低阈值极化电压玻璃光波导电光效应的研究(英文)

采用热极化技术对掺锗玻璃条形光波导进行极化,通过光纤连接(单模)的Mach ZehnderInterferometer系统测量条形波导内诱导出的电光效应,系统地研究了大气环境下极化条件(极化温度、极化时间、极化电压)对电光效应的影响.结果表明:在最佳极化条件下(406℃、-2.4kV、20min),波导内的电光系数为rTM=0.059±0.001pm/V,rTE=0.053±0.001pm/V,且波导结构中存在一个较低的阈值极化电压(100V)和阈值极化温度(80℃),此时在波导样品内仍能被激发出可观察的电光效应;实验还发现采用负极化诱导方式产生的电光系数较正极化提高15%左右.     

PT-PEK-c电光聚合物薄膜的厚度和介电性质

研制了新的PT-PEK-c电光聚合物薄膜材料,用准波导耦合m线方法测量了PT-PEK-c电光聚合物薄膜的厚度,并测量了该聚合物薄膜在1×10²Hz到1×10⁷Hz频率范围内的室温介电常数.测量结果为:厚度d=2.328±0.315μm,在10KHz下,介电常数ε_r＝4023±0.063,介电损耗tanδ＝0.003.     

SiO2脊形条波导热极化引起的电光效应

通过理论模拟对具有上覆盖层的SiO₂脊形条波导结构进行了优化，在此基础上利用微电子工艺制作了SiO₂脊形波导Mach-Zehnder型电光调制器，并进行热极化引起的电光和非线性效应的研究.热极化过程大幅增强了样品的电光及非线性效应，二次电光系数由热极化前的1.56×10^-22(m/V)²提高到热极化后的8.50×10^-22(m/V)²，极化后得到了0.093pm/V的线性电光系数，对热极化的物理机理进行了理论分析. 关键词： 电光调制器 2光波导')" href="#">SiO₂光波导 电光效应 热极化     

SiO2脊形条波导热极化引起的电光效应

通过理论模拟对具有上覆盖层的SiO2脊形条波导结构进行了优化,在此基础上利用微电子工艺制作了SiO2脊形波导Mach-Zehnder 型电光调制器,并进行热极化引起的电光和非线性效应的研究.热极化过程大幅增强了样品的电光及非线性效应,二次电光系数由热极化前的1.56×10-22(m/V)2提高到热极化后的8.50×10-22(m/V)2,极化后得到了0.093pm/V的线性电光系数,对热极化的物理机理进行了理论分析.     

ConCm±(n=1-5; m=1,2)团簇的密度泛函理论研究

本文采用基于自旋极化的密度泛函理论系统研究了Co_nC_m^± (n=1-5; m=1,2)团簇的几何结构和电子结构特性. 将Co_nC^± (n=2-5)团簇中的一个Co替换为C原子, 个体的基态几何结构发生明显变化; 在Co_nC₂^± (n=1-5)团簇的生长序列中, 发现从n=3开始团簇中的两个C原子有彼此分离分布的趋势, 我们分析, 这是Co金属能够维持单壁碳纳米管(SCNTs)保持开口生长, 成为非常有效的一种催化剂的重要原因. 同时, 将Co_nC^± (n=2-5)团簇中添加一个Co原子后系统的总磁矩出现大幅下降的趋势, 但仍保持奇偶交替的规律. 通过比较中性及带电的Co_nC以及Co_nC₂ (n=1-5)团簇的碎裂能, 本工作发现: 由实验获取的SCNTs应均为带正电的体系, 这一结论与已有的实验模型拟合得很好.     

Studies in molecular structure,symmetry and conformation—Part XIV. Crystal and molecular structure of L-isoleucine hydrochloride monohydrate form II

The crystal structure of a new form of L-isoleucine hydrochloride monohydrate C₆H₁₃O₂NHClH₂O (termed form II) has been determined using three-dimensional photographic data. This differs conformationally from the hydrochloride derivative (termed form I, Trommel and Bijvoet 1954) reported earlier. The crystal belongs to the orthorhombic space group P2₁2₁2₁ with cell dimensions,a=5.87±0.01,b=24.77±0.02 andc=6.85±0.01 ? and four molecules per cell,ρ _obs=1.240 g/cm³,ρ _cal=1.238 g/cm³,μ for CuKa=32.6 cm⁻¹. Contribution No. 420 from the Department of Crystallography and Biophysics, University of Madras, Madras 600025.     

基于二维光子晶体耦合腔波导的新型慢光结构研究

对二维介质柱光子晶体耦合腔波导慢光结构进行了研究,发现随着缺陷腔之间晶格个数增多,群速度减小很快,选用7×7超胞单元时耦合腔波导结构的导模最大群速度ν_g-max只有光子晶体线缺陷波导的1/251.然后对7×7超胞单元的缺陷腔周围四个介质柱半径进行调整,发现新型结构导模的ν_g-max进一步减小,最小可达到589×10^-4c,约为未调整之前的1/5.最后通过比较发现,当改变缺陷腔上下相邻两个介质柱半径时得到的结构具有更好的慢光特性.     

阵列波导光栅解复用器输入/输出波导结构串扰的数值分析

本论文采用Marcatili方法分析矩形波导的模场特性,在此基础上计算了AWG波分复用/解复用器串扰与输入/输出波导间隙参数(dr/w),波导结构参数V的变化关系.计算了串扰值一定时,选取V参数与dr/w的关系曲线.分析了在不同折射率差波导中,串扰与偏振的相关性,为器件的整体优化设计提供了参考数据.     

开放的V型三能级系统中原子注入和退出速率对位相相关的无反转激光增益和强度空间演化的调制作用

利用数值计算结果, 研究了具有自发辐射诱导相干的开放V 型三能级原子系统中的传播效应. 研究表明: 改变探测场和驱动场之间的相对位相对无反转激光(LWI)增益和 强度随传播距离的变化即空间演化具有重要的影响; 而原子的注入速率比(S)和退出速率(r₀)的改变将对位相相关的LWI增益和强度的空间演化产生明显的调制作用. 在S(r₀)的一定取值范围内, S(r₀)的值越大, LWI增益和强度越大且强度达到极大值需要的传播距离越长; 相应封闭系统中LWI增益和强度的最大值及能产生增益的传播距离都小于开放系统. Doppler效应对LWI增益和强度的空间演化也具有明显的影响, 存在Doppler效应时得到的LWI增益和强度明显小于无Doppler效应时的值.     

弱激光诱导神经元兴奋性改变的实验研究

利用全细胞膜片钳技术研究弱激光诱导下大鼠海马CA3区锥体神经元兴奋性.实验结果显示：弱激光作用使神经元钠通道激活电位向超极化方向移动,钠电流幅度增大,且这种增大作用具有电压依赖性和可逆性.激光作用显著影响钠电流稳态激活与失活特性，对照组和照射组通道半数激活电压分别为(-4414±528)mV和(-5655±614)mV(n=8,P<001)，半数失活电压分别为(-6902±1031)mV和(-5660±897)mV(n=8, P<0     

Second-order nonlinear optical properties of poled coumaromethacrylate copolymers

Second-order nonlinear optical properties of newly designed and synthesized coumaromethacrylate side-chain polymers are reported. The optimum poling conditions were determined experimentally. The optimum poling temperature for these side-chain polymers is well above the glass transition temperature. The second harmonic coefficient of films poled by coronaonset at elevated temperature and the linear electro-optic coefficient of films poled by contact electrodes were measured. The stabilized value of the second harmonic coefficient, d ₃₃, at 1064nm fundamental wavelength was found to be 13 pm/V. The linear electro-optic coefficient, r ₃₃, exhibits strong dispersion ranging from 2 to 12pm/V in the wavelength range 477 to 1115 nm.     

光折变晶体Ce:BaTiO3电光和压电系数的测量

用干涉仪的方法测量了Ce:BaTiO₃晶体的低频电光系数和压电系数．排除压电效应对光通过晶体引起相位的变化，得到低频下经极化的Ce:BaTiO₃单晶的电光系数r₄₂=1945±220pm/V和r₁₃=11.8±1pm/V．从而，为研究Ce:BaTiO₃晶体的光折变效应和理论计算提供了精确的线性电光系数 关键词：     

Spatial filtering using poled polymer etalon light modulators

Spatial filtering using poled polymer light modulators is studied. The use of a resonator structure is proposed to minimize the driving voltage. Side-chain polymer poly-orange tom-1 isophoronedisocyanate is used as a material. The measured electro-optic coefficient r ₃₃ is 23 pm/V at the wavelength of 633 nm. Spatial filtering of the input images are realized with 30 V applied voltage.     

Optimized second-order optical nonlinearity in thermally poled GeS<Subscript>2</Subscript>-Ga<Subscript>2</Subscript>S<Subscript>3</Subscript>-KI chalcohalide glass

0.56GeS₂-0.24Ga₂S₃-0.2KI (mol%) chalcohalide glass was prepared and second-harmonic generation was observed by the thermal poling process. Second-order optical nonlinearity in the glass was also investigated by different poling temperature, voltage and time to optimize the poling parameters to improve χ ⁽²⁾. The maximum χ ⁽²⁾ in our study as large as 3.74 pm/V was obtained under the optimized poling condition with 5.2 kV, 260°C and 120 minutes.     

Index of refraction, optical activity and electro-optic coefficient of bismuth titanium oxide (Bi12TiO20)

12 TiO₂₀. The first two can be measured by simple and classical methods, but the coexistence of optical activity, electrogyration, field-induced linear birefringence, and piezoelectric and photoelastic effects in photorefractive materials such as Bi₁₂TiO₂₀ complicate the measurement of the electro-optic coefficient. For normal incidence of linearly polarized light we derive analytic expressions for the polarization of light that has passed through the crystal. The ellipticity of the polarization is a function of the electric-field-induced linear birefringence and hence of the electro-optic coefficient of the crystal. Therefore measurement of the ellipticity as a function of an electric field externally applied to the crystal leads to an electro-optic coefficient r₄₁ of 5.3±0.1 pm/V. Received: 22 December 1996/Revised version: 21 March 1997     

Investigation on the nonlinear optical properties of the DCNP/PEK-c guest–host polymer films

The polyetherketone (PEK-c) guest-host polymer thin films doped with 3-(1,1-dicyanothenyl)-1-phenyl-4,5-dihydro-1H-pryazole (DCNP) were prepared. The polymer films were investigated with in situ second-harmonic generation (SHG) measurement. The corona poling temperature was optimized by the temperature dependence of the in situ SHG signal intensity under the poling electric field applying. The temporal and temperature stability of the second-order properties of the poled polymer film were measured by the in situ SHG signal intensity probing. The second-order NLO coefficient L₃₃⁽²⁾=32.65 pm/V at 5=1064 nm was determined by using the Maker fringe method after poling under the optimal poling condition. The dispersion of the NLO coefficient of the guest-host polymer system was determined by the measured value of L₃₃⁽²⁾ at 1064 nm and the two-level model.     

High Accuracy and High Sensitivity Measurements of the Electrooptic Effect in Undoped and MgO-Doped LiNbO3 Crystals

Accurate measurements of the composite electrooptic (EO) coefficients r_c consisting of the EO coefficients r₁₃, r₃₃, and the piezoelectric constant d₃₁ in undoped and MgO-doped LiNbO₃ (LN) were made by extracting the fundamental and third harmonic components from photo-detection signals of the parallel Nicol optics including the LN crystal driven by minimal sinusoidal voltage. The analysis of relationship between multiple-reflection rays in the EO crystal and the accuracy of measurement indicates that anti-reflection films must be coated on the end faces of the crystal for highly accurate measurements. Measured values of r_c of undoped and MgO-doped LN crystals at a wavelength of 632.8 nm were 19.8 ± 0.1 pm/V and 19.2 ± 0.1 pm/V, respectively.     

Waveguide electro-optic modulator in fused silica fabricated by femtosecond laser direct writing and thermal poling

An integrated electro-optic waveguide modulator is demonstrated in bulk fused silica. A Mach-Zehnder interferometer waveguide structure is fabricated by direct writing with a femtosecond laser followed by thermal poling. A 20 degrees electro-optic phase shift is achieved at an operating wavelength of 1.55 microm with an applied voltage of 400 V and an interaction length of 25.6 mm, which correspond to an estimated effective electro-optic coefficient of 0.17 pm/V for the TE-polarized mode.