聚苯氧基磷酸联苯二酚酯/聚磷酸铵膨胀阻燃剂对环氧树脂阻燃性能影响研究

以聚苯氧基磷酸联苯二酚酯(PBPP)与聚磷酸铵(APP)组成复合阻燃剂,对环氧树脂(EP)进行阻燃改性.通过氧指数(LOI)、垂直燃烧(UL-94)、热失重(TGA)、锥形量热(CONE)和扫描电镜(SEM)等方法研究改性环氧树脂的阻燃性能和阻燃机理.结果表明,PBPP/APP体系对EP具有较好的阻燃性能,阻燃剂添加量为10%时能使环氧树脂的氧指数提高到29.6%,垂直燃烧等级达到UL94 V-0级,残炭量大大增加;平均热释放速率下降45.7%,热释放速率峰值下降51.0%,有效燃烧热平均值下降21.1%;TGA、CONE、SEM等综合分析显示了PBPP/APP改性后的环氧树脂比纯环氧树脂具有更高的热稳定性,燃烧后能够形成连续、致密、封闭、坚硬的焦化炭层,在聚合物表面产生有效覆盖、隔绝了氧气,改善了环氧树脂的燃烧性能.     

磷杂菲类阻燃剂的合成及其与聚磷酸铵复合膨胀体系对环氧树脂的阻燃性能研究

以9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)、五硫化二磷(P2S5)为原料合成9,10-二氢-9-氧杂-10-磷杂菲-10-硫化物(DOPS),并将DOPS与聚磷酸铵(APP)组成复合阻燃剂,用于环氧树脂(EP)的阻燃改性.通过氧指数(LOI)、垂直燃烧(UL-94)、热失重(TGA)、锥形量热(CONE)和扫描电镜(SEM)等方法对改性后的环氧树脂的阻燃性能和阻燃机理进行了测试和分析.实验结果表明,DOPS/APP阻燃体系对EP具有很好的阻燃性能,且复配阻燃剂的阻燃效果比单一的阻燃剂阻燃效果好;其中,当阻燃剂的总添加量达到30%时即W_(DOPS)=10%、W_(APP)=20%时,阻燃EP复合材料的LOI值可达到29.2%,垂直燃烧等级达到UL-94 V-0级,残炭量可达49.3%.     

Synthesis of a novel phosphorus‐containing curing agent and its effects on the flame retardancy,thermal degradation and moisture resistance of epoxy resins

A novel phosphorus‐containing compound diphenyl‐(1, 2‐dicarboxylethyl)‐phosphine oxide defined as DPDCEPO was synthesized and used as a flame retardant curing agent for epoxy resins (EP). The chemical structure of the prepared DPDCEPO was well characterized by Fourier transform infrared spectroscopy, and ¹H, ¹³C and ³¹P nuclear magnetic resonance. The DPDCEPO was mixed with curing agent of phthalic anhydride (PA) with various weight ratios into epoxy resins to prepare flame retardant EP thermosets. The flame retardant properties, combustion behavior and thermal analysis of the EP thermosets were respectively investigated by limiting oxygen index (LOI), vertical burning tests (UL‐94), cone calorimeter measurement, dynamic mechanical thermal analysis and thermogravimetric analysis (TGA) tests. The surface morphologies and chemical compositions of the char residues for EP thermosets were respectively investigated by scanning electron microscopy and X‐ray photoelectron spectroscopy (XPS). The water resistant properties of the cured EP were evaluated by putting the samples into distilled water at 70°C for 168 hr. The results revealed that the EP/20 wt% DPDCEPO/80 wt% PA thermosets successfully passed UL‐94 V‐0 flammability rating and the LOI value was as high as 33.2%. The cone test results revealed that the incorporation of DPDCEPO effectively reduced the combustion parameters of the epoxy resin thermosets, such as heat release rate and total heat release. The dynamic mechanical thermal analysis test demonstrated that the glass transition temperature (Tg) decreased with the increase of DPDCEPO content. The TGA results indicated that the incorporation of DPDCEPO promoted the decomposition of epoxy resin matrix ahead of time and led to a higher char yield and thermal stability at high temperatures. The surface morphological structures and analysis of the XPS of the char residues of EP thermosets revealed that the introduction of DPDCEPO benefited the formation of a sufficient, compact and homogeneous char layer with rich flame retardant elements on the epoxy resin material surface during combustion. The mechanical properties and water resistance of the cured epoxy resins were also measured. After water resistance tests, the EP/20 wt% DPDCEPO/80 wt% PA thermosets retained excellent flame retardancy, and the moisture adsorption of the EP thermosets decreased with the increase of DPDCEPO content in EP thermosets because of the existence of the P–C bonds and the rigid aromatic hydrophobic structure in DPDCEPO. Copyright © 2015 John Wiley & Sons, Ltd.     

聚磷酸酯阻燃剂复配聚磷酸铵对环氧树脂阻燃性能的影响

合成了一种9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)的衍生物——聚苯氧基磷酸-2-10-氢-9-氧杂-磷杂菲基对苯二酚酯(POPP), 以间苯二胺(m-PDA)为固化剂, 环氧树脂(EP)为基料, POPP为阻燃剂, 复配聚磷酸铵(APP), 制备了不同磷含量的阻燃环氧树脂. 利用极限氧指数(LOI)和垂直燃烧(UL94)实验表征了环氧树脂的阻燃性能; 以热重分析、 锥型量热和扫描电镜分析了阻燃环氧树脂的热性能和表面形态. 研究结果表明, 阻燃剂总加入量(质量分数)为5%时即可达到UL94 V-0级, 同时LOI值为27.7%; 当总加入量为15%, 即w_POPP=5%, w_APP=10 %时, 其LOI值可达到33.8%. 随着磷含量的增加, 阻燃环氧树脂的初始降解温度略有降低, 但高温下的残炭率明显增加. POPP/APP的加入在很大程度上降低了环氧树脂的热释放速率、 有效燃烧热、 烟释放量和有毒气体释放量. 阻燃环氧树脂在高温下形成比较稳定的致密膨胀炭层, 为底层的环氧树脂主体隔绝了分解产物及热量和氧气交换, 增强了高温下的热稳定性.     

A novel intumescent flame retardant imparts high flame retardancy to epoxy resin

Intumescent flame retardant (IFR) has received the considerable attention ascribed to the inherent advantages including non‐halogen, low toxicity, low smoke release and environmentally friendly. In this work, a novel charring agent poly (piperazine phenylaminophosphamide) named as PPTA was successfully synthesized and characterized by Fourier transform infrared spectra (FTIR) and X‐ray photoelectron spectroscopy (XPS). Then, a series of flame‐retardant EP samples were prepared by blending with ammonium polyphosphate (APP) and PPTA. Combustion tests include oxygen Index (LOI), vertical Burning Test (UL‐94) and cone calorimeter testing,these test results showed that PPTA greatly enhances the flame retardancy of EP/APP. According to detailed results, EP containing 10 wt% APP had a LOI value of 30.2%,but had no enhancement on UL‐94 rating. However, after both 7.5 wt% APP and 2.5 wt% PPTA were added, EP‐7 passed UL‐94 V‐0 rating with a LOI value of 33.0%. Moreover, the peak heat release rate (PHRR) and peak of smoke product rate (PSPR) of EP‐7 were greatly decreased. Meanwhile, the flame‐retardant mechanism of EP‐7 was investigated by scanning electron microscopy (SEM), thermogravimetric analysis/infrared spectrometry (TG‐IR) and X‐ray photoelectron spectroscopy (XPS). The corresponding results presented PPTA significantly increased the density of char layer, resulting in the good flame retardancy.     

Flame‐retardant performance and mechanism of epoxy thermosets modified with a novel reactive flame retardant containing phosphorus,nitrogen, and sulfur

A novel phosphorus‐containing, nitrogen‐containing, and sulfur‐containing reactive flame retardant (BPD) was successfully synthesized by 1‐pot reaction. The intrinsic flame‐retardant epoxy resins were prepared by blending different content of BPD with diglycidyl ether of bisphenol‐A (DGEBA). Thermal stability, flame‐retardant properties, and combustion behaviors of EP/BPD thermosets were investigated by differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), limited oxygen index (LOI) measurement, UL94 vertical burning test, and cone calorimeter test. The flame‐retardant mechanism of BPD was studied by TGA/infrared spectrometry (TGA‐FTIR), pyrolysis‐gas chromatography/mass spectrometry (Py‐GC/MS), morphology, and chemical component analysis of the char residues. The results demonstrated that EP/BPD thermosets not only exhibited outstanding flame retardancy but also kept high glass transition temperature. EP/BPD‐1.0 thermoset achieved LOI value of 39.1% and UL94 V‐0 rating. In comparison to pure epoxy thermoset, the average of heat release rate (av‐HRR), total heat release (THR), and total smoke release (TSR) of EP/BPD‐1.0 thermoset were decreased by 35.8%, 36.5% and 16.5%, respectively. Although the phosphorus content of EP/BPD‐0.75 thermoset was lower than that of EP/DOPO thermoset, EP/BPD‐0.75 thermoset exhibited better flame retardancy than EP/DOPO thermoset. The significant improvement of flame retardancy of EP/BPD thermosets was ascribed to the blocking effect of phosphorus‐rich intumescent char in condensed phase, and the quenching and diluting effects of abundant phosphorus‐containing free radicals and nitrogen/sulfur‐containing inert gases in gaseous phase. There was flame‐retardant synergism between phosphorus, nitrogen, and sulfur of BPD.     

Synergistic effect between a novel hyperbranched charring agent and ammonium polyphosphate on the flame retardant and anti-dripping properties of polylactide

A novel hyperbranched polyamine charring agent (HPCA), a derivative of triazines, was synthesized and well characterized by ¹H NMR and FTIR. HPCA and ammonium polyphosphate (APP) were added into polylactide (PLA) resin as an intumescent flame retardant (IFR) system to impart flame retardancy and dripping resistance to PLA. The flammability and thermal stability of IFR-PLA composites were investigated by limiting oxygen index (LOI), UL-94 vertical burning, cone calorimetry and thermogravometric analysis (TGA) tests. The results showed that the IFR system had both excellent flame retardant and anti-dripping abilities for PLA. The TGA curves suggested that HPCA has good ability of char formation and when combined with APP, would induce synergistic effect which could be clearly observed. This effect greatly promoted the char formation of IFR-PLA composites, hence improved the flame retardant property. Additionally, the structure and morphology of char residues were studied by XPS, FTIR and SEM.     

Co-flame retarding effect of ethanolamine modified titanium-containing polyhedral oligomeric silsesquioxanes in epoxy resin

A metal-doped organic and inorganic hybrid polyhedral oligomeric silsesquioxanes (POSS) with a titanium atom in the POSS cage and an ethanolamine substitute group in the corner, namely MEA-Ti-POSS, was synthesized through simple condensation reaction and substitute reaction. It was blended with 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) to form a kind of blending-type flame retardant system for the modification of epoxy resins. The thermal stability, flame retardancy and mechanical properties of cured epoxy resin composites were studied. Comparing with pure epoxy resin, the LOI value of EP/MEA-Ti-POSS/DOPO composites was raised from 25.2% to 32.7%, and the UL-94 grade reached V-0 level at a loading of the mixture of 5% MEA-Ti-POSS and 5% DOPO. In addition, the cone calorimetry results showed that the heat release rate, total heat release and total smoke production as well as smoke production rate were all reduced during the combustion of EP/MEA-Ti-POSS/DOPO composites. The residual char analysis revealed that carbon residues of EP/MEA-Ti-POSS/DOPO composite served as a physical protective layer to insulate the oxygen and combustible gases to reduce the ablation of the matrix. It was concluded that the mixture of MEA-Ti-POSS and DOPO not only effectively raised the thermal stability and flame retardancy of epoxy composited materials, but also improved their mechanical properties, which expanded a promising application of the metal-POSS derivatives as non-halogen additives in the flame retardant polymers.     

Intrinsically flame retardant epoxy resin - Fire performance and background - Part I

The flame retardant effect of newly synthesized phosphorus-containing reactive amine, which can be used both as crosslinking agent in epoxy resins and as a flame retardant, was investigated. The effect of montmorillonite and sepiolite additives on the fire induced degradation was compared to pristine epoxy resin. The effect of combining the organophosphorous amine with clay minerals was also studied. It could be concluded that the synthesized phosphorus-containing amine, TEDAP can substitute the traditional epoxy resin curing agents providing additionally excellent flame retardancy: the epoxy resins flame retarded this way reach 960 °C GWFI value, 33 LOI value and V-0 UL-94 rating - compared to the 550 °C GWFI value, 21 LOI value and “no rate” UL-94 classification of the reference epoxy resin. The peak of heat release was reduced to 1/10 compared to non-flame retarded resin, furthermore a shift in time was observed, which increases the time to escape in case of fire. The flame retardant performance can be further improved by incorporating clay additives: the LOI and the HRR results showed that the optimum of flame retardant effect of clay additives is around 1 mass% filler level in AH-16-TEDAP system. Applying a complex method for mechanical and structural characterization of the intumescent char it was determined that the flame retarded system forms significantly more and stronger char of better uniformity with smaller average bubble size. Incorporation of clay additives (owing to their bubble nucleating activity) results in further decrease in average bubble diameter.     

六苯氧基环三磷腈的热解及其对环氧树脂的阻燃机理

采用极限氧指数仪和锥形量热仪测试了以六苯氧基环三磷腈(HPCP)阻燃环氧树脂的燃烧性能,结果显示,与纯环氧树脂相比,阻燃环氧树脂的极限氧指数值(LOI)明显提高、热释放速率峰值(pk-HRR)和总热释放量(THR)明显下降、环氧树脂的点燃时间提前以及分解速度加快.采用热失重(TGA)、热重红外联用(TGA-FTIR)、X射线光电子能谱(XPS)和热裂解气相色谱质谱联用(Py-GC/MS)研究了HPCP及其阻燃环氧树脂的热解路线和阻燃机理.结果表明,在阻燃环氧树脂过程中,一方面,HPCP分子中的苯氧基团首先解离并发生歧化反应,由此产生的苯氧基及其歧化产物的焠灭效应在环氧树脂中发挥气相阻燃作用,剩余的磷腈环和苯环基团会进一步裂解产生小分子碎片;另一方面,环氧树脂基体在HPCP的作用下提前分解,产生了基于双酚A结构的大分子碎片并在HPCP裂解产物作用下加速炭化,从而使更多的基体组分以残炭的形式被固定在凝聚相中,提高了阻燃环氧树脂的残炭产率,发挥了凝聚相阻燃作用.     

A facile strategy for enhancing the fire safety of unsaturated polyester resins through introducing an efficient mono‐component intumescent flame retardant

Unsaturated polyester resins (UPRs) are usually used in the field of automotive and electronic appliances, but their natural flammability severely constrain their wide application. In this research, a mono‐component intumescent flame retardant piperazine pyrophosphate (PPAP) was incorporated into the UPR matrix and the fire retardancy, thermal properties, combustion performance, and flame‐retarded mechanisms of UPR/PPAP were comprehensively investigated. With as low as 18 wt% PPAP introduced, UPR/18 wt% PPAP thermosets fulfilled UL‐94 V‐0 grade during vertical burning tests and the limiting oxygen index value reached 29.8%. Cone calorimeter tests shown that the peak of heat release and CO production were prominently declined with the decrease of 60.9% and 70.2% compared with those of UPR. The incorporation of PPAP efficaciously enhanced the fire safety of UPR thermosets. The investigation of flame‐retarded mechanisms for UPR/PPAP thermosets indicated that PPAP stimulated UPR thermosets to form sufficient, compact, partially graphitized, and expanded char layer on thermosets surface in advance and the char layer effectively exerted shielding effect in condensed phase. Thus, the total amount of heat of UPR/PPAP was suppressed with the reduction of 42.5% compared with that of UPR. Overall, the excellent fire safety performance promised the flame‐retardant UPR/PPAP thermosets crucial application values in some key areas.     

New flame retardant epoxy resins based on cyclophosphazene-derived curing agents

To obtain high-efficiency flame retardancy of epoxy resins, a cyclophosphazene derivative tri-(o-henylenediamino)cyclotriphosphazene (3ACP) was successfully synthesized and used as a curing agent for the thermosetting of an epoxy resin system. The flame retardant properties, thermal stability, and pyrolysis mechanism of the resultant thermosets were investigated in detail. The experiments indicated that the synthesized thermoset achieved a UL-94 V-0 rate under a vertical burning test as well as a limiting oxygen index (LOI) of 29.2%, which was able to reach V-0 even when a small amount of 3ACP was incorporated. Scanning electronic microscopic observation demonstrated that the char residue of the thermosets was extremely expanded after the vertical flame test. Thermal analysis showed that the samples had a lower initial decomposition temperature when 3ACP was introduced into the epoxy resin systems. This indicates that the carbonization ability of the thermosets was significantly improved at elevated temperatures. In addition, the incorporation of 3ACP can effectively suppress the release of combustible gases during the pyrolysis process, and the decomposition of E-44/DDS-3ACP curing systems also promotes the formation of polyphosphoramides charred layer in the condensed phase. The investigation on the chemical structures of both the gaseous and condensed phase pyrolysis process confirmed the flame-retardant mechanism of the 3ACP-cured epoxy resins. Therefore, the nonflammable halogen-free epoxy resin developed in this study has potential applications in electric and electronic fields for environment protection and human health.     

A vanillin-derived flame retardant based on 2-aminopyrimidine for enhanced flame retardancy and mechanical properties of epoxy resin

In order to give epoxy resin good flame retardance, a novel bio-based flame retardant based on 2-aminopyrimidine (referred to as VAD) was synthesized from renewable vanillin as one of the starting materials. Its structure was confirmed by NMR and mass spectra. The epoxy resins containing VAD were prepared by utilizing 4,4-diaminodiphenylmethane (DDM) as a co-curing agent, and their flame-retardant, mechanical and thermal properties and corresponding mechanisms were studied. VAD accelerated the cross-linking reaction of DDM and E51 (diglycidyl ether of bisphenol A). 12.5 wt% VAD made the epoxy resin achieve UL-94 V-0 rating and its limited oxygen index (LOI) value increase from 22.4% to 32.3%. The cone calorimetric testing results revealed the decline in the values of total heat release (THR) and peak of heat release rate (pk-HRR) and the obvious enhancement of residue yield. A certain amount of VAD enhanced the flame inhibition, charring and barrier effects, resulting in good flame retardance of the epoxy resin. Furthermore, the tensile strength, flexural strength and flexural modulus of the epoxy resin with 12.5 wt% loading of VAD were 6.5%, 14.9%, 15.2% higher than those of EP, indicating the strengthening effect of VAD. This work guarantees VAD to be a promising flame retardant for enhancing the fire retardancy of epoxy resin without compromising its mechanical properties.     

Thermal and flame retardant properties of epoxy resin cured by a novel phosphorus-containing 4,4′-bisphenol novolac curing agent

A novel flame retardant curing agent for epoxy resin (EP), i.e., a DOPO (9,10-dihydro-9-oxa-10-phosphaphenan-threne-10-oxide)-containing 4,4'-bisphenol novolac (BIP-DOPO) was synthesized and characterized by Fourier transform infrared (FTIR), ¹H NMR, ³¹P NMR spectroscopy, and gel permeation chromatography. The epoxy resin cured by BIP-DOPO itself or its mixture with a commonly used bisphenol A-formaldehyde novolac resin (NPEH720) was prepared. The flame retardancy of the cured EP thermosets were studied by limiting oxygen index (LOI), UL 94 and cone calorimeter test (CCT), and the thermal properties by thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC). The results show that the cured epoxy resin EPNP/BI/3/1, which contains 2.2% phosphorus, possesses a value of 26.2% and achieves the UL 94 V-0 rating. The data from cone calorimeter test demonstrated that the peak release rate, average heat release rate, total heat release decline sharply for the flame retarded epoxy resins, compared with those of pure ones. DSC results show that the glass-transition temperatures of cured epoxy resins decrease with increasing phosphorus content. TGA indicates that the incorporation of BIP-DOPO promotes the decomposition of epoxy resin matrix ahead of time and leads to higher char yield. The surface morphological structures of the char residues reveal that the introduction of BIP-DOPO benefits to the formation of a continuous and solid char layer on the epoxy resin material surface during combustion.     

Synergistic flame‐retardant effect and mechanisms of boron/phosphorus compounds on epoxy resins

To explore the component synergistic effect of boron/phosphorus compounds in epoxy resin (EP), 3 typical boron compounds, zinc borate (ZB), boron phosphate (BPO₄), and boron oxide (B₂O₃), blended with phosphaphenanthrene compound TAD were incorporated into EP, respectively. All 3 boron/phosphorus compound systems inhibited heat release and increased residue yields and exerted smoke suppression effect. Among 3 boron/phosphorus compound systems, B₂O₃/TAD system brought best flame‐retardant effect to epoxy thermosets in improving the UL94 classification of EP composites and also reducing heat release most efficiently during combustion. B₂O₃ can interact with epoxy matrix and enhance the charring quantity and quality, resulting in obvious condensed‐phase flame‐retardant effect. The combination of condensed‐phase flame‐retardant effect from B₂O₃ and the gaseous‐phase flame‐retardant effect from TAD effectively optimized the action distribution between gaseous and condensed phases. Therefore, B₂O₃/TAD system generated component synergistic flame‐retardant effect in epoxy thermosets.     

Low flammability and smoke epoxy resins with a novel DOPO‐based imidazolone derivative

In this work, a DOPO‐based imidazolone derivative named DHI was synthesized using DOPO, 5‐amino‐2‐benzimidazolinone and 4‐hydroxybenzaldehyde as raw materials. The chemical structure of DHI was characterized by ¹H‐NMR, ³¹P‐NMR and Fourier transform infrared spectra (FTIR). Then, a series of different flame‐retardant epoxy resin (EP) thermosets were prepared by mixing flame retardant DHI. The thermal properties of the cured EPs was investigated by thermogravimetry analysis (TGA) and differential scanning calorimeter (DSC), and the results showed the thermal stability and glass transition temperature (T_g) of the cured EP modified with DHI declined slightly compared with that of neat EP. The limited oxygen index (LOI) and UL94 test results exhibited DHI imparted good flame retardancy to EP. The EP‐4 (phosphorus content of 1.25%) possessed a LOI value of 36.5% and achieved a V‐0 rating. Furthermore, the peak of heat release rate (PHRR) and total heat release rate (THR) of EP‐4 decreased by 38.7% and 24.5%, respectively. Excitedly, the total smoke production (TSP) of EP‐4 sample declined by 62.5%, which meant DHI also made EP obtain excellent smoke suppression property. Moreover, the flame‐retardant mechanism was studied by scanning electron microscopy (SEM) and pyrolysis‐gas chromatography/mass spectrometry (Py‐GC/MS). It was reasonable inferred that DHI could not only promote EP to form dense char layer in condensed phase, but also restrain combustion in gaseous phase through catching the free radicals sourced from the degradation of EP.     

Flame retardant and toughening behaviors of bio‐based DOPO‐containing curing agent in epoxy thermoset

Based on bio‐based furfural, a phosphorus‐containing curing agent (FPD) was successfully synthesized, via the addition reaction between 9,10‐dihydro‐9‐oxa‐10 phosphaphenanthrene‐10‐oxide (DOPO) and furfural‐derived Schiff base. Then, as co‐curing agent, FPD was used to prepare flame retardant epoxy thermosets (EP) cured by 4, 4′‐diaminodiphenyl methane. The incorporated FPD improved the flame retardancy and toughness of epoxy thermoset, simultaneously. When 5 wt% FPD was added into EP, the FPD/EP achieved 35.7% limited oxygen index (LOI) value and passed UL94 V‐0 rating, meanwhile. In FPD/EP thermoset, the incorporated FPD reduced the thermal decomposition rate, increased the charring capacity, and inhibited the combustion intensity of epoxy thermoset. Through gas‐phase and condensed‐phase actions in weakening fuel supply, suppressing volatile combustion, and enhancing charring barrier effect, FPD decreased the heat release of burning epoxy thermoset, significantly. For the outstanding effectiveness on both flame retardancy and toughness, the study on FPD provides a promising way to manufacture high‐performance epoxy thermoset.     

聚磷酸铵-苯并噁嗪微胶囊的制备及其对环氧树脂燃烧性能影响

以多聚甲醛、丙烯胺、苯酚为原料,通过Mannich反应合成烯丙基型苯并噁嗪单体(Bala),并通过核磁共振氢谱(~1H-NMR)确定了其化学结构.将Bala在聚磷酸铵(APP)原位开环聚合后,制备APP微胶囊(BMAPP).傅里叶变换红外(FTIR)和静态接触角测试表明,Bala在APP表面成功聚合,并有效提高APP的疏水性,与纯APP相比,BMAPP的接触角从10.8°提高到了71.3°.将BMAPP添加到环氧树脂(EP)中,制备EP/BMAPP复合材料.通过热重分析仪(TGA)、垂直燃烧(UL-94)、极限氧指数(LOI)、锥型量热仪(CONE)和动态热机械分析仪(DMA)对EP和EP/BMAPP的热性能以及燃烧性能进行对比分析.结果显示,10%的BMAPP的成炭效果最佳,有良好的阻燃性能,可使EP的LOI值从22.6%提高到33.6%,并通过UL-94 V-0级,600°C下残炭率达26.3%.同时,BMAPP可大幅度降低EP燃烧过程中烟密度和热释放速率,提高EP的玻璃化转变温度(T_g).BMAPP/EP-10%中,PBala和APP协同后使EP热释放速率峰值(PHRR)由1247 kW·m~(-2)降低到434 kW·m~(-2),生烟速率(SPR)降低67%左右,T_g从169°C提高到了173°C.     

Facile synthesis of bio-based phosphorus-containing epoxy resins with excellent flame resistance

The development of high-performance biomass-derived epoxy thermosets with excellent flame resistance is vital to various applications (i.e., composites, coatings and adhesives). Herein, a difunctional epoxy monomer bis(2-methoxy-4-(oxiran-2-ylmethyl)phenyl) phenyl phosphate (BEU-EP) was synthesized from abundant and biobased eugenol. In addition, BEU-EP was cured by 4,4′-diaminodiphenyl methane (DDM) and the cured resin diglycidyl ether of bisphenol A (DGEBA)/DDM was used as a reference. Results indicated that BEU-EP/DDM not only showed a 58.1%, 28.8% and 35.1% increase in residual char (at 700 °C), flexural and storage modulus (at 30 °C) compared with DGEBA/DDM, but also exhibited excellent flame resistance and smoke suppression. BEU-EP/DDM passed V-0 rating (in UL-94 testing) with limiting oxygen index (LOI) of 38.4% and greatly decreased the peak heat release rate (pHRR) and total smoke production (TSP) by 84.9% and 80.5%, respectively. The mechanism analysis confirmed that the phosphorus-containing group and aromatic structure from BEU-EP contributed both the gas and condensed-phase flame retardation of BEU-EP/DDM network. This work provides an efficient and scalable route for synthesizing biobased epoxy thermosets with high integrated performance and superior flame resistance.     

含亚胺结构新型磷-氮协效阻燃化合物的合成及对环氧树脂的阻燃作用

采用醛胺缩合反应,以4-(5,5-二甲基-1,3-二氧杂环己内磷酰基)苯甲醛(PCHO)分别与对苯二胺、乙二胺反应合成两种磷酸酯-亚胺双官能化合物阻燃剂(FR:N¹,N⁴-二[4-(5,5-二甲基-1,3-二氧杂环己内磷酰氧基)苯基亚甲基]-1,4-苯二胺(PNB)和N¹,N²-二[4-(5,5-二甲基-1,3-二氧杂环己内磷酰氧基)苯基亚甲基]-1,2-乙二胺(PNE)),研究了FR对4,4'-二氨基二苯砜(DDS)固化双酚A二缩水甘油醚型环氧树脂(DGEBA)体系的阻燃作用及阻燃机理。 研究发现FR的引入显著提高了DGEBA/DDS在700 ℃时的残炭率(R_c),同时提升了材料的阻燃性能,其中以乙二胺合成的PNE阻燃性能显著优于以苯二胺合成的PNB。 当磷添加质量分数为1.5%时,PNE-1.5/DGEBA/DDS在N₂气下的R_c为35.1%,在空气下的R_c为14.4%,极限氧指数(LOI)为33.2%,并可达阻燃等级UL-94最高阻燃级别V-0级。 同时,PNE-1.5/DGEBA/DDS相较于DGEBA/DDS保持了弯曲强度和76%以上的冲击强度,机械性能显著优于PNB-1.5/DGEBA/DDS。 通过阻燃机理分析FR在DGEBA/DDS体系中具有凝聚相、气相及磷-氮协效共同作用的阻燃特点。 磷酸酯-亚胺双官能团化合物FR对环氧树脂体系具有良好的阻燃作用,其中PNE阻燃效率高、机械性能负面影响小,具有潜在应用价值。