两步法制备超疏水性ZnO纳米棒薄膜

采用两步法制备了超疏水性ZnO纳米棒薄膜,在用磁控溅射在普通玻璃衬底上生长一层ZnO籽晶层基础上,利用液相法制备了空间取向高度一致的ZnO纳米棒阵列,经修饰后由亲水性转变为超疏水性.用扫描电子显微镜观察了纳米棒的表面结构,用接触角测量仪测出水滴在ZnO纳米棒薄膜表面的接触角为151°±05°,滚动角为7°.用Cassie模型对ZnO纳米棒薄膜的超疏水性进行了验证. 关键词： ZnO纳米棒 超疏水 两步法     

两步法制备空间取向高度一致的ZnO纳米棒阵列

采用两步法,即先用磁控溅射在Si(100)表面生长一层ZnO籽晶层、再利用液相法制备空间取向高度一致的ZnO纳米棒阵列.用扫描电子显微镜、X射线衍射、高分辨透射电子显微镜和选区电子衍射对样品形貌和结构特征进行了表征.结果表明,ZnO纳米棒具有垂直于衬底沿c轴择优生长和空间取向高度一致的特性和比较大的长径比,X射线衍射的(XRD)(0002)峰半高宽只有0.06°,选区电子衍射也显示了优异的单晶特性.光致发光谱表明ZnO纳米棒具有非常强的紫外本征发光和非常弱的杂质或缺陷发光特性. 关键词： ZnO纳米棒阵列 ZnO籽晶层 两步法 液相生长     

水浴法制备ZnO纳米棒及其场发射性能

用硝酸锌(Zn(NO3)2·6H2O)与六亚甲基四胺(C6H12N4)以等浓度配制成反应溶液,通过水浴法制备出了形貌可控的棒状ZnO纳米结构,讨论了不同反应浓度及衬底对ZnO表面形貌的影响.样品的XRD和扫描电子显微镜分析结果表明,所得产物均为六方纤锌矿结构,在有晶种层的衬底上制备出的ZnO纳米棒沿(001)方向并垂直于衬底表面生长.随着反应浓度的增加,ZnO纳米棒的直径增大,长径比减小.样品的场发射性能测试表明,反应溶液浓度为0.005 mol/L,以铜膜为晶种层的硅衬底上制备出的场发射阴极具有较好的场发射性能.     

ZnO纳米棒/CdS量子点的制备及紫外-可见探测性能研究

本文采用水热法在ITO衬底上制备了ZnO纳米棒阵列,然后用化学水浴沉积法在纳米棒上制备CdS量子点。分别利用SEM和XRD对样品形貌和晶体结构进行表征。结果表明,球状的CdS量子点均匀地包覆在ZnO纳米棒表面,且结晶质量较好。基于ZnO纳米棒和ZnO纳米棒/CdS量子点制备的探测器对紫外光都具有很好的响应,然而与ZnO纳米棒探测器相比,ZnO纳米棒/CdS量子点探测器在相同条件下的光电流提高了7倍,为0. 52 mA。此外,ZnO纳米棒/CdS量子点探测器对绿光和蓝光也表现出了很好的响应。     

电化学沉积法制备ZnO纳米柱及自驱动紫外探测性能研究

采用提拉法在ITO衬底上制备种子层,并使用电化学沉积制备高度取向的氧化锌纳米棒,研究了不同提拉次数下籽晶层厚度与电化学沉积电位对氧化锌纳米棒形貌的影响。在此基础上,制备了自驱动型紫外探测器并测试了其光响应谱。结果表明,该探测器可以对部分紫外波段(300~400 nm)有选择性地光响应,峰值响应度为0.012 A/W。     

氧化锌纳米棒形貌控制及其在钙钛矿太阳能电池中作为电子传输层的应用

在钙钛矿电池中, ZnO纳米棒的垂直性是影响器件效率的关键因素. AZO(ZnO:Al)玻璃作为一种廉价的透明导电衬底,由于与ZnO纳米棒无晶格失配,有望获得最佳垂直性.然而目前在大气环境下,以AZO为衬底、ZnO纳米棒为电子传输层的钙钛矿太阳能电池还鲜有报道.本文通过水热法制备ZnO纳米棒作为电子传输层,系统研究不同条件对ZnO纳米棒的形貌及结晶性能的调控规律,分析其微观生长机理.并在此基础上于大气环境下制备太阳能电池,将以AZO为衬底在大气条件下制备的钙钛矿光伏器件的最佳效率从目前文献报道的7.0%提高到9.63%.这对丰富钙钛矿电池的设计思路及进一步降低成本具有重要意义.     

籽晶层对喷雾热分解法生长ZnO薄膜结晶质量和光电性能的影响

通过脉冲激光沉积(PLD)方法在Si(100)衬底上沉积一层高质量的ZnO籽晶层,在籽晶层上进一步采用超声喷雾热分解(USP)法生长ZnO薄膜,研究了籽晶层对ZnO薄膜结晶质量和ZnO/Si异质结光电特性的影响。研究结果表明,在籽晶层的诱导作用下,USP法生长ZnO薄膜由多取向结构变为(002)单一取向,结晶性能得到了显著改善;籽晶层上生长的薄膜呈现出垂直于衬底生长的柱状晶结构,微观结构更加致密。通过研究紫外光照前后ZnO/Si异质结的整流特性,发现引入籽晶层后,反向偏压下异质结的光电响应显著增加,并且在开路状态下出现明显的光伏效应。     

水热法制备Co掺杂ZnO纳米棒及其光学性能

采用水热法在石英衬底上以Zn(CH3COO)2.2H2O和Co(NO3)2.6H2O水溶液为源溶液,以C6H12N4(HMT)溶液作为催化剂,在较低温度下制备了Co掺杂的ZnO纳米棒。采用X射线衍射(XRD)和扫描电子显微镜(SEM)对所生长ZnO纳米棒的晶体结构和表面形貌进行了表征,考察了Co掺杂对ZnO纳米棒微观结构和对发光性能影响的机制。结果表明:Co掺杂的ZnO纳米棒呈六方纤锌矿结构,具有沿(002)面择优生长特性,Co掺杂使ZnO纳米棒的直径变细;同时室温光致发光(PL)谱检测显示Co掺杂ZnO纳米棒具有很强的近带边紫外发光峰,而与深能级相关的缺陷发光峰则很弱。本研究采用水热法在石英衬底上于较低温度下生长出了具有较高光学质量的Co掺杂ZnO纳米棒。     

直立Zn_2GeO_4/ZnO纳米棒阵列的制备及其发光性质研究

利用化学气相沉积法(CVD)在表面溅射Au和沉积ZnO籽晶的硅衬底上分别生长高度有序、垂直密布的直立Zn2GeO4/ZnO纳米棒阵列,利用扫描电子显微镜(SEM)、X射线衍射仪(XRD)和光致发光(PL)谱测试手段对所制备样品进行表征和发光特性的研究。所制备的Zn2GeO4/ZnO纳米棒的直径为350~400 nm,高度为10~11μm;室温PL谱观察到3个来源于Zn2GeO4的典型发光峰。最后,对CVD法制备的Zn2GeO4/ZnO纳米棒生长机理进行了分析。该种直立性良好的一维纳米棒材料可以广泛地应用到纳米光电子器件中。     

有序ZnO纳米阵列的制备及其光学特性

纳米球刻蚀技术和磁控溅射方法在普通玻璃衬底上制备有序氧化锌(ZnO)纳米阵列。利用扫描电子显微镜对样品表面形貌进行了观测,并对样品进行荧光(PL)光谱测试。结果表明,相比于普通ZnO薄膜,ZnO纳米阵列的有序结构可以提高在紫外区域的发光性能,减少蓝绿光的发射缺陷。研究了不同ZnO纳米阵列粒径大小和不同ZnO纳米阵列的厚度对其光学性质的影响。溅射时间30min的有序ZnO纳米阵列样品的质量和结晶状态较好,随着聚苯乙烯(PS)纳米球粒径的减小,样品吸收峰和荧光光谱均发生"蓝移"。     

Guided-Wave Two-Dimensional Acousto-Optic Scanner Using Proton-Exchanged Lithium Niobate Waveguide

Two-dimensional scanning of a 0.6328 mum guided-light beam has been realized using noncolinear acousto-optic (AO) coplanar Bragg diffraction together with colinear AO guided-mode to substrate radiation-mode conversion in a Z-cut Xpropagation LiNbO3 proton-exchanged (PE) waveguide. The two surface acoustic (SAW) waves utilized are at the center frequencies of 500 and 200 MHz, propagating in the Y and X axes, respectively. Two-dimensional scanning of approximately 720 resolvable light beam spots, namely, 18 40 (horizontal vertical) scanning, has been demonstrated using a light beam of 1.0 mm aperture. The total number of resolvable beam spots can be greatly increased from 720 by simply utilizing SAW transducers of larger bandwidth and a light beam of greater aperture. It should also be possible to significantly increase the diffraction efficiency from 3 % by optimizing the parameters of the PE waveguide and the SAWs.     

Femtosecond Transform-Limited Pulse Generation by Compensating for the Linear Chirp of SPM Spectra in Dispersion Shifted Fibers

A simple technique of pulse compression, based on the linear chirp compensation of self-phase modulation (SPM) spectra in dispersion shifted fibers, is demonstrated. The optimization procedure is carried out, for a short span of a single-mode fiber, using a parabolic law, which describes the behavior of the squared output pulse width versus the pump peak power in the case of Gaussian pulses. The experimental results give a minimum pulse duration of 233 fs, which is in good agreement with the model. Shorter and coherent pulses, down to 90 fs, have been obtained by inserting an interference filter at the optical output.     

Effect ofγ-radiation on the spectral luminescence characteristics of impure cadmium tungstate crystals

Results of a study of the effect of γ-radiation on the spectral luminescence properties of cadmium tungstate crystals doped with silver, bismuth, and molybdenum cations are presented. Spectral characteristics of the nondnnnoped crystals are briefly described. Absorption and photo and X-ray luminescence spectra of the crystals taken before and after exposure to γ-radiation (5.5·10⁴ Gy) are compared. It is found that the spectral characteristics of the crystals doped with silver, bismuth, and molybdenum cations do not change markedly after the exposure. The relation between the type of impurity-induced defects, individual characteristics of the impurity cations, and the character of the effect of γ-radiation on the spectral luminescence properties of impure crystals is analyzed (preliminarily). Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 64, No. 1, pp. 55–60, January–February, 1997.     

Theoretical analysis and simulation of conjugate heights for dual-conjugate AO system in lidar

A multi-conjugate adaptive optics （MCAO） can offer a possibility of widening field of view （FOV） characterized by the isoplanatic angle, and the choose of conjugate height becomes a basic problem for MCAO, which influences the size of iosplanatic angle. Considering the application of lidar, the isoplanatic angle＇s expressions of two deformable mirrors （DMs） MCAO for uplink and downlink are deduced. The effects of conjugate heights for dual-conjugate AO are thoughtfully discussed, and the isoplanatic angles are further analyzed. The results show that the isopanatic angle varies with the conjugate height and reaches the maximum as the conjugate height is at the optimal altitude. Moreover, the optimal conjugate height changes with the propagation distance.     

Quick single-photon detector with many avalanche photo diodes working on the time division

Due to the limit of response speed of the present single-photon detector, the code rate is still too low to come into practical use for the present quantum key distribution (QKD) system.A new idea is put up to design a quick single-photon detector.This quick single-photon detector is composed of a multi-port optic-fiber splitter and many avalanche photo diodes (APDs).Au of the ports with APDs work on the time division and cooperate with a logic discriminating and deciding unit driven by the clock signal.The operation frequency lies on the number N of ports, and can reach N times of the conventional single-photon detector.The single-photon prompt detection can come true for high repetition-rate pulses.The applying of this detector will largely raise the code rate of the QKD, and boost the commercial use.     

Sorting of bending magnets for the SSRF booster

The Shanghai Synchrotron Radiation Facility(SSRF)booster ring,a full energy injector for the storage ring,is deigned to accelerate the electron beam energy from 150MeV to 3.5GeV that demands high extraction efficiency at the extraction energy with low beam loss rate when electrons are ramping.Closed orbit distortion(COD)caused by bending magnet field uniformity errors which affects the machine performance harmfully could be effectively reduced by bending magnet location sorting.Considering the affections of random errors in measurement,both ideal sorting and realistic sorting are studied based on measured bending magnet field uniformity errors and one reasonable combination of bending magnets which can reduce the horizontal COD by a factor of 5is given as the final installation sequence of the booster bending magnets in this paper.     

Improvement of four-wave mixing-based wavelength conversion efficiency in dispersion shifted fiber by 40-GHz clock pumping

40-GHz clock modulated signal as a pump to improve the efficiency of four-wave mixing (FWM)-based wavelength conversion in a 26.5-km dispersion shifted fiber (DSF) is investigated. The experimental results demonstrate that the conjugated FWM component has higher intensity with the clock pumping than that with the continuous-wave (CW) light pumping. The improvement of FWM-based wavelength conversion efficiency is negligible when the pump power is less than Brillouin threshold. But when the pump power is greater than Brillouin threshold, the improvement becomes significant and increases with the increment of pump power. The improvement can increase up to 9 dB if pump power reaches 17 dBm.     

Characterization of PolyA and PolyC mismatches by Raman spectroscopy

A.C mismatches are studied by Raman spectral characterization of PolyA, PolyC, and their equimolar complex in solution of 0.14 mol/L Na ,pH7.0.Experimental results show that A·C mismatches occur to be A/B (mainly A) conformers, and unlike Watson-Crick base pairing, this kind of mismatches is stabilized by only one hydrogen bond involving cytosine N4H2 and adenine N7.The formation of A·C complex makes the base stacking interactions much stronger, and conformation of the backbone more ordered, which leads to obvious Raman hypochromic effect with some shifts in corresponding bands.