Low‐temperature Synthesis of Peony‐like Spinel Li4Ti5O12 as a High‐performance Anode Material for Lithium Ion Batteries

Peony‐like spinel Li₄Ti₅O₁₂ was synthesized via calcination of precursor at the temperature of 400°C, and the precursor was prepared through a hydrothermal process in which the reaction of hydrous titanium oxide with lithium hydroxide was conducted at 180°C. The as‐prepared product was investigated by SEM, TEM and XRD, respectively. As anode material for lithium ion battery, the Li₄Ti₅O₁₂ obtained was also characterized by galvanostatic tests and cyclic voltammetry measurements. It is found that the peony‐like Li₄Ti₅O₁₂ exhibited high rate capability of 119.7 mAh·g⁻¹ at 10 C and good capacity retention of 113.8 mAh·g⁻¹ after 100 cycles at 5 C, and these results indicate the peony‐like Li₄Ti₅O₁₂ has promising applications for lithium ion batteries with high performance.