The study of below and above band-edge imperfection states in In2S3 solar energy materials

β-In₂S₃ is a nontoxic buffer layer material usually used in a thin-film solar cell due to a lot of vacancies and surface states naturally existing in the crystal to assist in photoelectric conversion. Transition metal (TM)-incorporated β-In₂S₃ has also been proposed to increase conversion efficiency in In₂S₃ since multi-photons absorption by intermediate band (IB) would happen in the sulfide. In this paper, single crystals of undoped and Nb-doped β-In₂S₃ have been grown by the chemical vapor transport (CVT) method using ICl₃ as a transport agent. Optical properties of the imperfection states of the crystals are probed by thermoreflectance (TR), photoconductivity (PC), photoluminescence (PL), surface photoconductive response (SPR), optical absorption and photo–voltage–current (photo V–I) measurements. The TR and optical-absorption measurements confirmed that the undoped and Nb-doped β-In₂S₃ are direct semiconductors with energy gap of 1.935 eV for undoped β-In₂S₃, 1.923 eV for β-In₂S₃:Nb_0.005, and 1.901 eV for β-In₂S₃:Nb_0.01. For undoped β-In₂S₃, PC and PL measurements are used to characterize defect transitions below band gap. The above band-edge transitions of undoped β-In₂S₃ have also been evaluated using PL, PC, and SPR measurements. For the evaluation of Nb-doped β-In₂S₃, an intermediate band with energy of ∼0.4 eV below the conduction band edge has been detected in the TR measurements in both β-In₂S₃:Nb_0.005 and β-In₂S₃:Nb_0.01. The photo V–I measurements also verified that the photoelectric-conversion efficiency would be enhanced in the β-In₂S₃ with higher niobium content. Based on the experimental analyses, the optical behavior of the defects, surface states, and IB (formed by Nb) in the In₂S₃ crystals is thus explored.