Study of molecular motion of block copolymers in solution by high-resolution proton magnetic resonance

Molecular motions of hydrophobic–hydrophilic water-soluble block copolymers in solution were investigated by high-resolution proton magnetic resonance (NMR). Samples studied include block copolymers of polystyrene–poly(ethylene oxide), polybutadiene–poly(ethylene oxide), and poly(ethylene oxide)–poly(propylene oxide)–poly(ethylene oxide). NMR measurements were carried out varying molecular weight, temperature, and solvent composition. For AB copolymers of polystyrene and poly(ethylene oxide), two peaks caused by the phenyl protons of low-molecular-weight (M?_n = 3,300) copolymer were clearly resolved in D₂O at 100°C, but the phenyl proton peaks of high-molecular-weight (M?_n = 13,500 and 36,000) copolymers were too broad to observe in the same solvent, even at 100°C. It is concluded that polystyrene blocks are more mobile in low-molecular-weight copolymer in water than in high-molecular-weight copolymer in the same solvent because the molecular weight of the polystyrene block of the low-molecular-weight copolymer is itself small. In the mixed solvent D₂O and deuterated tetrahydrofuran (THF-d₈), two peaks caused by the phenyl protons of the high-molecular-weight (M?_n = 36,000) copolymer were clearly resolved at 67°C. It is thought that the molecular motions of the polystyrene blocks are activated by the interaction between these blocks and THF in the mixed solvent.     

Block copolymer from α,ω-dihydroxyl polystyrene and polyethylene glycol

α,ω-Dihydroxyl polystyrene was synthesized by the addition of styrene oxide to polystyryl dianion initiated with sodium naphthalene. Diglyme was found to be an unsuitable solvent for the preparation of low molecular weight compounds. Block copolymerization of the α,ω-dihydroxyl polystyrenes (M?_n = 2250, 3140, and 6200) with poly(ethylene glycols) (M?_n = 404, 1960, and 5650) was pursued by introducing urethane linkages with 4,4′-diphenylmethane diisocyanate. The mechanical, thermal, and viscoelastic properties, solution viscosity, molecular weight distribution, and moisture absorption of the block copolymers obtained were examined. Incorporation of styrene blocks was found to disturb the crystallization and fusion of poly(ethylene glycol) blocks. Films cast from benzene solution were soft and elastic and absorbed up to 5.8% moisture.     

Melting behavior of ethylene oxide–propylene oxide (sym-PEP) block copolymers

Melting points and lamellar thicknesses have been measured for ethylene oxide–propylene oxide block copolymers (sym-PEP) with central poly(ethylene oxide) block lengths of 70–100 chain units and end poly(propylene oxide) block lengths of 0–30 chain units. Melting points of the block copolymers are lower than those of the corresponding poly(ethylene oxide) homopolymer by an amount (up to 15°C) which increases as the poly(propylene oxide) block length increases. Most samples have more than one melting transition, which can be assigned to variously folded chain crystals. End interfacial free energies σ_e for the various crystals have been estimated by use of Flory's theory of melting of block copolymers. For a given crystal type (e.g., once-folded-chain) σ_e is higher the longer the chain length of the end poly(propylene oxide) blocks. For a given copolymer σ_e is lower, the more highly folded the poly(ethylene oxide) chain.     

Synthesis of polystyrene-block-polyoxyethylene for use as a stabilizer in the emulsion polymerization of styrene

Five well-defined polystyrene-block-polyoxyethylene copolymers were synthesized by anionic polymerization for use as stabilizers in the emulsion polymerization of styrene. The size of the blocks and their relative weight ratios to each other were the main variables. The molecular weights of the blocks varied from M?_n = 1000–7000 for polystyrene, and M?_w = 3000–9000 for polyoxyethylene. The results of the styrene emulsion polymerization with these block copolymers as stabilizers indicate that for efficient anchoring the block length need not be more than 10 monomer units, possibly even less, and that the polyoxyethylene block M?_w = 3000 is just as capable of stabilizing the polystyrene particle as the higher molecular weight blocks. A very important factor was found to be the weight ratio of the two blocks: block copolymers with a polyoxyethylene content between 75 and 90 wt % were effective stabilizers for the emulsion polymerization of styrene © 1992 John Wiley & Sons, Inc.     

Preparation of (AB)n-type block copolymers by use of polyazoesters

Polyesters of the formula, [(OR)_n? O? CO? C(CH₃)₂? N?N? C(CH₃)₂? CO]_m, where (OR)_n are poly(ethylene oxide), Poly(propylene oxide), or PTHF units, were used to prepare block copolymers with styrene. Ester and ether groups were cleaved with HI, NaOCH₃, and diisobutylaluminum hydride. The resulting polystyrene is telechelic with two COOH and OH groups, respectively. The number of styrene blocks per polymer molecule is 3–4.     

Synthesis of new amphiphilic diblock copolymers containing poly(ethylene oxide) and poly(α‐olefin)

This article discusses an effective route to prepare amphiphilic diblock copolymers containing a poly(ethylene oxide) block and a polyolefin block that includes semicrystalline thermoplastics, such as polyethylene and syndiotactic polystyrene (s‐PS), and elastomers, such as poly(ethylene‐co‐1‐octene) and poly(ethylene‐co‐styrene) random copolymers. The broad choice of polyolefin blocks provides the amphiphilic copolymers with a wide range of thermal properties from high melting temperature ～270 °C to low glass‐transition temperature ～?60 °C. The chemistry involves two reaction steps, including the preparation of a borane group‐terminated polyolefin by the combination of a metallocene catalyst and a borane chain‐transfer agent as well as the interconversion of a borane terminal group to an anionic (? O^?K⁺) terminal group for the subsequent ring‐opening polymerization of ethylene oxide. The overall reaction process resembles a transformation from the metallocene polymerization of α‐olefins to the ring‐opening polymerization of ethylene oxide. The well‐defined reaction mechanisms in both steps provide the diblock copolymer with controlled molecular structure in terms of composition, molecular weight, moderate molecular weight distribution (M_w/M_n < 2.5), and absence of homopolymer. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3416–3425, 2002     

Hydrophilic–hydrophobic AB diblock copolymers containing poly(trimethylene carbonate) and poly(ethylene oxide) blocks

AB‐type block copolymers with poly(trimethylene carbonate) [poly(TMC); A] and poly(ethylene oxide) [PEO; B; number‐average molecular weight (M_n) = 5000] blocks [poly(TMC)‐b‐PEO] were synthesized via the ring‐opening polymerization of trimethylene carbonate (TMC) in the presence of monohydroxy PEO with stannous octoate as a catalyst. M_n of the resulting copolymers increased with increasing TMC content in the feed at a constant molar ratio of the monomer to the catalyst (monomer/catalyst = 125). The thermal properties of the AB diblock copolymers were investigated with differential scanning calorimetry. The melting temperature of the PEO blocks was lower than that of the homopolymer, and the crystallinity of the PEO block decreased as the length of the poly(TMC) blocks increased. The glass‐transition temperature of the poly(TMC) blocks was dependent on the diblock copolymer composition upon first heating. The static contact angle decreased sharply with increasing PEO content in the diblock copolymers. Compared with poly(TMC), poly(TMC)‐b‐PEO had a higher Young's modulus and lower elongation at break. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4819–4827, 2005     

Synthesis and characterization of amphiphilic triblock copolymers by iron‐mediated atom transfer radical polymerization

The atom transfer radical polymerization of methyl methacrylate (MMA) and n‐butyl methacrylate (n‐BMA) was initiated by a poly(ethylene oxide) chloro telechelic macroinitiator synthesized by esterification of poly(ethylene oxide) (PEO) with 2‐chloro propionyl chloride. The polymerization, carried out in bulk at 90 °C and catalyzed by iron(II) chloride tetrahydrate in the presence of triphenylphosphine ligand (FeCl₂ · 4H₂O/PPh₃), led to A–B–A amphiphilic triblock copolymers with MMA or n‐BMA as the A block and PEO as the B block. A kinetic study showed that the polymerization was first‐order with respect to the monomer concentration. Moreover, the experimental molecular weights of the block copolymers increased linearly with the monomer conversion, and the molecular weight distribution was acceptably narrow at the end of the reaction. These block copolymers turned out to be water‐soluble through the adjustment of the content of PEO blocks (PEO content >90% by mass). When the PEO content was small [monomer/macroinitiator molar ratio (M/I) = 300], the block copolymers were water‐insoluble and showed only one glass‐transition temperature. With an increase in the concentration of PEO (M/I = 100 or 50) in the copolymer, two glass transitions were detected, indicating phase separation. The macroinitiator and the corresponding triblock copolymers were characterized with Fourier transform infrared, proton nuclear magnetic resonance, size exclusion chromatography analysis, dynamic mechanical analysis, and differential scanning calorimetry. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5049–5061, 2005     

Surface properties of styrene–ethylene oxide block copolymers

Hydrophobic–hydrophilic block copolymers were prepared by “living” anionic polymerization. They consist of polystyrene and poly(ethylene oxide) blocks, and are soluble in water. Their interfacial properties were investigated, employing aqueous solutions. The block copolymers lowered the surface tension of water in analogy with the low molecular weight surfactants such as sodium lauryl sulfate and heptaethylene oxide n-dodecyl ether. Their aqueous solutions exhibited solubilization properties differing from those of polyethylene glycol. Therefore, it is thought that the polystyrene blocks produce solubilization phenomena. In samples of the same styrene content, the precipitation temperature of a high molecular weight copolymer in water was lower than that of a low molecular weight copolymer at the same concentration in the same solvent. The surface tension and precipitation temperature of aqueous solutions seem to be influenced by molecular weight and composition.     

Synthesis of four‐armed poly(ε‐caprolactone)‐block‐poly(ethylene oxide) by diethylzinc catalyst

Biodegradable, amphiphilic, four‐armed poly(?‐caprolactone)‐block‐poly(ethylene oxide) (PCL‐b‐PEO) copolymers were synthesized by ring‐opening polymerization of ethylene oxide in the presence of four‐armed poly(?‐caprolactone) (PCL) with terminal OH groups with diethylzinc (ZnEt₂) as a catalyst. The chemical structure of PCL‐b‐PEO copolymer was confirmed by ¹H NMR and ¹³C NMR. The hydroxyl end groups of the four‐armed PCL were successfully substituted by PEO blocks in the copolymer. The monomodal profile of molecular weight distribution by gel permeation chromatography provided further evidence for the four‐armed architecture of the copolymer. Physicochemical properties of the four‐armed block copolymers differed from their starting four‐armed PCL precursor. The melting points were between those of PCL precursor and linear poly(ethylene glycol). The length of the outer PEO blocks exhibited an obvious effect on the crystallizability of the block copolymer. The degree of swelling of the four‐armed block copolymer increased with PEO length and PEO content. The micelle formation of the four‐armed block copolymer was examined by a fluorescent probe technique, and the existence of the critical micelle concentration (cmc) confirmed the amphiphilic nature of the resulting copolymer. The cmc value increased with increasing PEO length. The absolute cmc values were higher than those for linear amphiphilic block copolymers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 950–959, 2004     

Interaction between styrene–ethylene oxide block copolymers and sodium lauryl sulfate in aqueous solution

Interactions of water-soluble AB block copolymers of polystyrene and poly(ethylene oxide) with sodium lauryl sulfate (SLS) in aqueous solution were investigated by high-resolution proton magnetic resonance (NMR). The viscosity in aqueous SLS solution was also measured. From the NMR results in D₂O, it appears that molecular motions of the polystyrene blocks of the copolymer in aqueous solution are activated by interaction between the polystyrene blocks and the added SLS. From solution viscosity, on the other hand, it is apparent that a complex is formed between the copolymer and SLS and that it exhibits typical polyelectrolyte properties. The polyelectrolyte character is attributable largely to intrachain repulsions between like charges of the SLS anions adsorbed on the poly(ethylene oxide) blocks of the copolymers since the polystyrene blocks are insoluble in water and the styrene content is less than 10%.     

Synthesis of three‐arm star block copolymers

We describe the synthesis and characterization of three‐arm star block copolymers based on polystyrene, poly(ethylene oxide), poly(ϵ‐caprolactone), poly(methyl methacrylate), poly(tert‐butyl methacrylate) and poly(L‐lactide) blocks. The copolymers were obtained by a route consisting of two successive initiation steps on functional macroinitiator. Some results on micellization and crystallization are given. They indicate an increase in the miscibility of different incompatible blocks.     

Synthesis and self‐assembly morphologies of amphiphilic multiblock copolymers [poly(ethylene oxide)‐b‐polystyrene]n via trithiocarbonate‐embedded PEO macro‐RAFT agent

An amphiphilic multiblock copolymer [poly(ethylene oxide)‐b‐polystyrene]_n [(PEO‐b‐PS)_n] is synthesized by using trithiocarbonate‐embedded PEO as macro‐RAFT agent. PEO with four inserted trithiocarbonate (M_n = 9200 and M_w/M_n = 1.62) groups is prepared first by condensation of α, ω‐dihydroxyl poly(ethylene oxide) with S, S′‐Bis(α, α′‐dimethyl‐α″‐acetic acid)‐trithiocarbonate (BDATC) in the presence of pyridine, then a series of goal copolymers with different St units (varied from 25 to 218 per segment) are obtained by reversible addition‐fragmentation chain transfer (RAFT) polymerization. The synthesis process is monitored by size exclusion chromatography (SEC), ¹H NMR and FT‐IR. The self‐assembled morphologies of the copolymers are strongly dependent of the length of PS block chains when the chain length of PEO is fixed, some new morphologies as large leaf‐like aggregates (LLAs), large octopus‐like aggregates (LOAs), and coarse‐grain like micelles (CGMs) are observed besides some familiar aggregates as large compound vesicles (LCVs), lamellae and rods, and the effect of water content on the morphologies is also discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6071–6082, 2006     

Organizing thermodynamic data obtained from multicomponent polymer electrolytes: Salt‐containing polymer blends and block copolymers

The objective of this review is to organize literature data on the thermodynamic properties of salt‐containing polystyrene/poly(ethylene oxide) (PS/PEO) blends and polystyrene‐b‐poly(ethylene oxide) (SEO) diblock copolymers. These systems are of interest due to their potential to serve as electrolytes in all‐solid rechargeable lithium batteries. Mean‐field theories, developed for pure polymer blends and block copolymers, are used to describe phenomenon seen in salt‐containing systems. An effective Flory–Huggins interaction parameter, χ_eff , that increases linearly with salt concentration is used to describe the effect of salt addition for both blends and block copolymers. Segregation strength, χ_effN , where N is the chain length of the homopolymers or block copolymers, is used to map phase behavior of salty systems as a function of composition. Domain spacing of salt‐containing block copolymers is normalized to account for the effect of copolymer composition using an expression obtained in the weak segregation limit. The phase behavior of salty blends, salty block copolymers, and domain spacings of the latter systems, are presented as a function of chain length, composition and salt concentration on universal plots. While the proposed framework has limitations, the universal plots should serve as a starting point for organizing data from other salt‐containing polymer mixtures. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2019 , 57, 1177–1187     

Synthesis,characterization, and self‐assembly of comb‐dendronized amphiphilic block copolymers

Novel amphiphilic comb‐dendronized diblock copolymers composed of hydrophobic Percec‐type dendronized polystyrene block and hydrophilic comb‐like poly(ethylene oxide) grafted polymethacrylate P(PEOMA) block were designed and synthesized via two steps of atom transfer radical polymerization (ATRP). The comb‐like P(PEOMA) prepared by ATRP of macromonomers (PEOMA) with two different molecular weights (M_n = 300 and 475) were used to initiate the sequent ATRP of dendritic styrene macromonomer (DS). The molecular weights and compositions of the obtained block copolymers were determined by ¹H NMR analysis. The copolymers with relatively narrow polydispersities (1.27–1.38) were thus obtained. The bulk properties of comb‐dendronized block copolymers were studied by using differential scanning calorimetry, polarized optical microscopy and wide‐angle X‐ray diffraction (WAXD). Similar to dendronized homopolymers, the block copolymers exhibited hexagonal columnar liquid‐crystalline phase structure. By using such amphiphilic comb‐dendronized block copolymers as building blocks, the rich self‐assembly morphologies, such as twisted string, vesicle, and large compound micelle (LCM), were obtained in a mixture of CH₃OH and THF. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4205–4217, 2008     

Novel Thermoreversible Gelation of Biodegradable PLGA‐block‐PEO‐block‐PLGA Triblock Copolymers in Aqueous Solution

The BAB‐type triblock copolymers composed of a central poly(ethylene oxide) (PEO, M̄_nPEO = 1 000) block and two poly[(D ,L ‐lactic acid)‐co‐(glycolic acid)] end blocks with molecular weights between 900 and 1 600 exhibited an interesting phase transition behavior. The copolymer aqueous solution can form micelles with PLGA loops in the core and a PEO shell and groups of micelles because of bridging between micelles caused by the PLGA blocks with raising temperature. A possible micellar gelation mechanism was suggested.     

Synthesis and characterization of ABA‐type amphiphilic tri‐block copolymers through anionic polymerization using end functionalized poly(ethylene oxide) oligomers

ABA‐type amphiphilic tri‐block copolymers were successfully synthesized from poly(ethylene oxide) derivatives through anionic polymerization. When poly(styrene) anions were reacted with telechelic bromine‐terminated poly(ethylene oxide) ( 1 ) in 2:1 mole ratio, poly(styrene)‐b‐poly(ethylene oxide)‐b‐poly(styrene) tri‐block copolymers were formed. Similarly, stable telechelic carbanion‐terminated poly(ethylene oxide), prepared from 1,1‐diphenylethylene‐terminated poly (ethylene oxide) ( 2 ) and sec‐BuLi, was also used to polymerize styrene and methyl methacrylate separately, as a result, poly (styrene)‐b‐poly(ethylene oxide)‐b‐poly(styrene) and poly (methyl methacrylate)‐b‐poly(ethylene oxide)‐b‐poly(methyl methacrylate) tri‐block copolymers were formed respectively. All these tri‐block copolymers and poly(ethylene oxide) derivatives, 1 and 2 , were characterized by spectroscopic, calorimetric, and chromatographic techniques. Theoretical molecular weights of the tri‐block copolymers were found to be similar to the experimental molecular weights, and narrow polydispersity index was observed for all the tri‐block copolymers. Differential scanning calorimetric studies confirmed the presence of glass transition temperatures of poly(ethylene oxide), poly(styrene), and poly(methyl methacrylate) blocks in the tri‐block copolymers. Poly(styrene)‐b‐poly(ethylene oxide)‐b‐poly(styrene) tri‐block copolymers, prepared from polystyryl anion and 1 , were successfully used to prepare micelles, and according to the transmission electron microscopy and dynamic light scattering results, the micelles were spherical in shape with mean average diameter of 106 ± 5 nm. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Electrolytes for quasi solid‐state dye‐sensitized solar cells based on block copolymers

The first use of PS_n‐b‐PEO_m‐b‐PS_n block copolymers (PS = polystyrene, PEO = poly(ethylene oxide)) as solid hosts for iodine/iodide electrolytes in dye‐sensitized solar cells (DSSCs) is described. Using the benchmark photosensitizer N719, DSSC based on the quasi solid‐state electrolytes afforded efficiencies up to 6.7%, to be compared with an efficiency of 7.3% obtained in similar conditions with a conventional iodine/iodide liquid electrolyte. By varying the PS:PEO relative volume ratio in the block copolymers different properties and morphologies were obtained. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 719–727     

Synthesis and characterization of well‐defined [polystyrene‐b‐poly(2‐vinylpyridine)]n star‐block copolymers with poly(2‐vinylpyridine) corona blocks

This article describes the synthesis and characterization of [polystyrene‐b‐poly(2‐vinylpyridine)]_n star‐block copolymers with the poly(2‐vinylpyridine) blocks at the periphery. A two‐step living anionic polymerization method was used. Firstly, oligo(styryl)lithium grafted poly(divinylbenzene) cores were used as multifunctional initiators to initiate living anionic polymerization of styrene in benzene at room temperature. Secondly, vinylpyridine was polymerized at the periphery of these living (polystyrene)_n stars in tetrahydrofuran at ?78 °C. The resulting copolymers were characterized using size exclusion chromatography, multiangle laser light scattering, ¹H NMR, elemental analysis, and intrinsic viscosity measurements. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 3949–3955, 2007     

Monolayer films of PS-b-PEO diblock copolymers at the air/water- and an oil/water-interface

 Amphiphilic diblock copolymers consisting of a hydrophobic polystyrene block (PS) and a hydrophilic poly(ethylene oxide) block (PEO) with block sizes of 1000 or 3000 g/mol for both blocks were studied at the air/water and toluene/water interface. Measurements of the film pressure π of spread monolayers at the water surface reveal two limiting regimes of the π−a _m isotherms, in which the mean molecular area a _m is determined either by the size of the hydrophilic or the hydrophobic blocks of the PS-PEO molecules. The interfacial activity of the block copolymers at the toluene/water interface was studied by measuring the interfacial tension σ over a wide range of concentrations. Pronounced differences in the temperature dependence of the interfacial tension were observed, depending mostly on the block length of the hydrophilic PEO block. From the temperature dependence of σ it is inferred that for the block copolymers with the PEO block size of 3000 g/mol the phase inversion temperature (PIT) is well above 60 °C while for those with a PEO block size of 1000 g/mol the PIT is below or near 25 °C in the toluene/water system. Received: 5 February 1998 Accepted: 16 February 1998