Surface characterization and luminescent properties of SrAl2O4:Eu,Dy nano thin films

SrAl₂O₄:Eu²⁺, Dy³⁺ thin films were grown on Si (1 0 0) substrates in different atmospheres using the pulsed laser deposition (PLD) technique. The effects of vacuum, oxygen (O₂) and argon (Ar) deposition atmospheres on the structural, morphological and photoluminescence (PL) properties of the films were investigated. The films were ablated using a 248 nm KrF excimer laser. Improved PL intensities were obtained from the unannealed films prepared in Ar and O₂ atmospheres compared to those prepared in vacuum. A stable green emission peak at 520 nm, attributed to 4f⁶5d¹→4f⁷ Eu²⁺ transitions was obtained. After annealing the films prepared in vacuum at 800 °C for 2 h, the intensity of the green emission (520 nm) of the thin film increased considerably. The amorphous thin film was crystalline after the annealing process. The diffusion of adventitious C into the nanostructured layers deposited in the Ar and O₂ atmospheres was most probably responsible for the quenching of the PL intensity after annealing.