在硅酸盐矿物,玻璃和熔体中Si和Al的配位与局部结构：K—边 …

本文采用步辐射的ＳｉＫ－边Ｘ－射线吸收近边结构（ＸＡＮＥＳ）谱研究了Ｓｉ在ＳｉＯ２－Ｐ２Ｏ５和Ｎａ２Ｏ－ＳｉＯ２－Ｐ２Ｏ５的低压磷硅酸盐玻璃中结构与配位，以及Ｓｉ的配位几何随玻璃中Ｐ２Ｏ５含量而变化：同步辐射的Ａｌ Ｋ－边ＸＡＮＥＳ谱研究了Ａｌ在铝硅酸盐成分为ＮａＡｌＳｉ２Ｏ６－ＮａＡｌＳｉ３Ｏ８的玻璃和熔体中的配位和局部结构，并提供了直接的实验证据该成分的玻璃体系中由于压力的变化所诱导Ａｌ配位的

Coordination and Local Structure of Si and Al in Silicate Glasses and Melts:X-ray Absorption Spectroscopic Study

The coordination and local structure of Si and Al in silicate glasses and melts have been studied using Si and Al K-edge X-ray absorption spectroscopy for the first time. It has been verified that in SiO2-P2O5 and Na2O-SiO2-P2O5 join phosphate silicate glasses, Si atoms remains tetrahedrally coordinated with oxygen when the content of P2O5 is below 32 mol%, but partial Si atoms become octahedrally coordinated with oxygen when the content of P2O5 increases above 32 mol%, and the proportion of the octahedrally coordinated Si atoms increases with the increasing content of P2O5. It has also been demonstrated that Al remains four-fold coordinated with oxygen in ambient NaAlSi2O6-NaAlSi3O8 glasses, but in the same composition glasses quenched at 4.4 GPa and 1,575 degrees C, partial Al atoms becomes five- and six-fold coordinated with oxygen, and at the same pressure and temperature, the proportions of five- and six-fold coordinated Al atoms increases with the increasing content of NaAlSi2O6 in the glasses. Thus, the pressure-induced coordination change of Al in aluminosilicate glasses and melts has been observed for the first time by Al K-edge X-ray absorption spectroscopy.