镍基非晶复合涂层激光制备及其纳米压痕测试

采用大功率半导体激光熔覆和重熔的工艺在低碳钢表面制备Ni-Fe-B-Si-Nb合金非晶复合涂层,并对所得涂层进行了纳米压痕性能测试。研究结果表明,当激光熔覆时激光功率为0.8kW,熔覆速度为0.36m/min,送粉速度为12g/min,重熔时激光功率为3.5kW,熔覆速度为8m/min,在低碳钢表面成功制备了Ni40.8Fe27.2B18Si10Nb4非晶复合涂层,涂层主要由非晶相和NbC颗粒相组成。纳米压痕测试结果表明经激光重熔后所得非晶复合涂层的显微硬度和弹性模量远远大于未重熔的熔覆层,并且也大于同成分大块非晶。     

稀土CeO_2对镍基纳米Al_2O_3激光熔覆复合涂层组织和性能的影响

采用激光熔覆技术在45钢基体上制备了不同CeO2含量的镍基纳米Al2O3复合涂层,对熔覆层进行了微观组织分析和显微硬度测试。结果表明,随着CeO2含量的增加,熔覆层组织由亚共晶向共晶组织转变;加入1.0%CeO2对镍基纳米Al2O3熔覆层的组织起到明显的细化和净化作用,枝晶生长的方向性减弱,组织趋向均匀,熔覆涂层的显微硬度值比未加稀土的涂层提高了60-95HV0.2。     

铁基合金激光熔覆层高温润滑磨损性能

 为提高40Cr合金钢的表面耐磨性,采用预置激光熔覆法在40Cr基体表面制备铁基合金涂层, 利用扫描电镜观察分析熔覆层显微组织形貌,用显微硬度仪测试熔覆层截面显微硬度,用摩擦磨损试验机测定在润滑条件下基体、熔覆层的摩擦系数随温度变化的规律。研究结果表明:熔覆层与基体实现良好冶金结合,熔覆层横截面微观组织呈现平面晶、树枝晶和胞状晶分布;熔覆层硬度值介于617.5~926.6 HV0.2之间,基体硬度介于205.2~278.2 HV0.2之间;在200 ℃以下,熔覆层摩擦系数在磨程中趋于平稳,在0.1附近轻微波动,小于基体平均摩擦系数;当温度超过200 ℃,油膜分解,引发润滑失效,磨损方式向干摩擦转化,磨损机理从微切削磨损主导向粘着磨损、磨粒磨损和氧化磨损复合磨损方式转化。     

激光熔覆Al2O3/Fe901复合涂层的强化机制及耐磨性

为提高金属材料表面涂层的耐磨性,采用激光熔覆工艺制备了Al_2O_3增强Fe901金属陶瓷复合涂层,研究了Al_2O_3陶瓷增强相对Fe基熔覆层组织与性能的影响。利用扫描电镜和X射线衍射仪检测了复合涂层的微观组织和物相;采用显微硬度仪和摩擦磨损试验机分析了复合涂层的显微硬度与耐磨性。结果表明:Fe901涂层的组织以柱状枝晶和等轴枝晶为主,添加的Al_2O_3可促使涂层组织转变为均匀的白色网状晶间组织及其包裹的细小黑色晶粒;复合涂层中的Al_2O_3陶瓷颗粒表面发生微熔,与Fe、Cr结合生成Fe3Al及(Al,Fe)4Cr金属间化合物,起到增加Al_2O_3陶瓷颗粒与金属黏结相结合强度的作用;当Al_2O_3陶瓷颗粒的质量分数为10%时,复合涂层的显微硬度较Fe901涂层增加了16.4%,复合涂层的摩擦磨损质量损失较Fe901涂层降低了50%;添加适量的Al_2O_3陶瓷有助于提高涂层的显微硬度及耐磨性。     

TiN对Co基合金激光熔覆层组织与性能的影响

采用5 kW CO2激光器在低碳钢表面熔覆Co基合金涂层及TiN/Co基合金复合涂层,研究了两种涂层的组织、显微硬度以及滑动磨损性能。结果表明,Co基合金涂层主要组成相为-γCo,-εCo,Cr23C6等,TiN/Co基合金复合涂层组成相为-γCo,-εCo,Cr23C6,TiN和TiC等。Co基合金涂层由发达的-γCo枝晶和其间共晶组织所组成,TiN/Co基合金涂层典型组织为等轴固溶体以及细小的共晶组织。TiN对熔覆层的组织有显著的改善作用,促使其组织细化,树枝晶向等轴晶转化,同时可显著提高Co基合金涂层的显微硬度及耐磨性能。     

镍-磷/纳米碳管化学复合镀层的研究

采用化学复合镀方法,在基体铜片上进行Ni-P／纳米碳管复合镀．用金相显微镜、扫描电子显微镜、X射线衍射仪和显微硬度计等实验手段研究复合镀层的组织、结构和性能．结果表明:随着镀液中纳米碳管含量的增加,复合镀层表面的颗粒变小且密度增加;复合镀层的硬度随纳米碳管含量的增加而提高;此外,纳米碳管的加入,使镀层由非晶变成了纳米晶,促进了复合镀层的晶化．     

斜齿轮激光熔覆Fe基合金组织与性能研究

采用激光熔覆技术在斜齿轮钢表面制备Fe基熔覆层。通过光学显微镜、显微硬度计对熔覆层进行金相组织与显微硬度分析,采用磨损机对熔覆层和基材进行摩擦实验。结果表明:当激光功率为750W,送粉速率为20g/min,扫描速度10mm/s,离焦量为16.4mm时,铁基熔覆层与基体结合界面有明显的白亮带,激光熔覆效果较好,熔覆层的显微硬度值分布在845.3HV至955.6HV之间,约为基体硬度(419.7HV)2倍;熔覆层摩擦磨损性能得到了提高;熔覆层显微组织为均匀而细小的铁素体和珠光体,力学性能优于基体材质。     

SHS等离子喷涂制备FeAl2O4-Al2O3-Fe纳米复合涂层的研究

利用SHS等离子喷涂技术，将经过机械团聚法制备的Fe₂O₃-Al复合粉体送入等离子焰流，沉积出厚度约为400 μm的复合涂层.利用XRD，SEM 和TEM等检测手段对涂层的成分和组织进行了分析，测定了涂层的显微硬度、断裂韧性以及耐磨性.结果表明涂层为具有纳米结构的FeAl₂O₄-Al₂O₃-Fe纳米复合组织；涂层的显微硬度为HV_100g870；断裂韧性是普通Al₂O₃涂层的2倍；无润滑磨损的耐磨性是普通Al₂O₃涂层的2.5倍. 关键词： SHS等离子喷涂 纳米涂层 断裂韧性     

反应等离子喷涂纳米TiN涂层的显微硬度及微观结构研究

阐述了反应等离子喷涂(RPS)方法的基本思想.利用气体隧道等离子喷枪，通过RPS方法在Q23 5钢基底上成功制备了氮化钛涂层.检测了TiN涂层在不同载荷下的显微硬度，结果显示TiN涂层具有明显的硬度压痕尺寸效应，在高载荷下加工硬化效应较弱.XRD,TEM及HRTEM等分析 表明,通过RPS方法制备得到了纳米TiN涂层，涂层由直径约为50—70nm的TiN晶粒及非晶Ti N所组成. 关键词： 反应等离子喷涂 纳米 氮化钛 微观结构     

激光熔覆TiC陶瓷涂层的组织和摩擦磨损性能研究

采用激光熔覆技术在TC4合金表面上制备了TiC陶瓷涂层,分析了熔覆层的微观组织,测试了熔覆层的硬度和摩擦磨损性能。结果表明:TiC激光熔覆层分为熔覆区和稀释区两个区域,熔覆区未受到基底的稀释,由TiC颗粒和TiC树枝晶组成;稀释区受到了基底的稀释,由TiC树枝晶和钛合金组成;TiC激光熔覆层的显微硬度在HV700~1500之间,明显地改善了TC4合金表面的摩擦和磨损性能。     

Study on the laser treatment of electroless Ni-P-SiC composite coatings

Effect of the laser treatment on electroless Ni-P-SiC composite coatings was investigated. The microscopic structure, surface morphology, ingredient, and performance of the Ni-P-SiC composite coatings were synthetically analyzed by the use of X-ray diffraction apparatus, scanning electron microscope, energy distribution spectrometer, micro-hardness tester, wear tester and so on. It was found that the composite coatings did make crystalloblastic transformation after laser heating. Structural analysis confirmed that some new types of phase Ni2Si or Ni3Si compound would emerge in the Ni-P-SiC coatings after laser treatment. The micro-hardness measurement results showed that when the laser power was 450 W with scanning speed of 0.5 m/min, the hardness of the coating was superior to the coating obtained by the conventional furnace heating, and wear resistance of the composite coating after laser treating could also improve.     

Ni-Co-TiO2 nanocomposite coating prepared by pulse and pulse reversal methods using acetate bath

Ni-Co/nano TiO₂ (Ni-Co-TiO₂) composite coatings were prepared under pulse current and pulse reverse current methods using acetate bath. The microstructure and corrosion resistance of the coatings were characterized by means of XRD, SEM and EIS. Both the Ni-Co alloy and composite coatings exhibited single phase of Ni matrix with face centered cubic (fcc) crystal structure. The crystal orientation of the Ni-Co-TiO₂ composite coating was transformed from crystal face (2 0 0) to (1 1 1) compared with Ni-Co alloy coatings. The results showed that the microstructure and performances of the coatings were greatly affected by TiO₂ content on the deposits prepared by PC and PRC methods. The microhardness and corrosion resistance were enhanced in the optimum percentage of TiO₂ composite coatings. The PRC composite coatings were exhibited from compact surface, higher microhardness and good corrosion resistance compared with that of the PC composite coating.     

Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts

The Al-Mn alloy coatings were electrodeposited on AZ31B Mg alloy in AlCl₃-NaCl-KCl-MnCl₂ molten salts at 170 °C aiming to improve the corrosion resistance. However, in order to prevent AZ31B Mg alloy from corrosion during electrodeposition in molten salts and to ensure excellent adhesion of coatings to the substrate, AZ31B Mg alloy should be pre-plated with a thin zinc layer as intermediate layer. Then the microstructure, composition and phase constituents of the coatings were investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDX), and X-ray diffraction (XRD). It was indicated that, by adjusting the MnCl₂ content in the molten salts from 0.5 wt% to 2 wt%, the Mn content in the alloy coating was increased and the phase constituents were changed from f.c.c Al-Mn solid solution to amorphous phase. The corrosion resistance of the coatings was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was confirmed that the Al-Mn alloy coatings exhibited good corrosion resistance with a chear passive region and significantly reduced corrosion current density at anodic potentiodynamic polarization. The corrosion resistance of the alloy coatings was also related with the microstructure and Mn content of the coatings.     

Effect of spraying power on the microstructure and mechanical properties of supersonic plasma-sprayed Ni-based alloy coatings

The aim of this paper was to investigate the microstructure and mechanical properties of the supersonic plasma-sprayed Ni-Cr-B-Si-C coatings prepared at different spraying powers. The microstructure, phase composition, porosity, Young's modulus, micro-hardness, and residual stresses of the coatings were investigated and determined. The variations of the porosity, Young's modulus and micro-hardness of the coatings were evaluated by using statistical method. Results showed that the variations of porosity, Young's modulus and micro-hardness of the coatings followed the Weibull distributions. With increasing the porosity, the micro-hardness and Young's modulus of the coating decreased. The mean value of the Young's modulus of the coating calculated from Weibull plot was almost proportional to the square root of the micro-hardness of the coating. With increasing the power, Young's modulus of the coating increased, which, in turn, resulted in the increment of the residual stress at the coating surface.     

Effect of Ni-to-Fe ratio on structure and properties of Ni-Fe-B-Si-Nb coatings fabricated by laser processing

Ni-Fe-B-Si-Nb coatings have been deposited on mild steel substrates using high power laser cladding process followed by laser remelting. The influence of Ni-to-Fe concentration ratio in (Ni_100−xFe_x)₆₂B₁₈Si₁₈Nb₂ (x = 55, 50, 45 and 40) powders on the phase composition and microstructure is analyzed by X-ray diffraction, scanning- and transmission-electron microscopies. The microhardness and corrosion resistance properties of the coatings are also measured. The results reveal that amorphous matrix layers are obtained for all coatings. The increase of the Ni-to-Fe ratio can promote the formation of γ(Fe-Ni) phase and decrease the formation of Fe₂B phase and α-Fe phase. The coating with 1:1 ratio of Ni-to-Fe exhibits the highest microhardness of 1200 HV_0.5 and superior corrosion resistance property due to its largest volume fraction of amorphous phase in the coating. Higher or lower than 1:1 ratio of Ni-to-Fe may result in lower amorphous forming ability. However, even that the coating with ratio of 3:2, shows a minimum of microhardness, it shows a better corrosion resistance than other two coatings.     

激光熔覆FeCrNiMnMoxB0.5高熵合金涂层组织与耐蚀性能

为了获得性能优异的涂层材料,采用激光熔覆的方法在Q235钢基体上制备了不同Mo含量的FeCrNiMnMoB0.5系高熵合金涂层,着重探究Mo对高熵合金组织与性能的影响。通过金相、X射线衍射、扫描电镜、硬度计、电化学工作站分别研究了高熵合金涂层的显微组织、相结构、显微硬度及耐蚀性能。结果表明:FeCrNiMnMoB0.5系高熵合金组织为树枝晶,主要由fcc相和少量金属间化合物构成。当添加少量Mo时,涂层的硬度较低,为290 HV,随着Mo的增加,晶格畸变加剧,出现少量金属化合物,涂层硬度最大增加到658 HV。在模拟饱和盐水泥浆溶液中FeCrNiMnMo0.4B0.5表现出较好的耐腐蚀性。     

Ti6Al4V合金表面激光沉积复合涂层的组织和性能

为了增强Ti6Al4V钛合金的耐磨性,采用激光沉积制造方法在其表面上制备了以原位生成的TiC颗粒和直接添加的WC颗粒为增强相的耐磨涂层,观察了各涂层的微观组织,并测量了涂层的显微硬度和涂层在室温大气条件下的摩擦磨损性能。结果表明各涂层和基体呈现冶金结合,原位自生的TiC和部分熔化的WC颗粒均能够均匀弥散分布于基体上,由于增强相颗粒的弥散强化及激光沉积组织的细晶强化作用,基材的硬度和耐磨性均得到了提高。原位自生的TiC涂层比WC涂层硬度梯度分布平缓,但耐磨性稍差。     

Electrodeposition and tribological properties of Ni-SrSO4 composite coatings

Ni-SrSO₄ composite coatings were electrodeposited on superalloy Inconel 718 from a Watts electrolyte containing a SrSO₄ suspension. Ni-SrSO₄ coatings were investigated by scanning electron microscope, microhardness tester, and friction and wear tester in sliding against a bearing steel ball under unlubricated condition. The incorporation of SrSO₄ into Ni matrix increases the microhardness of electrodeposited coatings. Ni-SrSO₄ composite coating exhibits a distinctly low friction coefficient and a small wear rate as contrasted with pure Ni coating and the substrate. The effect of SrSO₄ particles on microstructure and tribological properties of Ni-SrSO₄ composite coatings is discussed.