The annealing behaviors of photoluminescence of SiO_x and Er-doped SiO_x grown by molecular beam epitaxy in the wavelength range of visible and infrared light are studied. For SiO_x, four PL bands located at 510, 600, 716 and 810 nm, respectively, are observed. For Er-doped SiO_x, the 716 nm band, which is believed to be originated from the electron–hole recombination at the interface between crystalline Si and amorphous SiO₂, disappears in the annealing temperature range of 500–900°C. It is suggested the enhancement of Er luminescence is partially due to the energy transfer from the recombination at the interface between crystalline Si and SiO₂ to Er ions.