Synthesis of micro- or nano-crystalline diamond films on WC-Co substrates with various pretreatments by hot filament chemical vapor deposition

Diamond films deposited on tungsten carbide can lead to major improvements in the life and performance of cutting tools. However, deposition of diamond onto cemented tungsten carbide (WC-Co) is problematic due to the cobalt binder in the WC. This binder provides additional toughness to the tool but results in poor adhesion and low nucleation density of any diamond film. A two-step chemical etching pretreatment (Murakami reagent and Caro acid, (MC)-pretreatment) and a boronization pretreatment have both been used extensively to improve adhesion of CVD diamond film on WC-Co substrates. Here we discuss the applicability of MC-pretreatment for a range of Co-containing WC-Co substrates, and demonstrate a controlled synthesis process based on liquid boronizing pretreatment for obtaining smooth and dense micro- or nano-crystalline diamond films on high Co-containing WC-Co substrates. Substrate treatments and deposition parameters were found to have major influences on the smoothness, structure and quality of the diamond films. The best quality diamond films were achieved under conditions of relatively high substrate temperature (T_s) and the best adhesion was achieved at T_s = 800 °C.     

Co元素对硬质合金基底金刚石涂层膜基界面结合强度的影响

采用基于密度泛函理论的第一性原理平面波赝势方法, 研究了硬质合金刀具基底黏结相Co元素对金刚石涂层膜基界面结合强度的影响机理. 借助Materials Studio软件建立了WC/Diamond膜基界面模型和WC-Co/Diamond膜基界面模型, 采用CASTEP仿真软件计算了WC/Diamond膜基界面模型和WC-Co/Diamond膜基界面模型的最优稳定结构. 通过仿真计算, 获得了WC/Diamond膜基界面模型和WC-Co/Diamond膜基界面模型的界面结合能、电荷密度图及Mulliken重叠布居数. 经对比分析后发现, 硬质合金基底中磁性元素Co的存在能转移金刚石涂层膜基界面处W元素及C元素的电荷, 从而使膜基界面处的原子因失电荷而相斥, 这直接导致了金刚石涂层膜基界面间距变大, 使得金刚石涂层膜基界面结合能降低.     

The effects of temperature on nanocrystalline diamond films deposited on WC-13 wt.% Co substrate with W-C gradient layer

A tungsten-carbide gradient coating (WCGC) was prepared by reactive sputtering as an intermediate layer on the cemented carbide, WC-13 wt.% Co, substrate to improve the nucleation, smoothness and adhesion of diamond film. The diamond film was deposited by hot filament chemical vapor deposition (HFCVD). The effects of the substrate temperature on the WCGC and the diamond film were investigated. The characterization of the WCGC and the diamond films was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), micro-Raman spectroscopy and Rockwell hardness indentation. It is found that the WCGC plays an important role in improving the nucleation, smoothness and adhesion of diamond film; and the diamond films exhibit better quality and adhesion as substrate temperature increases during the CVD processes.     

液相电化学法制备类金刚石薄膜及其摩擦性能研究

采用自行设计的液相法沉积装置,以甲醇有机溶剂作为碳源,利用液相电化学沉积技术在不锈钢及Si基底上制备了类金刚石薄膜;用扫描电镜、Raman光谱仪表征了沉积薄膜的表面形貌和结构;用UMT-2M摩擦磨损试验机对两种沉积薄膜进行了摩擦性能测试。结果表明:经电化学沉积的类金刚石薄膜均匀、致密,表面粗糙度小;Raman光谱在1 332cm-1处有强的谱峰,与金刚石的特征峰相吻合,其中不锈钢基底上薄膜的sp3含量更高;不锈钢基底沉积膜的摩擦系数为0.12,Si片基底沉积膜的摩擦系数为0.10;不锈钢基底沉积膜的耐磨性较Si片沉积膜高。     

脉冲偏压电弧离子镀C-N-V薄膜的成分、结构与性能

用脉冲偏压电弧离子镀方法在硬质合金基体上制备了一系列不同成分的C-N-V薄膜.用X射线光电子能谱、激光Raman光谱、 X射线衍射(XRD)、透射电子显微镜(TEM)和纳米压痕等方法分别研究了薄膜的成分、结构与性能.Raman光谱,XRD和TEM结果表明,所制备的薄膜为在类金刚石(DLC)非晶基体上匹配有VN晶体的碳基复合薄膜.随V和N含量的增加,薄膜硬度与弹性模量先增加后下降,在N含量为204%,V含量为218%时薄膜硬度与弹性模量具有最大值,分别为368和5697 GPa,高于相同条件下制备的 关键词： C-N-V薄膜 类金刚石薄膜 纳米复合薄膜 电弧离子镀     

The microstructure, mechanical and friction properties of protective diamond like carbon films on magnesium alloy

Protective hard coatings deposited on magnesium alloys are believed to be effective for overcoming their poor wear properties. In this work, diamond-like carbon (DLC) films as hard protective films were deposited on AZ91 magnesium alloy by arc ion plating under negative pulse bias voltages ranging from 0 to −200 V. The microstructure, composition and mechanical properties of the DLC films were analyzed by scanning electron microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy and nanoindentation. The tribological behavior of uncoated and coated AZ91 magnesium alloy was investigated using a ball-on-disk tribotester. The results show that the negative pulse bias voltage used for film deposition has a significant effect on the sp³ carbon content and mechanical properties of the deposited DLC films. A maximum sp³ content of 33.3% was obtained at −100 V, resulting in a high hardness of 28.6 GPa and elastic modulus of 300.0 GPa. The DLC films showed very good adhesion to the AZ91 magnesium alloy with no observable cracks and delamination even during friction testing. Compared with the uncoated AZ91 magnesium alloy, the magnesium alloy coated with DLC films exhibits a low friction coefficient and a narrow, shallow wear track. The wear resistance and surface hardness of AZ91 magnesium alloy can be significantly improved by coating a layer of DLC protective film due to its high hardness and low friction coefficient.     

Understanding the friction behavior of sulfur-terminated diamond-like carbon films under high vacuum by first-principles calculations

Generally, the repulsive force was a key factor account for superlow friction of H or F doped diamond-like carbon (DLC) films under high vacuum. As we known, H or F doped DLC usually exhibited superlow friction under high vacuum. However, the superlow friction of S doped DLC under high vacuum was not found so far. This phenomenon was desirable to be well investigated. In this work, S-terminated diamond interfaces also exhibited strong repulsive force, however, the estimated friction coefficient was variable for S-terminated diamond interfaces. The lowest and largest friction coefficient was about 0.003 and 0.4 respectively, which indicated that the superlow friction of S doped DLC could achieve in theory. In order to well probe the unusual friction behavior of S doped DLC under high vacuum, using first-principles method, the repulsive interaction between sliding surfaces was well investigated in order to understand the unusual friction behavior of S doped DLC films.     

脉冲激光沉积无氢钨掺杂类金刚石膜的摩擦与机械性能

采用脉冲激光沉积技术制备出无氢钨掺杂非晶态类金刚石膜.膜中的钨含量与靶材中的钨含量保持稳定的线性关系,显示了脉冲激光沉积在难熔金属掺杂技术方面的亮点.由于碳-钨结构的形成和表面粗糙度影响,膜层的干摩擦系数随着钨含量的增加显现出先减后增的趋势,钨含量为9.67 at.%时达到最低值0.091.钨含量的增大降低了类金刚石膜纳米硬度和杨氏模量,但最佳的膜层耐磨性参数并非表现在硬度最大(52.2 GPa)的纯类金刚石膜中,而是出现在低掺杂含量(6.28 at.%)的类金刚石膜中.研究为脉冲激光沉积技术制备低摩擦、高硬度无氢钨掺杂类金刚石膜的应用提供了技术实践.     

脉冲准分子激光淀积薄膜的实验研究

 利用两种脉宽(30ns，500fs)的KrF准分子激光展开了淀积类金刚石薄膜的实验研究，并且成功地制备了大面积不含氢成分的HF-DLC薄膜，运用时空分辨的等离子体发射光谱诊断系统和离子探针系统研究了等离子体特性对薄膜性能的影响。尝试了利用准分子激光制备非晶硅薄膜，研究了实验参数对非晶硅薄膜制备的影响，并分析了制备具有良好电学和光学性能的非晶硅薄膜的条件。     

脉冲准分子激光淀积薄膜的实验研究

利用两种脉宽 (30ns,5 0 0fs)的KrF准分子激光展开了淀积类金刚石薄膜的实验研究 ,并且成功地制备了大面积不含氢成分的HF DLC薄膜 ,运用时空分辨的等离子体发射光谱诊断系统和离子探针系统研究了等离子体特性对薄膜性能的影响。尝试了利用准分子激光制备非晶硅薄膜 ,研究了实验参数对非晶硅薄膜制备的影响 ,并分析了制备具有良好电学和光学性能的非晶硅薄膜的条件     

Influence of crystalline diamond nanoparticles on diamond-like carbon friction behavior

Crystalline diamond (CD) particles have been incorporated in diamond-like carbon (DLC) film structure in order to improve DLC electrochemical corrosion resistance. This paper shows the investigation of CD-DLC friction behavior according to the CD average sizes and concentration. The films were growth over 304 stainless steel using plasma enhanced chemical vapor deposition. The response surface methodology was used to develop a mathematical modeling of friction for these films, using the experimental results, in order to identify parameters that control friction and construct tribological maps according to the CD average sizes. The presence of bigger CD particles (250 and 500 nm) increased the film roughness. Films with CD particles of 4 nm presented the most homogeneous friction map, with minor variation in friction coefficient with the increase/decrease of load and sliding speed even when the CD concentration increase. This result suggests that in CD-DLC films containing CD particles of 4 nm average size, the nanoparticles are better incorporated in DLC structure due to its average size (4 nm) that is near than DLC grain size and could occupy the nanospaces between DLC grains.     

Influence of sulfidation treatment on the structure and tribological properties of nitrogen-doped diamond-like carbon films

The nitrogen-doped diamond-like carbon (DLC) films were deposited on high speed steel (HSS) substrates in the direct current unbalanced magnetron sputtering system. Sulphurized layer was formed on the surface of DLC films by means of liquid sulfidation in the intermixture of urea and thiourea solution in order to improve the tribological properties of DLC films. The influence of sulfidation treatment on the structure and tribological properties of DLC films was investigated in this work. The structure and wear surface morphology of DLC films were analyzed by Raman spectroscopy, XPS and SEM, respectively. It reveals that the treated films are smooth and uniform; and sulfur atoms are bonded chemically. The treated films have broader distribution of Raman spectra in the range of 1000-1800 cm⁻¹ and higher I_D/I_G ratio than the untreated films as a result of the appearance of the crystalline graphite structure after the sulfidation treatment. It is showed that the sp² relative content increase in the treated films from the XPS measurement. The Raman results are consistent with the XPS results. The tribological properties of DLC films were investigated using a ball-on-disk rotating friction and wear tester under dry friction conditions. It is found that the sulfidation concentration plays an important part in the tribological properties of the treated DLC films. The results showed the treated films with low sulfidation concentration have a lower friction coefficient (0.1) than the treated films with high sulfidation concentration (0.26) and the untreated films (0.27) under the same friction testing conditions, which can be attributed to both the presence of sulfur-containing materials and the forming of the mechanical alloyed layer on the wear surface. Adding the dry nitrogen to the sliding surface in the testing system helps the friction coefficient of the treated films with low sulfidation concentration to decrease to 0.04 further in this work. On the basis of the experimental results, it is indicated that the liquid sulfidation technique, which is low-cost, non-polluting and convenience, would be an appropriate method for the surface treatment of DLC films.     

Tribological effect of iron oxide residual on the DLC film surface under seawater and saline solutions

This paper discusses the seawater and saline solutions effects on the tribological behavior of diamond-like carbon (DLC) films. The adsorption of Fe on DLC surface is one of the mechanisms that is believed to be the cause of the decrease in dispersive component of the surface energy and increase of the I_D/I_G ratio leading to low friction coefficient and wear rate under corrosive environments. Tribological behaviors DLC films were experimentally evaluated under corrosive environments by using steel ball and DLC coated steel flat under rotational sliding conditions. The DLC films were prepared on 440 stainless steel disks by DC-pulsed PECVD using methane as a precursor gas. Two different set of tribological system was assembled, one when the liquids and the pairs were put inside of a stainless steel vessel and others inside of a PTFE. Every tribological test was performed under 10 N normal load120 mms^? 1 of sliding speed. The friction coefficients were evaluated during 1000 cycles.     

乙炔气体流量对纳米TiC类金刚石复合膜的化学结构及力学性能影响

采用离子注入与反应磁控溅射相结合的方法在钛合金及硅片基体表面上制备了纳米TiC类金刚石(DLC)复合膜.通过纳米压痕技术检测了薄膜的纳米硬度，显微划痕试验评估了薄膜的结合力.通过X射线光电子能谱及X射线衍射表征了薄膜的化学结构.结果表明，通过改变C₂H₂气体流量，可以达到控制薄膜中钛原子含量的目的，合适的C₂H₂气体流量可以在DLC膜中形成较多的纳米TiC晶粒，形成DLC包覆TiC晶粒的复合结构，使DLC膜力学性能得到明显提高.另外，划痕试验表明掺钛、先注入后沉积工艺都使薄膜的结合力得到了较大提高. 关键词： 纳米TiC类金刚石复合膜 类金刚石膜 力学性能     

Characterization of the bonding structure of nanocrystalline diamond and amorphous carbon films prepared by plasma assisted techniques

Thin nanocrystalline diamond/amorphous carbon (NCD/a-C) composite films and amorphous diamond-like carbon (DLC) films were prepared by three methods: microwave plasma chemical vapour deposition (MWCVD) from methane/nitrogen mixtures (NCD/a-C), RF magnetron sputtering of a pure graphite target in argon/methane ambients, and pulsed laser deposition (PLD) in vacuum or argon atmosphere (DLC). The films prepared by the three techniques were comprehensively characterized with respect to their bonding structure by Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS). PACS 81.05.Uw; 82.80.Pv     

Tribological behavior of diamond-like carbon film with different tribo-pairs: A size effect study

A friction force microscope (FFM) with different probes and a ball-on-disk (BOD) tribo-meter were used to investigate the tribological properties of diamond-like carbon (DLC) films. DLC films were prepared by chemical vapor deposition (CVD) method by altering the deposition parameters, and their morphologies and structural information were examined with an atomic force microscope (AFM) and the Raman spectrum. The wear traces of the DLC films after frictional tests were analyzed by an optical microscope. It is found that surface roughness and adhesion play important roles in characterizing the tribological properties of DLC films using FFM. Moreover, the debris accumulation is another significant factor affecting the frictional behavior of DLC films, especially for the sharp tip. The difference in coefficients of friction (COFs) obtained by the BOD method among different DLC films under water lubrication is much smaller than the case without water lubrication. The variation trends in COF for the flat tip and the BOD test are similar in comparison with the result obtained with the sharp tip. The wear traces after frictional tests suggest that DLC films under water lubrication are prone to be damaged more readily.     

Effects of hydrogen and oxygen on the electrochemical corrosion and wear-corrosion behavior of diamond films deposited by hot filament chemical vapor deposition

A diamond film was deposited on silicon substrate using hot filament chemical vapor deposition (HFCVD), and H₂ and O₂ gases were added to the deposition process for comparison. This work evaluates how adding H₂ and O₂ affects the corrosion and wear-corrosion resistance characteristics of diamond films deposited on silicon substrate. The type of atomic bonding, structure, and surface morphologies of various diamond films were analyzed by Raman spectrometry, X-ray diffraction (XRD) and atomic force microscopy (AFM). Additionally, the mechanical characteristics of diamond films were studied using a precision nano-indentation test instrument. The corrosion and wear-corrosion resistance of diamond films were studied in 1 M H₂SO₄ + 1 M NaCl solution by electrochemical polarization. The experimental results show that the diamond film with added H₂ had a denser surface and a more obvious diamond phase with sp³ bonding than the as-deposited HFCVD diamond film, effectively increasing the hardness, improving the surface structure and thereby improving corrosion and wear-corrosion resistance properties. However, the diamond film with added O₂ had more sp² and fewer sp³ bonds than the as-deposited HFCVD diamond film, corresponding to reduced corrosion and wear-corrosion resistance.     

Optical and Electrical Properties Evolution of Diamond-Like Carbon Thin Films with Deposition Temperature

Optical and electrical properties of diamond-like carbon （DLC） films deposited by pulsed laser ablation of graphite target at different substrate temperatures are reported. By varying the deposition temperature from 400 to 25℃, the film optical transparency and electrical resistivity increase severely. Most importantly, the transparency and resistivity properties of the DLC films can be tailored to approaching diamond by adjusting the deposition temperature, which is critical to many applications. DLC films deposited at low temperatures show excellent optical transmittance and high resistivity. Over the same temperature regime an increase of the spa bonded C content is observed using visible Raman spectroscopy, which is responsible for the enhanced transparency and resistivity properties.     

Fe纳米颗粒嵌埋对类金刚石薄膜结构及电学性能的影响

 采用脉冲激光气相沉积方法制备了不同Fe嵌埋浓度的Fe: DLC多层纳米复合薄膜。用X射线光电子能谱仪(XPS)对薄膜的组成成分进行分析。利用透射电子显微镜（TEM）、拉曼光谱、电流-电压曲线研究Fe纳米颗粒嵌埋对薄膜的微观结构及电学性能的影响。XPS和TEM表明,Fe纳米颗粒周期性地均匀地嵌埋在碳薄膜中。拉曼光谱表明薄膜中的C为典型的类金刚石结构,Fe纳米颗粒促进芳香环式结构的形成,薄膜结构的有序度提高。电流 电压曲线表明,Fe纳米颗粒的嵌埋导致薄膜的室温电导率增加。     

Improving the conductivity of diamond-like carbon films with zinc doping and its material properties

Zinc doped diamond-like carbon (DLC) nanocomposite thin films are fabricated by KrF pulsed laser deposition. Carbon targets containing 3.0, 5.0 and 10.0 atomic percentages of zinc are used as the source for the laser system. Investigation of electrical properties by the four-point probe shows that doping zinc into DLC can lower the electrical sheet resistivity. Microstructural analysis by Raman spectroscopy and XPS show a lower sp³ content but a higher SiC content with an increasing amount of zinc incorporation. The increase of SiC leads to an increase in adhesion strength. Surface roughness of the films also increases while the coefficients of friction for the films do not change.