚苯乙烯薄膜

 为增强聚苯乙烯(PS)与聚乙烯醇(PVA)之间的结合力,进而提高PS-VA双层空心微球存活率。利用臭氧化改性法在酸性介质中对聚苯乙烯薄膜进行表面改性,用红外光谱对处理后的表面进行了半定量的分析。结果表明：改性过后聚苯乙烯表面产生羟基、羰基等极性基团;接触角测试证明,处理后的表面由憎水变为亲水,并通过纳米压痕划痕法得到了处理前后PS与PVA薄膜之间的相互作用强度,臭氧化改性后PS与PVA膜间作用强度增大了40%。     

非离子型表面活性剂Tween 20对大尺寸双层空心微球制备的影响

为了改善臭氧处理聚苯乙烯(PS)单层球与聚乙烯醇(PVA)溶液生成的双层乳粒在油相中的分散性,提高大尺寸双层球的成活率,在双层球制备过程中采用了非离子型表面活性剂Tween 20(T-20)来改性该种PS单层球。结果表明经表面活性剂T-20改性后显著降低了PS薄膜的亲水接触角,提高了PS与PVA间的相互作用,同时也大幅度提高了PS薄膜对PVA的吸附速率。红外光谱和紫外-可见分光光度计的测试结果证明:在PVA固化过程中,由于PVA与T-20的相比太大,PS表面吸附的表面活性剂T-20部分会被PVA置换、迁移至PVA溶液中。T-20的迁移提高了制备双层球过程中水相与外油相的粘度比且显著降低PVA溶液表面张力,从而有利于实现双重乳粒在油相中的单分散。因此,T-20是制备大尺寸PS-PVA双层空心微球有效的表面活性剂。     

离子型表面活性剂对双重乳粒分散性能的影响

为了改善臭氧处理PS单层球与PVA溶液生成的双重乳粒在油相中的分散性,采用了低分子量阴离子型表面活性剂十二烷基硫酸钠(SDS)和十二烷基苯磺酸钠(SDBS)及高分子量混合型表面活性剂十八烷基胺聚氧乙烯醚双季铵盐(PAVDA)来改性该种PS单层球,测试并分析了不同表面活性剂对相应薄膜亲水接触角及其对PVA吸附速率的影响,同时也考察并对比了静电排斥作用和空间位阻作用对双重乳粒分散性的影响。实验结果表明这三种表面活性剂均能不同程度的改善双重乳粒在油相中的分散性。其中,经SDS和SDBS处理后,双重乳粒在油相中固化时会发生絮凝作用而无法以较高成活率制得大尺寸双层球;经PAVDA处理PS单层球后,实现了以较高的成活率制得700~900μm的PS-PVA双层空心微球。同时,也表明在改善PS单层球的分散性方面,空间位阻稳定作用较静电排斥作用更为有效。     

充气温度对PS-PVA-CH塑料微球性能的影响

 主要研究了PS-PVA-CH空心塑料微球充气时，充气平衡温度对微球强度、球形度和表面形貌的影响。对PS，PVA和CH材料的热重分析结果表明，PS和PVA具有较高的分解温度，而PS-PVA双层球和PS-PVA-CH塑料微球升温后的耐外压实验表明，温度升高后双层球耐外压强度降低很快，不能满足充Ar气需要；而3层球在100~120℃仍有很高强度，在该温度下，可以实现充Ar气。微球表面形貌分析结果显示，高温充气后，3层球表面粗糙度升高。     

PS-RF双层空心微球的制备

 采用聚苯乙烯(PS)空心微球为模板,间苯二酚-甲醛(RF)为前驱体溶液,邻苯二甲酸二丁酯为分散剂,以界面聚合反应为基础初步总结出一条PS-RF双层聚合物空心微球的制备工艺,并就制备过程中RF溶液与分散剂油相的选择、预聚时间、搅拌速率、固化温度等影响因素进行了讨论。当RF溶液质量分数为25%,间苯二酚与碳酸钠的物质的量之比为100,预聚24 h,搅拌速率120～200 r/min,固化温度35 ℃时,制得了球形度和同心度达到95%以上,表面粗糙度小于10 nm的PS-RF双层空心微球。     

塑料微球表面制备聚乙烯醇涂层研究进展

在聚苯乙烯（PS）-聚乙烯醇（PVA）-碳氢聚合物（CH）三层球的设计中制备PVA涂层的方法主要包括乳液微封装法、炉内成球涂层法、浸(旋)涂法、界面缩聚法及喷涂法等,前三种方法目前最为常用。总结了前三种制备PVA涂层方法的优缺点及目前的研究和制备现状。乳液微封装法适合于500 m以下小尺寸双层球的制备,具有微球成活率高、产品质量较好等优点,但制备过程受人为因素影响较大,且不易制备大直径双层球。炉内成球涂层法也适用于小尺寸双层球的制备,其制备周期短,但液滴发生器的设计苛刻,PVA层的均匀性差,且不易制得较大尺寸的双层球。浸（旋）涂法可制备1000 m以上的大直径双层球,但该方法中影响PVA涂层铺展的因素较多,得到的PVA涂层均匀性较差,且涂层很薄。     

点火靶尺度聚苯乙烯空心微球的球形度

为提高惯性约束聚变(ICF)点火靶尺度(约2mm)聚苯乙烯(PS)空心微球的球形度,研究了油相与外水相界面张力、初始油相质量分数和固化旋转流场转速对PS微球球形度的影响。结果表明,将双重乳液体系外水相中的表面活性剂聚乙烯醇(PVA)替换为聚丙烯酸(PAA)后,油相与外水相之间的界面张力增大了约10倍,PS空心微球的球形度显著提高,球形偏离度小于1μm的微球比例由5%增加至约50%;但是,在较宽范围内改变油相初始质量分数及旋转固化流场转速,对PS微球球形度的影响并不显著,球形偏离度值小于1μm的PS微球比例介于40%~60%之间。     

炉内成球法制备PVA涂层理论模拟研究

 根据炉内成球法制备PVA涂层原理，建立了炉内成球法在PS微球表面制备PVA涂层的数学模型，并利用数值方法进行了求解，研究了初始PS壁厚和直径、载气种类、炉内温度、PVA含量等实验条件的影响。计算结果表明，包裹PS微球的PVA水溶液复合微球在下落过程中速度迅速增加，短时间内达到最大值后又逐渐降低；复合微球的PVA水溶液涂层厚度逐渐减少，微球表观密度降低；炉内温度较低时，PVA涂层不易烘干；空气和纯Ar做炉内气氛时，微球烘干时间延长，而在He和Ar混合气体中，随着He含量增加，微球烘干时间缩短；小直径PS微球及高含量PVA溶液有利于制备厚的PVA涂层。     

聚芳亚胺酮空心微球的制备

 利用微流体技术和双重乳液技术对大直径聚芳亚胺亚胺酮空心微球的制备条件进行了讨论。完成了微球壁厚和直径的控制研究,并讨论了密度不匹配对微球质量的影响。获得了直径0.6～2.0 mm,壁厚5.0～20.0 μm的聚合物微球材料,并对微球制备过程中相分离对聚合物微球形貌的影响进行了分析,结果表明：在聚合物微球外表面易于进行spinodal分相,而在内表面易于进行binodal分相,因此微球内外表面具有不同的形貌结构。同批次制备微球中,平均直径±5%范围内的微球数占88%,球形度大于99%。     

紫外臭氧处理聚-α-甲基苯乙烯微球表面化学镀镍

 通过对微球表面进行紫外臭氧的处理,改善了镍层在微球表面的沉积性,经紫外臭氧处理的聚-α-甲基苯乙烯微球通过红外图谱和红外图像表征,用扫描电镜测量处理前后的镀镍微球表面形貌。结果表明：经过紫外臭氧联合处理后,微球表面被氧化,同时接入了氨基,且处理过的微球镀镍后的结合力和表面形貌得到了明显改善。从而得出用紫外臭氧表面改性的方法可以提高塑料微球和金属壳的结合力。     

干凝胶炉法制备聚苯乙烯空心微球

研究了一步乳化法制备初始粒子的过程中相比及搅拌强度对初始粒子直径的影响 ,初步探讨了干凝胶炉内成球过程中 ,炉温、炉内气氛、压力等对聚苯乙烯 (PS)空心微球产率及同心度的影响。以分子量为 2 2万的聚苯乙烯制得了直径在 70～ 550μm的初始粒子 ,经乙醇浸泡后 ,制得了含 2 %质量分数发泡剂的干凝胶粒子 ,并在 Polymer-70 0干凝胶炉上制备出了外直径为 4 0 0～ 90 0 μm、壁厚为 2～1 0 μm、同心度≥ 95%的     

Fabrication of polystyrene hollow microspheres as laser fusion targets by optimized density-matched emulsion technique and characterization

Inertial confinement fusion, frequently referred to as ICF, inertial fusion, or laser fusion, is a means of producing energy by imploding small hollow microspheres containing thermonuclear fusion fuel. Polymer microspheres, which are used as fuel containers, can be produced by solution-based micro-encapsulation technique better known as density-matched emulsion technique. The specifications of these microspheres are very rigorous, and various aspects of the emulsion hydrodynamics associated with their production are important in controlling the final product. This paper describes about the optimization of various parameters associated with density-matched emulsion method in order to improve the surface smoothness, wall thickness uniformity and sphericity of hollow polymer microspheres. These polymer microshells have been successfully fabricated in our lab, with 3–30 μm wall thickness and 50–1600 μm diameters. The sphericity and wall thickness uniformity are better than 99%. Elimination of vacuoles and high yield rate has been achieved by adopting the step-wise heating of W₁/O/W₂ emulsion for solvent removal.     

红外双波段双层谐衍射光学系统设计

将谐衍射透镜应用在传统红外单波段佩茨瓦尔(Petzval)物镜上,设计得到工作波段处于3.4~4.2μm和8~11μm的红外双波段单层谐衍射光学系统。但单层谐衍射元件的衍射效率只在设计波长处衍射效率最高,随着波长相对设计中心波长向两侧偏离,主衍射级次的衍射效率逐渐下降。为提高含单层谐衍射元件光学系统的衍射效率,基于双层衍射元件衍射效率表达式研究了双层谐衍射元件的结构优化,给出了优化方法。设计出佩茨瓦尔型红外双波段双层谐衍射光学系统,其在3.4~4.2μm和8~11μm两个工作波段的衍射效率均达到90%以上,相比含有单层谐衍射面的光学系统衍射效率有了很大提升,提高了像面衬比度,完善了系统成像质量。     

Microwave absorption properties of double-layer absorbers made of NiCoZn ferrites and hollow glass microspheres electroless plated with FeCoNiB

Amorphous FeCoNiB coatings were deposited by an electroless plating technique on the hollow glass microspheres. NiCoZn spinel ferrites sintered show two dispersion peaks (1.81 and 6.98 GHz). By fitting its permeability dispersion spectra, the one at low frequency is believed to be due to the domain wall movement mechanism, the other one is due to the spin rotation mechanism. Used in a single-layer absorber structure, neither the hollow glass microspheres coated nor the NiCoZn could meet the demand of light weight. However, if a double-layer absorber structure is used, not only the total weight of an absorber is reduced, but also the microwave absorption performance is enhanced.     

厚壁空心微球的球形度和壁厚均匀性的表征研究

为建立高效简洁的厚壁空心微球球形度和壁厚均匀性的表征和测量方法,以内径850μm、壁厚25μm的厚壁聚苯乙烯(PS)微球为测量对象,分析球形度和壁厚均匀性的表征方法,探讨测量过程中采样方式对表征微球球形度和壁厚均匀性的影响。研究表明:对于批量微球球形度和壁厚均匀性的表征,当抽样数目不小于30时,测量结果之间的差异很小;而对于单一微球的球形度和壁厚均匀性的表征,至少3个不同投影面的测量结果的平均值才趋于稳定。不同投影面导致球形度或壁厚均匀性较差的批次样品的测量结果有一定差异,多次投影测量可提高测量结果的可靠性。     

聚苯乙烯相对分子量对薄壁聚苯乙烯空心微球质量的影响北大核心CSCD

激光惯性约束聚变(ICF)作为探索受控核聚变的有效途径,有望获得清洁无污染的能源,而薄壁聚苯乙烯(PS)空心微球是ICF物理实验中亟需的一类微球。针对薄壁空心微球因径厚比(直径/壁厚)增大导致其在干燥、使用中易开裂的问题,研究了PS原料对薄壁微球质量的影响,探讨了其影响机制。结果表明:当油相PS质量分数为4%时,随着油相粘度增加,W1/O/W2复合乳粒稳定性逐渐提高;当油相质量分数不低于8%时,复合乳粒稳定性良好。PS原料对微球表面粗糙度影响较小,微球球形度和壁厚均匀性随初始油相粘度的增大而降低,在干燥过程中微球开裂率随原料力学性能提高而减小。在外水相中引入氟苯(FB)液滴,延缓固化速率,可减小油相粘度增加对微球球形度和壁厚均匀性的不利影响。     

中空Ag纳米球壳的制备及性能表征

 以改性聚苯乙烯微球为模板,采用化学镀法在聚苯乙烯微球表面包覆一层银,在四氢呋喃溶液中将聚苯乙烯微球溶解,得到中空Ag纳米球壳。采用扫描电镜、透射电镜和X射线衍射仪对样品进行了表征及分析,并用紫外可见分光光度计研究了粒子的光学性质。实验结果表明：运用此法成功地制备出中空Ag纳米球壳的内径为250 nm,壁厚约为15 nm,并且成功地使纳米粒子的紫外吸收光谱由600 nm红移至900 nm左右,实现了在可见光至近红外光区调节Ag纳米结构的吸收峰。