烧结型NdFeB永磁体表面有机纳米复合膜的制备及性能

采用自组装分子膜技术在烧结型NdFeB永磁体表面制备了三嗪硫醇三乙基硅烷(TES)自组装分子膜(TES-SAMs), 在TES-SAMs的基础上利用自主开发的有机镀膜技术制备了具有含氟官能团的三嗪硫醇(ATP)有机纳米复合薄膜(TES-ATP). 通过X射线光电子能谱仪(XPS)、傅里叶变换红外(FTIR)光谱仪、椭圆偏振光谱仪、原子力显微镜(AFM)和接触角测量仪对薄膜的表面状况进行评价, 使用UMT-2型摩擦磨损试验机研究TES-SAMs和TES-ATP的微摩擦学性能. 研究结果表明: TES-SAMs和TES-ATP的膜厚分别是5.08和29.78nm; 表面自由能从基体的73.13 mJ·m^-2下降到TES-SAMs的63.69 mJ·m^-2和TES-ATP复合膜的10.19 mJ·m^-2, 且TES-ATP复合膜对蒸馏水的接触角为123.5°, 成功实现了NdFeB表面由亲水到疏水的转换.TES-SAMs和TES-ATP均能有效降低摩擦系数, TES-SAMs的摩擦系数为0.22, TES-ATP的摩擦系数为0.12, 而基体的摩擦系数为0.71; 同时, TES-ATP还表现出良好的抗磨性能. TES-ATP复合膜为微机电系统中的摩擦磨损问题的解决提供了一种新思路.     

用于电卡制冷的聚(偏氟乙烯-三氟乙烯)(55/45)/0.75BiFeO3-0.25BaTiO3复合材料的制备及热导率增强

以聚(偏氟乙烯-三氟乙烯)(55/45)(P (VDF-TrFE)(55/45))作为聚合物基体,0.75BiFeO₃-0.25BaTiO₃(BFO-BTO)纳米纤维作为填料以提高共聚物的热导率。结果表明,少量的BFO-BTO纳米纤维即可实现共聚物热导率的提高。在75℃时,纳米纤维含量为2%的复合材料的热导率为0.21 W·m^-1·K^-1,几乎是P (VDF-TrFE)(55/45)共聚物膜的2倍。同时,加入纳米纤维后共聚物的电热效应(ECE)几乎没有变化。这些结果表明少量BFO-BTO纳米纤维的加入在有效提高P (VDF-TrFE)(55/45)共聚物热导率的同时能够保持共聚物较高的ECE。     

MXene/枝状Co/聚偏氟乙烯复合光热膜制备及其界面蒸发性能

使用湿法刻蚀方式将Ti₃AlC₂刻蚀剥离成单/少层Ti₃C₂T_xMXene纳米片,采用电化学还原法制备枝状Co,然后以亲水的聚偏氟乙烯(PVDF)膜为基底通过真空抽滤制备Ti₃C₂T_x/枝状Co/PVDF复合光热膜。对复合材料的结构和形貌进行表征,研究了复合光热膜的光吸收性能和界面蒸发性能。结果表明,在模拟1个太阳光照下(光照强度为1kW·m^-2),Ti₃C₂T_x/枝状Co/PVDF复合光热膜的光吸收率达到95.3%,纯水蒸发速率达到1.78kg·m^-2·h^-1,界面蒸发效率高达97.5%。此外,还测试了在模拟海水中的界面蒸发性能,蒸发冷凝得到的水达到世界卫生组织(WHO)和美国环境保护署(EPA)饮用水标准,蒸发速率达到1.61kg·m^-2·h^-1,循环5次后稳定在1.59kg·m^-2·h^-1。     

自组装的四(4-N,N-二乙胺基苯基)卟啉/多酸(钠)有机/无机复合薄膜及其气敏性质

选择Keggin型12-磷钨酸（TPA）及其钠盐（NaTP）水溶液为亚相,用四（4-N,N-二乙胺基苯基）卟啉化合物（H₂TNPP）自组装膜为功能模板,釆用低成本的QLS法成功制备了2种新型有机/无机复合材料：H₂TNPP/TPA,H₂TNPP/NaTP QLS薄膜。薄膜结构、形貌及半导体性质测试发现：H₂TNPP分子在H₂TNPP/TPA,H₂TNPP/NaTP复合膜中均采取H-聚集模式,TPA亚相上H-聚集程度更大。而在纯H₂TNPP膜中其为J-聚集模式。3种薄膜表面均为纳米颗粒形貌,以H₂TNPP/NaTP膜表面颗粒均一,颗粒尺寸最小（~60 nm）,H₂TNPP/TPA膜表面缺陷较多,颗粒尺寸最大（~150 nm）。薄膜导电性依次为H₂TNPP/NaTP（3.00×10^-5 S·cm^-1）>H₂TNPP/TPA（2.49×10^-5 S·cm^-1）>H₂TNPP膜（1.53×10^-5 S·cm^-1）。常温气敏测试发现：3种薄膜在30 s内对浓度小于1.88 mg·m^-3的NO₂气体都有响应,灵敏度依次为H₂TNPP/NaTP（43%）>H₂TNPP膜（16%）>H₂TNPP/TPA（4.5%）。具有最小颗粒尺寸和最高导电性的H₂TNPP/NaTP复合薄膜具有最高的灵敏度,并且对NO₂检测限低至0.094 mg·m^-3。显示出了非常高的实际应用价值。本研究为制备低成本、高灵敏度、环境友好的快速室温NO₂气敏器件提供了一种新的策略。     

钇离子掺杂对二氧化钛纳米薄膜光诱导超亲水性能的影响及其机理

用溶胶-凝胶法和浸渍-提拉法工艺,在玻璃表面上制备了均匀、透明的钇离子(Y³⁺)掺杂二氧化钛纳米薄膜。用XRD分析了样品的晶相及其与热处理温度的关系,用X射线光电子能谱(XPS)分析了薄膜表面氧的状态,用可见光吸收光谱分析了涂膜层数对透光率的影响,用接触角仪测定了其亲水性。研究了Y³⁺掺杂本身和具体的掺杂量、光照强度和时间对薄膜亲水性的影响。研究结果表明,掺杂Y³⁺的二氧化钛纳米薄膜,在物质的量分数x(Y³⁺/Ti⁴⁺)=1.5%时,经紫外光照30min或自然光照1h后,与水的接触角小于5°,表现出超亲水性;与纯二氧化钛纳米薄膜相比,其超亲水性对光诱导更为敏感;在有实用意义的超亲水性的稳定方面也有明显的改善;这应部分地与固体化学所描述的Y³⁺掺杂所造成固定、额外并且是高浓度的氧空位有关。     

热处理对二氧化锰电化学行为的影响

以高锰酸钾和醋酸锰为前驱体, 通过液相沉淀法合成得到二氧化锰. 在不同温度热处理条件下研究二氧化锰的结构转变及其作为超级电容器电极材料的电化学行为. 采用X射线衍射(XRD), 扫描电镜(SEM), 氮气物理吸附和热重(TG)等手段表征产物的结构特点; 采用循环伏安和恒流充放电等方法表征其电化学行为. 结果表明: 合成的二氧化锰是具有中孔特征的α-MnO₂, 比表面积为253 m²·g^-1, 颗粒尺寸在50-100 nm之间. 350 °C以下的低温热处理使氧化锰仍能保持α-MnO₂的晶体结构, 比表面积为170 m²·g^-1左右, 单电极比电容值由原来未热解时的267 F·g^-1增加到250 °C热处理后的286 F·g^-1. 高温热处理(>450 °C)导致氧化锰逐渐过渡为α-Mn₂O₃, 且表面积下降约为30 m²·g^-1, 比电容急剧下降. 低温热处理后氧化锰的电化学稳定性明显提高, 在50 mV·s^-1的快速扫描速率下, 电极具有良好的倍率特性.     

疏水介孔二氧化硅膜的制备与表征

用甲基三乙氧基硅烷(MTES)代替部分正硅酸乙酯(TEOS)作为前驱体，以聚乙烯醚-聚丙烯醚-聚乙烯醚三嵌段共聚物(P123)作有机模板剂，通过共水解缩聚反应制备了甲基修饰的介孔SiO₂膜。利用N₂吸附、FTIR、²⁹Si MAS NMR以及接触角测量仪对膜的孔结构和疏水性进行了表征。结果表明，修饰后的膜材料具有良好的介孔结构，最可几孔径为4.65 nm，孔体积为0.69 cm³·g^-1，比表面积为938.4 m²·g^-1；同时疏水性明显提高，当n_MTES/n_TEOS达到1.0时，其对水的接触角达到109°± 1.1°。气体渗透实验表明气体通过膜孔的扩散由努森机制所控制。     

有机功能化α-Al2O3陶瓷中空纤维表面合成高性能分离氢用NaA分子筛膜

通过浸渍3-氨丙基甲基二乙氧基硅烷(ADMS)对α-Al₂O₃中空纤维载体进行有机功能化改性, 使载体表面带正电, 利用NaA分子筛晶种负电性与功能化载体之间的静电吸附机理进行预涂晶种, 采用微波加热-二次生长法于载体表面合成了NaA分子筛膜. 采用X射线衍射(XRD)、zeta 电位、扫描电子显微镜(SEM)等分析手段和气体渗透实验对NaA分子筛膜进行了表征. 考察了未改性NaA分子筛膜与改性NaA分子筛膜的形貌、结构和气体渗透性能差异. XRD结果表明载体表面只有NaA分子筛生成; zeta 电位分析表明NaA分子筛晶种及分子筛前驱体与有机功能化载体电位相反, 存在静电吸附作用; SEM结果显示改性NaA分子筛膜表面颗粒相互联结呈孪生态, 膜厚约5 μm, 膜层致密、均匀、平整; 在不同温度下对H₂、O₂、N₂和C₃H₈进行气体渗透测试,35 °C条件下改性NaA分子筛膜对H₂的渗透率仅为3.6×10^-7 mol·m^-2·s^-1·Pa^-1, 较未改性NaA分子筛膜的渗透率(4.0×10^-7 mol·m^-2·s^-1·Pa^-1)低, 而改性NaA分子筛膜的H₂/C₃H₈理想分离系数则高达11.25, 远大于未改性NaA分子筛膜的H₂/C₃H₈理想分离系数(5.06).     

介孔氧化钨电色薄膜的制备与性能研究

采用一种新的非离子型gemini表面活性剂结构导向模板, 成功制备了介孔氧化钨薄膜. 通过SAXRD, TEM和N₂吸附-脱附等方法考察薄膜的制备和微结构特性, 发现获得的产物具有三维蠕虫介孔结构, 比表面积可达145.5 m²• g^－1. 测定了该薄膜在无水高氯酸锂/碳酸丙烯酯电解质溶液中的循环伏安和电致变色性能, 并与无模板薄膜进行了对比研究. 研究表明, 由于具有更大的电化学活性比表面, 纳米介孔氧化钨薄膜表现出增强的电色性能, 在633 nm波长处的透过率调制幅度可达60%以上, 着色效率为51.7 cm²•C^－1.     

硫化镉纳米膜的生物还原-化学沉淀耦合制备及其性能表征

本文应用生物还原-化学沉淀耦合反应(CRBRCP-EDTA)制备出硫化镉纳米薄膜,并借助XRD和SEM对合成材料的物相、结构、形貌进行了表征。研究表明,以铝片为基底时CdS难以沉积,CdS纳米薄膜不能形成;以导电玻璃和单晶硅片为基底时CdS纳米薄膜方可生成。导电玻璃和单晶硅片薄膜都是双层结构,导电玻璃薄膜下层厚度大约40~50 nm,上层厚度大约450~500 nm,整体厚度大约500~550 nm;硅片薄膜的上下两层厚度基本相等,均为300 nm左右,而整体厚度达到600~650 nm。Cd²⁺浓度增加和分散剂PAM加入显著改善了导电玻璃薄膜质量,膜的致密性、均匀性和光催化活性都有所提高。     

AZ31镁合金表面聚吡咯的化学氧化合成及其耐蚀性能

以对甲苯磺酸钠为掺杂剂, 三氯化铁为氧化剂, 用化学氧化聚合法在AZ31 镁合金表面制备聚吡咯(PPy)膜. 采用傅里叶变换红外(FTIR)光谱分析了镁合金表面聚吡咯膜结构, 通过电化学极化曲线、电化学阻抗谱(EIS)研究了其耐蚀性能, 通过扫描电子显微镜(SEM)、X射线能量散射谱(EDS)分析了表面形貌和成分. 和镁合金裸样相比, 聚吡咯膜对镁合金腐蚀有一定的抑制作用. 硅烷预处理改善了镁合金/聚吡咯体系的耐腐蚀性能, 使腐蚀电位较镁合金裸样正移了110 mV, 电流密度减小了约2个数量级.     

Stearate as a green corrosion inhibitor of magnesium alloy ZE41 in sulfate medium

The efficiency of stearate as a corrosion inhibitor for magnesium alloy ZE41 has been studied in sodium sulfate medium, employing electrochemical techniques like potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The results of polarization study imply that stearate functions as a mixed-type corrosion inhibitor with a predominant anodic control. The adsorption of stearate on alloy surface is found to obey the Langmuir adsorption isotherm. The proposed inhibition mechanism involved adsorption of stearate onto metal surface, followed by precipitation of magnesium stearate within the microdefects of Mg(OH)₂ surface film which enhanced the barrier effect of an otherwise porous partially protective film.     

Corrosion resistance and durability of superhydrophobic surface formed on magnesium alloy coated with nanostructured cerium oxide film and fluoroalkylsilane molecules in corrosive NaCl aqueous solution

The corrosion resistant performance and durability of the superhydrophobic surface on magnesium alloy coated with nanostructured cerium oxide film and fluoroalkylsilane molecules in corrosive NaCl aqueous solution were investigated using electrochemical and contact angle measurements. The durability of the superhydrophobic surface in corrosive 5 wt% NaCl aqueous solution was elucidated. The corrosion resistant performance of the superhydrophobic surface formed on magnesium alloy was estimated by electrochemical impedance spectroscopy (EIS) measurements. The EIS measurements and appropriate equivalent circuit models revealed that the superhydrophobic surface considerably improved the corrosion resistant performance of magnesium alloy AZ31. American Society for Testing and Materials (ASTM) standard D 3359-02 cross cut tape test was performed to investigate the adhesion of the superhydrophobic film to the magnesium alloy surface. The corrosion formation mechanism of the superhydrophobic surface formed on the magnesium alloy was also proposed.     

XPS study of the effect of aluminium on the atmospheric corrosion of the AZ31 magnesium alloy

The surface characteristics and corrosion behaviour of the AZ31 magnesium alloy exposed to a high relative humidity (RH) atmosphere were investigated. During the first 15 days of humidity test at 98% RH and 50 °C, a significant increase of magnesium carbonate and a decrease of magnesium oxide were detected on the surface film by XPS; after this stage, increased exposure times did not produce substantial changes on the relative amounts of these compounds. The surface film of commercially pure magnesium, also examined for comparison purposes, revealed more magnesium carbonate and less magnesium oxide compared with the AZ31 alloy. Unlike the AZ31 alloy, the surface of pure Mg disclosed almost complete substitution of MgO by magnesium carbonate after 30 days of exposure time. Mass gain values of tested specimens and scanning electron microscope characterisation of corroded surfaces indicated lower corrosion susceptibility of the AZ31 alloy compared with the commercially pure Mg, suggesting superior chemical stability of the oxide/hydroxide film formed over the magnesium–aluminium alloy surface. XPS and energy dispersive X‐ray (EDX) analyses did not revealed any substantial enrichment of aluminium in the corrosion products film on the AZ31 alloy after 30 days of testing. Copyright © 2008 John Wiley & Sons, Ltd.     

Effects of film-forming conditions on surface properties and structures of diblock copolymer with perfluoroalkyl side chains

Film-forming conditions (cast solvents and film-forming technique: casting or spin-coating) are found to regulate the surface free energy of a diblock copolymer composed of methyl methacrylate and 2-perfluorooctylethyl methacrylate (PMMA-b-PFEMA). The surface properties and structures both in the solid state and in the solution of this polymer were investigated using dynamic contact angle, X-ray photoelectron spectroscopy, X-ray diffraction, reflection-adsorption Fourier transform infrared spectroscopy, dynamic light scattering, and surface pressure measurements. The surface free energy of the PMMA-b-PFEMA film drastically changed from 7.8 to 28.4 mJ/m(2), depending on the film-forming conditions. For the film cast from the micellar solution, the surface free energy is governed by the unimers, localized at the air-solution interface. On the other hand, higher amounts of micelles with the laid perfluoroalkyl side chains were exposed on the surface of the spin-coated film, which yielded a relatively high surface free energy. These findings demonstrated a significant effect of the in-solution molecular association on the surface structures and properties of the solid. In particular, the in-solution unimers played the most important role in lowering the surface free energy of the PMMA-b-PFEMA films.     

硼砂-对苯二甲酸电解液中AZ91D镁合金的阳极氧化处理

研究了硼砂-对苯二甲酸环保型电解液中AZ91D镁合金的阳极氧化.考察了对苯二甲酸对镁合金阳极氧化过程及其氧化膜性能的影响,并利用扫描电镜(SEM)、X射线衍射(XRD)、能量散射谱(EDS)、动电化极化和电化学交流阻抗谱(EIS)等进行了分析表征.结果表明,对苯二甲酸的浓度对阳极氧化成膜过程、氧化膜的表面形貌、厚度、相结构和耐腐蚀性能都有重要影响.在硼酸盐电解液中加入适量的对苯二甲酸后,氧化电流密度降低,过度放电现象受到了明显的抑制,所制得的阳极氧化膜的质量也有了显著改善.氧化膜表面变得光滑、致密,膜厚度略有降低.氧化膜与镁合金基底的结合更紧密,而且其耐腐蚀性能也得到了明显增强.该研究对于镁合金阳极氧化处理工艺的环保化及阳极氧化膜质量的提高都具有积极意义.     

铝合金表面原位自组装超疏水膜层的制备及耐蚀性能

采用阳极氧化法在铝合金表面原位构造粗糙结构, 经表面自组装硅氧烷后得到超疏水自清洁表面, 与水滴的接触角最大可达157.5°±2.0°, 接触角滞后小于3°. 通过傅立叶变换红外(FT-IR)光谱分析仪、场发射扫描电子显微镜(FE-SEM)、能谱仪(EDS)、原子力显微镜(AFM)和接触角测试对阳极氧化电流密度、硅氧烷溶液中水的含量和自组装时间等参数进行了分析, 并得到制备超疏水自清洁表面的最优工艺参数. FE-SEM及AFM的测试结果表明, 由自组装硅氧烷膜层的无序性形成的纳米结构和阳极氧化构造的微米级粗糙结构与硅氧烷膜层的低表面能的协同作用构成了稳定的超疏水表面. 电化学测试(动电位极化)的结果表明, 原位自组装超疏水膜层极大地提高了铝合金的耐蚀性.     

丹皮酚的电化学氧化及其反应机理研究

研究了在碱性磷酸盐缓冲溶液体系中,丹皮酚在固体电极上的电化学吸附氧化行为。与苯酚的电化学性质比较表明,碱性溶液中丹皮酚在电极表面上发生类似的不可逆的氧化。氧化产物发生随后化学反应,在电极表面生成致密的不导电聚合物膜。利用超微电极技术研究了丹皮酚电化学氧化的动力学过程,并用时间分辨快速扫描现场红外光谱电化学证明了电极表面的聚合物膜是芳醚类聚合物。     

Study on microarc oxidation of AZ31B magnesium alloy in alkaline metal silicate solution

The effects of pulsating current and voltage sources with different magnitudes on an oxide film formed by microarc oxidation (MAO) of AZ31B magnesium alloy in alkaline metal silicate solution were investigated. The thickness of an oxide film increased with increasing current source but the uniformity of the surface of an oxide film became worse. The unstable oxidation process represented by fluctuating voltage established across an oxide film was discussed and related to the surface roughness and the melting down of magnesium alloy. By comparing the surface of an oxide film a pulsating current source produced more uniform oxide film on magnesium alloy than a pulsating voltage source.