Visible photoluminescence in porous GaAs capped by GaAs

A typical porous structure with pores diameters ranging from 10 to 50 nm has been obtained by electrochemical etching of (1 0 0) heavily doped p-type GaAs substrate in HF solution. Room temperature photoluminescence (PL) investigations of the porous GaAs (π-GaAs) reveal the presence of two PL bands, I₁ and I₂, located at 1.403 and 1.877 eV, respectively. After GaAs capping, the I₁ and I₂ PL bands exhibit opposite shift trends. However, the emission efficiency of these two bands is not strongly modified. Low temperature PL of capped porous GaAs versus injection levels shows that the I₁ PL band exhibits a red shift while the I₂ PL band exhibits a blue shift with increasing injection levels. The I₂ PL band intensity temperature dependence shows an anomalous behaviour and its energy location shows a blue shift as temperature increases. The observed PL bands act independently and are attributed to electron – hole recombination in porous GaAs and to the well-known quantum confinement effects in GaAs nanocrystallites. The I₂ PL band excitation power and temperature dependencies were explained by the filling effect of GaAs nanocrystallites energy states.