Structural analysis of Si(1 1 1)-√21 × √21-(Ag, Au) surface by using reflection high-energy positron diffraction

The Au adsorption induced √21 × √21 super-lattice structure on the Si(1 1 1)-√3 × √3-Ag structure has been investigated using reflection high-energy positron diffraction. The height of the Au adatom was determined to be 0.59 Å from the underlying Ag layer from the rocking curve analysis with the dynamical diffraction theory. The adatoms were preferentially situated at the center of the large Ag triangle of the inequivalent triangle structure of the Si(1 1 1)-√3 × √3-Ag substrate. From the intensity distribution in the fractional-order Laue zone, the in-plane coordinate of the Au adatoms was obtained.     

Structural study of Si(1 1 1)-6 × 1-Ag surface using surface X-ray diffraction

The surface structure of Si(1 1 1)-6 × 1-Ag was investigated using surface X-ray diffraction techniques. By analyzing the CTR scattering intensities along 00 rod, the positions of the Ag and reconstructed Si atoms perpendicular to the surface were determined. The results agreed well with the HCC model proposed for a 3 × 1 structure induced by alkali-metals on a Si(1 1 1) substrate. The heights of the surface Ag and Si atoms did not move when the surface structure changed from Si(1 1 1)-√3 × √3-Ag to Si(1 1 1)-6 × 1-Ag by the desorption of the Ag atoms. From the GIXD measurement, the in-plane arrangement of the surface Ag atoms was determined. The results indicate that the Ag atoms move large distances at the phase transition between the 6 × 1 and 3 × 1 structures.     

Study of the surface structure of Si(1 1 1)-6 × 1(3 × 1)-Ag using X-ray crystal truncation rod scattering

The structure of the Si(1 1 1)-6 × 1-Ag surface is investigated using crystal truncation rod (CTR) scattering along 00 rod. For the measurement, we developed a manipulator suitable for observing CTR scattering at large momentum transfer perpendicular to the surface. The heights of the silver and reconstructed silicon atoms from the substrate were determined. We also compared the obtained positions with those of the Si(1 1 1)-√3 × √3-Ag surface and found that the heights of those reconstructed atoms are almost the same.     

Growth of (√3 × √3)-Ag and (1 1 1) oriented Ag islands on Ge/Si(1 1 1) surfaces

We have studied the growth of Ag on Ge/Si(1 1 1) substrates. The Ge/Si(1 1 1) substrates were prepared by depositing one monolayer (ML) of Ge on Si(1 1 1)-(7 × 7) surfaces. Following Ge deposition the reflection high energy electron diffraction (RHEED) pattern changed to a (1 × 1) pattern. Ge as well as Ag deposition was carried out at 550 °C. Ag deposition on Ge/Si(1 1 1) substrates up to 10 ML has shown a prominent (√3 × √3)-R30° RHEED pattern along with a streak structure from Ag(1 1 1) surface. Scanning electron microscopy (SEM) shows the formation of Ag islands along with a large fraction of open area, which presumably has the Ag-induced (√3 × √3)-R30° structure on the Ge/Si(1 1 1) surface. X-ray diffraction (XRD) experiments show the presence of only (1 1 1) peak of Ag indicating epitaxial growth of Ag on Ge/Si(1 1 1) surfaces. The possibility of growing a strain-tuned (tensile to compressive) Ag(1 1 1) layer on Ge/Si(1 1 1) substrates is discussed.     

Electron and lattice structure of ultra thin Ag films on Si(1 1 1) and Si(0 0 1)

We studied the low temperature (T ? 130 K) growth of Ag on Si(0 0 1) and Si(1 1 1) flat surfaces prepared by Si homo epitaxy with the aim to achieve thin metallic films. The band structure and morphology of the Ag overlayers have been investigated by means of XPS, UPS, LEED, STM and STS. Surprisingly a (√3 × √3)R30° LEED structure for Ag films has been observed after deposition of 2-6 ML Ag onto a Si(1 1 1)(√3 × √3)R30°Ag surface at low temperatures. XPS investigations showed that these films are solid, and UPS measurements indicate that they are metallic. However, after closer STM studies we found that these films consists of sharp Ag islands and (√3 × √3)R30°Ag flat terraces in between. On Si(0 0 1) the low-temperature deposition yields an epitaxial growth of Ag on clean Si(0 0 1)-2 × 1 with a twinned Ag(1 1 1) structure at coverage’s as low as 10 ML. Furthermore the conductivity of few monolayer Ag films on Si(1 0 0) surfaces has been studied as a function of temperature (40-300 K).     

Surface structure and phase transition of Ge(1 1 1)-3 × 3-Pb studied by reflection high-energy positron diffraction

We studied the structures and the phase transition of Pb/Ge(1 1 1) surface by using the reflection high-energy positron diffraction. The surface structures at 60 K and 293 K have the 3 × 3 and √3 × √3 periodicities, respectively. The rocking curves measured at both temperatures are nearly the same. This indicates that the equilibrium positions of the surface atoms do not change according to the phase transition. From the analysis of the rocking curve based on the dynamical diffraction theory, we found that at both temperatures the surface structures are composed of the so-called one-up and two-down model. The 3 × 3-√3 × √3 phase transition for the Pb/Ge(1 1 1) surface is interpreted in terms of order-disorder transition.     

Unoccupied band dispersion of Si(1 1 1):√3 × √3-Ag surface studied by time- and angle-resolved two-photon photoemission spectroscopy

Band dispersion and transient population of unoccupied electronic states on Si(1 1 1):√3 × √3-Ag surface have been studied by time-resolved (TR) and angle-resolved (AR) two-photon photoemission (2PPE) spectroscopy. The band dispersions originating from unoccupied electronic states have been identified from the comparison between AR-2PPE spectra and angle-resolved one-photon photoemission spectra with synchrotron radiation. A lifetime of unoccupied surface state has been determined from the TR-2PPE spectra.     

An STM investigation of the interaction and ordering of pentacene molecules on the Ag/Si(1 1 1)-(√3×√3)R30° surface

Scanning tunneling microscopy has been used to study the ordering of pentacene (C₂₂H₁₄) molecules on the Ag/Si(1 1 1)-(√3×√3)R30° surface at room temperature. Two solid phases, S1 and S2, are observed at coverages of ∼0.35 monolayer (ML) and ∼1.0 ML respectively. It is shown that the solid phase S1 has a high-order commensurate lattice, Ag/Si(1 1 1)-(25 × 25)-pentacene, containing 75 molecules. The structure of this phase is determined from STM measurements at very low coverages where it is possible to image both the pentacene molecules and the structure of the Ag/Si(1 1 1) substrate. Two adsorption sites are identified, a three-fold hollow site at the centre of a Ag-trimer (CA-site) and a six-fold hollow site at the centre of the hexagonal arrangement of silver atoms (CB-site). A higher pentacene coverage of ∼1 ML lead to a molecular reorganization and forms a new commensurate structure Ag/Si(1 1 1)-(2 × 3)-pentacene, containing two molecules per unit cell. Because low energy electron diffraction patterns were not obtainable for this system, the structure of this second phase is determined by using the bias voltage as a tunable parameter to “focus” on either the molecular film or on the substrate. In this phase adsorption takes place exclusively on the Ag-trimer (CA) site and the CB-site is lost because of strong lateral molecule-molecule interactions. The role of competition between intermolecular and molecule-substrate interactions and the nature of the adsorption sites in determining the structure of the pentacene layers is discussed.     

Fabrication and scanning tunneling microscopy studies of the Si(1 1 1)-(√31 × √31)-In surface

We report on the fabrication of single phase of the Si(1 1 1)-(√31 × √31)-In reconstruction surface, observed by scanning tunneling microscopy (STM) at room temperature. By depositing specific amounts of indium atoms while heating the Si(1 1 1)-(7 × 7) substrate at a critical temperature, the single phase of Si(1 1 1)-(√31 × √31)-In surfaces could be routinely obtained over the whole surface with large domains. This procedure is certified by our high-resolution STM images in the range of 5-700 nm. Besides, the high resolution STM images of the Si(1 1 1)-(√31 × √31)-In surface were also presented.     

Fabrication of nanostructures by selective growth of C60 and Si on Si(1 1 1) substrate

Using two types of selective growth, selective C₆₀ growth and selective Si growth, on a common Si(1 1 1) substrate, an array of C₆₀ nanoribbons with controlled values of width and thickness is fabricated. On a surface that has Si(1 1 1)√3 × √3R30°-Ag (referred to as Si(1 1 1)√3-Ag hereafter) and bare Si(1 1 1) regions at the same time, the preferential growth of C₆₀ multilayered film is recognized on the Si(1 1 1)√3-Ag region. The growth of Si selectively occurs on a bare Si(1 1 1) region if the substrate surface has C₆₀-adsorbed and bare Si(1 1 1) regions at the same time. As a demonstration of the use of these selective growths, we fabricate an array of well-isolated C₆₀ nanoribbons, which show a well-ordered molecular arrangement and have sizes of about 40 nm in widths and 3-4 nm in thicknesses.     

Reconstructions 3 × 3 and √3 × √3 on SiC(0 0 0 1) studied using RHEED

The 3 × 3 and √3 × √3 reconstructions on 6H-SiC(0 0 0 1) surface were obtained via depositing thin silicon layer and annealing it in ultrahigh vacuum (without Si flux). Rocking curves of reflection high energy electron diffraction (RHEED) were measured for integer and fractional order beams. They were fitted with results of many-beam calculation on the basis of dynamical theory of RHEED to determine structural parameters. For √3 × √3 superstructure, it was found that the occupancy of adatom states is 0.45 (incomplete coverage). In the sequence of Si-C double layers ABCACB, the lattice is terminated with the layer A. For 3 × 3 superstructure, the rocking curves support the model with twisted tetra-cluster. The best-fit twist is as half of that predicted in ab initio calculations; it is due to limited source of Si atoms to build up the superstructure. Larger twist correlates with higher occupancy of corner sites and with slower cooling rate of the sample after annealing.     

Fabrication of uniform Au silicide islands on the Si(1 1 1)-(7 × 7) substrate

The Au silicide islands have been fabricated by additional deposition of Au on the prepared surface at 270 °C where the Si islands of magic sizes were formed on the Si(1 1 1)-(7 × 7) dimer-adatom-stacking fault substrate. The surface structure on the Au silicide islands shows the Au/Si(1 1 1)-√3 × √3 reconstructed structure although the substrate remains 7 × 7 DAS structure. The size of the Au silicide islands depends on the size distribution of the preformed Si islands, because the initial size and shape of the Si islands play important roles in the formation of the Au silicide island. We have achieved the fabrication of the Au silicide islands of about the same size (∼5 nm) and the same shape by controlling the initial Si growth and the additional Au growth conditions.     

A structural parallel between Ge- and Si-induced 4 × 4 and 3 × 3 reconstructions on SiC(0 0 0 1) drawn from comparative RHEED oscillations

The initial Ge growth stages on a (√3 × √3)R30°-reconstructed SiC(0 0 0 1) surface (√3) have been studied using a complete set of surface techniques such as reflection high energy electron diffraction (RHEED), low energy electron diffraction (LEED), atomic force microscopy (AFM) and photoemission and compared with similar Si surface enrichments in place of Ge. The investigations essentially focus on the wetting growth-regimes that are favoured by the use of the √3 surface as a starting substrate, this surface being the closest to a smooth and ideally truncated Si-terminated face of hexagonal SiC(0 0 0 1). Depending on temperature and Ge or Si coverages, varying surface organizations are obtained. They range from unorganized layer by layer growths to relaxed Ge(1 1 1) or Si(1 1 1) island growths, through intermediate attempts of coherent and strained Ge or Si surface layers, characterized by 4 × 4 and 3 × 3 surface reconstructions, respectively. RHEED intensity oscillation recordings, as a function of Ge or Si deposited amounts, have been particularly helpful to pinpoint the limited (by the high lattice mismatch) existence domains of these interesting coherent phases, either in terms of formation temperature or surface coverages. Prominently comparable data for these two Ge- and Si-related reconstructions allow us to propose an atomic model for the still unexplained Ge-4 × 4 one. It is based on a same local organization in trimer and ad-atom units for the Ge excess as admitted for the Si-excess of the 3 × 3 surface, the higher strain nevertheless favouring arrangements, for the Ge-units, in 4 × 4 arrays instead of 3 × 3 Si ones. Admitting such models, 1.25 and 1.44 monolayers of Ge and Si, should, respectively, be able to lie coherently on SiC, with respective lattice mismatches near 30% and 25%. The experimental RHEED-oscillations values are compatible with such theoretical ones. Moreover, these RHEED coverage determinations (for layer completion, for instance) inform us in turn about the initial Si richness of the starting √3 reconstruction and help us to discriminate between earlier contradictory atomic models proposed in the literature.     

Structure and electronic properties of gold adsorbed on Ti(0 0 0 1)

The Au/Ti(0 0 0 1) adsorption system was studied by low energy electron diffraction (LEED) and photoemission spectroscopy with synchrotron radiation after step-wise Au evaporation onto the Ti(0 0 0 1) surface. For adsorption of Au at 300 K, no additional superstructures were observed and the (1 × 1) pattern of the clean surface simply became diffuse. Annealing of gold layers more than 1 ML thick resulted in the formation of an ordered Au-Ti surface alloy. Depending on the temperature and annealing time, three surface reconstructions were observed by LEED: (√3 × √3) R30°, (2 × 2) and a one-dimensional incommensurate (√3 × √3) rectangular pattern. The Au 4f core level and valence band photoemission spectra provided evidence of a strong chemical interaction between gold and titanium. The data indicated formation of an intermetallic interface and associated valence orbital hybridization, together with diffusion of gold into the bulk. Au core-level shifts were found to be dependent on the surface alloy stoichiometry.     

Observation of a (√3 × √3)-R30° reconstruction on GaN(0 0 0 1) by RHEED and LEED

A new reconstruction of √3 × √3-R30° has been observed on a GaN film grown on a 6H-SiC (0 0 0 1)-√3 × √3 surface using RHEED and LEED experimental techniques. The experimental LEED PF shows that the GaN film is Ga-terminated hexagonal. The surface is a mixture of two structures with a single bilayer height difference between them. One is a √3 × √3-R30° reconstruction with Ga-adatoms occupying the T4 sites. Another is a Ga-terminated 1 × 1 with no extra Ga on top. The area ratio of the √3 × √3 part to the 1 × 1 part is slightly larger than 1. The first principle total energy calculations and Tensor-LEED I-V curves simulations further confirm this structure model.     

Self-assembled germanium nano-clusters on silver(1 1 0)

The adsorption of germanium on Ag(1 1 0) has been investigated by scanning tunnelling microscopy (STM), as well as surface X-ray diffraction (SXRD). At 0.5 germanium monolayer (ML) coverage, Low Energy Electron Diffraction (LEED) patterns reveals a sharp c(4 × 2) superstructure. Based on STM images and SXRD measurements, we present an atomic model of the surface structure with Ge atoms forming tetramer nano-clusters perfectly assembled in a two-dimensional array over the silver top layer. The adsorption of the germanium atoms induces a weak perturbation of the Ag surface. Upon comparison with results obtained on the (1 1 1) and (1 0 0) faces, we stress the role played by the relative interactions between silver and germanium on the observed surface structures.     

Substitutional adsorption geometry for Pb(1 1 1)-(√3 × √3)R30°-K

Intermixed structures for alkalis (larger than Li) on close-packed substrates have previously been observed only on Al(1 1 1). This study shows that K forms an ordered intermixed structure on Pb(1 1 1). The structures of clean Pb(1 1 1) and Pb(1 1 1)-(√3 × √3)R30°-K were studied using dynamical low-energy electron diffraction (LEED). The clean Pb(1 1 1) surface at 47 K was found to be a relaxed version of the bulk structure, in agreement with an earlier study of the same surface [Y.S. Li, F. Jona, P.M. Marcus, Phys. Rev. B 43 (1991) 6337]. At room temperature, adsorption of K on this surface results in a (√3 × √3)R30° structure, which was shown using dynamical LEED to consist of K atoms substituted in surface vacancies. The K-Pb bond length was found to be 3.62 ± 0.3 Å, with no significant change to the Pb interlayer spacings.     

Spectroscopic interpretation for Na-induced phase transitions on Na/Si(1 1 1)3 × 1

Na adsorption at room temperature causes the Na/Si(1 1 1)3 × 1 surface with Na coverage of 1/3 monolayer (ML) to transit into the Na/Si(1 1 1)6 × 1 surface at 1/2 ML and sequentially into the Na/Si(1 1 1)3 × 1 surface at 2/3 ML. The phase transition was studied by Si 2p core-level photoemission spectroscopy. The detailed line shape analysis of the Si 2p core-level spectrum of the Na/Si(1 1 1)3 × 1 surface (2/3 ML) is presented and compared to the Na/Si(1 1 1)3 × 1 surface (1/3 ML) which is composed of Si honeycomb chain-channel structures. This suggests that as additional Na atoms form atomic chains resulting in the Na/Si(1 1 1)3 × 1 surface (2/3 ML), the inner atoms of the Si honeycomb chain-channel structure is buckled due to the additional Na atoms.     

Structural evolution of sulfur overlayers on Pd(1 1 1)

Low energy ion scattering spectroscopy (LEISS) has been used to characterize the evolution of ordered structures of S on the Pd(1 1 1) surface during annealing. During exposure of the Pd(1 1 1) surface to 0.7 L H₂S at 300 K—conditions that produce the S(√3 × √3)R30 overlayer—the intensity of the Pd LEIS signal decreases and a feature assigned to adsorbed S appears as the adsorbed layer forms. When the surface is held at 300 K after exposure to H₂S is stopped, the LEIS Pd intensity partially recovers and the S signal weakens, presumably as surface S atoms assume their equilibrium positions in the S(√3 × √3)R30 overlayer. Subsequent annealing of the S(√3 × √3)R30 structure at 700 K causes it to convert into a S(√7 × √7)R19 overlayer, whose LEIS spectrum is identical to that of clean Pd(1 1 1). The absence of LEIS evidence for S atoms at the exposed surface of the S(√7 × √7)R19 overlayer is at odds with published models of a mixed Pd-S top layer. Despite the similarity of the LEIS spectra of Pd(1 1 1) and Pd(1 1 1)-S(√7 × √7)R19, their activities for dissociative hydrogen adsorption are very different—the former readily adsorbs hydrogen at 100 K, while the latter does not—suggesting that S exerts its influence on surface chemistry from subsurface locations.     

Bi induced step-flow growth in the homoepitaxial growth of Au(1 1 1)

Homoepitaxial growth of Au on Bi-covered Au(1 1 1) was studied at room temperature using reflection high-energy electron diffraction (RHEED) and Auger electron spectroscopy (AES). From observations of RHEED it is found that the Au(1 1 1) (23 × 1) reconstruction structure changes to a (1 × 1) by about 0.16-0.5 ML deposition of Bi and to a (2√3 × 2√3)R30° by about 1.0 ML deposition of Bi, respectively. The surface morphology evolution by Bi deposition leads to a change of Au homoepitaxial growth behavior from layer-by-layer to step flow. This indicates that the surface diffusion distance of Au atoms on the Bi-precovered (1 × 1) and (2√3 × 2√3)R30° surfaces is longer than that on the Au(1 1 1) (23 × 1) clean surfaces. A strong surface segregation of Bi was found at top of surface. It is concluded that Bi atoms acted as an effective surfactant in the Au homoepitaxial growth by promoting Au intralayer mass transport.