Dielectric and conduction mechanism studies of PVA-orthophosphoric acid polymer electrolyte

Polyvinyl alcohol (PVA)-based proton conducting polymer electrolytes have been prepared by the solution cast technique. The conductivity is observed to increase from 10⁻⁹ to 10⁻⁴ S cm⁻¹ as a result of orthophosphoric acid (H₃PO₄) addition. The plot of conductivity vs temperature shows that a phase transition occurred at 343 K in the sample PVA-33 wt% H₃PO₄. The β-relaxation peak is observed at 313 K. The glass transition temperature of PVA-33 wt% H₃PO₄ is 343 K. Orthophosphoric acid seems to play a dual role, i.e., as a proton source and as a plasticizer. The ac conductivity σ _ac = Aω ^s was also calculated in the temperature range from 303 to 353 K. The conduction mechanism was inferred by plotting the graph of s vs T from which the conduction mechanism for sample PVA-17 wt% H₃PO₄ was inferred to occur by way of the overlapping large polaron tunneling (OLPT) model and the conduction mechanism for the sample PVA-33 wt% H₃PO₄ by way of the correlated barrier height (CBH) model.