| 红外辐射多相复合粉体常温发射率的提高及波段宽化 |
| |
| 引用本文： | 张孔,刘庆峰,刘茜.红外辐射多相复合粉体常温发射率的提高及波段宽化[J].高等学校化学学报,2011,32(11):2498-2503. |
| |
| 作者姓名： | 张孔 刘庆峰 刘茜 |
| |
| 作者单位： | 1. 中国科学院上海硅酸盐研究所,高性能陶瓷和超微结构国家重点实验室,上海200050;中国科学院研究生院,北京100049
2. 中国科学院上海硅酸盐研究所,高性能陶瓷和超微结构国家重点实验室,上海200050 |
| |
| 基金项目： | 中国科学院上海硅酸盐研究所创新项目基金(批准号:SCX0620)资助 |
| |
| 摘 要： | 通过多相成分分析,以镁铝硝酸盐、正硅酸乙酯、钛酸四丁酯和氧氯化锆等为原料,采用溶胶-凝胶燃烧法合成了新型复相氧化物粉体,研究了Ni和Fe离子掺杂及粉体细化对红外辐射率的提高及波段宽化的影响.XRD物相分析发现,在1100～1200℃范围内煅烧可获得结晶良好的氧化物粉体,该粉体的结构为堇青石及金红石等多相结构.采用碳酸氢...
|
| 关 键 词： | 复合氧化物粉体 溶胶-凝胶 掺杂 红外辐射率 晶格畸变 |
| 收稿时间： | 2010-11-10 |
Infrared Emission Enhancement and Wavelength Widen of Composite Oxide Powders |
| |
| ZHANG Kong,LIU Qing-Feng,LIU Qian.Infrared Emission Enhancement and Wavelength Widen of Composite Oxide Powders[J].Chemical Research In Chinese Universities,2011,32(11):2498-2503. |
| |
| Authors: | ZHANG Kong LIU Qing-Feng LIU Qian |
| |
| Institution: | ZHANG Kong1,2,LIU Qing-Feng1,LIU Qian1 (1.State Key Labcratory of High Ceramics and Superfine Microstructure,Shanghai Institute of Ceramics,Chinese Academy of Sciences,Shanghai 200050,China,2.Graduate University of Chinese Academy of Sciences,Beijing 100049,China) |
| |
| Abstract: | A new kind of nanoscaled composite oxide powders was prepared by a sol-gel combustion method to study the effect of doping on the infrared radiation. When calcined at 1100~1200 ℃, anatase, zircon and cordierite phases were crystallized in the resultant composite powders, proved from XRD patterns. The microstructural features and infrared emission performance were observed and measured by TEM and IR spectrometer. The infrared emission performance of the powder-packed disk samples showed a higher emissivity in a wide infrared range of 1~22 μm. The infrared emission peak appeared at about 10 μm with a maximal value of 98%. With the doping of Ni2+ and Fe2+, the infrared emission intensity increased obviously, due to the enhancement of anharmonic interaction, causing lattice deformation of the substituted cordierite structure. |
| |
| Keywords: | Composite oxide powder Sol-gel Doping Infrared radiation Lattice deformation |