| DBS包覆TiO2纳米粒子的表面光伏及光致发光性能 |
| |
| 引用本文： | 王百齐,井立强,屈宜春,孙志华,薛连鹏,姬少靓,付宏刚.DBS包覆TiO2纳米粒子的表面光伏及光致发光性能[J].化学物理学报,2005,18(5):807-811. |
| |
| 作者姓名： | 王百齐 井立强 屈宜春 孙志华 薛连鹏 姬少靓 付宏刚 |
| |
| 作者单位： | 哈尔滨工业大学应用化学系，黑龙江大学化学化工与材料学院，黑龙江大学化学化工与材料学院，黑龙江大学化学化工与材料学院，黑龙江大学化学化工与材料学院，黑龙江大学化学化工与材料学院，哈尔滨工业大学应用化学系 哈尔滨150001，物理化学重点实验室，哈尔滨150080，物理化学重点实验室，哈尔滨150080，物理化学重点实验室，哈尔滨150080，物理化学重点实验室，哈尔滨150080，物理化学重点实验室，哈尔滨150080，哈尔滨150001，黑龙江大学化学化工与材料学院，物理化学重点实验室，哈尔滨150080 |
| |
| 基金项目： | ProjectsupportedbytheNationalNatureScienceFoundationofChina(20431030,20301006),theNatureScienceFoundationofHeilongjiangProvinceofChina(ZJG0404,B0305),theScienceFoundationforExcellentYouthofHeilongjiangProvinceofChina(2002),theSupportingPlanofEducationBureauofHeilongjiangProvince(1054G035),thePostdoctoralScienceFoundationofChina(20040350168)andtheScienceFoundationforExcellentYouthofHeilongjiangUniversityofChina(2003). |
| |
| 摘 要： | 采用溶胶-水热法合成了十二烷基苯磺酸钠(DBS)包覆的TiO2纳米粒子,并利用X射线衍射仪、透射电镜、表面光电压谱(SPS)和光致发光光谱(PL)等对样品进行表征.重点探讨了DBS包覆的适宜条件及DBS包覆对TiO2光伏和发光等性质的影响.结果表明,进釜前pH值在4.5~5.5,DBS用量为TiO2质量的1.0%~3.0%时,能够获得理想包覆.在水热过程中,DBS的引入对锐钛矿型TiO2微晶的生长有抑制作用.由于DBS的包覆,使TiO2的SPS和PL信号强度显著下降,这可能与磺酸基的吸电子性以及表面缺陷等的减少有关.
|
| 关 键 词： | TiO2 DBS 表面包覆 表面光伏 光致发光 |
| 收稿时间： | 2004/10/15 0:00:00 |
SPV and PL Performances of TiO2 Nanoparticles Capped with DBS |
| |
| Wang Baiqi,Jing Liqiang,Qu Yichun,Sun Zhihu,Xue Lianpeng,Ji Shaojing and Fu Honggang.SPV and PL Performances of TiO2 Nanoparticles Capped with DBS[J].Chinese Journal of Chemical Physics,2005,18(5):807-811. |
| |
| Authors: | Wang Baiqi Jing Liqiang Qu Yichun Sun Zhihu Xue Lianpeng Ji Shaojing and Fu Honggang |
| |
| Institution: | Wang Baiqi~a,Jing Liqiang~b,Qu Yichun~b,Sun Zhihua~b,Xue Lianpeng~b,Ji Shaojing~b,Fu Honggang~ |
| |
| Abstract: | The TiO_2 nanoparticles capped with sodium dodecylbenzenesulfonate (DBS) were synthesized by a sol-hydrothermal method, and were also characterized by XRD, TEM, Surface Photovoltage Spectroscopy (SPS) and Photoluminescence (PL). The effects of capping DBS on photovoltage and photoluminescence performances of TiO_2 nanoparticle as well as appropriate capping conditions were principally investigated. The results show that the capping situation is desirable when the pH value and adding DBS amount are in the range of 4.5-5.5 and (1.0%)-3.0% of TiO_2 weight in advance of the hydrothermal process, respectively. The added DBS could inhibit the growth of anatase crystallite during the hydrothermal process. Moreover, the intensities of SPS and PL of TiO_2 nanoparticle decreased after DBS was capped, which is possibly attributed to the electrophilic property of sulfonic acid group (-SO_3-) as well as the decrease of surface defect. |
| |
| Keywords: | TiO_2 DBS Surface capping Surface photovoltage Photoluminescence |