| Abstract: | Polyimide containing an indan unit and alkyl moiety with a high molecular weight was prepared from 5,7‐diamino‐1,1,4,6‐tetramethylindan and 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride. This polyimide was amorphous and soluble in common organic solvents, such as tetrahydrofuran, chloroform, and cyclopentanone. Thermogravimetry of the polyimide showed good thermal stability, indicating that a 10% weight loss of the polyimide was observed at 500 °C in nitrogen. The glass‐transition temperature of the polyimide was not observed by DSC measurement between room temperature and 400 °C at a heating rate of 10 °C/min (Apparatus: DSC3100 MAC Science Co., Ltd.). Transparency of the polyimide at 365 nm was 80%. The polyimide acted as a photosensitive resist of negative type by UV radiation. The resist had a sensitivity of 31 mJ/cm2 and a contrast of 2.3 when it was developed with cyclopentanone at room temperature. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 423–428, 2002 |