The chemisorption of CO,CO2, C2H2, C2H4, H2 and NH3 on the clean Fe(100) and (111) crystal surfaces

The chemisorption of small molecules (CO, CO₂, C₂H₂, C₂H₄, H₂ and NH₃) has been studied on the clean Fe(110) and (111) crystal faces by low-energy electron diffraction (LEED) and thermal desorption. C₂H₄ and C₂H₂ yield the same sequence of surface structures that change with temperature and crystal orientation. CO and CO₂ chemisorption similarly results in the formation of the same types of surface structures that change with surface temperature and crystal orientation. Ammonia forms several ordered surface structures on both iron crystal faces. All of the molecules decompose as a function of temperature on the iron surfaces as indicated by the Auger and thermal desorption spectra.     

LEED and thermal desorption studies of small molecules (H2, O2, CO,CO2, NO,C2H4, C2H2 and C) chemisorbed on the stepped rhodium (755) and (331) surfaces

The chemisorption of H₂, O₂, CO, CO₂, NO, C₂H₂, C₂H₄ and C has been studied on the clean stepped Rh(755) and (331) surfaces. Low energy electron diffraction (LEED), Auger electron spectroscopy (AES) and thermal desorption spectroscopy (TDS) were used to determine the size and orientation of the unit cells, desorption temperatures and decomposition characteristics for each adsorbate. All of the molecules studied readily chemisorbed on both stepped surfaces and several ordered surface structures were observed. The LEED patterns seen on the (755) surface were due to the formation of surface structures on the (111) terraces, while on the (331) surface the step periodicity played an important role in the determination of the unit cells of the observed structures. When heated in O₂ or C₂H₄ the (331) surface was more stable than the (755) surface which readily formed (111) and (100) facets. In the CO and CO₂ TDS spectra a peak due to dissociated CO was observed on both surfaces. NO adsorption was dissociative at low exposures and associative at high exposures. C₂H₄ and C₂H₂ had similar adsorption and desorption properties and it is likely that the same adsorbed species was formed by both molecules.     

LEED,AES and thermal desorption studies of chemisorbed Hydrogen and hydrocarbons (C2H2, C2H4, C6H6, C6H12) on the (111) and stepped [6(111) × (100)] iridium crystal surfaces; comparison with platinum

The adsorption of hydrogen, ethylene, acetylene, cyclohexane and benzene was studied on both the (111) and stepped [6(111) × (100)] crystal surfaces of iridium. The techniques used were low energy electron diffraction, Auger electron spectroscopy, and thermal desorption mass spectrometry. At 30°C, acetylene, ethylene and benzene are adsorbed with a sticking probability near unity. The sticking probability of cyclohexane is less than 0.1 on both surfaces. Heating the (111) surface above 800°C, in the presence of the hydrocarbons, results in the formation of an ordered carbonaceous overlayer with a diffraction pattern corresponding to a (9 × 9) surface structure. No indication for ordering of the carbonaceous residue was found on the stepped iridium surface in these experimental conditions. The hydrocarbon molecules form only poorly ordered surface structures on both iridium surfaces when the adsorption is carried out at 30°C. Benzene is the only gas that can be desorbed from the surfaces in large amounts by heating. Ethylene remains largely on the surface, only a few percent is removed by heating while acetylene and cyclohexane cannot be desorbed at all. When adsorption is carried out at 30°C and the crystal is subsequently flashed to high temperature, hydrogen is liberated from the surface. The hydrogen desorption spectra from the iridium surfaces exposed to C₂H₄, C₂H₂, or C₆H₆ exhibit two hydrogen desorption peaks, one around 200°C and the second around 350°C. The temperatures where these peaks appear vary slightly with the type of hydrocarbon. The relative intensities of these two peaks depend strongly on the surface used. Arguments are presented that decomposition of the hydrocarbon molecules (C-H bond breaking nd possibly also C-C bond breaking) occurs easier on the stepped iridium surface than on the (111) surface. Hydrogen is desorbed at a higher temperature from an iridium surface possessing a high density of surface imperfections than from a perfect iridium (111) surface. The results are compared with those obtained previously on similar crystal surfaces of platinum. It appears that C-H bond breaking occurs more easily on iridium than on platinum.     

Adsorption studies on a stepped Pt(111) surface: O2, CO,C2H4, C2N2

A comparative study of the adsorption of several gases on a Pt(S)-[9(111) × (111)] surface was performed using LEED, Auger spectroscopy, flash desorption mass spectrometry and work function changes as surface sensitive techniques. Adsorption was found to be generally less ordered on the stepped surface than on the corresponding flat surface with the exception of the oxygen, where r well ordered overlayer in registry over many terraces was found. Absolute coverages were determined from flash desorption experiments for O₂, CO and C₂N₂. Similar values were obtained as on flat Pt surfaces. Two different surface species seem to be formed upon adsorption of C₂H₄ depending on the adsorption temperature. Contrary to reports from Pt(111) surfaces conversion between the two surface species is heavily restricted on the stepped surface. Work function changes revealed nonlinear adsorbate effects where the adsorbate is electronegative with respect to the substrate. Various adsorption models are discussed in the light of complementary experimental evidence. The results of this study are compared with data available from flat Pt surfaces and possible influences of steps are discussed. No general trends, however, emerge from this comparison and it seems that eventual influences of steps have to be considered individually for every adsorbate.     

The chemisorption of O2, CO,D2 and C2H4 over epitaxially grown rhenium crystalline films

The adsorption and desorption of oxygen, carbon monoxide, deuterium and ethylene has been studied over rhenium films using thermal desorption spectroscopy, low energy electron diffraction and Auger electron spectroscopy. The films, obtained by evaporating rhenium onto a platinum (111) single crystal, grow over the substrate forming (0001) basal plane rhenium surfaces. Oxygen chemisorbs on this film, forming an ordered structure, consisting of three (2 × 1) overlayer domains and giving a saturation coverage of half a monolayer of atomic oxygen. CO chemisorption is mainly molecular, although some dissociation occurs at temperatures above about 700 K. A complicated LEED pattern is obtained when saturating the surface at 150 K with CO, but it changes to a (2 × 2) or (2 × 1) structure upon heating. Also, CO chemisorption can be modified by predissociated CO or preadsorbed oxygen on the rhenium surface. Deuterium desorbs in three peaks, starting at temperatures as low as 150 K. Ethylene desorbs partially intact at around 250 K, the rest decomposing and yielding hydrogen, that appears as two main peaks at 357 K and 460 K during thermal desorption. We conclude that epitaxially grown films may be an alternative to single crystals for studying chemisorption over well ordered surfaces.     

Adsorption of carbon monoxide,oxygen, hydrogen,nitrogen, ethylene and benzene on an iridium (110) surface; Correlation with other iridium crystal faces

The interaction of CO, O₂, H₂, N₂, C₂H₄ and C₆H₆ with an Ir(110) surface has been studied using LEED, Auger electron spectroscopy and flash desorption mass spectroscopy. Adsorption of oxygen at 30°C produces a (1× 2) structure, while a c(2 × 2) structure is formed at 400°C. Two peaks have been detected in the thermal desorption spectrum of oxygen following adsorption at 30°C. The heat of adsorption of hydrogen is slightly higher on Ir(110) than on Ir(111). Adsorption of carbon monoxide at 30°C produces a (2 × 1) surface structure. The main CO desorption peak is found around 230, while two other desorption peaks are observed around 340 and 160°C. At exposures between 250 and 500°C carbon monoxide adsorption yields a c(2 × 2) structure and a desorption peak around 600°C. Carbon monoxide is adsorbed on an Ir(110) surface partly covered with oxygen or carbon in a new binding state with a significantly higher desorption temperature than on the clean surface. Adsorption of nitrogen could not be detected on either clean or on carbon covered Ir(110) surfaces. The hydrocarbon molecules do not form ordered surface structures on Ir(110). The thermal desorption spectra obtained after adsorption of C₆H₆ or C₂H₄ are similar to those reported previously for Ir(111) consisting mostly of hydrogen. Heating the (110) surface above 700°C in the presence of C₆H₆ or C₂H₄ results in the formation of an ordered carbonaceous overlayer with (1 × 1) structure. The results are compared with those obtained previously on the Ir(111) and Ir(755) or stepped [6(111) × (100)] surfaces. The CO adsorption results are discussed in relation to data on similar surfaces of other Group VIII metals.     

Auger spectra of CO,C2H4, C2N2 and C6H6 adsorbed on Pt(111)

Electron excited carbon KVV Auger spectra of CO, C₂H₄, C₂N₂ and C₆H₆ adsorbed on Pt(111) are compared. By estimating the effective Coulomb interaction between the final-state holes it is possible to associate some features with transitions observed in free molecule spectra, but others must involve at least one electron with energy within the conduction band of the metal. Such “cross-transitions” are associated with strong 2π* character of filled states in the presence of a core hole in molecules such as CO.     

The influence of structural defects on the adsorption of simple molecules (H2, C2H2, C2H4, C2H6, CO,NO) on rhenium single crystals

Using Thermal Programmed Desorption (TPD), Low Energy Electron Diffraction (LEED) and Auger Electron Spectroscopy (AES) we have studied the adsorption of hydrogen-containing molecules (H₂, C₂H₂, C₂H₄, C₂H₆) and oxygen-containing molecules (CO and NO) on two vicinal planes of the Re(0001) surface. The two surfaces are designated thus: ReS ¦14(0001)(101̄1)¦, ReS |6(0001)(167̄1) | . The structural defects have little effect on the adsorption of hydrogen and the hydrocarbons. They are more influential in the case of the oxygen-containing molecules. This is particularly true for CO; on the kink sites the CO molecules can completely dissociate whereas only a partial dissociation is possible on the steps. These results should be viewed in relation to the strong bond energy between carbon and oxygen in a CO molecule of 256 kcal/mole and the great affinity of oxygen for rhenium; E_Re?O = 127 kcal/mole.     

Interaction of O2, CO2, CO,C2H4 and C2H4O with Ag(110)

The interaction of O₂, CO₂, CO, C₂H₄ AND C₂H₄O with Ag(110) has been studied by low energy electron diffraction (LEED), temperature programmed desorption (TPD) and electron energy loss spectroscopy (EELS). For adsorbed oxygen the EELS and TPD signals are measured as a function of coverage (θ). Up to θ = 0.25 the EELS signal is proportional to coverage; above 0.25 evidence is found for dipole-dipole interaction as the EELS signal is no longer proportional to coverage. The TPD signal is not directly proportional to the oxygen coverage, which is explained by diffusion of part of the adsorbed oxygen into the bulk. Oxygen has been adsorbed both at pressures of less than 10^-4 Pa in an ultrahigh vacuum chamber and at pressures up to 10³ Pa in a preparation chamber. After desorption at 10³ Pa a new type of weakly bound subsurface oxygen is identified, which can be transferred to the surface by heating the crystal to 470 K. CO₂ is not adsorbed as such on clean silver at 300 K. However, it is adsorbed in the form of a carbonate ion if the surface is first exposed to oxygen. If the crystal is heated this complex decomposes into O_ad and CO₂ with an activation energy of 27 kcal/mol(1 kcal = 4.187 kJ). Up to an oxygen coverage of 0.25 one CO₂ molecule is adsorbed per two oxygen atoms on the surface. At higher oxygen coverages the amount of CO₂ adsorbed becomes smaller. CO readily reacts with O_ad at room temperature to form CO₂. This reaction has been used to measure the number of O atoms present on the surface at 300 K relative to the amount of CO₂ that is adsorbed at 300 K by the formation of a carbonate ion. Weakly bound subsurface oxygen does not react with CO at 300 K. Adsorption of C₂H₄O at 110 K is promoted by the presence of atomic oxygen. The activation energy for desorption of C₂H₄O from clean silver is ～ 9 kcal/mol, whereas on the oxygen-precovered surface two states are found with activation energies of 8.5 and 12.5 kcal/mol. The results are discussed in terms of the mechanism of ethylene epoxidation over unpromoted and unmoderated silver.     

AP/(N2 + C2H2 + C2H4) gaseous fuel diffusion flame studies

Counterflow diffusion flame experiments and modeling results are presented for a fuel mixture consisting of N₂, C₂H₂, and C₂H₄ flowing against decomposition products from a solid AP pellet. The flame zone simulates the diffusion flame structure that is expected to exist between reaction products from AP crystals and a hydrocarbon binder. Quantitative species and temperature profiles have been measured for one strain rate, given by a separation of 5 mm, between the fuel exit and the AP surface. Species measured include C₂H₂, C₂H₄, N₂, CN, NH, OH, CH, C₂, NO, NO₂, O₂, CO₂, H₂, CO, HCl, H₂O, and soot volume fraction. Temperature was measured using a combination of a thermocouple at the fuel exit and other selected locations, spontaneous Raman scattering measurements throughout the flame, NO vibrational populations, and OH rotational population distributions. The burning rate of the AP was also measured for this flame’s strain rate. The measured eighteen scalars are compared with predictions from a detailed gas-phase kinetics model consisting of 105 species and 660 reactions. Model predictions are found to be in good agreement with experiment and illustrate the type of kinetic features that may be expected to occur in propellants when AP particles burn with the decomposition products of a polymeric binder.     

Carbon K-shell excitation of C2H2, C2H4, C2H6 and C6H6 by 2.5 keV electron impact

Energy loss spectra of 2.5 keV electrons in the region of the carbon K-edge in C₂H₂, C₂H₄, C₂H₆ and C₆H₆ are report     

Exploring the mechanism of NO–C2H4 reactions on the surface of stepped Pt(3 3 2)

Fourier transform infra red reflection–absorption spectroscopy (FTIR-RAS), thermal desorption spectroscopy (TDS), and auger electron spectroscopy (AES), were employed to explore the mechanism of NO reduction in the presence of C₂H₄ on the surface of stepped Pt(3 3 2). Both NO–Pt and C₂H₄–Pt interactions are enhanced when NO and C₂H₄ are co-adsorbed on Pt(3 3 2). As a result, C₂H₄ is dissociated at surface temperatures as low as 150 K, and the N–O stretch band is weakened. The presence of post-exposed C₂H₄ leads NO desorption from steps to decrease significantly, but the same effect on NO desorption from terraces becomes appreciable only at higher post-exposures of C₂H₄, e.g., 0.6 L and 1.2 L, and proceeds to a much slighter extent. Auger spectra indicate that as a result of the reaction with O from NO dissociation, the amount of surface C species is greatly reduced when NO is post-exposed to a C₂H₄ adlayer. It is concluded that reduction of NO in the presence of C₂H₄ proceeds very effectively on the surface of the Pt(3 3 2), through a mechanism of NO dissociation and subsequent O removal. Following this mechanism, the significant dissociation of adsorbed NO molecules on steps at surface temperatures below 400 K, and subsequent rapid reaction between the resultant O and C-related species, accounts for the considerable amount of N₂ desorption at temperatures below 400 K.     

Adsorption-desorption studies using ESD of CCl2F2, C2H2F2 and C2F6 on tungsten

The behavior of the desorbing F⁺ ion current from electron bombarded CCl₂F₂, C₂H₂F₂ and C₂F₆ adsorbed on tungsten has been used to investigate the processes of adsorption and desorption of these gases. For tungsten near room temperature, measurements of the F⁺ ion current as a function of electron bombardment time indicated very similar or even identical F⁺-yielding adsorbed species resulting from adsorption of either CCl₂F₂ or C₂H₂F₂ and widely different species from C₂F₆. Cl⁺ ions were also observed to desorb from CCl₂F₂ ad-layers. The behavior of the Cl⁺ ion current with time during electron bombardment indicated electronic conversion between adsorbed binding modes. Complementary investigations on the interaction of CCl₂F₂, C₂H₂F₂ and C₂F₆ with tungsten were carried out by thermal desorption experiments in which the F⁺ ion signal was used to observe the coverage decrease of the F⁺-yielding species. The experiments were performed at tungsten temperatures in the 1200–1600 K range. It was concluded that the F⁺-yielding adsorbed species from CCl₂F₂ and C₂H₂F₂ were strongly bound to the tungsten surface. The F⁺-yielding species from C₂F₆ were found to be weakly bound. From a comparison of the ESD and thermal desorption results, the possibility of dissociative adsorption as well as the nature of the adsorbed species is discussed.     

Low-energy electron diffraction,Auger electron spectroscopy,and thermal desorption studies of chemisorbed CO and O2 on the (111) and stepped [6(111) × (100)] iridium surfaces

The adsorption of CO, O₂, and H₂O was studied on both the (111) and [6(111) × (100)] crystal faces of iridium. The techniques used were LEED, AES, and thermal desorption. Marked differences were found in surface structures and heats of adsorption on these crystal faces. Oxygen is adsorbed in a single bonding state on the (111) face. On the stepped iridium surface an additional bonding state with a higher heat of adsorption was detected which can be attributed to oxygen adsorbed at steps. On both (111) and stepped iridium crystal faces the adsorption of oxygen at room temperature produced a (2 × 1) surface structure. Two surface structures were found for CO adsorbed on Ir(111); a (√3 × √3)R30° at an exposure of 1.5–2.5 L and a (2√3 × 2√3)R30° at higher coverage. No indication for ordering of adsorbed CO was found on the Ir(S)-[6(111) × (100)] surface. No significant differences in thermal desorption spectra of CO were found on these two faces. H₂O is not adsorbed at 300 K on either iridium crystal face. The reaction of CO with O₂ was studied on Ir(111) and the results are discussed. The influence of steps on the adsorption behaviour of CO and O₂ on iridium and the correlation with the results found previously on the same platinum crystal faces are discussed.     

The adsorption of CO,O2, and H2 on Pt(100)-(5×20)

The adsorption/desorption characteristics of CO, O₂, and H₂ on the Pt(100)-(5 × 20) surface were examined using flash desorption spectroscopy. Subsequent to adsorption at 300 K, CO desorbed from the (5×20) surface in three peaks with binding energies of 28, 31.6 and 33 kcal gmol^?1. These states formed differently from those following adsorption on the Pt(100)-(1 × 1) surface, suggesting structural effects on adsorption. Oxygen could be readily adsorbed on the (5×20) surface at temperatures above 500 K and high O₂ fluxes up to coverages of $\text{2}\text{3}$ of a monolayer with a net sticking probability to ssaturation of ? 10^?3. Oxygen adsorption reconstructed the (5 × 20) surface, and several ordered LEED patterns were observed. Upon heating, oxygen desorbed from the surface in two peaks at 676 and 709 K; the lower temperature peak exhibited atrractive lateral interactions evidenced by autocatalytic desorption kinetics. Hydrogen was also found to reconstruct the (5 × 20) surface to the (1 × 1) structure, provided adsorption was performed at 200 K. For all three species, CO, O₂, and H₂, the surface returned to the (5 × 20) structure only after the adsorbates were completely desorbed from the surface.     

Coadsorption of NO and other small gases (H2 and CO) on polycrystalline rhodium surface

The coadsorption of NO and other small gases (H₂ and CO) on a polycrystalline Rh filament has been studied by thermal desorption mass spectroscopy, using ¹⁵NO. The sample was exposed to a mixture of nitric oxide and other gases with various concentrations of ¹⁵NO at room temperature. It is indicated that NO, CO and H₂ coadsorbs on the rhodium surface, and NO desorbs as N₂ and O₂. NO is adsorbed mainly in the dissociation at lower coverage and molecular adsorption becomes dominant at higher coverage. But the amount of desorbed O₂ was very small. The chemisorption of CO is affected by the chemisorbed NO. Thermal desorption of hydrogen is detected when the value of P_15NO/P_CO is very small. The hydrogen adsorbed on the rhodium surface is replaced by NO with a longer exposure time.     

Thermal evolution of C2H2 and C4H2 on Pd(111) studied by high-resolution electron energy loss spectroscopy

The thermal evolution of acetylene and ethylene on a palladium (111) surface has been studied by high-resolution electron energy loss spectroscopy in the temperature range 150K–500K. Formation of ethylidyne ( CCH₃) near room temperature is important for both molecules, whereas CH is the major surfaces hydrocarbon species formed at high temperatures.     

Geometric shielding corrections for total cross section calculations of electron scattering by CH4, C2H6, C2H3F3, C2H4, C2F4, C2Cl4 and C2Cl2F2 from 30–5000?eV

To quantify the changes in the geometric shielding effect in a molecule as the incident electron energy varies, an empirical fraction, which represents the total cross section contributions of shielded atoms in a molecule at different energies, is presented. Using this empirical fraction, the total cross sections for electron scattering by CH₄, C₂H₆, C₂H₃F₃, C₂H₄, C₂F₄, C₂Cl₄ and C₂Cl₂F₂ are calculated over a wide energy range from 30 to 5000 eV by the additivity rule model at the Hartree-Fock level. The quantitative total cross sections are compared with those obtained by experiment and other theories where available. Good agreement is attained above 100 eV.     

C2H4在Ru(1010)表面吸附与分解的研究

用X射线电子能谱(XPS)、热脱附谱(TDS)和紫外光电子能谱(UPS)方法研究了乙烯(C_{2H4)在Ru(1010)表面的吸附,在低温下(200K以下)乙稀(C2Ｈ4})可以在Ru(1010)表面上以分子状态稳定吸附,在200K以上乙烯(C₂H ₄)则发生了脱氢分解反应.TDS结果表明乙烯(C₂H₄)分 解后的主要产物为乙炔(C< 关键词： 乙烯 钌(1010)表面 吸附与分解     

Interaction of CO,CO2 and O2 with nonpolar,stepped and polar Zn surfaces of ZnO

The nonpolar (10$\text{1}$0), stepped (40$\text{4}$1) and (50$\text{5}$1), and the polar (0001) surfaces of ZnO were prepared. Stable unreconstructed nonpolar and stepped surfaces were obtained. LEED analyses showed that the step height and the step width of the stepped surfaces were similar to the theoretical values. The polar surface showed a 1 × 1 LEED pattern of six-fold symmetry after annealing at 500°C, and evidence of a more complicated pattern at 300–400°C. Temperature programmed desorption of CO resulted in the desorption of CO from the stepped and the polar surfaces. However, desorption of CO₂ was observed from the stoichiometric nonpolar surface, and no desorption from the reduced nonpolar surface. CO₂ was also observed by interacting CO with all surfaces at elevated temperatures. A total of four temperature programmed desorption peaks of CO₂, α, β, γ, and δ were observed. The α and β peaks were observed on the nonpolar and the stepped surfaces, and the γ peak was observed on the polar surface. The α peak was assigned to adsorption on a surface ZnO pair, and the β peak was assigned to adsorption on an anion vacancy or a step. While adsorbed water enhanced the β, preadsorbed methanol reduced it. O₂ adsorption was similar on the nonpolar and the stepped surfaces, but was weak on the polar surface.