Au5+ ion implantation induced structural phase transitions probed through structural,microstructural and phonon properties in BiFeO3 ceramics,using synergistic ion beam energy

Implanted Au⁵⁺-ion-induced modification in structural and phonon properties of phase pure BiFeO₃ (BFO) ceramics prepared by sol–gel method was investigated. These BFO samples were implanted by 15.8?MeV ions of Au⁵⁺ at various ion fluence ranging from 1?×?10¹⁴ to 5?×?10¹⁵?ions/cm². Effect of Au⁵⁺ ions’ implantation is explained in terms of structural phase transition coupled with amorphization/recrystallization due to ion implantation probed through XRD, SEM, EDX and Raman spectroscopy. XRD patterns show broad diffuse contributions due to amorphization in implanted samples. SEM images show grains collapsing and mounds’ formation over the surface due to mass transport. The peaks of the Raman spectra were broadened and also the peak intensities were decreased for the samples irradiated with 15.8?MeV Au⁵⁺ ions at a fluence of 5?×?10¹⁵?ion/cm². The percentage increase/decrease in amorphization and recrystallization has been estimated from Raman and XRD data, which support the synergistic effects being operative due to comparable nuclear and electronic energy losses at 15.8?MeV Au⁵⁺ ion implantation. Effect of thermal treatment on implanted samples is also probed and discussed.     

Phase transformation in Ni–Mn–Sn ferromagnetic shape memory alloy thin films induced by dense ionization

The effects of 200 MeV Au ions irradiation on the structural and magnetic properties of Ni–Mn–Sn ferromagnetic shape memory alloy (FSMA) thin films have been systematically investigated. In order to understand the role of initial microstructure and phase of the film with respect to high energy irradiation, the two types of Ni–Mn–Sn FSMA films having different phases at room temperature were irradiated, one in martensite phase (Ni_58.9Mn_28.0Sn_13.1) and other in austenite phase (Ni₅₀Mn_35.6Sn_14.4). Transmission electron microscope (TEM) and scanning electron microscope (SEM) images along with the diffraction patterns of X-rays and electrons confirm that martensite phase transforms to austenite phase at a fluence of 6×10¹² ions/cm² and a complete amorphization occurs at a fluence of 3×10¹³ ions/cm², whereas ion irradiation has a minimal effect on the austenitic structure (Ni₅₀Mn_35.6Sn_14.4). Thermo-magnetic measurements also support the above mentioned behaviour of Ni–Mn–Sn FSMA films with increasing fluence of 200 MeV Au ions. The results are explained on the basis of thermal spike model considering the core and halo regions of ion tracks in FSMA materials.     

Modifications of structural,optical and electrical properties of nanocrystalline bismuth sulphide by using swift heavy ions

Modified chemical bath deposited (MCBD) bismuth sulphide (Bi₂S₃) thin films’ structural, optical and electrical properties are engineered separately by annealing in air for 1 h at 300 °C and irradiating with 100 MeV Au swift heavy ions (SHI) at 5 × 10¹² ions/cm² fluence. It is observed that the band gap of the films gets red shifted after annealing and irradiation from pristine (as deposited) films. In addition, there is an increase in the grain size of the films due to both annealing and irradiation, leading to the decrease in resistivity and increase in thermoemf of the films. These results were explained in the light of thermal spike model.     

Effect of irradiating ion fluence on optical properties of ZnO1−x:Nx thin films

Swift heavy ion (SHI) irradiation is an effective technique to modify the optical properties of the materials. In the present investigation, the effect of 100?MeV?Ag⁷⁺ SHI irradiation fluence on the optical properties of ZnO_1?x:N_x thin films was studied. The post irradiation spectroscopic characterizations such as UV–VIS reflectance spectroscopy, Raman spectroscopy and photoluminescence (PL) spectroscopy analysis were carried out. The studies imply that when the SHI passes through the solid, the higher electronic stopping power of ions can weaken oxygen bonds in ZnO, resulting in the formation of donor defects such as oxygen vacancies and zinc interstitials. The formation of donor defects has been acknowledged through the increase in bandgap with irradiating ion fluence. The blue shift observed from the Raman spectra for the 3?×?10¹³ ions/cm² fluence-irradiated films implies the existence of compressive stress in the films. The PL analysis acknowledges the formation of donor defects upon irradiation. Furthermore, it conveys that the presence of N atoms in ZnO lattice leads to the formation of a less number of defects as compared with undoped ZnO while irradiation.     

Synthesis of α-In 2 Te 3 thin films from In/Te bilayer by Si ion irradiation

In this work, In/Te bilayer thin films were prepared using sequential thermal evaporation method and subsequently irradiated using swift heavy ions (SHIs) of 100 MeV silicon (Si) with different fluences (1×10¹³ to 5×10¹³/cm²). The inter-diffusion of In and Te layers was highly controlled by SHI irradiation and the In₂Te₃ formation capability was compared with that of the conventional annealing method. The structural as well as optical properties of a post-sintered SHI-irradiated In/Te bilayer were investigated using X-ray diffraction (XRD) measurements and UV–visible spectroscopy, respectively. We found that irradiated samples showed single-phase In₂Te₃ under post-annealed conditions at 150 °C unlike that prepared using the conventional thermal annealing method, which showed mixed phases under similar conditions. This confirms the effective inter-diffusion in bilayer films by SHI irradiation toward the formation of single-phase In₂Te₃. The estimated optical band gap energy was found to be 1.1±0.5 eV and strongly corroborated the XRD results. In addition, the estimated refractive index (n) value of the SHI-irradiated sample (～3.3) was higher than that of the sample obtained through the conventional annealing method (～2.8). This proves that SHI offers a highly compact nature even at low temperatures. This work has a wide scope for achieving single-phase alloyed films through bilayer mixing by SHI irradiation.     

Swift heavy ion provoked structural, optical and electrical properties in SnO2 thin films

SnO₂ thin films grown on glass substrates at 300 ^°C by reactive thermal evaporation and annealed at 600 ^°C were irradiated by 120 MeV Ag⁹⁺ ions. Though irradiation is known to induce lattice disorder and suppression of crystallinity, we observe grain growth at a certain fluence of irradiation. X-ray diffraction (XRD) revealed the crystalline nature of the films. The particle size estimated by Scherrer’s formula for the irradiated films was in the range 10–25 nm. The crystallite size increases with increase in fluence up to 1×10¹² ions?cm^?2, whereas after that the size starts decreasing. Atomic force microscope (AFM) results showed the surface modification of nanostructures for films irradiated with fluences of 1×10¹¹ ions?cm^?2 to 1×10¹³ ions?cm^?2. The UV–visible spectrum showed the band gap of the irradiated films in the range of 3.56 eV–3.95 eV. The resistivity decreases with fluence up to 5×10¹² ions?cm^?2 and starts increasing after that. Rutherford Backscattering (RBS) reveals the composition of the films and sputtering of ions due to irradiation at higher fluence.     

Interaction of oxygen (O+7) ion beam on polyaniline thin films

High-energy ion beam irradiation of the polymers is a good technique to modify the properties such as electrical conductivity, structural behaviour and mechanial properties. Polyaniline thin films doped with hydrochloric acid (HCl) were prepared by oxidation of ammonium persulphate. The effect of Swift Heavy Ions irradiation on the electrical and structural properties of polyaniline has been measured in this study. Polyaniline films were irradiated by oxygen ions (energy 80 MeV, charge state O⁺⁷) with fluence varying from 1 × 10¹⁰ to 3 × 10¹² ions/cm². The studies on electrical and structural properties of the irradiated polymers were investigated by measuring V-I using four probe set-up and X-ray diffraction (XRD) using Bruker AXS, X-ray powder diffractometer. V-I measurements shows an increase in the conductivity of the film, XRD pattern of the polymer shows that the crystallinity improved after the irradiation with Swift Heavy Ions (SHI), which could be attributed to cross linking mechanism.      

Raman spectroscopy study of damage induced in fluorapatite by swift heavy ion irradiations

Raman spectroscopy was used to study the radiation damage of fluorapatite single crystals and sinters. Krypton and iodine ion irradiations were performed at high energies (∼1 MeV amu⁻¹) for fluences ranging between 1 × 10¹¹ and 5 × 10¹³ cm⁻². Evolution of the symmetric stretching mode of the PO₄³⁻ tetrahedral building blocks (strongest Raman mode observed at 965 cm⁻¹) versus ion fluence was investigated. After irradiation, this peak decreases in intensity and a second broader peak appears at lower wavenumber. The well‐resolved peak has been assigned to the crystalline phase, and the broader one to the amorphous phase. The integrated intensity ratios of these two peaks versus fluence are in good agreement with the damage fractions determined by X‐ray diffraction (XRD). Fits of the amorphous fraction versus fluence show that the amorphization mechanisms is dominated by a single‐impact process for iodine ions and by a double‐impact process for krypton ions in the case of single crystals and sinters. For both irradiations, complete amorphization could not be obtained. The amorphous fraction saturates at a maximum value of 88% for sinters and 72% for single crystals. This is attributed to a recrystallization effect which is more important in single crystals than in sinters. For both types of samples, the crystalline peak shifts slightly to a lower wavenumber with fluence, and then shifts back to its initial value for an amorphous fraction larger than 60%. This feature is attributed to a stress relaxation, as shown in the XRD data, which is accompanied by a decrease of the crystalline peak full‐width at half‐maximum. Copyright © 2011 John Wiley & Sons, Ltd.     

Investigation of structural and optical properties of 100 MeV F7+ ion irradiated Ga10Se90-xAlx thin films

Present work focuses on the effect of swift heavy ion (SHI) irradiation of 100 MeV F⁷⁺ ions by varying the fluencies in the range of 1 × 10¹² to 1 × 10¹³ ions/cm² on the morphological, structural and optical properties of polycrystalline thin films of Ga₁₀Se_90-xAl_x (x = 0, 5). Thin films of ~300 nm thickness were deposited on cleaned Al₂O₃ substrates by thermal evaporation technique. X-ray diffraction pattern of investigated thin films shows the crystallite growth occurs in hexagonal phase structure for Ga₁₀Se₉₀ and tetragonal phase structure for Ga₁₀Se₈₅Al₅. The further structural analysis carried out by Raman spectroscopy and scanning electron microscopy verifies the defects or disorder of the investigated material increases after SHI irradiation. The optical parameters absorption coefficient (α), extinction coefficient (K), optical band gap (E_g) and Urbach’s energy (E_U) are determined from optical absorption spectra data measured from spectrophotometry in the wavelength range 200–1100 nm. It was found that the values of absorption coefficient and extinction coefficient increase while the value of optical band gap decreases with the increase in ion fluence. This post irradiation change in the optical parameters was interpreted in terms of bond distribution model.     

Enhancement in electrochemical properties of ionic liquid-based nanocomposite polymer electrolytes by 100 MeV Si9+ swift heavy ion irradiation

Swift heavy ion (SHI) irradiation has been used as a tool to enhance the electrochemical properties of ionic liquid-based nanocomposite polymer electrolytes dispersed with dedoped polyaniline (PAni) nanorods; 100 MeV Si⁹⁺ ions with four different fluences of 5?×?10¹⁰, 1?×?10¹¹, 5?×?10¹¹, and 1?×?10¹² ions cm^?2 have been used as SHI. XRD results depict that with increasing ion fluence, crystallinity decreases due to chain scission up to fluence of 5?×?10¹¹ ions cm^?2, and at higher fluence, crystallinity increases due to cross-linking of polymer chains. Ionic conductivity, electrochemical stability, and dielectric properties are enhanced with increasing ion fluence attaining maximum value at the fluence of 5?×?10¹¹ ions cm^?2 and subsequently decrease. Optimum ionic conductivity of 1.5?×?10^?2 S cm^?1 and electrochemical stability up to 6.3 V have been obtained at the fluence of 5?×?10¹¹ ions cm^?2. Ac conductivity studies show that ion conduction takes place through hopping of ions from one coordination site to the other. On SHI irradiation, amorphicity of the polymer matrix increases resulting in increased segmental motion which facilitates ion hopping leading to an increase in ionic conductivity. Thermogravimetric analysis (TGA) measurements show that SHI-irradiated nanocomposite polymer electrolytes are thermally stable up to 240–260 °C.     

Effect of high‐energy light‐ion irradiation on SI‐GaAs and GaAs:Cr as observed by Raman spectroscopy

The structural evolutions of high‐energy (50 MeV) lithium ion (Li³⁺) irradiated undoped semi‐insulating GaAs (SI‐GaAs) and chromium‐doped SI‐GaAs (GaAs:Cr) were investigated by Raman measurements. It is shown that high‐energy Li³⁺ irradiation causes amorphization beyond a fluence of 3 × 10¹³ ions/cm² in undoped SI‐GaAs. Interestingly, the same fluence of ions does not seem to affect the crystallinity in GaAs:Cr appreciably. The effect of ion irradiation on the change in lattice ordering and anharmonicity of the phonon modes of undoped SI‐GaAs and GaAs:Cr is also compared. Copyright © 2011 John Wiley & Sons, Ltd.     

Effect of swift heavy ion irradiation on dilute Fe-doped Sb0.95Se0.05 magnetic semiconductor

A thin film of dilute Fe (0.008)-doped Sb_0.95Se_0.05 alloy was grown on silicon substrate using the thermal evaporation technique. This film was irradiated with swift heavy ions (SHIs) Ag⁺¹⁵ having 200?MeV energy at ion fluences of 1?×?10¹² and 5?×?10¹² ions per cm², respectively. The thickness of the thin film was ～500?nm. We study the effect of irradiation on structural, electrical, surface morphology and magnetic properties of this film using grazing angle XRD (GAXRD), DC resistivity, atomic force microscopy (AFM) and magnetic force microscopy (MFM), respectively. GAXRD suggests that no significant change is observed in this system due to SHI irradiation. The average crystallite size increases with fluence, whereas the AFM image shows the rms roughness decreases due to irradiation with respect to the un-irradiated thin film. The MFM image shows that the magnetic interaction in irradiated film decreases due to the irradiation effect. Although the un-irradiated sample shows metal to semiconducting transition, but after irradiation with fluence of 5?×?10¹² ions per cm², the sharpness of the metal to semiconducting phase transition is observed to increase dramatically at ～300?K. This characteristic of the thin film makes it a promising candidate for an electrical switching device after irradiation.     

RBS and TEM studies of indium phosphide irradiated with 100 keV Au ions

Transmission Electron Microscopy (TEM) and Rutherford Backscattering (RBS) have been used to observe the spatially isolated disordered zones in InP resulting from 100 keV Au ion irradiation at room temperature. Studies were carried out in interval of irradiation fluences less than lower value of full amorphization fluence. Such a value of fluence, as was established in the studies, can be estimated of order ∼2.5 × 10¹³cm⁻². The accumulation of damage due to the 100 keV Au ion irradiation was described in this material using a composite theoretical model accounting for both homogeneous and heterogeneous amorphization processes.     

Li3+ ion irradiation effects on ionic conduction in P(VDF–HFP)–(PC + DEC)–LiClO4 gel polymer electrolyte system

Swift heavy ion irradiation of P(VDF–HFP)–(PC + DEC)–LiClO₄ gel polymer electrolyte system with 48 MeV Li³⁺ ions having five different fluences was investigated with a view to increase the Li⁺ ion diffusivity in the electrolyte. Irradiation with swift heavy ion (SHI) shows enhancement of conductivity at lower fluences and decrease in conductivity at higher fluences with respect to unirradiated polymer electrolyte films. Maximum room temperature (303 K) ionic conductivity is found to be 2.2 × 10^− 2 S/cm after irradiation with fluence of 10¹¹ ions/cm². This interesting result could be ascribed to the fluence-dependent change in porosity and to the fact that for a particular ion beam with a given energy higher fluence provides critical activation energy for cross-linking and crystallization to occur, which results in the decrease in ionic conductivity. The XRD results show decrease in the degree of crystallinity upon ion irradiation at low fluences (≤ 10¹¹ ions/cm²) and increase in crystallinity at high fluences (> 10¹¹ ions/cm²). The scanning electron micrographs (SEM) exhibit increased porosity of the polymer electrolyte films after low fluence ion irradiation.     

Effect of Si ion irradiation on polycrystalline CdS thin film grown from novel photochemical deposition technique

CdS thin films have been deposited from aqueous solution by photochemical reactions. The solution contains Cd(CH₃COO)₂ and Na₂S₂O₃, and pH is controlled in an acidic region by adding H₂SO₄. The solution is illuminated with light from a high-pressure mercury-arc lamp. CdS thin films are formed on a glass substrate by the heterogeneous nucleation and the deposited thin films have been subjected to high-energy Si ion irradiations. Si ion irradiation has been performed with an energy of 80 MeV at fluences of 1×10¹¹, 1×10¹², 1×10¹³ and 1×10¹⁴ ions/cm² using tandem pelletron accelerator. The irradiation-induced changes in CdS thin films are studied using XRD, Raman spectroscopy and photoluminescence. Broadening of the PL emission peak were observed with increasing irradiation fluence, which could be attributed to the band tailing effect of the Si ion irradiation. The lattice disorder takes place at high Si ion fluences.     

Carbon (70 MeV) and copper (120 MeV) ions irradiation effects in Makrofol-N

Makrofol-N polycarbonate was irradiated with carbon (70 MeV) and copper (120 MeV) ions to analyze the induced effects with respect to optical and structural properties. In the present investigation, the fluence for carbon and copper beams was kept in the range of 1×10¹¹– 1×10¹³ ions/cm² to study the swift heavy ion induced modifications. UV–VIS, FTIR and XRD techniques were utilized to study the induced changes. The analysis of UV–VIS absorption studies revealed that the optical energy gap was reduced by 17% on carbon irradiation, whereas the copper beam leads to a decrease of 52% at the highest fluence of 1×10¹³ ions/cm². The band gap can be correlated to the number of carbon atoms, N, in a cluster with a modified Robertson's equation. In copper (120 MeV) ions irradiated polycarbonate, the number of carbon atoms in a cluster was increased from 63 to 269 with the increase of ion fluence from 0 to 1×10¹³ ions/cm², whereas N is raised only up to 91 when the same polymer films were irradiated with carbon (70 MeV) ions under similar conditions. FTIR analysis showed a decrease in almost all characteristic absorption bands under irradiation. The formation of hydroxyl (? OH) and alkene (C?C) groups were observed in Makrofol-N at higher fluence on irradiation with both types of ions, while the formation alkyne end (R? C≡ CH) group was observed only after copper ions irradiation. The radii of the alkyne production of about 3.3 nm were deduced for copper (120 MeV) ions. XRD measurements show a decrease in intensity of the main peak and an increase of the average intermolecular spacing with the increase of ion fluence, which may be attributed to the structural degradation of Makrofol-N on swift ion irradiation.     

XRD and AFM study of radiation damage induced by swift heavy ions in Y3Al5O12 single crystals

Defects induced in Y₃Al₅O₁₂ single crystals by swift heavy ions are investigated by X-ray diffraction (XRD) and atomic force microscopy. The irradiation was performed at GANIL with 561 MeV ⁵¹Cr, 466 MeV ¹²⁸Te, and 957 MeV ²⁰⁸Pb ions. The XRD data reveal that the lattice strain increases with increasing electronic stopping power, whereas the hillock parameters (height and diameter) are not influenced by the electronic stopping power. According to our experimental data, for the same mean electronic stopping power, the hillock parameters are more pronounced for the lower range in contrast to swelling measurements. The experimental data show a strong increase in the hillock parameter at higher fluence, indicating the amorphization of Y₃Al₅O₁₂ single crystals.     

Ion-beam formation and track modification of InAs nanoclusters in silicon and silica

The implantation formation of InAs nanoclusters in silicon and silica and their modification via irradiation with Xe ions with an energy of 167 MeV and a fluence of 3 × 10¹⁴ cm^–2 are studied. It is found that post-implantation annealing and irradiation with high-energy ions alter the size and shape of nanoclusters and cause structural transformations within them. The ordering of nanoclusters and their elongation along the trajectory of Xe ions in a SiO₂ matrix is observed.     

Observation of grain growth in swift heavy ion irradiated NiO thin films

NiO thin films grown on Si(100) substrates by electron beam evaporation, were sintered at 500 °C and 700 °C. The films were irradiated with 120 MeV Au⁹⁺ ions. Irradiation had different effects depending upon the initial microstructure of the films. Irradiation of the films at a fluence of 3 × 10¹¹ ions cm⁻² leads to grain growth for the films sintered at 500 °C and grain fragmentation for the films sintered at 700 °C. At still higher fluences of irradiation, grain size in 500 °C sintered film decreased, but the same improved in 700 °C sintered film. Associated with the grain size, texturing of the films was also shown to undergo significant modifications under irradiation.     

Electrical and structural properties of the swift heavy ion irradiated Au/n-GaAs schottky barrier diodes

Abstract

Au/n-GaAs Schottky Barrier Diodes (SBDs) have been fabricated on LEC grown silicon doped (100) GaAs single crystals. The SBDs were irradiated using high energy (120 MeV) silicon ion with fluences of 1 × 10 ¹¹ and 1 × 10¹² ions/cm². Current-Voltage (I-V) characteristics of unirradiated and irradiated diodes were analyzed. The change in the reverse leakage current increases with increasing ion fluence. This is due to the irradiation induced defects at the interface and its increase with the fluence. The diodes were annealed at 573 and 673 K. to study the effect of annealing. The rectifying behavior of the irradiated (fluence of 1 × 10¹² ions/cm¹²) SBDs improves upon as the annealing temperature increases and is attributed to the in situ self-annealing during irradiation. Scanning Electron Microscopic analysis was carried out on the irradiated samples to delineate the projected range and to observe defects.