Effect of post-annealing temperature on the microstructure and magnetic properties of Ce:YIG thin films deposited on Si substrates

Amorphous Ce₁Y₂Fe₅O₁₂ (Ce:YIG) thin films deposited on single crystal Si(1 0 0) and thermally oxidized Si(1 0 0) substrates by pulsed laser deposition were annealed in the temperature range of 700-1000 °C in air. The annealing temperature dependence of microstructure and magnetic properties of Ce:YIG films was studied using X-ray diffraction combined with vibrating sample magnetometer. The results show that single phase of polycrystalline Ce:YIG thin films can be obtained by the post-annealing of as-deposited films at the temperature of 700 °C. However, two steps of phase segregation of Ce:YIG occur as the post-annealing temperature increases: at first, Ce:YIG is decomposed into YIG and non-magnetic CeO₂ when annealed at 800 °C; then YIG continues to be decomposed forming Fe₂O₃ when the temperature is increased up to 900 °C. Consequently, the saturation magnetization of Ce:YIG films decreases first and then increases with the post-annealing temperature going up, which indicates that the saturation magnetization of Ce:YIG films is mainly related to the phase composition of the films. Meanwhile, the presence of SiO₂ buffer layer can significantly enhance the saturation magnetization of Ce:YIG films.