O<Subscript>2</Subscript> photodesorption from AuO<Stack><Subscript>2</Subscript><Superscript>−</Superscript></Stack> and Au<Subscript>2</Subscript>O<Stack><Subscript>2</Subscript><Superscript>−</Superscript></Stack>

Using time-resolved photoelectron spectroscopy, the decay channels of AuO₂⁻ and Au₂O₂⁻ following photoexcitation with 3.1-eV photons have been studied. For AuO₂⁻, a state with a rather long lifetime of 30 ps has been identified. Its decay path could not be determined but photodesorption can be excluded. For Au₂O₂⁻, the spectra indicate O₂ desorption after 3.1-eV photoexcitation on a time scale of 1 ps. While comparing these results on Au _n O₂⁻ with analogous data on Ag _n O₂⁻ clusters, a discernible pattern emerges: for dissociatively bound O₂(AuO₂⁻, Ag₃O₂⁻), there are long-living excited states which do not decay by oxygen desorption, while for molecular chemisorption (Au₂O₂⁻, Ag₂O₂⁻, Ag₄O₂⁻, Ag₈O₂⁻), the 3.1-eV photoexcitation triggers fast O₂ desorption with a high quantum yield.     

Magnetic and magnetoresistive properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–Sr<Subscript>2</Subscript>FeMoO<Subscript>6–δ</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanoheterostructures

A method has been developed for fabricating nanoporous matrices based on anodic aluminum oxide for the deposition of ferromagnetic nanoparticles in them. The modes of deposition of strontium ferromolybdate thin films prepared by the ion-plasma method have been worked out, and the magnetic and magnetoresistive properties, structure, and composition of the films have been investigated. It has been revealed that the microstructure and properties of the strontium ferromolybdate films deposited by ionplasma sputtering depend on the deposition rate and the temperature of the substrate. Based on the measurement of the electrical resistivity of nanoheterostructures in a magnetic field, it has been found that the magnetoresistance reaches 14% at T = 15 K and B = 8 T, which is due to the manifestation of tunneling magnetoresistance.     

Synthesis and characterization of Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>·LiMn<Subscript>0.33</Subscript>Fe<Subscript>0.67</Subscript>PO<Subscript>4</Subscript>/C cathode materials

A new polyanionic cathode material, Li₃V₂(PO₄)₃·LiMn_0.33Fe_0.67PO₄/C for lithium-ion batteries, was synthesized using a sol-gel method and with N,N-dimethyl formamide as a dispersion agent. The analysis of electron transmission spectroscopy and X-ray diffraction revealed that the composite contained two phases. The material has high crystallinity with a grain size of 20–50 nm. The valence states of Mn, V, and Fe in the composite were analyzed by X-ray photoelectron spectroscopy. The electrochemical kinetics in Li₃V₂(PO₄)₃ is effectively enhanced by the incorporation of LiMnPO₄ and LiFePO₄, via structure modification and reduced Li diffusion length. The Li₃V₂(PO₄)₃·LiMn_0.33Fe_0.67PO₄/C materials displayed high rate capacity and steady cycle performance with discharge capacity remained 148 mAh g^?1 after 50 cycles at the rate of 0.2C. In particular, the composite exhibited excellent reversible capacities, with the values of 157, 134, 120, 102, and 94 mAh g^?1 at charge/discharge 0.2, 0.5, 1, 2, and 5C rates, respectively.     

Cluster spin glass and superparamagnetism in RuSr<Subscript>2</Subscript>Eu<Subscript>1.5</Subscript>Ce<Subscript>0.5</Subscript>Cu<Subscript>2</Subscript>O<Subscript>10-</Subscript><Subscript>δ</Subscript>

We investigate in detail the dc magnetization and nonlinear ac susceptibility behavior of the superconducting ferromagnet RuSr₂Eu_1.5Ce_0.5Cu₂O_{10- δ} (Ru1222) to develop a comprehensive understanding of the spin glass and superparamagnetism in this material. The structural properties of the system result in the formation of magnetic (ferromagnetic) clusters of different sizes, shapes and properties. The magnetic clustering of the system leads to observation of various features in dc magnetization and ac susceptibility consistent with superparamagnetism and cluster spin glass states, which can coexist or stand alone, depending on the temperature range considered. Experimental results of magnetic measurements in combination with their analysis have enabled us to explain and distinguish these phenomena, as well as to propose a temperature dependent scenario of the system behavior.     

Preparation and characterization of organic–inorganic hybrid compound [N(C<Subscript>4</Subscript>H<Subscript>9</Subscript>)<Subscript>4</Subscript>]<Subscript>2</Subscript>Cu<Subscript>2</Subscript>Cl<Subscript>6</Subscript>

Organic–inorganic hybrid sample [N(C₄H₉)₄]₂Cu₂Cl₆ was prepared via the reaction between copper chloride and tetrabutylammonium chloride. The compound was characterized by X-ray powder diffraction, IR, Raman, differential scanning calorimetry (DSC), DTA-TGA analysis and electrical impedance spectroscopy. DSC studies indicate a presence of one-phase transition at 343 K. The complex impedance of compound [N(C₄H₉)₄]₂Cu₂Cl₆ have been investigated in temperature and frequency ranges 300–380 K and 200 Hz–5 MHz, respectively. The Z′ and Z″ versus frequency plots are well fitted to an equivalent circuit model. The circuits consist of the parallel combination of bulk resistance R _p and constant phase elements CPE. The frequency dependence of the conductivity is interpreted in term of Jonscher's law: s(w) = s_dc + Awⁿ \sigma (\omega ){ } = {\sigma_{\rm{dc}}} + { }A{\omega^n} . The conductivity follows the Arrhenius relation. The variation of the value of these elements with temperatures confirmed the availability of the phase transition at 343 K detected by DSC and electrical measurements.     

μSR study of Eu<Subscript>0.8</Subscript>Ce<Subscript>0.2</Subscript>Mn<Subscript>2</Subscript>O<Subscript>5</Subscript> and EuMn<Subscript>2</Subscript>O<Subscript>5</Subscript> multiferroics

A comparative μSR study of ceramic samples of the EuMn₂O₅ and Eu_0.8Ce_0.2Mn₂O₅ multiferroics is performed in the temperature range from 15 to 300 K. It is found that the Ce doping of the EuMn₂O₅ sample slightly reduces the temperature of the magnetic phase transition from T _N = 45 K for the EuMn₂O₅ sample to T _N = 42.5 K for the Eu_0.8Ce_0.2Mn₂O₅ sample. Below the temperature T _N for both samples, there are two types of localization of a thermalized muon with different temperature dependences of the precession frequency of the magnetic moment of the muon in an internal magnetic field. The higher frequency in both samples refers to the initial antiferromagnetic matrix. The behavior of this frequency in Eu_0.8Ce_0.2Mn₂O₅ follows the Curie–Weiss law with the exponent β = 0.29 ± 0.02, which differs from the value β = 0.39 standard for 3D Heisenberg magnetics and is observed in EuMn₂O₅, because of the strong frustration of the doped sample. The temperature-independent low frequency is due to the presence of Mn³⁺–Mn⁴⁺ ferromagnetic pairs located along the b axis of the antiferromagnetic matrix and in the regions of phase separation, which contain such ion pairs and e _g electrons recharging them. In both samples, polarization losses are the same (about 20%) and are associated with the formation of Mn⁴⁺–Mn⁴⁺ + Mu complexes near Mn³⁺–Mn⁴⁺ ferromagnetic pairs. In the temperature interval from 25 to 45 K, the separation of the Eu_0.8Ce_0.2Mn₂O₅ structure into two fractions where the relaxation rates of polarization of muons differ by an order of magnitude is revealed. This effect is due to a change in the state of regions of phase separation (1D superlattices) at the indicated temperatures. Such effect in EuMn₂O₅ is significantly weaker.     

Internal friction and magnetoelectric response in two-layer composites Tb<Subscript>0.12</Subscript>Dy<Subscript>0.2</Subscript>Fe<Subscript>0.68</Subscript>–PbZr<Subscript>0.53</Subscript>Ti<Subscript>0.47</Subscript>O<Subscript>3</Subscript>

The inverse magnetoelectric effect and internal friction in two-layer composites based on ferromagnetic Tb_0.12Dy_0.2Fe_0.68 and piezoelectric PbZr_0.53Ti_0.47O₃ are studied in an ac electrical field in the frequency range of 52–213 kHz at temperatures of 293 to 400 K. A correlation is found between the internal friction and the efficiency of the inverse magnetoelectric transformation at resonant frequencies.     

High-Temperature Heat Capacity of Zn<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript>–Cu<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript> Solid Solutions

Differential scanning calorimetry has been used to study the influence of temperature on the heat capacity of synthesized vanadates Zn₂V₂O₇, (Cu_0.56Zn_1.44)V₂O₇, and (Cu_1.0Zn_1.0)V₂O₇. It is found that dependences C_p = f(T) have extremes. The thermodynamic properties of Zn₂V₂O₇ have been determined.     

Structural properties of composite cathode material LiFePO<Subscript>4</Subscript>–Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>

Composite cathode material LiFePO₄–Li₃V₂(PO₄)₃ is synthesized through a chemical reduction and lithiation using FeVO₄·xH₂O as both iron and vanadium sources. The structural properties of LiFePO₄–Li₃V₂(PO₄)₃ are investigated. X-ray diffraction results show the composite material containing olivine type LiFePO₄ and monoclinic Li₃V₂(PO₄)₃ phases. High-resolution transmission electron microscopy and energy-dispersive X-ray spectrometry results indicate that mutual doping effects take place between the LiFePO₄ and Li₃V₂(PO₄)₃ particles with V³⁺ doping the LiFePO₄ while Fe²⁺ dopes the Li₃V₂(PO₄)₃. LiFePO₄–Li₃V₂(PO₄)₃ nanocomposites are formed in the carbon webs. There is no structural compatibility between monoclinic (Li₃V₂(PO₄)₃) and olivine (LiFePO₄) domains in composite material LiFePO₄–Li₃V₂(PO₄)₃.     

Electrical switching in the MoO<Subscript>3</Subscript>–WO<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript> and MoO<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript> glasses

High field electrical switching on blown films of MoO₃(60%)–P₂O₅(40%), MoO₃(50%)–WO₃(10%)–P₂O₅(40%), and MoO₃(45%)–WO₃(15%)–P₂O₅(40%) having different thicknesses was studied and compared. Switching was observed using two terminal samples. S-type current–voltage characteristic (current-controlled negative resistance—CCNR) with memory was observed in molybdenum–phosphate glasses, but N-type characteristic (voltage-controlled negative resistance—VCNR) with threshold in tungsten–molybdenum–phosphate glasses was observed. The important observation was that with the addition of WO₃ to binary MoO₃–P₂O5 led to a change of I–V characteristic from CCNR with memory to VCNR with threshold. The measurements of density and molar volume showed linear relation between MoO₃ content and density which decreased with the increase of MoO₃ content. The samples’ thickness had no significant effect on threshold voltage. The attained results also indicated that the electrode material had no effect on switching property of devices. The switching behavior of the devices did not show any dependence on the polarity of the applied voltage. In terms of the effect of heat on the switching behavior of molybdenum–phosphate glasses, it was found that threshold voltage decreases with increasing of temperature. Finally, the switching phenomenon was explained by thermal (formation of crystalline filaments) and electronic models.     

Large electrostrictive strain in lead-free Bi<Subscript>0.5</Subscript>Na<Subscript>0.5</Subscript>TiO<Subscript>3</Subscript>–BaTiO<Subscript>3</Subscript>–KNbO<Subscript>3</Subscript> ceramics

In the present work, (1−x)(0.935Bi_0.5Na_0.5TiO₃–0.065BaTiO₃)–xKNbO₃ (BNT–BT–KN, BNT–BT–100xKN) ceramics with x ranging from 0 to 0.1 were prepared by the conventional ceramic fabrication process. A large electrostrictive coefficient of ∼10⁻² m⁴ C⁻² is obtained with the composition x ranging from 0.02 to 0.1, which is close to the well-known electrostrictive material Pb(Mg_1/3Nb_2/3)O₃. Under an electric field of 4 kV/mm, the electrostrictive strain can reach as high as 0.08%. Besides, the electric field induced strain behavior indicates a temperature independent behavior within the temperature range of 20 to 150°C. The large electrostrictive strain is suggested to be ascribed to the formation of non-polar (NP) phase developed by the KNbO₃ substitution, and the high electrostrictive coefficient of BNT–BT–KN ceramics makes them great candidates to be applied in the new solid-state actuators.     

Superconductivity in Sr<Subscript>0.75</Subscript>Y<Subscript>0.75</Subscript>Ba<Subscript>1.5</Subscript>Cu<Subscript>3</Subscript> O<Subscript>7−<Emphasis Type="Italic">d</Emphasis></Subscript> compounds

The effect of simultaneous Sr substitution at the Ba and Y sites has been studied in the Sr_0.75Y_0.75Ba_1.5Cu₃O_7–dsystem. Attempts to replace 25% Y and 25% Ba have been successful and superconductivity was observed above 78 K for Sr_0.75Y_0.75Ba_1.5Cu₃O_7–d compound with high oxygen content, i.e., O_6.76, and having orthorhombic crystal symmetry. The compound was treated in argon gas at 800°C to reduce the oxygen content and to induce some structural changes. The Sr_0.75Y_0.75Ba_1.5Cu₃O_6.1 compound thus obtained has tetragonal symmetry and low oxygen content, O_6.1. It has also shown superconductivity at 28 K. The paper presents a careful comparison of the structural and electrical properties and infrared absorbance spectra of the two compounds with the same metallic composition, Sr_0.75Y_0.75Ba_1.5Cu₃, but with different oxygen content and crystal symmetry. The study clearly establishes the occurrence of superconductivity in tetragonal Sr-substituted (both at Y and Ba sites in) YBCO.     

Elastic properties of TeO<Subscript>2</Subscript>–B<Subscript>2</Subscript>O<Subscript>3</Subscript>–Ag<Subscript>2</Subscript>O glasses

A series of glasses [(TeO₂) _x (B₂O₃)_1−x ]_1−y [Ag₂O] _y with x = 70 and y = 10, 15, 20, 25 and 30 mol% were synthesised by rapid quenching. Longitudinal and shear ultrasonic velocity were measured at room temperature and at 5 MHz frequency. Elastic properties, Poisson's ratio, microhardness, softening temperature and Debye temperature have been calculated from the measured density and ultrasonic velocity at room temperature. The experimental results indicate that the elastic constants depend upon the composition of the glasses and the role of the Ag₂O inside the glass network is discussed. Estimated parameters based on Makishima–Mackenzie theory and bond compression model were calculated in order to analyse the experimental elastic moduli. Comparison between the experimental elastic moduli data obtained in the study and the calculated theoretically by the mentioned above models has been discussed.     

Investigation of quasicrystalline Al<Subscript>62.5</Subscript>Cu<Subscript>25</Subscript>Fe<Subscript>12.5</Subscript> and crystalline β-Al<Subscript>50</Subscript>Cu<Subscript>33</Subscript>Fe<Subscript>17</Subscript> alloys by X-ray photoelectron spectroscopy

The electronic spectra of the valence band and core levels of the surface of polygrain alloys with the icosahedral structure and the β-(CsCl)-type solid solution of Al₅₀Cu₃₃Fe₁₇ were investigated by X-ray photoelectron spectroscopy (XPS). The obtained XPS spectra of the Al_62.5Cu₂₅Fe_12.5 alloy, in comparison with those of the crystalline Al₅₀Cu₃₃Fe₁₇ alloy demonstrate narrowing and a decrease in asymmetry of the Fe2p core level and a decrease in the electron state density N(E _F ) near the Fermi level, features expected for the poorly conducting icosahedral phase. The XPS data are compared with the estimates of N(E _F ) based on the low-temperature specific heat measurements.     

Specific heat of the [NH<Subscript>2</Subscript>(CH<Subscript>3</Subscript>)<Subscript>2</Subscript>]<Subscript>2</Subscript>ZnCl<Subscript>4</Subscript> crystal in the temperature region 80–300 K

The specific heat of [NH₂(CH₃)₂]₂ZnCl₄ was measured calorimetrically in the temperature region 80–300 K. As the temperature T decreases, the C _p (T) dependence indicates a phase transition sequence, with the phase transition at T₆=151 K observed for the first time. The thermodynamic characteristics of the crystal were refined. The transformation occurring at T₂=298.3 K is shown to be an incommensurate-commensurate phase transition.     

Fractal magnetic microstructure in the (Co<Subscript>41</Subscript>Fe<Subscript>39</Subscript>B<Subscript>20</Subscript>)<Subscript>x</Subscript>(SiO<Subscript>2</Subscript>)<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript> nanocomposite films

Magnetostructural methods are applied to determine the exchange bond percolation limit in (Co₄₁Fe₃₉B₂₀)_x(SiO₂)_1?x nanocomposites (x _c = 0.30 ± 0.02), which separates the phase plane along the metal concentration axis into a superparamagnetic region and a ferromagnetic region. It is shown that, with respect to the singularities of the magnetization up to the magnetization saturation curves, the ferromagnetic region is further subdivided into three regions differing in the character of the spatial propagation of the magnetization ripples or in the magnetic correlation function characteristics. The fractal dimension of the nanocomposite magnetic microstructure near the percolation threshold is determined.     

Magnetorefractive effect in (Co<Subscript>50</Subscript>Fe<Subscript>50</Subscript>)<Subscript>x</Subscript>(Al<Subscript>2</Subscript>O<Subscript>3</Subscript>)<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript> granular films

The reflectivity spectra and the magnetorefractive effect (MRE) of (Co₅₀Fe₅₀)_x(Al₂O₃)_1?x metal-dielectric granular films (0.07<x<0.52) are analyzed in the IR spectral range λ=2.5–25 µm. It is revealed that the specific features observed in the spectra at λ≈8.5 and 20 µm are associated with the excitation of phonon modes in the dielectric matrix. The magnetorefractive effect in the films is observed below the percolation thresh-old only in p-polarized light and above the percolation threshold for both the p and s polarizations. It is demonstrated that the optical properties of (Co₅₀Fe₅₀)_x(Al₂O₃)_1?x films in the IR spectral range, to a first approximation, can be interpreted in the framework of the effective-medium theory and the magnetorefractive effect can be explained in terms of the modified Hagen-Rubens relation.     

Current dependent reorganization in superconducting Y<Subscript>1</Subscript>Ba<Subscript>2</Subscript>Cu<Subscript>3</Subscript>O<Subscript>7-δ</Subscript>

We present strong non-linear dynamic responses developing due to magnitude and type of driving current in bulk polycrystalline superconducting Y₁Ba₂Cu₃O_7-δ sample at zero magnetic field. Several novel types of dynamic changes induced by the transport current were observed via the time evolution of the voltage (V - t curves). The physical observations appearing in V - t curves were interpreted mainly with the reorganization of driving current in a multiply connected network of weak-link structure. It was found that such a dynamic process could cause an enhancement or suppression in superconducting order parameter due to the magnitude of the driving current and coupling strength of weak link structure together with the chemical and anisotropic states of the sample. It was shown that the general behavior of decays evolving in V - t curves is consistent with an exponential relation which is analogous to the glassy state relaxation.     

Optical activity of γ<Subscript>1</Subscript>-(Ga<Subscript>x</Subscript>In<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>)<Subscript>2</Subscript>Se<Subscript>3</Subscript> crystals

The optical activity of uniaxial γ₁-(Ga_xIn_1?x )₂Se₃ crystals (x=0.1, 0.2, 0.3, 0.4) is studied at T=295 and 77 K in the spectral range 0.5–0.8 πm. It is found that the cationic substitution In → Ga leads to a nonlinear increase in the specific rotation of the plane of polarization ρ and the component g ₃₃ of the gyration tensor. It is shown that the gyrotropy of the crystals studied is determined by high-energy transitions whose energy exceeds the energy of the edge transitions and that the gyrotropy observed has a molecular origin.