A new phase in the system lithium-aluminum: Characterization of orthorhombic Li2Al

Investigation of the Li rich part of the binary Li-Al system revealed the existence of a new phase, orthorhombic Li₂Al, which is isostructural to Li₂Ga and Li₂In. The crystal structure was determined from single crystal X-ray diffraction data (Cmcm, a=4.658(2) Å, b=9.767(4) Å, c=4.490(2) Å, Z=4). Refinement of atomic position site occupancies yielded a composition Li_1.92Al_1.08 (64 at% Li) indicating a small homogeneity range, Li_2−xAl_1+x. Li₂Al is the peritectic decomposition product of the stoichiometric compound Li₉Al₄, which is stable below 270±2 °C. Li₂Al itself decomposes peritectically to Li₃Al₂ and Li rich melt at 335±2 °C. The discovery of Li₂Al (Li_2−xAl_1+x) settles a long standing inconsistency in the Li-Al phase diagram which was based on the assumption that Li₉Al₄ possesses a high temperature modification.     

Synthesis, crystal structure and thermal behavior of Sr3B2SiO8 borosilicate

Single crystals of Sr₃B₂SiO₈ were obtained by solid-state reaction of stoichiometric mixture at 1200 °C. The crystal structure of the compound has been solved by direct methods and refined to R1=0.064 (wR=0.133). It is orthorhombic, Pnma, a=12.361(4), b=3.927(1), c=5.419(1) Å, V=263.05(11) Å³. The structure contains zigzag pseudo-chains running along the b axis and built up from corner sharing (Si,B)−O polyhedra. Boron and silicon are statistically distributed over one site with their coordination strongly disordered. Sr atoms are located between the chains providing three-dimensional linkage of the structure.The formation of Sr₃B₂SiO₈ has been studied using annealing series in air at 900-1200 °C. According powder XRD, the probe contains pure Sr₃B₂SiO₈ over 1100 °C. The compound is not stable below 900 °C. In the pseudobinary Sr₂B₂O₅-Sr₃B₂SiO₈ system a new series of solid solutions Sr_3−xB₂Si_1−xO_8−3x (x=0-0.9) have been crystallized from melt. The thermal behavior of Sr₃B₂SiO₈ was investigated using powder high-temperature X-ray diffraction (HTXRD) in the temperature range 20-900 °C. The anisotropic character of thermal expansion has been observed: α_a= −1.3, α_b=23.5, α_c=13.9, and α_V=36.1×10⁻⁶ °C⁻¹ (25 °C); α_a= −1.3, α_b=23.2, α_c=5.2, and α_V=27.1×10⁻⁶ °C⁻¹ (650 °C). Maximal thermal expansion of the structure along of the chain direction [0 1 0] is caused by the partial straightening of chain zigzag. Hinge mechanism of thermal expansion is discussed.     

Neutron powder diffraction study of tetragonal Li7La3Hf2O12 with the garnet-related type structure

We have successfully synthesized a polycrystalline sample of tetragonal garnet-related Li-ion conductor Li₇La₃Hf₂O₁₂ by solid state reaction. The crystal structure is analyzed by the Rietveld method using neutron powder diffraction data. The structure analysis identifies that tetragonal Li₇La₃Hf₂O₁₂ has the garnet-related type structure with a space group of I4₁/acd (no. 142). The lattice constants are a=13.106(2) Å and c=12.630(2) Å with a cell ratio of c/a=0.9637. The crystal structure of tetragonal Li₇La₃Hf₂O₁₂ has the garnet-type framework structure composed of dodecahedral La(1)O₈, La(2)O₈ and octahedral HfO₆. Li atoms occupy three types of crystallographic site in the interstices of this framework structure, where Li(1) atom is located at the tetrahedral 8a site, and Li(2) and Li(3) atoms are located at the distorted octahedral 16f and 32g sites, respectively. These Li sites are filled with the Li atom. The present tetragonal Li₇La₃Hf₂O₁₂ sample exhibits bulk Li-ion conductivity of σ_b=9.85×10⁻⁷ S cm⁻¹ and grain-boundary Li-ion conductivity of σ_gb=4.45×10⁻⁷ S cm⁻¹ at 300 K. The activation energy is estimated to be E_a=0.53 eV in the temperature range of 300-580 K.     

Sol-gel synthesis and characterization of LiNO3-Al2O3 composite solid electrolyte

Composite solid electrolytes in the system (1 − x)LiNO₃-xAl₂O₃, with x = 0.0-0.5 were synthesized by sol-gel method. The synthesis carried out at low temperature resulted in voluminous and fluffy products. The obtained materials were characterized by X-ray diffraction, differential scanning calorimetry, scanning electron microscopy/energy dispersive X-ray, Fourier transform infrared spectroscopy and AC impedance spectroscopy. Structural analysis of the samples showed base centred cell type of point lattice of LiNO₃ for the composite samples with x = 0.1-0.2 and body centred cell for the sample with x = 0.3. A trace amount of α-LiAlO₂ crystal phase was also present in these composite samples. The thermal analysis showed that the samples were in a stable phase between 48 °C and 230-260 °C. Morphological analysis indicated the presence of amorphous phase and particles with sizes ranging from micro to nanometre scale for the composite sample with x = 0.1. The conductivities of the composites were in the order of 10⁻³ and 10⁻² S cm⁻¹ at room temperature and 150 °C, respectively.     

Order-disorder transition in the complex lithium spinel Li2CoTi3O8

Li₂CoTi₃O₈ has an ordered Li₂BB′₃O₈ spinel structure, space group P4₃32, at room temperature with 3:1 ordering of Ti and Li on the octahedral sites, and Li, Co disordered over the tetrahedral site. Rietveld refinement of variable temperature neutron powder diffraction data has shown an order-disorder phase transition in Li₂CoTi₃O₈ which commences at ∼500 °C with Li and Co mixing on the tetrahedral and 4-fold octahedral sites and is complete at a first order structural discontinuity at ∼915 °C. The fraction of Ti on the 12-fold octahedral site exhibits a small decrease with increasing temperature, which may suggest that the disordering involves all three cations. Above 930 °C, the structure, space group Fd3¯m, has Li, Co and Ti sharing a single-octahedral site and Li, Co sharing a tetrahedral site, although Co still exhibits a preference for tetrahedral coordination. A labelling scheme for ordered and partially ordered 3:1 spinels is devised which focuses on the occupancy of the Li,B cations.     

Kinetic analysis of the thermal stability of lithium silicates (Li4SiO4 and Li2SiO3)

The kinetics describing the thermal decomposition of Li₄SiO₄ and Li₂SiO₃ have been analysed. While Li₄SiO₄ decomposed on Li₂SiO₃ by lithium sublimation, Li₂SiO₃ was highly stable at the temperatures studied. Li₄SiO₄ began to decompose between 900 and 1000 °C. However, at 1100 °C or higher temperatures, Li₄SiO₄ melted, and the kinetic data of its decomposition varied. The activation energy of both processes was estimated according to the Arrhenius kinetic theory. The energy values obtained were −408 and −250 kJ mol⁻¹ for the solid and liquid phases, respectively. At the same time, the Li₄SiO₄ decomposition process was described mathematically as a function of a diffusion-controlled reaction into a spherical system. The activation energy for this process was estimated to be −331 kJ mol⁻¹. On the other hand, Li₂SiO₃ was not decomposed at high temperatures, but it presented a very high preferential orientation after the heat treatments.     

Revised phase diagram of Li2MoO4-ZnMoO4 system, crystal structure and crystal growth of lithium zinc molybdate

Orthorhombic lithium zinc molybdate was first chosen and explored as a candidate for double beta decay experiments with ¹⁰⁰Mo. The phase equilibria in the system Li₂MoO₄-ZnMoO₄ were reinvestigated, the intermediate compound Li₂Zn₂(MoO₄)₃ of the α-Cu₃Fe₄(VO₄)₆ (lyonsite) type was found to be nonstoichiometric: Li_2−2xZn_2+x(MoO₄)₃ (0≤x≤0.28) at 600 °C. The eutectic point corresponds to 650 °C and 23 mol% ZnMoO₄, the peritectic point is at 885 °C and 67 mol% ZnMoO₄. Single crystals of the compound were prepared by spontaneous crystallization from the melts and fluxes. In the structures of four Li_2−2xZn_2+x(MoO₄)₃ crystals (x=0; 0.03; 0.21; 0.23), the cationic sites in the face-shared octahedral columns were found to be partially filled and responsible for the compound nonstoichiometry. It was first showed that with increasing the x value and the number of vacancies in M3 site, the average M3-O distance grows and the lithium content in this site decreases almost linearly. Using the low-thermal-gradient Czochralski technique, optically homogeneous large crystals of lithium zinc molybdate were grown and their optical, luminescent and scintillating properties were explored.     

Synthesis, structural characterization and Li ion conductivity of a new vanado-molybdate phase, LiMg3VMo2O12

A new vanado-molybdate LiMg₃VMo₂O₁₂ has been synthesized, the crystal structure determined an ionic conductivity measured. The solid solution Li_2−zMg_2+zV_zMo_3−zO₁₂ was investigated and the structures of the z=0.5 and 1.0 compositions were refined by Rietveld analysis of powder X-ray (XRD) and powder neutron diffraction (ND) data. The structures were refined in the orthorhombic space group Pnma with a∼5.10, b∼10.4 and c∼17.6 Å, and are isostructural with the previously reported double molybdates Li₂M₂(MoO₄)₃ (M=M²⁺, z=0). The structures comprise of two unique (Li/Mg)O₆ octahedra, (Li/Mg)O₆ trigonal prisms and two unique (Mo/V)O₄ tetrahedra. A well-defined 1:3 ratio of Li⁺:Mg²⁺ is observed in octahedral chains for LiMg₃VMo₂O₁₂. Li⁺ preferentially occupies trigonal prisms and Mg²⁺ favours octahedral sheets. Excess V⁵⁺ adjacent to the octahedral sheets may indicate short-range order. Ionic conductivity measured by impedance spectroscopy (IS) and differential scanning calorimetry (DSC) measurements show the presence of a phase transition, at 500-600 °C, depending on x. A decrease in activation energy for Li⁺ ion conductivity occurs at the phase transition and the high temperature structure is a good Li⁺ ion conductor, with σ=1×10⁻³-4×10⁻² S cm⁻¹ and E_a=0.6 to 0.8 eV.     

Li and Li MAS NMR Studies on Fast Ionic Conducting Spinel-Type Li2MgCl4, Li2-xCuxMgCl4, Li2-xNaxMgCl4, and Li2ZnCl4

⁶Li and ⁷Li MAS NMR spectra including 1D-EXSY (exchange spectroscopy) and inversion recovery experiments of fast ionic conducting Li₂MgCl₄, Li_2-xCu_xMgCl₄, Li_2-xNa_xMgCl₄, and Li₂ZnCl₄ have been recorded and discussed with respect to the dynamics and local structure of the lithium ions. The chemical shifts, intensities, and half-widths of the Li MAS NMR signals of the inverse spinel-type solid solutions Li_2-xM^I_xMgCl₄ (M^I=Cu, Na) with the copper ions solely at tetrahedral sites and sodium ions at octahedral sites and the normal spinel-type zinc compound, respectively, confirm the assignment of the low-field signal to Li^tet of inverse spinel-type Li₂MgCl₄ and the high-field signal to Lioct as proposed by Nagel et al. (2000). In contrast to spinel-type Li_2-2xMg_1+xCl₄ solid solutions with clustering of the vacancies and Mg²⁺ ions, the Cu⁺ and Na⁺ ions are randomly distributed on the tetrahedral and octahedral sites, respectively. The activation energies due to the various dynamic processes of the lithium ions in inverse spinel-type chlorides obtained by the NMR experiments are E_a=6.6-6.9 and ΔG^*>79 KJ mol⁻¹ (in addition to 23, 29, and 75 kJmol-1 obtained by other techniques), respectively. The largest activation energy of >79 KJ mol⁻¹ corresponds to hopping exchange processes of Li ions between the tetrahedral 8a sites and the octahedral 16d sites. The smallest value of 6.6-6.9 KJ mol⁻¹, which was derived from the temperature dependence of both the spin-lattice relaxation times T₁ and the correlation times τ_C of Li^tet, reveals a dynamic process for the Li^tet ions inside the tetrahedral voids of the structure, probably between fourfold 32e split sites around the tetrahedral 8a site.     

Synthesis and structure of Li4Sr3Ge2N6: a new quaternary nitride containing Ge2N6 anions

A new Li-containing quaternary nitride, Li₄Sr₃Ge₂N₆, was obtained as single crystals from constituent elements in molten Na. It crystallizes in space group C2/m (No. 12) with a=6.1398(7) Å, b=10.021(1) Å, c=6.3130(7) Å, β=91.279(2)°, and Z=2. It contains the first example of isolated nitridogermanate anions of Ge₂N₆¹⁰⁻, which is also the first example of edge-sharing tetrahedral [GeN₄].     

Oxygen permeability, thermal expansion and mixed conductivity of GdxCe0.8−xPr0.2O2−δ, x=0, 0.15, 0.2

The non-linear thermal expansion behaviour observed in Ce_1−yPr_yO_2−δ materials can be substantially controlled by Gd substitution. Coulometric titration shows that the charge compensation mechanism changes with increasing x, in the system Gd_xCe_0.8−xPr_0.2O_2−δ. For x=0.15, charge compensation is by vacancy formation and destabilises the presence of Pr⁴⁺. At x=0.2, further Gd substitution is charge compensated by additionally raising the oxidation state of Pr rather than solely the creation of further oxygen ion vacancies. Oxygen concentration cell e.m.f. measurements in an oxygen/air potential gradient show that increasing Gd content decreases ionic and electronic conductivities. Ion transference numbers measured under these conditions show a positive temperature dependence, with typical values t_o=0.90,0.98 and 0.80 for x=0,0.15 and 0.2, respectively, at 950 °C. These observations are discussed in terms of defect association. Oxygen permeation fluxes are limited by both bulk ambipolar conductivity and surface exchange. However, the composition dependent trends in permeability are shown to be dominated by ambipolar conductivities, and limited by the level of electronic conductivity. At the highest temperatures, oxygen permeability of composition x=0.2 approaches that of composition x=0, Ce_0.8Pr_0.2O_2−δ, with specific oxygen permeability values approximately 2×10⁻⁹ mol s⁻¹ cm⁻¹ at 950 °C, but offering much better thermal expansion properties.     

Synthesis and structural study of a new NASICON-type solid solution: Li1−xLax/3Zr2(PO4)3

A new complete solid solution of NASICON-type compounds between LiZr₂(PO₄)₃ and La_1/3Zr₂(PO₄)₃ was evidenced with the general formula Li_1−xLa_x/3Zr₂(PO₄)₃ (0?x?1). These phases were synthesized by a complex polymerizable method and structurally characterized from Rietveld treatment of their X-ray and neutron powder diffraction data. This solid solution results from the substitution mechanism Li⁺→1/3La³⁺+2/3□ leading to an increase of the vacancies number correlated to an increase of the La content. According to this substitution mechanism, the general formula can then be written Li_1−xLa_x/3□_2x/3Zr₂(PO₄)₃ (0?x?1) in order to underline the correlation between the La content and the vacancies rate. For all the compounds, the structure is clearly related to that of the NASICON family with three crystallographic domains evidenced. For 0?x?0.5, all the members adopt at high temperature the typical NASICON-type structure (s.g. R3¯c), while at lower temperature, their structure distorts to a triclinic form (s.g. C 1¯), as observed for LiZr₂(PO₄)₃ prepared above 1100 °C. Moreover, in this domain, the reversible transition is clearly soft and the transition temperature strongly depends of the x value. For 0.6?x?0.9, the compounds crystallize in a rhombohedral cell (s.g. R3¯), while for x=1, the phase La_1/3Zr₂(PO₄)₃ is obtained (s.g. P3¯, Z=6, a=8.7378(2) Å, c=23.2156(7) Å).This paper is devoted to the structure analysis of the series Li_1−xLa_x/3Zr₂(PO₄)₃ (0?x?1), from X-ray and neutron powder thermo diffraction and transmission electron microscopy (TEM) studies.     

Series of compositions Bi2(M′xM1−x)4O9 (M′, M=Al, Ga, Fe; 0≤x≤1) with mullite-type crystal structure: Synthesis, characterization and O/O exchange experiment

Series of compositions Bi₂(M′_xM_1−x)₄O₉ with x=0.0, 0.1,…, 1.0 and M′/M=Ga/Al, Fe/Al and Fe/Ga were synthesized by dissolving appropriate amounts of corresponding metal nitrate hydrates in glycerine, followed by gelation, calcination and final heating at 800 °C for 24 h. The new compositions with M′/M=Ga/Al form solid-solution series, which are isotypes to the two other series M′/M=Fe/Al and Fe/Ga. The XRD data analysis yielded in all cases a linear dependence of the lattice parameters related on x. Rietveld structure refinements of the XRD patterns of the new compounds, Bi₂(Ga_xAl_1−x)₄O₉ reveal a preferential occupation of Ga in tetrahedral site (4 h). The IR absorption spectra measured between 50 and 4000 cm⁻¹ of all systems show systematic shifts in peak positions related to the degree of substitution. Samples treated in ¹⁸O₂ atmosphere (16 h at 800 °C, 200 mbar, 95% ¹⁸O₂) for ¹⁸O/¹⁶O isotope exchange experiments show a well-separated IR absorption peak related to the M-¹⁸O_c-M vibration, where O_c denotes the common oxygen of two tetrahedral type MO₄ units. The intensity ratio of M-¹⁸O_c/M-¹⁶O_c IR absorption peaks and the average crystal sizes were used to estimate the tracer diffusion coefficients of polycrystalline Bi₂Al₄O₉ (D=2×10⁻²² m²s⁻¹), Bi₂Fe₄O₉ (D=5×10⁻²¹ m²s⁻¹), Bi₂(Ga/Al)₄O₉ (D=2×10⁻²¹ m²s⁻¹) and Bi₂Ga₄O₉ (D=2×10⁻²⁰ m²s⁻¹).     

High-temperature X-ray diffraction study of crystallization and phase segregation on spinel-type lithium manganese oxides

To study crystallization process of spinel-type Li_1+xMn_2−xO₄, in-situ high-temperature X-ray diffraction technique (HT-XRD) was utilized for the mixture consisting of Li₂CO₃ and Mn₂O₃ as starting material in the temperature range of 25-700 °C. In-situ HT-XRD analysis directly revealed that crystallization process of Li_1+xMn_2−xO₄ was significantly affected by the difference in the Li/Mn molar ratio in the precursor. Single phase of stoichiometric LiMn₂O₄ formed at 700 °C. The formation of single phase of spinel was achieved at the lower temperature than the stoichiometric sample as Li/Mn molar ratio in the precursor increased. Lattice parameter of the stoichiometric LiMn₂O₄ at 25 °C was 8.24 Å and expanded to 8.31 Å at 700 °C, which corresponds to the approximately 3% expansion in the unit cell volume. From the slope of the lattice parameter change as a function of temperatures, linear thermal expansion coefficient of the stoichiometric LiMn₂O₄ was calculated to be 1.2×10⁻⁵ °C⁻¹ in this temperature range. When the Li/Mn molar ratio in Li_1+xMn_2−xO₄ increased (x > 0.1), the spinel phase segregated into the Li_1+yMn_2−yO₄ (x > y) and Li₂MnO₃ during heating, which involved the oxygen loss from the materials. During the cooling process from 700 °C, and the segregated phase merged into Li_1+xMn_2−xO₄ with oxygen incorporation. Such trend directly observed by in-situ HT-XRD was supported by thermal gravimetric analysis as reversible weight (oxygen) loss/gain at higher temperature (500-700 °C).     

La(Li1/3Ti2/3)O3: a new 1:2 ordered perovskite

A new 1:2 ordered perovskite La(Li_1/3Ti_2/3)O₃ has been synthesized via solid-state techniques. At temperature >1185°C, Li and Ti are randomly distributed on the B-sites and the X-ray powder patterns can be indexed in a tilted (b⁻b⁻c⁺) Pbnm orthorhombic cell (a=a_c√2=5.545 Å, b=a_c√2=5.561 Å, c=2a_c=7.835 Å). However, for T?1175°C, a 1:2 layered ordering of Li and Ti along 〈111〉_c yields a structure with a P2₁/c monoclinic cell with a=a_c√6=9.604 Å, b=a_c√2=5.552 Å, c=a_c3√2=16.661 Å, β=125.12°. While this type of order is well known in the A²⁺(B²⁺_1/3B⁵⁺_2/3)O₃ family of niobates and tantalates, La(Li_1/3Ti_2/3)O₃ is the first example of a titanate perovskite with a 1:2 ordering of cations on the B-sites.     

MAS-NMR studies of lithium aluminum silicate (LAS) glasses and glass-ceramics having different Li2O/Al2O3 ratio

Emergence of phases in lithium aluminum silicate (LAS) glasses of composition (wt%) xLi₂O-71.7SiO₂-(17.7−x)Al₂O₃-4.9K₂O-3.2B₂O₃-2.5P₂O₅ (5.1≤x≤12.6) upon heat treatment were studied. ²⁹Si, ²⁷Al, ³¹P and ¹¹B MAS-NMR were employed for structural characterization of both LAS glasses and glass-ceramics. In glass samples, Al is found in tetrahedral coordination, while P exists mainly in the form of orthophosphate units. B exists as BO₃ and BO₄ units. ²⁷Al NMR spectra show no change with crystallization, ruling out the presence of any Al containing phase. Contrary to X-ray diffraction studies carried out, ¹¹B (high field 18.8 T) and ²⁹Si NMR spectra clearly indicate the unexpected crystallization of a borosilicate phase (Li,K)BSi₂O₆, whose structure is similar to the aluminosilicate virgilite. Also, lithium disilicate (Li₂Si₂O₅), lithium metasilicate (Li₂SiO₃) and quartz (SiO₂) were identified in the ²⁹Si NMR spectra of the glass-ceramics. ³¹P NMR spectra of the glass-ceramics revealed the presence of Li₃PO₄ and a mixed phase (Li,K)₃PO₄ at low alkali concentrations.     

Dependence of the mixed alkali effect on temperature and total alkali oxide content in y[xLi2O·(1−x)Na2O]·(1−y)B2O3 glasses

The complex conductivity spectra of mixed alkali borate glasses of compositions y [xLi₂O·(1−x)Na₂O]·(1−y)B₂O₃ (with x=0.0, 0.2, 0.4, 0.6, 0.8, 1.0; y=0.1, 0.2, 0.3) in a frequency range between 10⁻² Hz and 3 MHz and at temperatures ranging from 298 to 573 K have been studied. For each glass composition the conductivities show a transition from the dc values into a dispersive regime where the conductivity is found to increase continuously with frequency, tending towards a linear frequency dependence at sufficiently low temperatures. Mixed alkali effects (MAEs) in the dc conductivity and activation energy are identified and discussed. It has been for the first time found that the strength of the MAE in the logarithm of the dc conductivity linearly increases with the total alkali oxide content, y, and the reciprocal temperature, 1/T.     

K2Li(NH2)3 and K2Na(NH2)3—synthesis and crystal structure of two crystal-chemically isotypic mixed-cationic amides

K₂Li(NH₂)₃ (1) was the only crystalline product obtained from the reaction of potassium with dilithium decahydro-closo-decaborate Li₂B₁₀H₁₀ in liquid ammonia at −38 °C. The compound crystallizes in the space group P4₂/m with Z=4, a=6.8720(5) Å, c=11.706(1) Å and V=552.81(7) Å³. The investigated crystal-chemically isotypic sodium compound K₂Na(NH₂)₃ (2) was merohedrally twinned and crystallized from a reaction mixture containing potassium and disodium decahydro-closo-decaborate Na₂B₁₀H₁₀ in liquid ammonia with a=7.0044(5) Å, c=12.362(1) Å and V=606.48(9) Å³. The compounds contain pairs of edge sharing tetraamidolithium or tetraamidosodium tetrahedra which are interconnected by potassium ions forming three-dimensional infinite networks.     

Mn environment in layered Li[Mg0.5−xNixMn0.5]O2 oxides monitored by EPR spectroscopy

X-band and high-frequency EPR spectroscopy were used for studying the manganese environment in layered Li[Mg_xNi_0.5−xMn_0.5]O₂, 0?x?0.5. Both layered LiMg_0.5Mn_0.5O₂ and monoclinic Li[Li_1/3Mn_2/3]O₂ oxides (containing Mn⁴⁺ ions only) were used as EPR standards. The EPR study was extended to the Ni-substituted analogues, where both Ni²⁺ and Mn⁴⁺ are paramagnetic. For LiMg_0.5−xNi_xMn_0.5O₂ and Li[Li_(1−2x)/3Ni_xMn_(2−x)/3]O₂, an EPR response from Mn⁴⁺ ions only was detected, while the Ni²⁺ ions remained EPR silent in the frequency range of 9.23-285 GHz. For the diamagnetically diluted oxides, LiMg_0.25Ni_0.25Mn_0.5O₂ and Li[Li_0.10Ni_0.35Mn_0.55]O₂, two types of Mn⁴⁺ ions located in a mixed (Mn-Ni-Li)-environment and in a Ni-Mn environment, respectively, were registered by high-field experiments. In the X-band, comparative analysis of the EPR line width of Mn⁴⁺ ions permits to extract the composition of the first coordination sphere of Mn in layered LiMg_0.5−xNi_xMn_0.5O₂ (0?x?0.5) and Li[Li_(1−2x)/3Ni_xMn_(2−x)/3]O₂ (x>0.2). It was shown that a fraction of Mn⁴⁺ are in an environment resembling the ordered “α,β”-type arrangement in Li_1−δ1Ni_δ1[Li_{(1−2x)/3+δ1}Ni_2x/3−δ1)_α(Mn_(2−x)/3Ni_x/3)_β]O₂ (where and δ₁=0.06 were calculated), while the rest of Mn⁴⁺ are in the Ni,Mn-environment corresponding to the Li_1−δ2Ni_δ2[Ni_1−yMn_y]O₂ () composition with a statistical Ni,Mn distribution. For Li[Li_(1−2x)/3Ni_xMn_(2−x)/3]O₂ with x?0.2, IR spectroscopy indicated that the ordered α,β-type arrangement is retained upon Ni introduction into monoclinic Li[Li_1/3Mn_2/3]O₂.     

Investigation of the quasi-ternary system LaMnO3-LaCoO3-“LaCuO3”—I: the series La(Mn0.5Co0.5)1−xCuxO3−δ

The La(Mn_0.5Co_0.5)_1−xCu_xO_3−δ series with x=0, 0.05, 0.1, 0.2, 0.4, 0.6, 0.8 and 1 was synthesized by the Pechini method to obtain insight into the phase formation in the quasi-ternary LaMnO₃-LaCoO₃-“LaCuO₃” system caused by the instability of LaCuO₃ under ambient conditions. After sintering at 1100°C some remarkable results were obtained: LaMn_0.3Co_0.3Cu_0.4O_3−δ crystallized as a single phase in the orthorhombic perovskite structure typical of LaCuO₃. Among the synthesized compositions this compound showed the highest electrical conductivity in air at 800°C (155 S cm⁻¹) and also the highest thermal expansion coefficient (α_30−800°C=15.4×10⁻⁶ K⁻¹). The LaCuO_3−δ composition also crystallized as a single phase but in a monoclinic structure although previous investigations have shown that other phases are preferably formed after sintering at 1100°C. The electrical conductivity and thermal expansion coefficient were the lowest within the series of compositions, i.e. 9.4 S cm⁻¹ and 11.9×10⁻⁶ K⁻¹, respectively.