Thermoluminescence studies on Cu-doped Li2B4O7 single crystals

Lithium tetraborate (Li₂B₄O₇) is a tissue equivalent material and single crystals of this material doped with Cu are promising for dosimetric applications. In the present study highly transparent single crystals of lithium tetraborate (Li₂B₄O₇) doped with Cu (0.5 wt%) have been grown using the Czochralski technique. The Li₂B₄O₇:Cu crystals were studied using photoluminescence, X-ray diffraction (XRD), UV-vis transmission, time resolved fluorescence and thermoluminescence (TL) techniques. The TL readout of Li₂B₄O₇:Cu crystals showed two well-defined glow peaks at 402 K (peak-1) and 513 K (peak-2) for a 4 K/s heating rate. While the low temperature TL peak-1 fades completely within 24 h at room temperatures, the main dosimetric peak-2 remains the same. The TL sensitivity of the grown single crystal is found to be 3.3 times that of a conventional TL phosphor, TLD-100. The Li₂B₄O₇:Cu crystals showed a linear TL dose-response in the range from 1 mGy to 1 kGy. The TL analysis using a variable dose method revealed first order kinetics for both the peaks. Trap depth and frequency factor for peak-1 were found to be 0.81 eV and 5.2×10⁹ s⁻¹, whereas for peak-2 the values were 1.7 eV and 1.7×10¹⁶ s⁻¹, respectively.