Ce3+掺杂SiO2-Al2O3-Gd2O3玻璃的闪烁性能

通常, Ce离子掺杂的低密度玻璃有较高的发光效率, 而高密度的Ce离子掺杂玻璃其发光效率很低. 为了解释这一现象, 采用高温熔融法获得了SiO₂-Al₂O₃-Gd₂O₃三元系统的玻璃形成区, 并在还原气氛下制备了Ce³⁺掺杂SiO₂-Al₂O₃-Gd₂O₃以及SiO₂-Al₂O₃-Gd₂O₃-Ln₂O₃ (Ln=Y, La, Lu)闪烁玻璃, 研究了其光谱和闪烁性能. 测试结果显示: 随着Gd₂O₃含量增加, 玻璃紫外截止波长发生红移, 荧光强度降低, 衰减时间缩短; 加入Lu₂O₃, La₂O₃, Y₂O₃后, 紫外截止波长发生红移, 荧光强度降低, 衰减时间变短; 当Gd₂O₃超过10% mol时, X射线荧光积分光产额从相当于锗酸铋 晶体的61%降低到13%. 荧光强度降低、衰减时间缩短的原因是随着玻璃的紫外截止波长红移玻璃的能带宽度变窄, 使得Ce³⁺离子的d电子轨道开始接近玻璃的导带, Ce³⁺离子受辐射后跃迁到d电子轨道的电子会通过导带与玻璃中的空穴复合, 产生电荷迁移猝灭效应.     

Ga2O3组分对Tm3+掺杂GeO2-Ga2O3-Li2O-BaO-La2O3玻璃的光谱性能影响

制备了Tm³⁺(8.0mol%)掺杂(77-x)GeO₂-xGa₂O₃-8Li₂O-10BaO-5La₂O₃(x=4,8,12,16)系列玻璃.系统地研究了Ga₂O₃从4mol%变化到16mol%时,玻璃的光谱性质与热学性质的变化规律.差热分析表明,随着Ga₂O₃含量的增加,锗酸盐玻璃的热稳定性增加.运用Judd-Ofelt(J_O)理论计算得到了Tm³⁺在不同Ga₂O₃含量的GeO₂-Ga₂O₃-Li₂O-BaO-La₂O₃玻璃中的J-O强度参数(Ω₂,Ω₄,Ω₆)及Tm³⁺各激发能级的自发跃迁概率、荧光分支比以及辐射寿命等光谱参量.在808nm激光二极管的激发下,测试并分析了Ga₂O₃对Tm³⁺荧光光谱特性的影响.随着Ga₂O₃从4mol%增加到16mol%,Tm³⁺在1.8μm处的荧光强度呈现先减弱后增强的特性.当Ga₂O₃含量大约在12mol%时,Tm³⁺在1.8μm处的荧光强度最弱,受激发射截面达到最小.还初步讨论了Ga₂O₃对玻璃结构与光谱参数的影响规律. 关键词： 3+掺杂锗酸盐玻璃')" href="#">Tm³⁺掺杂锗酸盐玻璃 光谱性能 Judd-Ofelt参数 热稳定性     

Bi2O3-B2O3-BaO玻璃的制备及其近红外发光性能的研究

采用高温熔融法制备了xBi₂O₃-50B₂O₃-(50-x)BaO玻璃, 测定了样品玻璃的近红外光区的发射谱、荧光寿命以及Raman光谱. 在808 nm波长光的激发下, 50Bi₂O₃-50B₂O₃二元玻璃中未观察到近红外发光; 随体系中BaO的加入, 当x为40, 45以及49时, 玻璃样品中观察到了近红外宽带发光现象; BaO含量进一步增加, 当x=10–30时, 近红外发光现象消失; 而当玻璃中Bi浓度很低时, 在0.5Bi₂O₃-50B₂O₃-50BaO及1Bi₂O₃-50B₂O₃-50BaO玻璃中发现了近红外发光现象, 且存在多个发光峰. 对铋离子近红外发光机理进行了初步的探讨.     

Li2O-(LiCl)2-B2O3-Al2O3系统玻璃的Raman光谱研究

我们用Raman光谱研究了Li₂O(LiCl)₂B₂O₃-Al₂O₃系玻璃的结构,着重研究了Al₂O₃的影响。对于Li₂O-B₂O₃系玻璃,Li₂O含量增加使玻璃中存在的BO₃三角体转变为BO₄四面体, 关键词：     

光学碱度对Tb3+掺杂Bi2O3-B2O3玻璃发光性能的影响

采用熔融法制备了Tb³⁺掺杂的Bi₂O₃-B₂O₃系统玻璃,使用激发、发射及拉曼光谱分析了光学碱度与玻璃结构及发光性能的关系,同时绘制了Tb³⁺、Bi³⁺和Bi²⁺的能级图。研究结果表明：Tb³⁺掺杂的Bi₂O₃-B₂O₃玻璃由[BO₃]、[BiO₃]、[BO₄]及[BiO₆]共同组成,且随着光学碱度由0.63增加到0.93,玻璃的结构逐渐疏松。高的光学碱度使部分Bi³⁺变为Bi²⁺,发出571 nm（²P_3/2（2）→²P_1/2）的光,Bi³⁺→Tb³⁺的能量降低。在光学碱度及Tb³⁺、Bi³⁺和Bi²⁺离子的共同作用下,随着光学碱度的提高,玻璃的发光颜色由黄绿色变为白色。     

Eu3+掺杂Bi2O3-PbO-B2O3-ZnO玻璃光谱性质

用高温融熔法制备了Eu³⁺掺杂浓度为1%的(60-x)Bi₂O₃xPbO30B₂O₃10ZnO(x=0,10,30,摩尔分数)玻璃.测定了玻璃的差热分析曲线、吸收光谱、声子边带谱、发射光谱与激发光谱.由发射光谱与稀土Eu³⁺离子光学跃迁矩阵元的特点,计算了Eu³⁺光学跃迁的J-O参数Ω₂与Ω₄.结果显示强度参数Ω₂随着PbO量的增加而略减少,表明材料的对称性略增加,Eu—O键强减弱,共价性降低.PbO组分的增加,使玻璃的结晶起始温度与软化温度差降低,导致玻璃的热温度性变差.随着PbO的增加,电-声子耦合减弱.     

Li2O-B2O3-SiO2系统玻璃的Raman光谱研究

在Li₂O≥30mol％的Li₂O-B₂O₃-SiO₂系统玻璃中,以Li₂O代B₂O₃或SiO₂都导致玻璃网络中带非桥氧的硼酸盐和硅酸盐基团的量的增加;以B₂O₃代SiO₂则使玻璃网络中带和不带非桥氧的硼酸盐基团以及带非桥氧的硅酸盐基团的量都增加。 关键词：     

Er3+/Yb3+共掺TeO2-WO3-Bi2O3玻璃的光谱性质和上转换发光

本文制备了Er³⁺/Yb³⁺共掺TeO₂-WO₃-Bi₂O₃(TWB)玻璃. 测试和分析了样品的吸收光谱、荧光光谱及上转换发光. 用Judd-Oflet(J-O)理论计算了Er³⁺在玻璃样品中的光谱强度参数,随着Bi₂O₃含量的增加,Ω₂增加,Ω₄ 关键词： 碲酸盐玻璃 光谱性质 上转换     

Bi离子掺杂GeO2-Al2O3-M(M=Na2O，BaO，Y2O3)玻璃的光学性质

用高温熔融法制备了Bi离子掺杂浓度为1mol%的GeO-B₂O₃-Na₂O (GBNB)，GeO₂-Al₂O₃-Na₂O(GANB)，GeO₂-Al₂O₃-BaO(GABB)和GeO₂-Al₂O₃-Y₂O₃(GAYB)玻璃.测定了样品玻璃的差热曲线、吸收、发射光谱及荧光衰减曲线.实验发现GBNB，GANB，GAYB，GABB的吸收边带逐步发生红移.由于这些吸收边带是由Bi³⁺的6s²电子到Bi⁵⁺ 6s⁰空轨道的跃迁引起.因此推断GBNB，GANB，GAYB，GABB玻璃中Bi⁵⁺离子的含量逐步增加.在GABB，GAYB，GANB三个样品中观察到发光中心约1220nm超宽带荧光发射.荧光强度从GABB，GAYB，GANB逐步减弱，荧光半高宽和荧光寿命逐步变小.这些超宽带的荧光归属为Bi⁵⁺离子的发光所致.从吸收与荧光光谱的变化，推断在GeO₂-Al₂O₃玻璃中引入BaO，Y₂O₃组分有利于Bi⁵⁺离子的形成.讨论了BaO，Y₂O₃化学组分对Bi离子在玻璃中的价态影响的内在机理. 关键词： 5+离子')" href="#">Bi⁵⁺离子 超宽带发光 吸收带 荧光寿命     

NaBO2-B2O3体系玻璃的形成和晶化机制

本文用热学分析、高温和室温X射线衍射分析、红外吸收光谱等方法研究了NaBO₂-B₂O₃体系玻璃的形成、热稳定性和晶化机制。这一体系十分容易形成稳定的非晶玻璃,晶化过程与非晶的宏观状态有关。块状玻璃的晶化温度比非晶粉末高。部分成份晶化后形成不同的物相,熔点也不同。晶化产物的晶体结构类似于玻璃的结构。NaBO₂-B₂O₃体系的电导率用交流阻抗直接测量法测定。玻璃态的电导率比晶态试 关键词：     

Optical properties of (ZnO)0.5(P2O5)0.5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Binary (ZnO)_0.5(P₂O₅)_0.5 glasses doped with Eu₂O₃ and nanoparticles of Gd₂O₃:Eu were prepared by conventional melt-quench method and their luminescence properties were compared. Undoped (ZnO)_0.5(P₂O₅)_0.5 glass is characterized by a luminescent defect centre (similar to L-centre present in Na₂O-SiO₂ glasses) with emission around 324 nm and having an excited state lifetime of 18 ns. Such defect centres can transfer the energy to Eu³⁺ ions leading to improved Eu³⁺ luminescence from such glasses. Based on the decay curves corresponding to the ⁵D₀ level of Eu³⁺ ions in both Gd₂O₃:Eu nanoparticles incorporated as well as Eu₂O₃ incorporated glasses, a significant clustering of Eu³⁺ ions taking place with the latter sample is confirmed. From the lifetime studies of the excited state of L-centre emission from (ZnO)_0.5(P₂O₅)_0.5 glass doped with Gd₂O₃:Eu nanoparticles, it is established that there exists weak energy transfer from L-centres to Eu³⁺ ions. Poor energy transfer from the defect centres to Eu³⁺ ions in Gd₂O₃:Eu nanoparticles doped (ZnO)_0.5(P₂O₅)_0.5 glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between luminescent centre and Eu³⁺ ions.     

Structure and electrical properties of SrO-borovanadate (V2O5)0.5(SrO)0.5−y(B2O3)y glassses

SrO-borovanadate glasses with nominal composition (V₂O₅)_0.5(SrO)_0.5−y(B₂O₃)_y, 0.0≤y≤0.4 were prepared by a normal quench technique and investigated by direct current (DC) electrical conductivity, inductively coupled plasma (ICP) spectroscopy, infrared (IR) spectroscopy and X-ray powder diffraction (XRD) studies in an attempt to understand the nature of mechanism governing the DC electrical conductivity and the effect of addition of B₂O₃ on the structure and electrical properties of these glasses. XRD patterns confirm the amorphous nature of the present glasses and actual compositions of the glasses were determined by ICP spectroscopy. The temperature dependence of DC electrical conductivity of these glasses has been studied in terms of different hopping models. The IR results agree with previous investigations on similar glasses and it has been concluded that similar to SrO-vanadate glasses, metavandate chain-like structures of SrV₂O₆ and individual VO₄ units also occur in SrO-borovanadate glasses. The SrV₂O₆ and VO_n polyhedra predominate in the low B₂O₃-containing SrO-borovanadate glasses as B substitutes into the V sites of the various VO_n polyhedra and only when the concentration of B₂O₃ exceeds the SrO content do BO_n structures appear. This qualitative picture of three distinct structural groupings for Sr-vanadate and Sr-borovanadate glasses is consistent with the proposed glass structure on previous IR and extended X-ray absorption fine structure (EXAFS) studies on these types of glasses. The conductivity results were analyzed with reference to theoretical models existing in the literature and the analysis shows that the conductivity data are consistent with Mott's nearest neighbor hopping model. Analysis of the conductivity data shows that they are consistent with Mott's nearest neighbor hopping model. However, both Mott VRH and Greaves models are suitable to explain the data. Schnakenberg's generalized polaron hopping model is also consistent with temperature dependence of activation energy. However, various model parameters such as density of states, hopping energy, etc. obtained from the best fits were not found to be in accordance with the prediction of the Mott model.     

Luminescence studies on ZnO-P2O5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Zinc phosphate glasses doped with Gd₂O₃:Eu nanoparticles and Eu₂O₃ were prepared by conventional melt-quench method and characterized for their luminescence properties. Binary ZnO-P₂O₅ glass is characterized by an intrinsic defect centre emission around 324 nm. Strong energy transfer from these defect centres to Eu³⁺ ions has been observed when Eu₂O₃ is incorporated in ZnO-P₂O₅ glasses. Lack of energy transfer from these defect centres to Eu³⁺ in Gd₂O₃:Eu nanoparticles doped ZnO-P₂O₅ glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between the luminescent centre and Eu³⁺ ions. Both doped and undoped glasses have the same glass transition temperature, suggesting that the phosphate network is not significantly affected by the Gd₂O₃:Eu nanoparticles or Eu₂O₃ incorporation.     

Emission features of Ho ion in Nb2O5, Ta2O5 and La2O3 mixed Li2O-ZrO2-SiO2 glasses

Li₂O-ZrO₂-SiO₂: Ho³⁺ glasses mixed with three interesting d-block elemental oxides, viz., Nb₂O₅, Ta₂O₅ and La₂O₃, were prepared. Optical absorption and photoluminescence spectra of these glasses have been recorded at room temperature. The luminescence spectra of Nb₂O₅ and Ta₂O₅ mixed Li₂O-ZrO₂-SiO₂ glasses (free of Ho³⁺ ions) have also exhibited broad emission band in the blue region. This band is attributed to radiative recombination of self-trapped excitons (STEs) localized on substitutionally positioned octahedral Ta⁵⁺ and Nb⁵⁺ ions in the glass network. The Judd-Ofelt theory was successfully applied to characterize Ho³⁺ spectra of all the three glasses. From this theory various radiative properties, like transition probability A, branching ratio β_r and the radiative lifetime τ_r, for ⁵S₂ emission levels in the spectra of these glasses have been evaluated. The radiative lifetime for ⁵S₂ level of Ho³⁺ ions has also been measured and quantum efficiencies were estimated. Among the three glasses studied the La₂O₃ mixed glass exhibited the highest quantum efficiency. The reasons for such higher value have been discussed based on the relationship between the structural modifications taking place around the Ho³⁺ ions.     

Dielectric dispersion in PbO-Sb2O3-As2O3:V2O5 glasses

Dielectric properties, viz. dielectric constant ε′, loss tan δ and a.c conductivity σ_ac (over a wide range of frequency and temperature) and dielectric breakdown strength of PbO-Sb₂O₃-As₂O₃ glasses doped with V₂O₅ (ranging from 0 to 0.5 mol%) are studied. Analysis of these results, based on optical absorption and ESR spectra, indicates that the insulating strength of the glasses is comparatively high when the concentration of V₂O₅ is about 0.3 mol% in the glass matrix.     

Comparative study of thermal stability and crystallization kinetics of 70B2O3-30Bi2O3 and 70B2O3-30PbO glasses

Glasses with compositions 70B₂O₃-30Bi₂O₃ and 70B₂O₃-30PbO have been prepared and studied by differential thermal analysis (DTA). The crystallization kinetics of the glasses were investigated under non-isothermal conditions. From the dependence of glass-transition temperature (T_g) on heating rate, the activation energy for the glass transition was derived. Similarly the activation energy of the crystallization process was determined. Thermal stability of these glasses were achieved in terms of the characteristic temperatures, such as glass-transition temperature, T_g, onset temperature of crystallization, T_in, temperature corresponding to the maximum crystallization rate, T_p, beside the kinetic parameters, K(T_g) and K(T_p). The results revealed that 70B₂O₃-30PbO is more stable than 70B₂O₃-30Bi₂O₃. The crystallization mechanism is characterized for both 70B₂O₃-30Bi₂O₃ and 70B₂O₃-30PbO glasses (kinetic exponent n=2.06 for 70B₂O₃-30Bi₂O₃, and n=3.03 for 70B₂O₃-30PbO). The phases at which the glass crystallizes after the thermal process were identified by X-ray diffraction.     

Modification in structural and optical properties of ZnO, CeO2 doped Al2O3-PbO-B2O3 glasses

The structural and optical analysis of glasses is carried out by XRD, FTIR, density and UV visible spectroscopic measurement techniques. XRD results have confirmed the glassy nature of the samples. The FTIR spectral analysis reveals that with the combined presence of ZnO and CeO₂ contents in Al₂O₃-PbO-B₂O₃ glasses, more BO₃ groups are transformed into BO₄. The optical analysis reveals that optical band gap energy decreases more for CeO₂-ZnO-Al₂O₃-PbO-B₂O₃ glasses (from 2.28 to 1.84 eV). The presence of CeO₂ and ZnO in the glass samples causes more compaction of the borate network due to the formation of more BO₄ groups and the presence of ZnO₄ groups, which results an increase in density, refractive index and decrease of molar volume.     

Role of WO3 in structural and optical properties of WO3-Al2O3-PbO-B2O3 glasses

Glass samples of composition xAl₂O₃-20PbO-(80−x)B₂O₃ and xWO₃-xAl₂O₃-20PbO-(80−2x)B₂O₃ with x varying from 0% to 10% mole fraction are prepared by melt quench technique. The optical band gap decreases (from 3.21 to 2.37 eV) more for WO₃-Al₂O₃-PbO-B₂O₃ glasses with an addition of WO₃ content. The FTIR spectral studies have pointed out the conversion of structural units of BO₃ to BO₄ and WO₄ to WO₆ in these glasses. The increase in density from 4.51 to 5.80 g cm⁻³ for WO₃-Al₂O₃-PbO-B₂O₃ glasses is observed with an increase in WO₃ content. This is observed that the atomic structure changes more with the incorporation of WO₃. This is due to the formation of WO₆, WO₄ and BO₄ units.