Photografting of vinyl polymers onto ultrafine inorganic particles: Photopolymerization of vinyl monomers initiated by AZO groups introduced onto these surfaces

The photografting of polymers onto ultrafine inorganic particles, such as silica and titanium oxide, initiated by azo groups introduced onto these surfaces was investigated. The introduction of azo groups onto the particles was achieved by the reaction of 4,4′-azobis(4-cyanopentanoic acid) with surface isocyanate groups, which were introduced by the treatment with tolylene 2,4-diisocyanate. It was found that the photopolymerization of vinyl monomers, such as methyl methacrylate (MMA), styrene, and N-vinylcarbazole, is initiated by ultrafine particles having azo groups. The corresponding polymers were effectively grafted onto these surfaces through the propagation of the polymer from the surface radicals formed by the photodecomposition of the azo groups: e.g., the percentage of grafting of PMMA and polystyrene onto silica was reached to 112 and 176%, respectively. The percentage of grafting onto silica in the graft polymerization initiated by photodecomposition of surface azo groups was much larger than that initiated by thermal decomposition. Polymer-grafted ultrafine particles thus obtained gave a stable colloidal dispersion in good solvents for the grafted chain. © 1994 John Wiley & Sons, Inc.     

Scale-up synthesis of vinyl polymer-grafted nano-sized silica by radical polymerization of vinyl monomers initiated by surface initiating groups in the solvent-free dry-system

For the purpose of the prevention of the environmental pollution and the simplification of reaction process, the scale-up radical graft polymerization of vinyl monomers onto nano-sized silica surface initiated by azo groups and peroxycarbonate groups previously introduced onto the surface in the solvent-free dry-system was investigated. The introduction of azo groups onto the silica surface was achieved by the reaction of surface amino groups with 4,4′-azobis(4-cyanopentanoic acid chloride). On the other hand, the introduction of peroxycarbonate groups onto the silica surface was achieved by Michael addition of surface amino groups to t-butylperoxy-2-methacryloyloxyethylcarbonate. The graft polymerization of vinyl monomers onto the surface was successfully achieved by splaying monomers to nano-sized silica having azo and peroxycarbonate groups in solvent-free dry-system. It is interesting to note that the formation of ungrafted polymer was depressed in comparison with graft polymerization in solution: the grafting efficiency was 90-95%. In addition, in the solvent-free dry-system, the grafting of copolymer having pendant peroxycarbonate groups onto the nano-sized silica surface and the radical postgraft polymerization of styrene initiated by the pendant initiating groups of the grafted copolymer chain on the silica surface was investigated.     

Radical Graft Polymerization of Vinyl Monomers Initiated by A20 Groups Introduced Onto a Carbon Black Surface: Effect of azo Groups on Graft Polymerization

The radical graft polymerization of vinyl monomers from carbon black initiated by azo groups introduced onto the surface was investigated. The introduction of azo groups onto carbon black surface was achieved by three methods: the reaction of 2,2′-azobis[2-(2-imidazolin-2-yl)propane] (AIP) with (1) epoxide groups, which were introduced by the reaction of carbon black with chlorometh-yloxirane; (2) acyl chloride groups, which were introduced by the reaction of carboxyl groups on the surface with thionyl chloride; and (3) 3-chloroformyl-1-cyano-1-methylpropyl groups, which were introduced by the reaction of carbon black with 4,4′-azobis(4-cyanovaleric acid) and then thionyl chloride. The amount of azo groups introduced onto the surface by the above methods was determined to be 0.07-0.19 mmol/g. The graft polymerization of methyl methacrylate was found to be initiated by azo groups introduced onto the carbon black surface. During the polymerization, poly(methyl methacrylate) was effectively grafted onto carbon black through propagation of the polymer from the radical produced on the surface by the decomposition of the azo groups. The percentage of grafting using carbon black having azo groups introduced by method 1 increased to 40%. It was also found that the graft polymerization of several vinyl monomers such as styrene, acrylonitrile, and acrylic acid was initiated by the azo groups introduced onto the surface and the corresponding polymer was effectively grafted onto the surface. Furthermore, the effect of the amount of carbon black having azo groups on the graft polymerization was investigated.     

Graft polymerization of methyl methacrylate initiated by pendant azo groups introduced onto γ-poly(glutamic acid)

The grafting of poly(methyl methacrylate) (PMMA) onto biosynthesized γ-poly(glutamic acid) (γ-PGA) initiated by pendant azo groups introduced onto γ-PGA was performed. The introduction of pendant azo groups onto γ-PGA was achieved by the reaction of carboxyl groups of γ-PGA with azo initiators having hydroxyl or amino groups, such as 2,2-azobis[2-(hydroxymethyl)propionitrile] (AHP), 2,2′-azobis[2-methyl-N-(2-hydroxyethyl)propionamide] (AMHP), and 2,2′-azobis[2-(2-imidazolin-2-yl)propane] (AIP), using N,N′-dicyclohexylcarbodiimide. The amount of pendant AHP groups introduced onto γ-PGA was estimated to be 0.15 mmol/g. Untreated γ-PGA failed to initiate the polymerization of MMA. On the contrary, the polymerization of MMA was found to be initiated in the presence of γ-PGA having azo groups: the polymerization rate was proportional to the square root of the concentration of γ-PGA having pendant azo groups. During the polymerization PMMA was grafted onto γ-PGA; the percentage of grafting of PMMA onto γ-PGA obtained from the graft polymerization initiated by pendant AHP, AMHP, and AIP groups was evaluated to be 65.0, 53.1, and 29.0%, respectively. Differential scanning calorimetric analysis shows that the endotherm transition point of γ-PGA at 220°C disappears by the grafting of PMMA onto the polymer. © 1993 John Wiley & Sons, Inc.     

Photografting of polymers onto nanosized silica surface initiated by eosin moieties immobilized onto the surface

The photograft polymerization of various vinyl monomers onto nanosized silica surfaces was investigated. It was initiated by eosin moieties introduced onto the silica surface. The preparation of the silica with eosin moieties was achieved by the reaction of eosin with benzyl chloride groups on the silica surface.These were introduced by the reaction of surface silanol groups with 4‐(chloromethyl)phenyltrimethoxysilane in the presence of t‐butyl ammonium bromide as a phase‐transfer catalyst. The photopolymerization of various vinyl monomers, such as styrene, acrylamide, acrylic acid, and acrylonitrile was successfully initiated by eosin moieties on the silica surface in the presence of ascorbic acid as a reducing agent and by oxygen. The corresponding polymers were grafted from the silica surface. The grafting efficiency (percentage of grafted polymer to total polymer formed) in the photoinitiation system was much larger than that in the radical polymerization initiated by surface radicals; these radicals were formed by the thermal decomposition of azo groups introduced onto the silica surface. It was found that the polymer‐grafted silica gave stable dispersions in good solvents of grafted polymer and the wettability of the surfaces can be easily controlled by grafting of polymers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 600–606, 2005     

Effect of polymerization conditions on the molecular weight of polystyrene grafted onto silica in the radical graft polymerization initiated by azo or peroxyester groups introduced onto the surface

The effect of polymerization conditions on the molecular weight of polystyrene grafted onto silica obtained from the radical graft polymerization initiated by azo and peroxyester groups introduced onto the surface was investigated. The molecular weight of polystyrene grafted onto silica obtained from the radical graft polymerization initiated by surface azo and peroxyester groups decreased with decreasing monomer concentration and polymerization temperature. The molecular weight of polystyrene was found to be controlled to some extent by the addition of a chain transfer agent. The molecular weight of grafted chain on silica surface obtained from the graft polymerization initiated by surface radicals formed by photodecomposition of azo groups was considerably smaller than that by thermal decomposition. The number of grafted polystyrene in photopolymeriztion, however, was much larger than that in thermal polymerization. These results are explained by the blocking of surface radicals formed on the silica surface by previously grafted polymer chain: when the decomposition of surface azo and peroxyester groups proceed instantaneously at the initial stage of the polymerization, the number of grafted polymer chains increased.     

Radical graft polymerization of vinyl monomers onto nanoparticles in ionic liquid initiated by azo groups introduced onto the surface

The radical graft polymerization of vinyl monomers, such as styrene and methyl methacrylate, initiated by azo groups introduced onto silica nanoparticle and carbon black surfaces in room temperature ionic liquid (IL) were investigated. In this work, 1‐butyl‐3‐methylimidazolium hexafluorophosphate ([C₄mim][PF₆]) was used as IL. The percentage of polystyrene and poly(methyl methacrylate) grafting onto silica nanoparticle and carbon black increased with increasing reaction time. The percentage of grafting in IL was much larger than that in 1,4‐dioxane. The molecular weight of polystyrene grafted onto the silica surface in IL was almost equal to that in 1,4‐dioxane. The result indicates that the amount of grafted polystyrene in IL is five times that in 1,4‐dioxane. This may be due to the fact that lifetime of the surface radical formed by the group of azo is prolonged because of high viscosity of IL. Therefore, the surface azo groups were effectively used as initiating sites for the graft polymerization. In addition, the reduction of waste solvent was achieved by use of IL as reaction solvent, because unreacted monomer could be removed under vacuum after the reaction and the reuse of IL was easily achieved. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1143–1149, 2007     

Grafting of Polymers onto Activated Carbon Surface: Graft Polymerization of Vinyl Monomers Initiated by Azo Groups That Were Introduced onto the Surface

Abstract

We examined the grafting of polymers onto an activated carbon powder surface by polymerization that was initiated by azo groups that were introduced onto the surface as well as the effects of grafted polymers on the adsorption of acetic acid. The introduction of azo groups onto the surface was achieved by the following methods: (1) a reaction of 4,4′-azobis(4-cyano-pentanoic acid) (ACPA) with surface isocyanate groups that were introduced beforehand by treatment with tolylene 2,4-diisocyanate (AC-Azo 1) and (2) the direct condensation of ACPA with surface phenolic hydroxyl groups by using N,N'-dicyclohexylcarbodiimide (AC-Azo 2). The radical polymerizations of styrene, methyl methacrylate, N,N-diethylacrylamide (DEAM), and N-isopropylacrylamide (NIPAM), were successfully initiated by the azo groups on the surface and the corresponding polymers were grafted onto the surface. There was a significant decrease in the adsorption of the acetic acid of the activated carbons when polymers were grafted onto them, particularly in regards to the grafting of hydrophobic polymers. On the other hand, a decrease in the adsorbability of the polyDEAM-grafted and polyNIPAM-grafted activated carbon was barely observed. In addition, polyDEAM-grafted and polyNIPAM-grafted activated carbons showed temperature-dependent adsorption of acetic acid: the adsorbability of these activated carbon decreased above lower critical solution temperature of these polymers, which is about 32°C.     

Grafting of polymers onto and/or from silica surface during the polymerization of vinyl monomers in the presence of γ‐ray‐irradiated silica

The effects of radicals on silica surface, which were formed by γ‐ray irradiation, on the polymerization of vinyl monomers were investigated. It was found that the polymerization of styrene was remarkably retarded in the presence of γ‐ray‐irradiated silica above 60 °C, at which thermal polymerization of styrene is readily initiated. During the polymerization, a part of polystyrene formed was grafted onto the silica surface but percentage of grafting was very small. On the other hand, no retardation of the polymerization of styrene was observed in the presence of γ‐ray‐irradiated silica below 50 °C; the polymerization tends to accelerate and polystyrene was grafted onto the silica surface. Poly(vinyl acetate) and poly(methyl methacrylate) (MMA) were also grafted onto the surface during the polymerization in the presence of γ‐ray‐irradiated silica. The grafting of polymers onto the silica surface was confirmed by thermal decomposition GC‐MS. It was considered that at lower temperature, the grafting based on the propagation of polystyrene from surface radical (“grafting from” mechanism) preferentially proceeded. On the contrary, at higher temperature, the coupling reaction of propagating polymer radicals with surface radicals (“grafting onto” mechanism) proceeded to give relatively higher molecular weight polymer‐grafted silica. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2972–2979, 2006     

Grafting of polymers onto a carbon‐fiber surface by ligand‐exchange reaction of poly(vinyl ferrocene‐co‐vinyl monomer) with polycondensed aromatic rings of the surface

To improve the surface of carbon fiber, the grafting reaction of copolymer containing vinyl ferrocene (VFE) onto a carbon‐fiber surface by a ligand‐exchange reaction between ferrocene moieties of the copolymer and polycondensed aromatic rings of carbon fiber was investigated. The copolymer containing VFE was prepared by the radical copolymerization of VFE with vinyl monomers, such as methyl methacrylate (MMA) and styrene, using 2,2′‐azobisisobutyronitrile as an initiator. By heating the carbon fiber with poly(VFE‐co‐MMA) (number‐average molecular weight: 2.1 × 10⁴) in the presence of aluminum chloride and aluminum powder, the copolymer was grafted onto the surface. The percentage of grafting reached 46.1%. On the contrary, in the absence of aluminum chloride, no grafting of the copolymer was observed. Therefore, it is considered that the copolymer was grafted onto the carbon‐fiber surface by a ligand‐exchange reaction between ferrocene moieties of the copolymer and polycondensed aromatic rings of carbon fiber. The molar number of grafted polymer chain on the carbon‐fiber surface decreased with increasing molecular weight of poly(VFE‐co‐MMA) because the steric hindrance of grafted copolymer on the carbon‐fiber surface increases with increasing molecular weight of poly(VFE‐co‐MMA). © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1868–1875, 2002     

纳米SiO_2粒子锚固偶氮引发剂及接枝聚甲基丙烯酸甲酯

对纳米SiO2 粒子锚固偶氮引发剂 ,进而引发甲基丙烯酸甲酯聚合而制备聚甲基丙烯酸甲酯(PMMA) 纳米SiO2 复合粒子进行了研究 .纳米SiO2 先用环氧型硅烷偶联剂处理 ,再与偶氮二氰基戊酸发生缩合反应而锚固上偶氮引发剂 ,通过差示扫描量热和元素分析证明了引发剂在纳米SiO2 表面的锚固 .通过改性纳米SiO2 存在下MMA的乳液聚合 ,制备得到了接枝率为 2 3 2 %、接枝效率为 36 1%的PMMA 纳米SiO2 复合粒子 .经乳液聚合后 ,纳米SiO2 粒子团聚程度减小 ,在水相中分散稳定 .     

Graft polymerization of methyl methacrylate from silica initiated by peroxide groups introduced onto the surface

The surface grafting onto ultrafine silica by the radical polymerization of methyl methacrylate (MMA) initiated by peroxide groups introduced onto the surface was investigated. The introduction of peroxide groups onto the silica surface was achieved by the reaction of hydrogen peroxide with chlorosilyl groups, which were introduced by the treatment of silica with thionyl chloride. The content of diisopropylbenzene peroxide and tert-butyl peroxide groups introduced onto the silica according to the above method was determined to be 0.11 and 0.08 mmol/g, respectively. It was found that the polymerization of MMA is initiated by silica having these peroxide groups. In the polymerization, polyMMA was grafted onto silica surface: the percentage of grafting reached about 70%. Therefore, it was concluded that the polymerization of MMA is initiated by surface radicals formed by the decomposition of peroxide groups on silica and polyMMA is grafted through the propagation from the surface. During the polymerization, ungrafted polyMMA was also formed because of the formation of initiator fragments by the decomposition of peroxide groups: the grafting efficiency of the graft polymerization was 30–40%. PolyMMA-grafted silica produced a stable colloidal dispersion in organic solvents for polyMMA. © 1992 John Wiley & Sons, Inc.     

Effective grafting of polymers onto ultrafine silica surface: Photopolymerization of vinyl monomers initiated by the system consisting of trichloroacetyl groups on the surface and Mn2(CO)10

The effective grafting of vinyl polymers onto an ultrafine silica surface was successfully achieved by the photopolymerization of vinyl monomers initiated by the system consisting of trichloroacetyl groups on the surface with Mn₂(CO)₁₀ under UV irradiation at 25 °C. The introduction of trichloroacetyl groups onto the surface of silica was achieved by the reaction of trichloroacetyl isocyanate with surface amino groups, which were introduced by the treatment of silica with 3‐aminopropyltriethoxysilane. During the polymerization, the corresponding polymers were effectively grafted onto the surface, based on the propagation of polymer from surface radicals formed by the interaction of trichloroacetyl groups and Mn₂(CO)₁₀. The percentage of poly(methyl methacrylate) grafting onto the silica reached 714.6% after 90 min. The grafting efficiency (proportion of grafted polymer to total polymer formed) in the polymerization of methyl methacrylate was very high, about 80%, indicating the depression of formation of ungrafted polymer. Polymer‐grafted silica gave a stable colloidal dispersion in good solvents for grafted polymer. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2157–2163, 2001     

Cationic Grafting of Vinyl Polymers onto a Carbon Whisker,Initiated by Acylium Perchlorate Groups Introduced onto the Surface

Abstract

The cationic graft polymerization of vinyl monomers onto a carbon whisker, vapor-grown carbon fiber, initiated by acylium perchlorate groups introduced onto the surface, was investigated. The introduction of acylium perchlorate groups onto a carbon whisker was achieved by the treatment of a carbon whisker having acyl chloride groups, which were introduced by the reaction of surface carboxyl groups with thionyl chloride, with silver perchlorate in nitrobenzene. It was found that the cationic polymerization of vinyl monomers, such as styrene, indene, N-vinyl-2-pyrrolidone, and n-butyl vinyl ether, is initiated by acylium perchlorate groups on a carbon whisker. In the polymerization, the corresponding vinyl polymers were grafted onto a carbon-whisker surface based on the propagation of polymer from the surface: the percentage of grafting of polystyrene and polyindene reached 42.5 and 100.3%, respectively. The percentage of polystyrene grafting decreased with increasing polymerization temperature because of preferential chain transfer reactions at higher temperatures. Polymer-grafted carbon whisker gave a stable colloidal dispersion in a good solvent for grafted polymer.     

Grafting of Polymers from Carbon Fiber. Anionic Graft Polymerization of Vinyl Monomers Initiated by Metallized Aromatic Rings on Carbon Fiber

The anionic graft polymerization of vinyl monomers onto carbon fiber initiated by metallized carbon fiber was investigated. The metalation of polycondensed aromatic rings of the carbon fiber surface was achieved by the treatment of carbon fiber with n-butyl-lithium (BuLi) in N, N, N′, N′ -tetramethylethylenediamine (TMEDA) or hexamethylphosphorous triamide (HMPT) at 0°C. The anionic polymerization of methyl methacrylate (MMA) and styrene (St) was initiated by the metallized carbon fiber, and these polymers were grafted onto the surface. The conversion and the percentage of grafting increased with increasing amount of BuLi used for the metalation of carbon fiber. When 0.20 g carbon fiber was treated with 0.3 mmol BuLi in TMEDA, the percentage of grafting of PMMA and PSt reached a maximum value (PMMA, 34.5%; PSt, 37.1 %). Furthermore, the metalation of aromatic rings of carbon fiber also proceeds by the treatment with BuLi in HMPT. On the contrary, no grafting was observed when carbon fiber was treated with BuLi in tetrahydrofuran (THF) or toluene. This may be due to the fact that metalation of carbon fiber does not proceed in THF or toluene.     

Grafting of Polymers Having Pendant Peroxycarbonate Groups Onto Carbon Black and Postpolymerization of Vinyl Monomers

Abstract

Postpolymerization of vinyl monomers initiated by pendant peroxycarbonate groups of grafted polymer chains on carbon black (CB) was investigated. The grafting of polymers having pendant peroxycarbonate groups onto CB was achieved by the trapping of polymer radicals formed by the thermal decomposition of copolymers of t-butylperoxy-2-methacryloyloxyethyl-carbonate (HEPO) with vinyl monomers such as vinyl acetate (VAc), styrene (St) and methyl methacrylate (MMA). The copolymers having pendant peroxycarbonate groups were prepared by copolym-erization of HEPO with vinyl monomers using azo initiator under irradiation of UV light at room temperature. The amount of remaining pendant peroxycarbonate groups of the poly(VAc-co-HEPO)-grafted CB obtained from the reaction at 90°C was maximum and decreased above the temperature. Furthermore, the postpolymerization of vinyl monomers, such as St, MMA, and VAc was initiated in the presence of poly(VAc-co-HEPO)-grafted and poly(St-co-HEPO)-grafted CB and the corresponding polymers were postgrafted onto CB to give branched polymer-grafted CB. The percentage of poly(St)-postgrafting (proportion of post-grafted poly(St) to poly(MMA-co-HEPO)-grafted CB used) increased with increasing polymerization time, but became constant at 20% after 4 hours.     

Functionalization of Graphene Sheets via Chemically Grafting of PMMA Chains Through in-situ Polymerization

In this work, we report the preparation of graphene nanoplatelet which covalently functionalized with PMMA chains by introduction of vinyl groups onto graphene surface through simple esterification reaction between hydroxyl groups of graphite oxide and methacrylic anhydride. The synthesis is followed by in-situ polymerization with MMA monomers. The structural properties were characterized with X-ray diffraction spectroscopy (XRD) and scanning electronic microscopy (SEM) that showed the crystalline graphite is converted to individual layers during the synthesis steps. The grafting of PMMA chains was monitored with IR spectroscopy (FT-IR) and thermogravimetric analysis (TGA). The TGA results revealed 40% wt of PMMA chains chemically grafted onto graphene surface. Significant increase in glass transition temperature (T_g) and existence of polymer chains in two positions (physically absorbed and chemically grafting onto graphite surface) are indicated by differential scanning calorimetric (DSC) analysis.     

Visible light‐induced living surface grafting polymerization for the potential biological applications

A novel visible light‐induced living surface grafting polymerization was developed by a strategy in which isopropyl thioxanthone (ITX) was first photoreduced under UV light and sequentially coupled onto the surface of polymeric substrates, and the produced isopropyl thioxanthone‐semipinacol (ITXSP) “dormant” groups were subsequently reactivated under visible light to initiate a surface grafting polymerization. By using glycidyl methacrylate (GMA) and low‐density polyethylene (LDPE) films as models, a “living” surface grafting polymerization initiated by ITXSP under visible light at room temperature was observed. Both the surface grafting chain length versus grafting conversion of monomer and the grafting polymerization rate versus monomer concentration demonstrated a linear dependence, which is in accord with the known characteristics of living polymerization. The livingness rendered it possible to accurately control the thickness of the grafted layer by simply altering the irradiation time. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Phys, 2009     

Grafting of polyesters from carbon whisker surface: Copolymerization of epoxides with cyclic acid anhydrides initiated by COOK groups introduced onto the surface

To modify the surface of carbon whisker (vapor-grown carbon fiber) the grafting of polyesters by use of potassium carboxylate (COOK) groups introduced onto the surface was investigated. The introduction of COOK groups onto the carbon whisker was achieved by the treatment of surface carboxyl groups with KOH aqueous solution. Untreated carbon whisker has no ability to initiate the polymerization. It was found that the anionic ring-opening alternating copolymerization of epoxides with cyclic acid anhydrides is successfully initiated by COOK groups on the carbon whisker surface. The corresponding polyester was grafted onto the surface based on the propagation of polymer from COOK groups introduced on the surface. The percentage of grafting of the polyester from styrene oxide and phthalic anhydride was determined to be 91.0%. The polymerization rate and percentage of grafting increased upon addition of crown ether. Furthermore, the rate of polymerization increased with increasing the dielectric constant of the solvent, but the percentage of grafting decreased. Polyester-grafted carbon whisker was found to give a stable colloidal dispersion in a good solvent for the grafted polymer. © 1993 John Wiley & Sons, Inc.     

Synthesis of well‐defined polymer brushes on the surface of zinc antimonate nanoparticles through surface‐initiated atom transfer radical polymerization

Zinc antimonate nanoparticles consisting of antimony and zinc oxide were surface modified in a methanol solvent medium using triethoxysilane‐based atom transfer radical polymerization (ATRP) initiating group (i.e.,) 6‐(2‐bromo‐2‐methyl) propionyloxy hexyl triethoxysilane. Successful grafting of ATRP initiator on the surface of nanoparticles was confirmed by thermogravimetric analysis that shows a significant weight loss at around 250–410 °C. Grafting of ATRP initiator onto the surface was further corroborated using Fourier transform Infrared spectroscopy (FT‐IR) and X‐ray photoelectron spectroscopy (XPS). The surface‐initiated ATRP of methyl methacrylate (MMA) mediated by a copper complex was carried out with the initiator‐fixed zinc antimonate nanoparticles in the presence of a sacrificial (free) initiator. The polymerization was preceded in a living manner in all examined cases; producing nanoparticles coated with well defined poly(methyl methacrylate) (PMMA) brushes with molecular weight in the range of 35–48K. Furthermore, PMMA‐grafted zinc antimonate nanoparticles were characterized using Thermogravimetric analysis (TGA) that exhibit significant weight loss in the temperature range of 300–410 °C confirming the formation of polymer brushes on the surface with the graft density as high as 0.26–0.27 chains/nm². The improvement in the dispersibility of PMMA‐grafted zinc antimonate nanoparticles was verified using ultraviolet‐visible spectroscopy and transmission electron microscopy. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010