Surfactant-free nanofluids containing double- and single-walled carbon nanotubes functionalized by a wet-mechanochemical reaction

Single-walled carbon nanotubes (SWNTs) and double-walled carbon nanotubes (DWNTs) have been functionalized through the wet-mechanochemical reaction method. Results from the infrared spectrum and zeta potential measurements show that the hydroxyl groups have been introduced onto the treated SWNT and DWNT surfaces. Transmission electron microscope observations revealed that the SWNTs and DWNTs were cut short after being milled. SWNTs and DWNTs with optimized aspect ratio can be obtained by adjusting the ball milling parameters. Thermal conductivity enhancement of water-based nanofluids containing treated carbon nanotubes (CNTs) shows augmentation with the increase of temperature mainly due to the effects of an ordering liquid layer forming around the chemical surfaces of CNTs. Moreover, the thicker interfacial layer of water molecules on the surfaces of CNTs with smaller diameter, such as SWNTs, is in favor of greater thermal conductivity enhancement compared with the thinner one on the surfaces of DWNTs or MWNTs with larger diameter.     

Aligned double-walled carbon nanotube long ropes with a narrow diameter distribution

Aligned double-walled carbon nanotube (DWNT) long ropes with a narrow diameter distribution were directly synthesized by sulfur-assisted floating catalytic decomposition of methane. The DWNT ropes are typically up to several centimeters in length and possess good alignment and high purity. High-resolution transmission electron microscopy (HRTEM) images and resonant Raman spectra revealed that the outer and inner tube diameters of the DWNTs are narrowly distributed in the range of 1.7-2.0 and 1.0-1.3 nm, respectively. Moreover, based on the resonant Raman measurements, the electronic properties of the two constituent tubes of the DWNTs were identified. The successful synthesis of such DWNTs opens the possibility for their fundamental studies and further applications as nanomechanical, nanooptical, and nanoelectronic devices.     

A catalytic chemical vapor deposition synthesis of double-walled carbon nanotubes over metal catalysts supported on a mesoporous material

Double-walled carbon nanotubes (DWNTs) have been synthesized by catalytic chemical vapor deposition (CCVD) over supported metal catalysts decomposed from Fe(CH₃COO)₂ and Co(CH₃COO)₂ on mesoporous silica. Bundles of tubes with relatively high percentage of DWNTs, in areas where tubular layered structures could be clearly resolved, have been observed by transmission electron microscopy (TEM). In other areas, crystal-like alignment of very uniform DWNTs was observed for the first time, suggesting that mesoporous silica might play a templating role in guiding the initial nanotube growth. In addition, compatible with nano-electronics research, bridging of catalytic islands by DWNTs has also been demonstrated.     

Enhanced photoluminescence from very thin double-wall carbon nanotubes synthesized by the zeolite-CCVD method

Photoluminescence (PL) from purified (>90%) double-wall carbon nanotubes (DWNTs), which have been synthesized by zeolite catalyst-supported chemical vapor deposition (zeolite-CCVD), of very small diameters (0.8-nm average inner tube) is reported. The PL contour mappings for various ratios (1-90%) of double- versus single-wall carbon nanotubes by thermal oxidation have enabled us to unambiguously identify the chirality of inner tubes for the DWNTs synthesized. After the extensive high-temperature oxidation at 700 degrees C, high-purity (>90%) DWNTs of approximately 0.8 nm inner diameter are obtained, and most of these correspond to the DWNTs having inner tubes with chiralities of (7,5), (7,6), and (9,4).     

Synthesis and characterization of high-quality double-walled carbon nanotubes by catalytic decomposition of alcohol

We report the synthesis of high-quality double-walled carbon nanotubes without defects by catalytic decomposition of alcohol over an Fe-Mo/Al2O3 catalyst; the synthesized DWNTs have outer diameters in the range of 1.52-3.54 nm and an average interlayer distance of 0.38 nm between graphene layers.     

Synthesis of single- and double-walled carbon nanotube forests on conducting metal foils

Here, we report a highly efficient growth of single-walled carbon nanotubes (SWNTs) and double-walled carbon nanotubes (DWNTs) on conducting metal foils. We found that foils made of Ni-based alloys with Cr or Fe serve as excellent substrates for SWNT (DWNT) synthesis. In significant contrast, a CNT grown on Ni, Fe foils contains a significant ratio of MWNTs. This result opens up an economical route for the mass production of SWNT (DWNT) forests and also enables the straightforward integration of CNTs into nanoelectronic devices, such as field emission displays.     

Fabrication of uniform magnetic nanocomposite spheres with a magnetic core/mesoporous silica shell structure

A novel kind of magnetic core/mesoporous silica shell nanospheres with a uniform particle diameter of ca. 270 nm was synthesized. The inner magnetic core endues the whole nanoparticle with magnetic properties, while the outer mesoporous silica shell shows high enough surface area and pore volume. The synthesized material is expected to be applied to targeted drug delivery and multiphase separation. The storage and release of ibuprofen into and from the pore channels of the mesoporous silica shell, as a typical example, are demonstrated.     

Triconstituent co-assembly to ordered mesostructured polymer-silica and carbon-silica nanocomposites and large-pore mesoporous carbons with high surface areas

Highly ordered mesoporous polymer-silica and carbon-silica nanocomposites with interpenetrating networks have been successfully synthesized by the evaporation-induced triconstituent co-assembly method, wherein soluble resol polymer is used as an organic precursor, prehydrolyzed TEOS is used as an inorganic precursor, and triblock copolymer F127 is used as a template. It is proposed for the first time that ordered mesoporous nanocomposites have "reinforced concrete"-structured frameworks. By adjusting the initial mass ratios of TEOS to resol, we determined the obtained nanocomposites possess continuous composition with the ratios ranging from zero to infinity for the two constituents that are "homogeneously" dispersed inside the pore walls. The presence of silicates in nanocomposites dramatically inhibits framework shrinkage during the calcination, resulting in highly ordered large-pore mesoporous carbon-silica nanocomposites. Combustion in air or etching in HF solution can remove carbon or silica from the carbon-silica nanocomposites and yield ordered mesoporous pure silica or carbon frameworks. The process generates plenty of small pores in carbon or/and silica pore walls. Ordered mesoporous carbons can then be obtained with large pore sizes of approximately 6.7 nm, pore volumes of approximately 2.0 cm(3)/g, and high surface areas of approximately 2470 m(2)/g. The pore structures and textures can be controlled by varying the sizes and polymerization degrees of two constituent precursors. Accordingly, by simply tuning the aging time of TEOS, ordered mesoporous carbons with evident bimodal pores at 2.6 and 5.8 nm can be synthesized.     

Synthesis and characterization of monolithic carbon aerogel nanocomposites containing double-walled carbon nanotubes

We report the synthesis and characterization for the first examples of monolithic low-density carbon aerogel (CA) nanocomposites containing double-walled carbon nanotubes. The CA nancomposites were prepared by the sol-gel polymerization of resorcinol and formaldehyde in an aqueous surfactant-stabilized suspension of double-walled carbon nanotubes (DWNTs). The composite hydrogels were then dried with supercritical CO 2 and subsequently carbonized under an inert atmosphere to yield monolithic CA structures containing uniform dispersions of DWNTs. The microstructures and electrical conductivities of these CA nanocomposites were evaluated for different DWNT loadings. These materials exhibited high BET surface areas (>500 m (2)/g) and enhanced electrical conductivities relative to pristine CAs. The details of these results are discussed in comparison with theory and literature.     

炭化温度对模板法合成介孔炭性能的影响

以蔗糖为炭源和硅酸钠为硅源,采用原位共聚法制备了炭/氧化硅复合体,除去氧化硅得到介孔炭材料.采用N2吸附-脱附、透射电子显微镜和红外光谱对不同炭化温度获得的样品进行表征.结果表明,随着炭化温度升高,所得的介孔炭比表面积和孔容均下降,650℃ ～ 950℃的炭化温度下获得的样品BET比表面积在586m2/g ～728 m2/g之间,孔容在0.549cm3/g～0.696cm3/g之间,孔径分布5-15nm之间.经红外光谱检测所得的介孔炭样品均含有氢和氧的功能团.     

Supercritical carbon dioxide processing of fluorinated surfactant templated mesoporous silica thin films

The effect of processing mesoporous silica thin films with supercritical CO2 immediately after casting is investigated, with a goal of using the penetration of CO2 molecules in the tails of fluorinated surfactant templates to tailor the final pore size. Well-ordered films with two-dimensional hexagonal close-packed pore structure are synthesized using a cationic fluorinated surfactant, 1-(3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluorodecyl)pyridinium chloride, as a templating agent. Hexagonal mesopore structures are obtained for both unprocessed films and after processing the cast films in CO2 at constant pressure (69-172 bar) and temperature (25-45 degrees C) for 72 h, followed by traditional heat treatment steps. X-ray diffraction and transmission electron microscopy analysis reveal significant increases in pore size for all CO2-treated thin films (final pore diameter up to 4.22 +/- 0.14 nm) relative to the unprocessed sample (final pore diameter of 2.21 +/- 0.20 nm) before surfactant extraction. Similar pore sizes are obtained with liquid and supercritical fluid treatments over the range of conditions tested. These results demonstrate that combining the tunable solvent strength of compressed and supercritical CO2 with the "CO2-philic" nature of fluorinated tails allows one to use CO2 processing to control the pore size in ordered mesoporous silica films.     

Novel ice structures in carbon nanopores: pressure enhancement effect of confinement

We report experimental results on the structure and melting behavior of ice confined in multi-walled carbon nanotubes and ordered mesoporous carbon CMK-3, which is the carbon replica of a SBA-15 silica template. The silica template has cylindrical mesopores with micropores connecting the walls of neighboring mesopores. The structure of the carbon replica material CMK-3 consists of carbon rods connected by smaller side-branches, with quasi-cylindrical mesopores of average pore size 4.9 nm and micropores of 0.6 nm. Neutron diffraction and differential scanning calorimetry have been used to determine the structure of the confined ice and the solid-liquid transition temperature. The results are compared with the behavior of water in multi-walled carbon nanotubes of inner diameters of 2.4 nm and 4 nm studied by the same methods. For D(2)O in CMK-3 we find evidence of the existence of nanocrystals of cubic ice and ice IX; the diffraction results also suggest the presence of ice VIII, although this is less conclusive. We find evidence of cubic ice in the case of the carbon nanotubes. For bulk water these crystal forms only occur at temperatures below 170 K in the case of cubic ice, and at pressures of hundreds or thousands of MPa in the case of ice VIII and IX. These phases appear to be stabilized by the confinement.     

以手性两亲小分子为模板剂制备介孔二氧化硅纳米空心球

以L-亮氨酸为手性源合成了手性阳离子两亲性小分子化合物L-18Leu6NEtBr,用其自组装体作为模板,氢氧化钠为催化剂,经溶胶-凝胶过程制备出介孔二氧化硅纳米空心球;分析了介孔二氧化硅纳米空心球的尺寸和孔径.结果表明,所制备的二氧化硅空心球直径约100nm;其介孔孔道平行于壳表面,孔径为3.1nm.     

Pt-Ru supported on double-walled carbon nanotubes as high-performance anode catalysts for direct methanol fuel cells

Pt-Ru supported on carbon nanotubes (CNTs) (single-walled nanotubes, double-walled nanotubes (DWNTs), and multi-walled nanotubes) catalysts are prepared by an ethylene glycol reduction method. Pt-Ru nanoparticles with a diameter of 2-3 nm and narrow particle size distributions are uniformly deposited onto the CNTs. A simple and fast filtration method followed by a hot-press film transfer is employed to prepare the anode catalyst layer on a Nafion membrane. The Pt-Ru/DWNTs catalyst shows the highest specific activity for methanol oxidation reaction in rotating disk electrode experiments and the highest performance as an anode catalyst in direct methanol fuel cell (DMFC) single cell tests. The DMFC single cell with Pt-Ru/DWNTs (50 wt %, 0.34 mg Pt-Ru/cm(2)) produces a 68% enhancement of power density, and at the same time, an 83% reduction of Pt-Ru electrode loading when compared to Pt-Ru/C (40 wt %, 2.0 mg Pt-Ru/cm(2)).     

Effect of Structure and Pore Size of Mesoporous Molecular Sieve Materials on the Growth of Carbon Nanotubes

Microporous and mesoporous molecular sieve materials with different channel structures and pore sizes were applied as supports for Fe-loaded catalysts to catalytically synthesize carbon nanotubes. The deposited carbon materials were characterized by the TEM technique. It was shown that the structures and pore sizes of supports greatly influence the forms and quality of the deposited carbon materials. The larger the pore size of the support used, the larger the diameter and pore size of the carbon nanotubes formed. It seems that the growth of carbon nanotubes can be orientated by the one-dimensional mesoporous structure of hexagonal mesoporous molecular sieve materials.     

以手性两亲小分子自组装体为模板制备介孔二氧化硅空心球

合成了手性阳离子型两亲性小分子化合物,利用圆二色谱分析了其在水中形成的自组装体的结构;以该化合物的自组装体为模板,在正丙醇和氨水的混合溶剂中制备得到了介孔二氧化硅空心球;利用扫描电镜、透射电镜、X射线衍射仪以及氮气吸附-脱附试验装置分析了二氧化硅空心球的形貌及孔结构.结果表明,两亲性小分子在水中形成的自组装体呈现手性堆积;合成的介孔二氧化硅空心球的直径约为600~800nm,壁厚约为100~150nm,其孔道垂直于球的表面,孔径约为3.0nm,比表面积约为306m2·g-1.正丙醇作为模板控制二氧化硅空心球的空腔尺寸和形貌,而两亲性小分子的自组装体作为模板控制放射状孔道的形貌和尺寸.     

Catalytic functions of Mo/Ni/MgO in the synthesis of thin carbon nanotubes

The functions and structures of Mo/Ni/MgO catalysts in the synthesis of carbon nanotubes (CNTs) have been investigated by transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy. Thin 2-5-walled CNTs with high purities (over 90%) have been successfully synthesized by catalytic decomposition of CH(4) over Mo/Ni/MgO catalysts at 1073 K. It has been found that the yield of CNTs as well as the outer diameter or thickness correlates well with the contents of these three elements. The three components Mo, Ni, and MgO are all necessary to synthesize the thin CNTs at high yields since no catalytic activity was observed for CNT synthesis when one of these components was not present. The outer diameter of the CNTs increases from 4 to 13 nm and the thickness of graphene layers also increases with increasing Mo content at a fixed Ni content, while the inner diameter stays at 2-3 nm regardless of their contents. Furthermore, the average outer diameter is in good agreement with the average particle size of metal catalyst. That is, the thickness or the outer diameter can be controlled by selecting the composition of the Mo/Ni/MgO catalysts. XRD analyses have shown that Mo and Ni form a Mo-Ni alloy before CNT synthesis, while the Mo-Ni alloy phase is separated into Mo carbide and Ni. These alloy particles are supported on MgO cubic particles 15-20 nm in width. It has been found that only small Mo-Ni alloy particles 2-16 nm in size catalyze CNT synthesis, with larger particles over 15 nm exhibiting no activity. Mo carbide and Ni should play different roles in the synthesis of the thin CNTs, in which Ni is responsible for the dissociation of CH(4) into carbon and Mo(2)C works as a carbon reservoir.     

Highly transparent and conductive thin films fabricated with nano-silver/double-walled carbon nanotube composites

This study develops a technique for enhancing the electrical conductivity and optical transmittance of transparent double-walled carbon nanotube (DWNT) film. Silver nanoparticles were modified with a NH(2)(CH(2))(2)SH self-assembled monolayer terminated by amino groups and subsequent surface condensation that reacted with functionalized DWNTs. Ag nanoparticles were grafted on the surface of the DWNTs. The low sheet resistance of the resulting thin conductive film on a polyethylene terephthalate (PET) substrate was due to the increased contact areas between DWNTs and work function by grafting Ag nanoparticles on the DWNT surfaces. Increasing the contact area between DWNTs and work function improved the conductivity of the DWNT-Ag thin films. The prepared DWNT-Ag thin films had a sheet resistance of 53.4 Ω/sq with 90.5% optical transmittance at a 550 nm wavelength. After treatment with HNO(3) and annealing at 150 °C for 30 min, a lower sheet resistance of 45.8 Ω/sq and a higher transmittance of 90.4% could be attained. The value of the DC conductivity to optical conductivity (σ(DC)/σ(OP)) ratio is 121.3.     

CVD growth of single-walled carbon nanotubes with narrow diameter distribution over Fe/MgO catalyst and their fluorescence spectroscopy

Single-walled carbon nanotubes (SWNTs) with a narrow diameter distribution are synthesized by thermal chemical vapor deposition (CVD) of methane over Fe/MgO catalyst on the basis of parametric study considering Fe loading, reaction temperature and time, methane concentration, and structure of a support material. We found that the porous MgO support gives the SWNTs with a narrow diameter distribution with the mean diameter and standard deviation of 0.93 and 0.06 nm, respectively, only when the Fe loading and reaction temperature are relatively low. The higher Fe loading and/or the higher reaction temperature enlarged the nanotube diameter, forming double-walled carbon nanotubes (DWNTs) in addition to SWNTs. This result indicates that only the diameter of Fe nanoparticles determines the growth of either SWNTs or DWNTs on the MgO support. The fluorescence and absorption spectra of the nanotube dispersion in D(2)O solution with sodium dodecyl sulfate (SDS) were studied to identify their chirality distribution. The fluorescence of the uniform-diameter SWNTs indicates the formation of the near armchair structures. On the other hand, the SWNTs synthesized over the catalyst with a high Fe loading, 3 wt %, showed a wide chirality distribution including the near zigzag structure. The synthesis of the SWNTs with a narrow diameter distribution could be applied to the selection of SWNTs with a specific chirality based on postsynthesis separation.     

Mesoporous silica spheres from colloids

A novel method has been developed to synthesize mesoporous silica spheres using commercial silica colloids (SNOWTEX) as precursors and electrolytes (ammonium nitrate and sodium chloride) as destabilizers. Crosslinked polyacrylamide hydrogel was used as a temporary barrier to obtain dispersible spherical mesoporous silica particles. The influences of synthesis conditions including solution composition and calcination temperature on the formation of the mesoporous silica particles were systematically investigated. The structure and morphology of the mesoporous silica particles were characterized via scanning electron microscopy (SEM) and N2 sorption technique. Mesoporous silica particles with particle diameters ranging from 0.5 to 1.6 microm were produced whilst the BET surface area was in the range of 31-123 m2 g-1. Their pore size could be adjusted from 14.1 to 28.8 nm by increasing the starting particle diameter from 20-30 nm up to 70-100 nm. A simple and cost effective method is reported that should open up new opportunities for the synthesis of scalable host materials with controllable structures.