新型红色荧光粉NaLa_(0.7)(MoO_4)_(2-x)(WO_4)_x∶0.3Eu~(3+)的制备及发光性质研究

采用高温固相法合成具有余辉性能的发光材料NaLa_(0.7)(MoO_4)_(2-x)(WO_4)_x∶0.3Eu~(3+)(x=0,0.5,1,1.5,2)。用X射线衍射(XRD)和荧光光谱对样品的晶体结构和发光特性进行表征。测试结果表明,在900℃下烧结8 h所合成的NaLa_(0.7)(MoO_4)_(2-x)(WO_4)_x∶0.3Eu~(3+)样品为纯相Na La(Mo O_4)_2,样品可被近紫外光393nm和蓝光462 nm有效激发,其发射主峰位于615 nm处,属于Eu3+的5D0-7F2跃迁。Na La_(0.7)(Mo O_4)_(2-x)-(WO_4)_x∶0.3Eu~(3+)的发光强度随着W6+浓度的增加而增大,当W6+掺杂量x=1时发光最强,而后随W6+掺杂浓度的增加出现浓度猝灭现象。通过计算得到样品在393 nm和462 nm激发下的色坐标,当W6+的掺杂量x=1时,样品的红光色纯度最好。     

Bi~(3+)和Eu~(3+)在Ca_2SiO_4中的发光和能量传递

用高温固态反应合成了Ca_2SiO_4:Bi~(3+),Ca_2SiO_4:Eu~(3+)和Ca_2SiO_4:Eu~(3+),Bi~(3+)发光体。讨论了不同掺杂量和掺杂种类时Bi~(3+)对Eu~(3+)的~5D_0-~7F_1,~5D_0-~7F_2发射的影响规律。实验发现,Ca_2SiO_4:Bi~(3+)在紫外线激发下发出明亮的蓝色光,Ca_2SiO_4:Eu~(3+),Bi~(3+)中的Bi~(3+)能将激发能传递给Eu~(3+),使Eu~(3+)的~5D_0-~7F_1和~5D_0-~7F_2两种跃迁都大大加强,同时,Bi~(3+)也发出鲜艳的紫色光。     

Eu~(2+)/Eu~(3+)掺杂的微晶玻璃发光特性研究

通过高温熔融法和热处理成功制备了白光发光的Eu~(2+)/Eu~(3+)掺杂SiO_2-Al_2O_3-ZnO-K_2CO_3微晶玻璃。测试了微晶玻璃的X射线衍射谱(XRD)、激发光谱和荧光光谱。研究发现,X射线衍射谱表明了玻璃基质中存在β-Zn_2SiO_4纳米晶粒,根据XRD结果和Scherrer公式计算得到β-Zn_2SiO_4晶粒大小约为35 nm。在紫外光激发下,观察到强烈的宽带蓝光(400～460 nm)和红光(574,587,611,650和700nm)发光,分别对应Eu~(2+)的4f~65d→4f~7能级跃迁以及Eu~(3+)的~5D_0→~7F_J(J=0,1,2,3,4)能级跃迁,与未热处理玻璃样品相比较,微晶玻璃的发光强度大大增强。研究结果表明,Eu~(2+)/Eu~(3+)掺杂的SiO_2Al_2O_3-ZnO-K_2CO_3晶玻璃是一种白光LED潜在的基质材料。     

一种LED用红色荧光粉BaZn_2(BO_3)_2∶Eu~(3+)的合成与发光性能研究（英文）

通过高温固相法制得双峰可调节本征半导体发光Ba Zn_2(BO_3)_2∶Eu~(3+)荧光粉,此类荧光粉在300~400nm的紫外波段有很强的吸收。在375 nm的紫外光激发下,该荧光粉产生了两个宽带的发射峰,分别位于550nm和615 nm处。并且,在395 nm的紫光激发下,荧光粉会由于Eu~(3+)离子的~5D_0→~7F_2电偶极跃迁产生一个位于615 nm的强宽发射峰,这表明Eu~(3+)离子占据了反演对称中心的位置,取代了Ba Zn_2(BO_3)_2中部分的Ba~(2+)离子。当Eu~(3+)的摩尔分数达到10%时,发生浓度猝灭。在不同浓度的Eu~(3+)离子的掺杂下,Ba Zn_2(BO_3)_2∶Eu~(3+)荧光粉的发光从黄色延伸到红色,实现了荧光粉的色度可调。     

Sr_2La_8(SiO_4)_6O_2∶Eu~(2+,3+)荧光粉的制备和发光性能

采用高温固相法合成了Sr_2La_8(SiO_4)_6O_2∶Eu~(2+,3+)荧光粉,X射线粉末衍射数据分析结果表明,试样为氧磷灰石结构,属于六方晶系,具有P63/m(176)空间点群结构.荧光光谱分析结果表明,Sr_2La_8(SiO_4)_6O_2∶Eu~(2+,3+)激发光谱为位于200~600nm,由275nm、336nm两个宽峰和392nm、461nm、466nm、523nm等锐线峰组成.两个宽带激发峰可由272nm、300nm、336nm三峰拟合而成,峰面积比为1:0.52:4.09.272nm、300nm峰归属于Eu3+的电荷迁移激发跃迁态,336nm峰来自Eu2+的f-d跃迁.在393nm激发下,Sr_2La_8(SiO_4)_6O_2∶Eu~(2+,3+)发射光谱在500~750nm范围内呈现多条锐线发射,在613nm处发射峰最强,以电偶极跃迁5D0→7F2为主,Eu3+占据无反演对称中心格位.Eu3+磁偶极跃迁5D0→7F1处的峰可由584.5nm、588.5nm、594nm、597nm四峰拟合而成,表明Eu3+进入基质晶格中占据4f(C3)和6h(Cs)两种格位.X射线光电子能谱图分析结果表明,试样中Eu3+与Eu2+的含量比接近2∶1.Eu2+与Eu3+存在能量传递作用,试样在紫外灯下照射呈现烛光黄色,可用于LED.     

碱土金属离子共掺杂对铕离子在Ca_(12)Al_(14)O_(32)F_2中发光性能的影响

采用高温固相还原法合成Ca_(12-x-y)M_xAl_(14)O_(32)F)2∶yEu(M=Mg,Sr,Ba)体系荧光粉,分别采用X射线粉末衍射仪和荧光光谱仪测试其物相及荧光性能,通过掺杂碱土金属离子可以调整Ca_(12)Al_(14)O_(32)F_2∶Eu~(3+)/Eu~(2+)的组成和结构,进而影响Ca_(12-x-y)M_xAl_(14)O_(32)F_2∶yEu的发光性能。研究结果表明:在Ca_(12)Al_(14)O_(32)F_2∶Eu中掺杂一定浓度的Mg~(2+)不利于Eu~(3+)的还原,掺杂一定浓度的Sr~(2+)或Ba~(2+)有利于Eu~(3+)的还原;通过改变碱土金属离子的掺杂浓度调节Eu~(3+)和Eu~(2+)的浓度比,可以调整蓝光发射和红光发射的强度比,进而使发光颜色从蓝色变为淡紫色,再变为蓝绿色。     

SrB_4O_7掺杂二价镧系离子的荧光光谱特性研究

采用高温固相法通过掺杂不同种类的镧系元素以及改变掺杂元素的浓度制备了系列SrB_4O_7∶Re~(2+)(Re代表Ce,Nd,Gd和Lu)荧光材料,利用实验室自建的非偏振显微共聚焦荧光/拉曼测量系统重点研究了其荧光光谱特性。研究发现,SrB_4O_7∶Re~(2+)和SrB_4O_7∶Sm~(2+)具有相似的荧光特性,最强单峰对应~5 D_0-~7 F_0电子跃迁所产生的荧光峰(0-0峰),峰位为685.41nm;在700和730nm附近还对应有~5 D_0-~7 F_1和~5 D_0-~7 F_2电子跃迁所产生的两条强度较弱的荧光带;在相同条件下,SrB_4O_7∶Re~(2+)的0-0峰强度较SrB_4O_7∶Sm~(2+)的0-0峰强度至少要弱一个量级。对SrB_4O_7∶Re~(2+)荧光光谱分析结果显示,掺杂元素种类和掺杂元素浓度是影响荧光光谱强度的关键因素,两者直接决定了能参与发光的Re~(2+)离子的总量。     

稀土离子共掺杂的钼酸钙发光材料的合成与光谱性质

采用了化学共沉淀法合成了一系列的镨、铽共掺杂的钼酸钙发光材料,研究了单掺Pr~(3+)和Tb~(3+)以及CaMoO4∶0.03Pr~(3+),yTb~(3+)共掺杂的浓度、温度对材料发光性能的影响。采用X射线衍射仪(XRD)和荧光光谱对样品进行了晶格结构、荧光性质表征。XRD分析表明:样品的主衍射峰与标准卡片(JCPDS 29-0351的衍射峰数据一致,说明少量Pr~(3+)掺杂没有改变基质晶格结构。荧光光谱分析表明,样品在275nm紫外光激发下,发射光谱主要包括多个发射峰,波长为488,560,621和652nm,分别对应于镨离子的~3P_0-~3H_4,~3P_0-~3H_5,~1D_2-~3H_4和~3P_0-~3F_2的跃迁,在掺杂量为3%时,样品特征发射峰最强,CaMoO4∶0.03Pr~(3+)和CaMoO4∶0.05Tb~(3+)的最佳煅烧温度分别为800和600℃。随着Pr~(3+)和Tb~(3+)掺入量的增加,CaMoO4∶Pr~(3+)发光材料的特征发射光谱和激发光谱的特征峰强度逐渐减小,而CaMoO4∶Tb~(3+)材料发光先减小后增大,存在着浓度猝灭效应。此外,在CaMoO4∶0.03Pr~(3+),yTb~(3+)发光体系中,Tb~(3+)的共掺杂可显著增强镨离子的特征发射峰,这是由于存在Tb~(3+)→Pr~(3+)的有效的能量传递。     

新型Gd2SiO5:RE荧光粉的制备和发光性能

以Gd_2O_3、SiO、稀土氧化物为原料采用高温固相法制备了Gd_(2(1-x))SiO_5∶2xRE荧光粉体。X射线衍射分析结果表明Gd/Si配比为1.9,BaF_2助熔剂用量为5‰,煅烧条件为1500℃保温3h得到结晶良好的Gd_2SiO_5及Gd_2SiO_5∶RE粉体。光谱分析表明,Gd_2SiO_5∶Eu荧光粉末激发波段为250～470nm,而Gd_2SiO_5∶Tb为250～320nm;前者发射主峰为620nm(与Eu~(3+)的~5D_0→~7F_2对应),后者为548nm(与Tb~(3+)的~5D_4→~7F_5对应);Eu~(3+)和Tb~(3+)的最佳掺杂量为7%。f_a(E)和发射带f_e(E)交叠越大,则电偶极-电偶极作用机制的跃迁几率越高,Gd~(3+)-Tb~(3+)能带交叠程度大于Gd~(3+)-Eu~(3+),Tb~(3+)的量子效率要高于Eu~(3+)。     

La2-x-yMgTiO6:xDy3+,yEu3+白色荧光粉的 荧光性能及能量传递

采用高温固相法合成了La_(2-x)MgTiO_6∶xDy~(3+)和La_(2-x-y)MgTiO_6∶xDy~(3+),yEu~(3+)系列荧光粉,通过X射线衍射对其相结构进行了表征,优化了荧光粉的组成,研究了Dy~(3+)和Eu~(3+)浓度对发光强度的影响,测试了荧光粉的荧光光谱和寿命,研究了Dy~(3+)和Eu~(3+)之间的能量传递机理和能量传递效率。结果表明:所有合成的掺杂荧光粉均为单相物质;La_(2-x)MgTiO_6∶xDy~(3+)最佳掺杂浓度为x=0.05;在350 nm近紫外光激发下,La_(2-x-y)MgTiO_6∶xDy~(3+),yEu~(3+)显示出Dy~(3+)的特征黄、蓝光发射和Eu~(3+)的特征红光发射;Dy~(3+)的荧光寿命呈双指数衰减,随着Eu~(3+)浓度的增大,Dy~(3+)的荧光寿命逐渐减小,证明了Dy~(3+)和Eu~(3+)离子之间存在着能量传递;能量传递效率随着Eu~(3+)掺杂浓度的增加而增加,La_(1.83)MgTiO_6∶0.05Dy~(3+),0.12Eu~(3+)荧光粉的能量传递效率为53.9%;改变调节Eu~(3+)的掺杂浓度可以得到从冷白色到暖白色的荧光粉,La_(1.83)MgTiO_6∶0.05Dy~(3+),0.12Eu~(3+)的色坐标为(0.337 3,0.354 4)。     

白光LED用红色荧光粉Sr2EuxGd1-xAlO5的制备及其发光性质

用高温固相反应法合成了Sr₂Eu_xGd_1-xAlO₅红色荧光粉,研究了荧光粉的晶体结构和发光性质。在紫外光和近紫外光激发下,样品的发射光谱由Eu³⁺的⁵D₀→⁷F_J(J=0,1,2,3,4) 特征发射组成,其中Eu³⁺离子的⁵D₀→⁷F₁(λ=590 nm)和⁵D₀→⁷F₂(λ=622 nm)跃迁发射的强度最大。当Eu³⁺离子的摩尔分数为 0.75时,样品的发光最强。研究结果表明,Sr₂Eu_xGd_1-xAlO₅荧光粉是一种在近紫外芯片白光LED上有应用前景的红光荧光粉。     

Local microstructural analysis for Y_2O_3/Eu~(3+)/Mg~(2+) nanorods by Raman and photoluminescence spectra under high pressure

In this paper, we investigate the Raman and photoluminescence spectra of Y_2O_3/Eu~(3+) and Y_2O_3/Eu~(3+)/Mg~(2+) nanorods under high pressures using 514-nm and 532-nm laser light excitation. We observe transitions from the initial cubic phase to amorphous at pressures higher than 24 GPa for both Y_2O_3/Eu~(3+) and Y_2O_3/Eu~(3+)/Mg~(2+) nanorods. In addition, Y_2O_3/Eu~(3+) and Y_2O_3/Eu~(3+)/Mg~(2+) nanorods exhibit different distorted states after the pressure has been raised to 8 GPa. The analyses of intensity ratios, I_(0-2)/I_(0-1) from ~5D_(0–)~7F2_to~5D_(0–)~7F_1and I_(0-2)A/B of ~5D_(0–)7F_2 transitions indicate that Y_2O_3/Eu~(3+)/Mg~(2+) nanorods exhibit stronger local micro-surrounding characteristics for Eu~(3+) ions in a pressuremodulated crystal field. The doped Mg2+ion results in reducing the crystal ionicity in the distorted lattice state under high pressures. The use of doped ions as an ion modifier can be applied to the study of small local microstructural changes through Eu~(3+) luminescence.     

M_2Eu_xLn_(1-x)AlO_5(M=Ca,Sr,Ba,Ln=La,Gd,Lu)红色荧光粉发光性质的研究

用高温固相反应法合成了M_2Eu_xLn_(1-x)AlO_5(M=Ca,Sr,Ba,Ln=La,Lu,Gd)荧光粉,研究了荧光粉的发光性质。在紫外光和近紫外光激发下,样品的发射光谱由Eu~(3+)的5D0→7FJ(J=0,1,2,3,4)特征发射组成。其中Eu3+离子位于590 nm附近的5D0→7F1和位于620 nm附近的5D0→7F2跃迁发射的强度最强。荧光粉的激发光谱都是由O~(2-)-Eu~(3+)电荷迁移带和Eu~(3+)的f-f跃迁构成的。M_2Eu_xLa_(1-x)AlO_5(M=Ca,Sr,Ba)的O2--Eu~(3+)的电荷迁移带的峰位按Ca、Sr、Ba顺序向长波方向移动。研究了用La、Gd和Lu替代M_2Eu_xLn_(1-x)AlO_5中Ln的位置对样品发光的影响。给出了Eu~(3+)浓度对发光强度的影响。分析了M_2Eu_xLn_(1-x)AlO_5和M_2Eu_xLn_(1-x)AlO_5的荧光寿命。     

稀土离子(Eu3+,Tb3+,Ce3+)掺杂ZnAl2O4/SiO2微晶玻璃的制备与发光性能

采用凝胶法分别制备出4.5ZnO-5.5Al₂O₃-90SiO₂(ZAS)以及ZAS[DK]:RE³⁺ (RE=Eu,Tb,Ce) 透明微晶玻璃。利用X射线衍射仪(XRD)、透射电子显微镜(TEM)和荧光光谱仪(PL)等测试手段,研究了稀土离子掺杂浓度对ZAS微晶玻璃的结构和发光性能的影响。XRD结果表明,ZAS[DK]:RE³⁺ (RE=Eu,Tb,Ce)微晶玻璃包含ZnAl₂O₄晶相和SiO₂非晶相,ZnAl₂O₄平均晶粒尺寸约为30 nm,稀土离子的掺杂没有显著改变原来的ZnAl₂O₄晶体结构。TEM结果表明,900 ℃时ZnAl₂O₄从ZAS体系中析出。PL光谱显示,Eu³⁺ 存在 ⁵D₀→⁷F₂跃迁,ZAS[DK]:Eu³⁺在611 nm 处发出强烈的红色光;由于Tb³⁺ 的⁵D₄→⁷F₅ 跃迁,ZAS[DK]:Tb³⁺在541 nm 处发出明亮的绿色光;ZAS[DK]:Ce³⁺ 在381 nm处显示了蓝光发射,对应于Ce³⁺ 的5d→4f 轨道跃迁。ZAS[DK]:RE³⁺ (RE=Eu, Tb, Ce)的PL发射光谱存在着浓度猝灭现象,Eu³⁺、Tb³⁺ 和Ce³⁺的最佳单掺杂摩尔分数分别为20%、20%和3%。CIE色度图表明,ZAS[DK]: RE³⁺ (RE=Eu,Tb,Ce)的色坐标分别位于红光、绿光和蓝光区域。实验结果表明,ZAS:RE³⁺ (RE=Eu,Tb,Ce) 微晶玻璃是一种良好的可用于全色显示的白光LED材料。     

真空紫外光激发下Ce3+、Tb3+激活的BaCa2(BO3)2的发光性质

利用XRD、VUV及UV光谱等方法对Ce³⁺、Tb³⁺离子掺杂以及Ce³⁺、Tb³⁺离子共掺的3种BaCa₂(BO₃)₂荧光粉的相纯度、发光性质、浓度猝灭现象进行研究。结果表明:3种荧光粉在VUV波段有较好的吸收,基质吸收带位于140～190 nm范围。Ce³⁺在BaCa₂(BO₃)₂的最低4f5d跃迁带位置在360 nm附近,其5d→²F_J(J=5/2, 7/2)发射峰分别位于393,424 nm。Tb³⁺掺杂的样品在172 nm激发下的发射光谱由4个窄带组成,分别对应⁵D₄→⁷F_J(J=3,4,5,6)的跃迁,其中占主导位置的是⁵D₄→⁷F₅的跃迁,大约位于543 nm处,主要为绿光发射。在Ce³⁺,Tb³⁺离子共掺杂的BaCa₂(BO₃)₂光谱中,观察到Ce³⁺-Tb³⁺离子间有能量传递。     

YVO_4∶Eu~(3+)@SiO_2核壳结构纳米复合材料的合成与表征

用沉淀法制备了尺寸约为8 nm的YVO4∶Eu3+纳米粒子,然后用反相微乳液法在YVO4∶Eu3+纳米粒子的表面包覆了一层Si O2壳。利用XRD、TEM、UV-Vis吸收光谱和光致发光光谱对合成的样品进行了表征。得到的复合物具有较好的核壳结构,通过改变硅酸四乙酯的用量可以改变Si O2壳的厚度。研究了Si O2壳对YVO4∶Eu3+发光性质的影响,结果表明:包覆和未包覆的样品在紫外光激发下都有Eu3+的特征发射;随着Si O2壳厚度的增加,发光强度和量子效率越来越低,Eu3+格位对称性越来越高。     

LiGd(W_yMo_(1-y))_2O_(8-x/2)F_x∶Eu~(3+)红色荧光粉的制备和发光特性

采用高温固相法制备了LiGd(W_yMo_(1-y))_2O_(8-x/2)F_x∶0.4Eu~(3+)(x=0~1,y=0~1)系列白光LED用红色荧光粉。通过扫描电子显微镜、X射线衍射仪、红外光谱仪、荧光光谱仪对荧光粉的形貌、结构、光学性能进行了表征。结果表明,Eu~(3+)、F-和WO_4~(2-)的掺杂没有改变LiGd(MoO_4)_2的四方晶系白钨矿结构;F~-和WO_4~(2-)最佳掺杂量分别为x=0.6,y=0.4。在396 nm激发下,LiGd(W_(0.4)Mo_(0.6))_2O_(7.7)F_(0.6)∶0.4Eu~(3+)的发光强度比未掺杂样品提高了60%,量子效率可达66.23%。当温度升高至100℃时,样品的发射强度降为25℃时的76.6%。在460 nm激发下,样品的最强窄带发射峰位于617 nm处,归属于~5D_0→~7F_2跃迁,色坐标为(0.649 9,0.346 3)。5D0能级的荧光寿命曲线遵循单指数规律衰减,随着F-掺杂浓度的增加,5D0能级的荧光寿命不断增加,归因于低声子能量的F-掺入有效减小了能量的无辐射跃迁概率。所制备的LiGd(W_(0.4)Mo_(0.6))_2O_(7.7)F_(0.6)∶0.4Eu~(3+)荧光粉有望应用于白光LED。     

Eu3+掺杂CaWO4红色荧光粉发光性质的浓度依赖关系研究

采用共沉淀法制备了不同Eu³⁺掺杂浓度的CaWO₄荧光粉材料.通过X射线衍射和场发射扫描电镜技术对样品的结构和形貌进行了表征.测量了各样品的激发光谱、发射光谱和荧光衰减曲线, 计算了各样品的部分Judd-Oflet (J-O)参数和^5D_0 (Eu³⁺)能级量子效率,以及荧光粉的色坐标, 讨论了样品电荷迁移带相对强度、J-O参数、量子效率与掺杂浓度的依赖关系.对Eu³⁺掺杂的CaWO₄ 发光材料的光致发光性质的研究表明,在CaWO₄: Eu³⁺中⁵D₀→⁷F₂跃迁的616~nm 红色发光能被394.5~nm和465~nm的激发光有效激发,具有近紫外(或蓝光)激发效率高和猝灭浓度大的优点, 有潜力成为高效的近紫外(或蓝光)激发白光发光二极管用红色荧光粉材料.     

近紫外激发具有颜色可调的Er3+/Eu3+共掺BiOCl荧光粉

本文采用固相法在500℃合成了Er³⁺/Eu³⁺共掺BiOCl 荧光粉, 并通过XRD, SEM, 吸收, 激发和发射光谱研究了其结构、形貌和发光特性. XRD 和SEM结果表明在500℃下即可成功合成纯四方相片层结构的Er³⁺/Eu³⁺共掺BiOCl荧光粉. 吸收光谱表明掺杂Er³⁺/Eu³⁺离子使BiOCl形成杂质能级; 激发光谱显示该荧光粉具有来自于基质BiOCl价带(VB)到导带(CB)跃迁的优异宽带近紫外激发特性. 在380 nm近紫外光激发下, 同时获得了Er³⁺离子和Eu³⁺离子的特征发射峰, 其中发光中心位于410 nm (²H_9/2→⁴I_15/2), 525 nm (²H_11/2→⁴I_15/2), 554 nm (⁴S_3/2→⁴I_15/2), 673 nm (⁴F_9/2→⁴I_15/2)的发射峰来自于Er³⁺离子的跃迁, 而581 nm(⁵D₀→⁷F₀), 594 nm (⁵D₀→⁷F₁), 622 nm (⁵D₀→⁷F₂), 653 nm (⁵D₀→⁷F₃), 699 nm (⁵D₀→⁷F₄)的发射峰则来自于Eu³⁺离子的跃迁. 值得注意的是, 与传统Er³⁺/Eu³⁺掺杂的材料不同, 该荧光粉还具有独特高效的紫光(Er³⁺)和长波红光(Eu³⁺)发射特性, 分析表明这与BiOCl的结构有关; 并且通过改变掺杂浓度, 实现了发光颜色由黄绿光→黄光→橙红光的调节. 研究结果表明Er³⁺/Eu³⁺共掺BiOCl荧光粉有望成为一种潜在的近紫外激发白光LED荧光粉.     

溶胶-凝胶法合成Sr3MgSi2O8:Eu3+ 红色荧光粉及其发光性能

采用溶胶-凝胶法合成了Sr_3MgSi_2O_8∶Eu~(3+)红色荧光粉,并通过X射线衍射(XRD)、傅立叶变换红外光谱(FTIR)、扫描电镜(SEM)以及荧光光谱(PL)、X射线光电子能谱(XPS)等分析方法,对不同烧结温度(950,1 050,1 150,1 250℃)热处理4 h后得到的粉体的物相、形貌及发光性能进行了表征分析。由XRD表征结果可知,制备出的样品为正交晶系的Sr_3MgSi_2O_8;由扫描电镜及比表面积的测试结果可知,经过1 150℃热处理得到的荧光粉具有最大比表面积,可达到90.213 1 m~2/g,且粒径大小均一;由红外光谱图可知:样品中含有Si—O—Si、Mg—O和Sr—O化学键;在394 nm的激发波长下,所有样品在614 nm和702 nm处出现了强发射峰,分别对应于Eu~(3+)的~5D_0→~7F_2和~5D_0→~7F_4跃迁,属红光发射。随着热处理温度的升高,样品所对应的发射峰强度呈现出先增大后减小的变化趋势,即出现温度猝灭效应;经1 150℃热处理合成的Sr_3MgSi_2O_8∶Eu~(3+)红色荧光粉的发光性能最好,即最佳的热处理温度为1 150℃。