Structural and magnetic properties of Co1−xZnxFe2O4 nanoparticles by co-precipitation method

Co_1−xZn_xFe₂O₄ nanoparticles were prepared by co-precipitation method with x varying from 0 to 1.0. The powder samples were characterized by X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and Fourier transform infrared spectroscopy (FTIR). The average crystallite sizes of the particles were determined from XRD. X-ray analysis showed that the samples were cubic spinel. The average crystallite size (D_aveXR) of the particles precipitated was found to vary from 6.92 to 12.02 nm decreasing with the increase in zinc substitution. The lattice constant (a_o) increased with the increase in zinc substitution. The specific saturation magnetization (M_S) of the particles was measured at room temperature. The magnetic parameters such as M_S, H_c, and M_r were found to decrease with the increase in zinc substitution. FTIR spectra of the Co_1−xZn_xFe₂O₄ with x varying from 0 to 1.0 in the range 400–4000 cm⁻¹ were reported. The spinel structure and the crystalline water adsorption of Co_1−xZn_xFe₂O₄ nanoparticles were studied by using FTIR.