Isotope effect for transport and magnetic properties of La 0.35 Pr 0.35 Ca 0.3 MnO 3 thin films

The effect of ¹⁶ O → ¹⁸ O isotope substitution on electrical resistivity, magnetoresistance, and ac magnetic susceptibility was studied for La_0.35Pr_0.35Ca_0.3MnO₃ epitaxial thin films deposited onto LaAlO₃ and SrTiO₃ substrates. For the films on LaAlO₃, the isotope substitution resulted in the reversible transition from a metal-like to insulating state. The applied magnetic field ( H ≥ 2 T) transformed the sample with ¹⁸O back to the metallic state. The films on SrTiO₃ remained metallic at low temperatures for both ¹⁶O and ¹⁸O, but the shift of the resistivity peak corresponding to onset of metallic state exceeded 63 K after ¹⁶ O → ¹⁸ O substitution. The temperature dependence of both resistivity and magnetic susceptibility was characterized by hysteresis, especially pronounced in the case of the films on LaAlO₃. Such a behavior gives certain indications of the phase separation characteristic of interplay between ferromagnetism and charge ordering. Received 11 February 2000 and Received in final form 13 September 2000