Biodegradable poly(carbonate‐ether)s with thermoresponsive feature at body temperature

Novel biodegradable poly(carbonate‐ether)s (PCEs) with lower critical solution temperature (LCST) at body temperature were synthesized by copolymerization of CO₂ and ethylene oxide (EO) under double metal cyanide (DMC) catalyst. The PCEs showed carbonate unit (CU) content of 1.0–42.4 mol % and molecular weight of 2.7–247 kg/mol, which exhibited reversible thermoresponsive feature in deionized water with LCST in a broad window from 21.5 to 84.1 °C. The LCST was highly sensitive to the CU content and the molecular weight of PCEs, and it showed a linear relation with CU content for PCEs with similar molecular weight. In particular, aqueous solution of PCE with a 26.0 mol % of CU showed an LCST around 36.1 °C, which was very close to the body temperature. Interestingly, it was found that the phase transition behavior changed with PCE concentration. For PCE with M_n of 2.7 kg/mol and CU content of 30.0 mol %, the LCST increased from 21.5 to 36.7 °C when the PCE concentration changed from 10 to 1 g/L. Dynamic light scattering indicated that the phase transition was possibly due to a coil‐to‐globule transition. The thermoresponsive biodegradable PCE with LCST at body temperature is promising for biomedical applications, especially for in vivo applications. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013