Preparation and Characterization of Storage and Emission Functional Material of Chlorine Anion: [Ca24Al28O64]4+·(Cl-)3.80(O2-)0.10

通过碳酸钙、γ-三氧化二铝、氯化钙在氯气/氩气混合气气氛下的固态反应制备了一种氯负离子存储-发射功能材料[Ca₂₄Al₂₈O₆₄]⁴⁺·(Cl^-)_3.80(O^2-)_0.10(C12A7-Cl^-)．通过离子色谱、电子顺磁共振、拉曼光谱验证,C12A7-Cl^-材料中存储的负离子主要是氯负离子,浓度为(2.21±0.24)×10²¹ cm^-3,此外还有小部分的氧二价负离子、氧负离子、氧分子负离子．这与通过飞行时间质谱得到的结果一致：从C12A7-Cl^-材料表面发射出的负离子主要是氯负离子(大约90%),还有小部分的氧负离子和电子．材料结构和表观变化分别由X射线衍射和场发射扫描电子显微镜表征     

Ti+(CO2)2Ar和Ti+(CO2)n(n=3-7)络合物离子的红外光解离光谱 (cited: 1)

利用脉冲激光溅射-超声分子束载带方法制备了气相Ti⁺(CO₂)₂Ar和Ti⁺(CO₂)_n(n=3-7)络合物离子．采用红外光解离光谱研究了这些选定的质量离子的振动光谱． 对于每一种络合物离子, 在CO伸缩振动频率范围都观察到了振动峰,表明这些离子具有插入的OTi⁺CO(CO₂)_n-1结构． 对于n≦5的OTi⁺CO(CO₂)_n-1离子,其CO振动和CO₂的反对称伸缩振动频率都比自由的CO和CO₂的频率要高,表明CO和CO₂配体与中心金属离子之间主要是静电相互作用．实验结果还表明TiO⁺可以直接络合五个配体(1个CO和4个CO₂分子)．对于n=2络合物体系,除了插入的OTi⁺CO(CO₂)结构以外,还观察到了具有弯曲结构的OCO-Ti⁺-OCO异构体的存在     

M2B7-(M=Mg,Zn)团簇的双重芳香性促进Mg-Mg和Zn-Zn单键的形成

本文使用密度泛函理论设计了两个无需配体的具有Mg-Mg和Zn-Zn单键的团簇Mg₂B₇^-和Zn₂B₇^-. 这两种团簇的全局能量最低构型均以M₂²⁺(B₇^3-)的形式存在，其中M-M单键处于准平面六边形形状的B₇部分的上方. 化学键分析证实了这些团簇中Mg-Mg和Zn-Zn单键的存在，这些单键是在异常稳定的B₇^3-的驱动下生成的. 该B₇^3-部分同时具有σ和π双重芳香性. 计算得到Mg₂B₇^-和Zn₂B₇^-的垂直跃迁能分别为2.79 eV和2.94 eV.     

RAMAN SCATTERING OF α-ET3(ReO4)2 CHARGE-TRANSFER SALT

We describe the results of Haman studies on C=C stretch modes in α-ET₃(ReO₄)₂ charge-transfer salt with the incident laser beam polarised perpendicular and parallel to the large flat face of plate-like crystal. We have assigned central C=C stretch mode at 1454 cm^-1 and ring C=C stretch mode at 1470cm^-1. The change in ring C=C stretch vibration was observed at the metal-insulator transition of α-ET₃(ReO₄)₂ on warming due to the distortion of the ET molecules.     

O2分子吸附的金属表面的O2(1Δg)猝灭

建立了一套流动装置测量单重态氧O₂(¹Δ_g)在O₂分子吸附的金属Cu、Cr、Ni和Ag表面的猝灭几率. 随实验时间和O₂(¹Δ_g)浓度增加,猝灭几率增加. 当上述金属样品在几帕斯卡的真空度下暴露数小时后猝灭几率会回到原先水平. 提出了一种基于表面吸附位上弱化学吸附的表面吸附氧分子O₂(¹∑_{g相似文献}   

NO分子b4Σ--a4Πi(4,0)带的吸收光谱

通过对NO与He流动混合气体放电, 产生了激发态的NO(a⁴Π_ii) 分子. 利用光外差-浓度调制吸收光谱技术测量了NO分子在12530-12850 cm^-1波段内的吸收光谱, 并标识出b⁴Σ^--a⁴Π_i(4,0)带在该波段内的324条光谱跃迁谱线. 采用标准⁴Σ^--⁴Π_i哈密顿量模型, 通过非线性最小二乘法拟合其中267条谱线, 拟合残差(0.0071 cm^-1) 接近实验系统测量误差(0.007 cm^-1). 获得的主要分子常数与文献提供的常数符合, 并且拟合得到了精细结构分子常数.     

基于从头算势能面对S-(2P)+H2(1Σ+g)→SH-(1Σ)+H(2S)反应的量子含时波包计算

本文基于离子分子SH₂^-基态势能面,应用含时波包方法研究了反应S^-(²P)+H₂(¹Σ⁺_g)→SH^-(¹Σ)+H(²S)的动力学行为. 给出了反应几率和积分截面随碰撞能的变化关系,结果表明,在讨论的所有碰撞能量范围内二者均存在显著的振荡结构. 当初始转动量子数j=0,2,4,6,8,10和振动量子数v=0,1,2,3,4时,从总反应几率数值计算中可以看出,双原子H₂的振动激发和转动激发显著提高了反应活性. 同时积分散射截面的理论值与前人的实验值相符合.     

LiO2(C2V，X2A2)分子的结构与势能函数

使用二次组态相互作用方法，在aug-cc-pvtz基组水平上对LiO₂(C_2V，X²A₂)基态分子进行了几何优化，得到了它的平衡几何构型和力常数.根据原子分子反应静力学原理得到可能的电子状态和离解极限.应用多体展式理论方法推导出了LiO₂(C_2V，X²A₂)基态分子的解析势能函数.     

银催化合成Tb(BO2)3纳米棒

采用固相反应银作催化剂成功合成出棒状结构的稀土硼酸盐Tb(BO₂)₃发光材料. 利用X射线衍射和区域电子衍射研究了产物的结构特性,在700 oC煅烧时,Tb(BO₂)₃纳米棒具有良好晶形. 透射电镜分析表明,Tb(BO₂)₃纳米棒直径为100～200 nm,厚度为30～50 nm,长约3 μm. 基于Ag纳米颗粒附在Tb(BO₂)₃纳米棒的顶端和中部的事实,探讨了Tb(BO₂)₃纳米棒的生长机理. 荧光光谱研究表明,在369 nm紫外光激发下,Tb(BO₂)₃能发出Tb³⁺的特征绿色荧光,发射主峰位于546 nm,归属于⁵D₄→⁷F₅跃迁. 同时,也探讨了煅烧温度对产物的结构、形貌以及发光性质的影响.     

光电子成像研究AgOCH3-和Ag-(CH3OH)x (x=1, 2)

用光电子成像技术和从头算法研究Ag^-(CH₃OH)_x (x=1, 2)和AgOCH₃^-. 从AgOCH₃^-振动分辨的光电子谱得 到AgOCH₃^-的绝热和垂直电离能分别为1.29(2)和1.34(2) eV. Ag^-(CH₃OH)_{1,2相似文献}   

Magnetic susceptibility studies of (CH2)3(NH3)2FeCl2Br2 and (CH2)6(NH3)2FeCl2Br2

The magnetic susceptibility of the layered compounds (CH₂)₃(NH₃)₂FeCl₂Br₂ and (CH₂)₆(NH₃)₂FeCl₂Br₂ has been measured in the range 80 < T < 300 K. The results follow a Curie-Weiss behavior in the range 120 < T < 300 K but are field dependent for T < 120 K. The results are interpreted in terms of a two-dimensional antiferromagnetic interaction which is canted. A comparison with the corresponding pure chloride compounds is given.     

metamagnetic behavior of linear chain pyridine compounds: Co(Pyridine)2Cl2, Fe(Pyridine)2Cl2, Fe(Pyridine)2(NCS)2 and Ni(Pyridine)2Cl2

Magnetic phase transitions in the pyridine (pyr) compounds Co(pyr)₂Cl₂, Fe(pyr)₂Cl₂, Fe(pyr)₂(NCS)₂ and Ni(pyr)₂Cl₂ have been observed at applied magnetic fields of ～0.7, 0.7, 1.1 and 2.7 kG respectively. These low field phase transitions are observed in the Fe and Ni compounds at T = 4.2 K, and in the Co compound at T < 3K, and are consistent with metamagnetic behavior. Magnetic saturation is not achieved in any of these compounds for fields of 60 kG, reflecting high anisotropy.     

Electron paramagnetic resonance of Mn IN (NH4)2Co2(SO4)3 and (NH4)2Ni2(SO4)3 single crystals

EPR studies are reported on single crystals of ammonium cobalt sulphate and ammonium nickel sulphate containing Mn²⁺ ions. In each case only one magnetic complex of Mn²⁺ ion is found. The resonance lines in the case of Mn²⁺ doped ammonium nickle sulphate are characterised by a strong angular dependence of line intensities. The resonance lines in both the cases are fitted to a spin-Hamiltonian corresponding to orthorhombic symmetry.     

Linear-chain antiferromagnetism in Ni(N2H5)2(SO4)2

The compound dihydrazinium bis(sulfato) niccolate(II), Ni(N₂H₅)₂(SO₄)₂, containing sulfato-bridged chains of Ni(II) ions, can be described as an antiferromagnetic Heisenberg linear-chain system. A reasonable agreement of susceptibility measurements in the temperature region 2–80K, with a theory developed by Weng for antiferromagnetic Heisenberg linear chains with spin S=1, is obtained for a value of the intra-chain interaction $\text{J}\text{k}\text{=?3.35K}$. Preliminary results of specific heat measurements, on the other hand, do not fit quite well using this model. The origin of this discrepancy is suggested to be a zero-field splitting of the single ion.     

Linear-chain ferromagnetism in the one-dimensional compounds CoCl2(pyrazole)2 and CoCl2(indazole)2

Two linear-chain compounds of formula CoCl₂L₂, with L = pyrazole (pz) and indazole (indz), have been investigated with the aid of IR, far-IR, ligand field and ESR spectra. Magnetic susceptibility data have been collected in the temperature region 4.2–80 K. Analysis of the susceptibility data in terms of the Ising model yielded the values of the ferromagnetic intrachain exchange constants J = 7.2(6) and 7.4(9) cm^-1 for the pz and indz compound, with corresponding g-values of g∥ = 7.9(7), g⊥ = 4.6(9) and g∥ = 10.8(9), g⊥ = 3(1), respectively. The results are discussed and compared with the similar compound CoCl₂(pyridine)₂. The influence of the bridge geometry and of the π-bonding properties of the organic ligands on the exchange constant are considered for the explanation of different J-values. It is suggested that the π-bonding properties of the organic ligand influence the magnitude of the superexchange constant to a great extent.     

On the room-temperature ferromagnetism in (ZnO)0.98(MnO2)0.02

Room-temperature ferromagnetism (RTFM) is investigated in the polycrystalline bulk (ZnO)_0.98(MnO₂)_0.02 samples prepared by a modified solid-state sintering route. Successive sintering of a sample was carried out in air at different temperatures in the range of 400-1000 °C. The study of magnetization and phase-investigation in the sample was carried out after each sintering step. The progressive suppression of impurities and the consequent reduction in RTFM is clearly observed in the samples with increase in the sintering temperature up to 800 °C. The subsequent successive sintering of the (ZnO)_0.98(MnO₂)_0.02 sample up to 1000 °C yields fully paramagnetic sample exhibiting wurtzite structure. The studies support the conjecture (Kundaliya et al., Nat. Mater. 3 (2004) 709 [18]) that RTFM in this system has an origin related to a randomly distributed impurity phase produced by local dissolution of ZnO and MnO₂.     

Magneto-optical measurement on the layer type magnet (CH2)2(ND3)2MnCl4

The linear birefringence (LB) of the antiferromagnet (CH₂)₂(ND₃)₂MnCl₄ has been measured as a function of temperature and in magnetic fields up to 100 kOe. The temperature dependence of the LB points to a pronounced two dimensional magnetic behaviour. No anomaly corresponding to the effect of three dimensional ordering could be detected at T_N. In theffield dependent measurements the spin flop at H_SF = 33.6 ± 1 kOe (T = 4K) could clearly be detected.     

Structure and electrical conductivity of a novel inorganic solid electrolyte: Na14.5[Al(PO4)2F2]2.5[Ti(PO4)2F2]0.5 (NATP)

A novel inorganic solid electrolyte with a layered framework structure stable up to 1043 K, Na_14.5[Al(PO₄)₂F₂]_2.5[Ti(PO₄)₂F₂]_0.5 (NATP), has been hydrothermally prepared and characterized by single-crystal and powder X-ray diffraction techniques, X-ray fluorescence (XRF) analysis, IR spectroscopic measurement, thermogravimetric and differential thermal analysis (TGA and DTA). NATP crystallizes in the acentric hexagonal space group P3 with a=10.448(2), b=10.448(2), , Z=1, containing a large number of Na⁺ cations in the interlamellar space and the cavities of its framework. There are six different crystallographic Na⁺ cationic sites, in which 8% Na(5) and 12% Na(6) sites are vacant. Electrical conductivity measurements show that Na⁺ cations exhibit a high mobility with two domains for the electrical conductivity versus temperature.     

Chlorine K X-ray absorption-edge structures of CIS-[Pt(NH3)2Cl2], trans-[Pt(NH3)2Cl2], trans-[Pd(NH3)2Cl2] and (NH4)2PdCl4

The K absorption-edge spectra of the ligand chlorine ion in square-planar complex compounds cis- and trans-[Pt(NH₃)₂Cl₂], trans-[Pd(NH₃)₂Cl₂], and (NH₄)₂PdCl₄ are reported and discussed in connection with the chlorine K absorption spectra of K₂PtCl₄ and K₂PdCl₄, reported previously. The observed chemical shift of a white line at the absorption threshold is interpreted in terms of the difference of the ligand-field splitting of electronic states for metal ions. The white line is attributed to the electronic transition from the Cl^? ls level to the lowest unoccupied antibonding molecular orbital (MO), which is specified by a $\text{MO}\text{b}{}_{\mathrm{1g}}\text{(σ}{}^1\text{)}$ in the square-planar complex with D_4h symmetry. The other absorption structures are regarded as continuum “shape resonances” of the outgoing electron trapped by the cage of the surrounding atoms. The effect of geometrical isomerism is found in the chlorine K absorption spectra of cis- and trans-[Pt(NH₃)₂Cl₂].     

Electrical conduction studies on one-dimensional Cs2[Pt(CN)4](FHF)0.39 and Rb2[Pt(CN)4](FHF)0.40

Variable temperature (300-40 K) 4-probe d.c. conduction studies on Cs₂[Pt(CN)₄](FHF)_0.39 and Rb₂[Pt(CN)₄](FHF)_0.40 are described. In these salts T_3D occurs at a lower temperature than in K₂[Pt(CN)₄]Br_0.3·3H₂O and this is attributed to the absence of an inter-chain network of hydrogen bonded water molecules in the bifluorides.