Enzyme mimics of spinel-type CoxNi1−xFe2O4 magnetic nanomaterial for eletroctrocatalytic oxidation of hydrogen peroxide

A series of spinel-type Co_xNi_1−xFe₂O₄ (x = 0, 0.2, 0.4, 0.5, 0.6, 0.8, 1.0) magnetic nanomaterials were solvothermally synthesized as enzyme mimics for the eletroctrocatalytic oxidation of H₂O₂. X-ray diffraction and scanning electron microscope were employed to characterize the composition, structure and morphology of the material. The electrochemical properties of spinel-type Co_xNi_1−xFe₂O₄ with different (Co/Ni) molar ratio toward H₂O₂ oxidation were investigated, and the results demonstrated that Co_0.5Ni_0.5Fe₂O₄ modified carbon paste electrode (Co_0.5Ni_0.5Fe₂O₄/CPE) possessed the best electrocatalytic activity for H₂O₂ oxidation. Under optimum conditions, the calibration curve for H₂O₂ determination on Co_0.5Ni_0.5Fe₂O₄/CPE was linear in a wide range of 1.0 × 10⁻⁸–1.0 × 10⁻³ M with low detection limit of 3.0 × 10⁻⁹ M (S/N = 3). The proposed Co_0.5Ni_0.5Fe₂O₄/CPE was also applied to the determination of H₂O₂ in commercial toothpastes with satisfactory results, indicating that Co_xNi_1−xFe₂O₄ is a promising hydrogen peroxidase mimics for the detection of H₂O₂.     

Crystal Structure of Pseudorhombohedral InFe1−xTixO3+x/2 (x=2/3)

The structure of pseudorhombohedral-type InFe_1−xTi_xO_3−x/2 (x=2/3) was refined by Rietveld profile fitting. The crystal is a commensurate member of a series in a solution range on InFeO₃-In₂Ti₂O₇ including incommensurate structures. The structure with the unit cell of a=5.9188(1), b=10.1112(2), and c=6.3896(1) Å, β=108.018(2)°, and a space group P2₁/a is the alternate stacking of an edge-shared InO₆ octahedral layer and an Fe/Ti-O plane along c^*. Metal sites on the Fe/Ti-O plane are surrounded by four oxygen atoms on the Fe/Ti-O plane and two axial ones. Electric conductivities of the order 10⁻⁴ S/cm were observed for the samples at 1000 K, while the oxide ion transport number is almost zero as no electromotive force was detected by an oxygen concentration cell.     

Structure and magnetic order in the series BixRE1−xFe0.5Mn0.5O3 (RE=La,Nd)

The influence of Bi³⁺ on the structural and magnetic properties of the rare-earth-containing perovskites REFe_0.5Mn_0.5O₃ (RE=La,Nd) was studied, and the limit of bismuth substitution was determined to be x≤0.5 in Bi_xRE_1−xFe_0.5Mn_0.5O_3+δ (RE=La,Nd) at ambient pressure. Crystal structures in both La and Nd series were determined to be GdFeO₃-type Pnma with the exception of the Bi_0.3La_0.7Fe_0.5Mn_0.5O₃ sample, which is monoclinic I2/a in the a⁻b⁻b⁻ tilt scheme. The samples undergo a transition to G-type antiferromagnetic order along with a weak ferromagnetic component, mixed with cluster-glass type behavior. The substitution of bismuth into the lattice results in a drop in T_N relative to the lanthanide end-members. Long range ordering temperatures T_N in the range 240-255 K were observed, with a significantly lower ordered magnetic moment in the case of lanthanum (M∼1.7-1.9 μ_B) than in the case of neodymium (M∼2.1 μ_B).     

Synthesis of layered cathode material Li[CoxMn1−x]O2 from layered double hydroxides precursors

Cathode materials Li[Co_xMn_1−x]O₂ for lithium secondary batteries have been prepared by a new route—precursor method of layered double hydroxides (LDHs). In situ high-temperature X-ray diffraction (HT-XRD) and thermogravimetric analysis coupled with mass spectrometry (TG-MS) were used to monitor the structural transformation during the reaction of CoMn LDHs and LiOH·H₂O: firstly the layered structure of LDHs transformed to an intermediate phase with spinel structure; then the distortion of the structure occurred with the intercalation of Li⁺ into the lattice, resulting in the formation of layered Li[Co_xMn_1−x]O₂ with α-NaFeO₂ structure. Extended X-ray absorption fine structure (EXAFS) data showed that the Co-O bonding length and the coordination number of Co were close to those of Mn in Li[Co_xMn_1−x]O₂, which indicates that the local environments of the transitional metals are rather similar. X-ray photoelectron spectroscopy (XPS) was used to measure the oxidation state of Co and Mn. The influences of Co/Mn ratio on both the structure and electrochemical property of Li[Co_xMn_1−x]O₂ have been investigated by XRD and electrochemical tests. It has been found that the products synthesized by the precursor method demonstrated a rather stable cycling behavior, with a reversible capacity of 122.5 mAh g⁻¹ for the layered material Li[Co_0.80Mn_0.20]O₂.     

LaxSr2−xFeyRu1−yO4±δ: a new family of K2NiF4 type oxides

The phases La_xSr_2−xFe_yRu_1−yO_4±δ (x=0.2-0.8; y=0.6-0.9) have been synthesized by solid-state techniques and yield tetragonal structures with I4/mmm symmetry. The oxygen stoichiometry and high-temperature structures have been examined using diffraction techniques and in situ Mössbauer spectroscopy at temperatures up to ∼600°C. Furthermore, new reduced phases that adopt structures with Immm symmetry have been discovered. Unusual coordination numbers have been determined for the most highly reduced samples with square planar coordination evident for the B site cations. The reduced orthorhombic Immm phases were found to readily reoxidize in air to the tetragonal I4/mmm structure at relatively low temperatures of only ∼500°C.     

Synthesis and electrical conductivity of perovskite-type PrCo1−xMgxO3

Oxides in the system PrCo_1−xMg_xO₃ (x=0.0, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized by citrate technique and characterized by powder X-ray diffraction and scanning electron microscope. All compounds have a cubic perovskite structure (space group ). The maximum ratio of doped Mg in the system PrCo_1−xMg_xO₃ is x=0.2. Further doping leads to the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃. The substitution of Mg for Co improves the performance of PrCoO₃ as compared to the electrical conductivity measured by a four-probe electrical conductivity analyzer in the temperature range from 298 to 1073 K. The substitution of Mg for Co on the B site may be compensated by the formations of Co⁴⁺ and oxygen vacancies. The electrical conductivity of PrCo_1−xMg_xO₃ oxides increases with increasing x in the range of 0.0-0.2. The increase in conductivity becomes considerable at the temperatures ?673 K especially for x?0.1; it reaches a maximum at x=0.2 and 1073 K. From x>0.2 the conductivity of PrCo_1−xMg_xO₃ starts getting lower. This is probably a result of the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃ , which blocks oxygen transport, and association of oxygen vacancies. A change in activation energy for all PrCo_1−xMg_xO₃ compounds (x=0-0.25) was observed, with a higher activation energy above 573 K and a lower activation energy below 573 K. The reasons for such a change are probably due to the change of dominant charge carriers from Co⁴⁺ to Vö in PrCo_1−xMg_xO₃ oxides and a phase transition mainly starting at 573 K.     

The Crystal Chemistry of Lithium in the Alluaudite Structure: A Study of the (Na1−xLix)CdIn2(PO4)3 Solid Solution (x=0 to 1)

Several compounds of the (Na_1−xLi_x)CdIn₂(PO₄)₃ solid solution were synthesized by a solid-state reaction in air, and pure alluaudite-like compounds were obtained for x=0.00, 0.25, and 0.50. X-ray Rietveld refinements indicate the occurrence of Cd²⁺ in the M(1) site, and of In³⁺ in the M(2) site of the alluaudite structure. This non-disordered cationic distribution is confirmed by the sharpness of the infrared absorption bands. The distribution of Na⁺ and Li⁺ on the A(1) and A(2)′ crystallographic sites cannot be accurately assessed by the Rietvled method, probably because the electronic densities involved in the Na⁺→Li⁺ substitution are very small. A comparison with the synthetic alluaudite-like compounds, (Na_1−xLi_x)MnFe₂(PO₄)₃, indicates the influence of the cations occupying the M(1) and M(2) sites on the coordination polyhedra morphologies of the A(1) and A(2)′ crystallographic sites.     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.     

Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Charge compensation and oxidation in NaxCoO2−δ and LixCoO2−δ studied by XANES

A comparative study on the oxidation and charge compensation in the A_xCoO_2−δ systems, A=Na (x=0.75, 0.47, 0.36, 0.12) and Li (x=1, 0.49, 0.05), using X-ray absorption spectroscopy at O 1s and Co 2p edges is reported. Both the O 1s and Co 2p XANES results show that upon removal of alkali metal from A_xCoO_2−δ the valence of cobalt increases more in Li_xCoO_2−δ than in Na_xCoO_2−δ. In addition, the data of O 1s XANES indicate that charge compensation by oxygen is more pronounced in Na_xCoO_2−δ than in Li_xCoO_2−δ.     

Synthesis, Characterization and Humidity Sensitive Properties of Nanocrystalline LaCoxFe1-xO3

The nanocrystalline LaCo_xFe_1-xO₃ with different concentrations of Co was prepared by polyethylene glycol (PEG) sol-gel method and characterized by differential thermal analysis and thermal gravimetric analysis (DTA-TGA), X-ray diffraction (XRD), and scanning electron microscope (SEM). It was found that the crystal structure of perovskite-type could be obtained at 600 °C, and the concentration of Co had significant effects on the solid-state reaction and the average particle size of the obtained nanocrystals. Furthermore, the humidity-sensitive properties of nanocrystalline LaCo_xFe_1-xO₃ were investigated, and it was found that LaCo_0.3Fe_0.7O₃ exhibited higher sensitivity to humidity compared with other samples. The addition of Na₂CO₃ improved the humidity-sensitive properties of this sample, and made its response to humidity good in the whole humidity range of 11%-95% relative humidity (RH).     

Synthesis, optical properties and electronic structures of polyoxometalates K3P(Mo1−xWx)12O40 (0?x?1)

Various compositions of solid solutions K₃P(Mo_1−xW_x)₁₂O₄₀ (0?x?1) were prepared using two solid state synthetic routes. The crystallite size was determined by linewidth refinements of X-ray diffraction patterns using the Warren-Averbach method, and the grain size distribution by laser scattering experiments. Optical properties were determined by diffuse reflectance measurements in the UV-visible range. The optical gap E_g was found to increase exponentially from ∼2.5 to ∼3.30 eV with increasing x, and is systematically shifted to a higher energy when the grain size decreases. The relation between E_g and x was analyzed by calculating the HOMO-LUMO gaps of the [P(Mo_1−xW_x)₁₂O₄₀]³⁻ anions on the basis of tight-binding electronic structure calculations.     

Series of compositions Bi2(M′xM1−x)4O9 (M′, M=Al, Ga, Fe; 0≤x≤1) with mullite-type crystal structure: Synthesis, characterization and O/O exchange experiment

Series of compositions Bi₂(M′_xM_1−x)₄O₉ with x=0.0, 0.1,…, 1.0 and M′/M=Ga/Al, Fe/Al and Fe/Ga were synthesized by dissolving appropriate amounts of corresponding metal nitrate hydrates in glycerine, followed by gelation, calcination and final heating at 800 °C for 24 h. The new compositions with M′/M=Ga/Al form solid-solution series, which are isotypes to the two other series M′/M=Fe/Al and Fe/Ga. The XRD data analysis yielded in all cases a linear dependence of the lattice parameters related on x. Rietveld structure refinements of the XRD patterns of the new compounds, Bi₂(Ga_xAl_1−x)₄O₉ reveal a preferential occupation of Ga in tetrahedral site (4 h). The IR absorption spectra measured between 50 and 4000 cm⁻¹ of all systems show systematic shifts in peak positions related to the degree of substitution. Samples treated in ¹⁸O₂ atmosphere (16 h at 800 °C, 200 mbar, 95% ¹⁸O₂) for ¹⁸O/¹⁶O isotope exchange experiments show a well-separated IR absorption peak related to the M-¹⁸O_c-M vibration, where O_c denotes the common oxygen of two tetrahedral type MO₄ units. The intensity ratio of M-¹⁸O_c/M-¹⁶O_c IR absorption peaks and the average crystal sizes were used to estimate the tracer diffusion coefficients of polycrystalline Bi₂Al₄O₉ (D=2×10⁻²² m²s⁻¹), Bi₂Fe₄O₉ (D=5×10⁻²¹ m²s⁻¹), Bi₂(Ga/Al)₄O₉ (D=2×10⁻²¹ m²s⁻¹) and Bi₂Ga₄O₉ (D=2×10⁻²⁰ m²s⁻¹).     

Structure and conductivity of strontium-doped cerium orthovanadates Ce1−xSrxVO4 (0≤x≤0.175)

A-site substituted cerium orthovanadates, Ce_1−xSr_xVO₄, were synthesised by solid-state reactions. It was found that the solid solution limit in Ce_1−xSr_xVO₄ is at x=0.175. The crystal structure was analysed by X-ray diffraction and it exhibits a tetragonal zircon structure of space group I4₁/amd (1 4 1) with a=7.3670 (3) and c=6.4894 (1) Å for Ce_0.825Sr_0.175VO₄. The UV-vis absorption spectra indicated that the compounds have band gaps at room temperature in the range 4.5-4.6 eV. Conductivity measurements were performed for the first time up to the strontium solid solution limit in air and in dry 5% H₂/Ar with conductivity values at 600 °C ranging from 0.3 to 30 mS cm⁻¹ in air to 30-45 mS cm⁻¹ in reduced atmosphere. Sample Ce_0.825Sr_0.175VO₄ is redox stable at a temperature below 600 °C although the conductivity is not high enough to be used as an electrode for solid oxide fuel cells.     

p(O2)-stability of LaFe1−xNixO3−δ solid solutions at 1100 °C

LaFe_1−xNi_xO_3−δ (x=0.1−1.0) perovskites were synthesized via citrate route. The p(O₂)-stability of the perovskite phases LaFe_1−xNi_xO_3−δ has been evaluated at 1100 °C based on the results of XRD analysis of powder samples annealed at various p(O₂) and quenched to room temperature. The isothermal LaFeO_3−δ-“LaNiO_3−δ” cross-section of the phase diagram of the La-Fe-Ni-O system has been proposed in the range of oxygen partial pressure −15<log p(O₂)/atm≤0.68. The unit cell parameters of orthorhombic perovskites O-LaFe_1−xNi_xO_3−δ increase with decrease in p(O₂) at fixed composition x. This behavior is explained on the basis of size factor. The decomposition temperatures of rhombohedral phases R-LaFe_1−xNi_xO_3−δ for x=0.7, 0.8, 0.9 and 1.0 in air were determined as 1137, 1086, 1060 and 995 °C, respectively.     

Crystal chemistry of M[PO2(OH)2]2·2H2O compounds (M=Mg, Mn, Fe, Co, Ni, Zn, Cd): Structural investigation of the Ni, Zn and Cd salts

The compounds M[PO₂(OH)₂]₂·2H₂O (M=Mg, Mn, Fe, Co, Ni, Zn, Cd) were prepared from super-saturated aqueous solutions at room temperature. Single-crystal X-ray structure investigations of members with M=Ni, Zn, Cd were performed at 295 and 120 K. The space-group symmetry is P2₁/n, Z=2. The unit-cell parameters are at 295/120 K for M=Ni: a=7.240(2)/7.202(2), b=9.794(2)/9.799(2), c=5.313(1)/5.285(1) Å, β=94.81(1)/94.38(1)°, V=375.4/371.9 Å³; M=Zn: a=7.263(2)/7.221(2), b=9.893(2)/9.899(3), c=5.328(1)/5.296(2) Å, β=94.79(1)/94.31(2)°, V=381.5/377.5 Å³; M=Cd: a=7.356(2)/7.319(2), b=10.416(2)/10.423(3), c=5.407(1)/5.371(2) Å, β=93.85(1)/93.30(2)°, V=413.4/409.1 Å³. Layers of corner-shared MO₆ octahedra and phosphate tetrahedra are linked by three of the four crystallographically different hydrogen bonds. The fourth hydrogen bond (located within the layer) is worth mentioning because of the short O_h?O bond distance of 2.57-2.61 Å at room temperature (2.56-2.57 Å at 120 K); only for M=Mg it is increased to 2.65 Å. Any marked temperature-dependent variation of the unit-cell dimension is observed only vertical to the layers. The analysis of the infrared (IR) spectroscopy data evidences that the internal PO₄ vibrations are insensitive to the size and the electronic configuration of the M²⁺ ions. The slight strengthening of the intra-molecular P-O bonds in the Mg salt is caused by the more ionic character of the Mg-O bonds. All IR spectra exhibit the characteristic “ABC trio” for acidic salts: 2900-3180 cm⁻¹ (A band), 2000-2450 cm⁻¹ (B band) and 1550-1750 cm⁻¹ (C band). Both the frequency and the intensity of the A band provide an evidence that the PO₂(OH)₂ groups in M[PO₂(OH)₂]₂·2H₂O compounds form weaker hydrogen bonds as compared with other acidic salts with comparable O?O bond distances of about 2.60 Å. The observed shift of the O-H stretching vibrations of the water molecule in the order M=Mg>Mn≈Fe≈Co>Ni>Zn≈Cd has been discussed with respect to the influence of both the character and the strength of M↔H₂O interactions.     

Sol-gel synthesized semiconducting LaCo0.8Fe0.2O3-based powder for thick film NH3 gas sensor

Perovskite type LaCo_xFe_1−xO₃ nanoparticles was synthesized by a sol-gel citrate method. The structural, electrical and sensing characteristics of the LaCo_xFe_1−xO₃ system were investigated. The structural characteristics were performed by using X-ray diffraction (XRD) and transmission electron microscopy (TEM) to examine the phase and morphology of the resultant powder. The XRD pattern shows nanocrystalline solid solution of LaCo_xFe_1−xO₃ with perovskite phase. Electrical properties of synthesized nanoparticles are studied by DC conductivity measurement. The sensor shows high response towards ammonia gas in spite of other reducing gases when x = 0.8. The effect of 0.3 wt.% Pd-doped LaCo_0.8Fe_0.2O₃ on the response and a recovery time was also addressed.     

Crystal structure and magnetic properties of high-oxygen pressure annealed Sr1−xLaxCo0.5Fe0.5O3−δ (0?x?0.5)

Structural and magnetic studies are presented for the perovskite type Sr_1−xLa_xCo_0.5Fe_0.5O_3−δ (0?x?0.5) materials annealed under moderately high-oxygen pressures of ∼200 atm. A detailed analysis of the room temperature neutron time-of-flight diffraction data reveals that the crystal structure of the sample SrCo_0.5Fe_0.5O_2.89(1), previously described as vacancy-disordered cubic, is similar to the formerly reported, oxygen-vacancy ordered Sr₈Fe₈O₂₃ compound, i.e. Sr₈Co₄Fe₄O₂₃ is tetragonal with the I4/mmm symmetry. With an increase of the La content the studied materials become nearly oxygen stoichiometric and a lowering of the crystal symmetry is observed from cubic (x=0.1 and 0.2) to tetragonal I4/mcm (x=0.3 and 0.4), and finally to monoclinic I12/c1 (x=0.5). Low-temperature structural and magnetic measurements show a ferromagnetic ordering with the maximum Curie temperature near 290 K at x=0.2.     

Synthesis, crystal structure, and density of (W1−xAlx)C

A new solid solution system of Al in WC, with the stoichiometry of (W_1−xAl_x)C (x=0.10, 0.25, 0.50, 0.75, 0.86), has been synthesized by a solid-state reaction between W_1−xAl_x alloys and carbon at around 1673 K in vacuum. Environment scanning electron microscope, energy-dispersive analysis of X-ray, X-ray photoelectron spectroscopy, and inductively coupled plasma analyses are used to certify the formation of the products. The mechanism of the solid-state reaction is also discussed. (W_1−xAl_x)C is identified to crystallize in the hexagonal space group P6m2 (No. 187) and belongs to the WC structure type. The atoms of W and Al occupy the same lattice site (1a site) in the cell of (W_1−xAl_x)C. The cell parameters for each specimen in the phase of W-Al-C are quite close to that of WC, while their densities are far lower than that of WC.     

A novel route to synthesize cubic ZrW2−xMoxO8 (x=0-1.3) solid solutions and their negative thermal expansion properties

Cubic ZrW_2−xMo_xO₈ (c-ZrW_2−xMo_xO₈) (x=0-1.3) solid solutions were prepared by a novel polymorphous precursor transition route. X-ray diffraction (XRD) analysis reveals that the solid solutions are single phase with α- and β-ZrW₂O₈ structure for 0?x?0.8 and 0.9?x?1.3, respectively. The optimum synthesis conditions of ZrWMoO₈ are obtained from differential scanning calorimetry-thermal gravimetric analysis (DSC-TGA), XRD and mass loss-temperature/time curves. Following the above experience, the stoichiometric solid solutions of c-ZrW_2−xMo_xO₈ (x=0-1) are obtained within 1 wt% of mass loss. The relationships of lattice parameters (a), phase transition temperatures (T_c) and instantaneous coefficients of thermal expansion (α_i) against the content x of Mo are discussed based on the variation of order degree parameters of ZrW_2−xMo_xO₈.