共沉淀法制备Y_2O_2S∶Eu~(3+),Mg~(2+),Ti~(4+)红色长余辉材料

用共沉淀法制备了Y2O2S∶Eu3 ,Mg2 ,Ti4 红色长余辉材料。测量了材料的电子显微形貌、晶体结构和发射光谱。通过与固相法制备的Y2O2S∶Eu3 ,Mg2 ,Ti4 长余辉材料比较,发现两种方法都可以制备粒度基本相同的纯相Y2O2S基质晶体,但共沉淀法样品的颗粒结构更松散。研究了Eu3 浓度对两种方法制备样品的谱线发射强度的影响,通过比较共沉淀法和高温固相法制备的样品中Eu3 的5D1→7F3较高能级跃迁的587.6 nm谱线强度随Eu3 浓度的变化,发现共沉淀法更有利于Eu3 均匀进入Y2O2S基质晶格而形成有效的发光中心。     

Ultraviolet Luminescence in Mg0.12Zn0.88O Alloy Films

We investigate the origin of ultraviolet （UV） emission from Mg0.12 Zn0.88 O alloy thin films with a wurtzite structure fabricated on c-plane Al2O3 substrates by plasma assisted molecular beam epitaxy. At room temperature, the absorption edge and UV emission band of the Mg0.12Zn0.88O film shift to high-energy side compared with ZnO films. Temperature dependence of the photoluminescence spectra shows that the UV emission is composed of free exciton and neutral donor bound exciton emissions. Two-step dissociation processes of the UV emission are observed with the increasing temperature. The thermal quenching mechanism is attributed to the dissociation of the free exciton from the neutral donor bound exciton in the low temperature region and the dissociation of free electron and hole from the free exciton in the high temperature region.     

Dextran-modified iron oxide nanoparticles

Dextran-modified iron oxide nanoparticles were prepared by precipitation of Fe（Ⅱ） and Fe（Ⅲ） salts with ammonium hydroxide by two methods. Iron oxide was precipitated either in the presence of dextran solution, or the dextran solution was added after precipitation. In the second method, the iron oxide particle size and size distribution could be controlled depending on the concentration of dextran in the solution. The nanoparticles were characterized by size-exclusion chromatography, transmission electron microscopy and dynamic light scattering. Optimal conditions for preparation of stable iron oxide colloid particles were determined, The dextran/iron oxide ratio 0-0,16 used in precipitation of iron salts can be recommended for synthesis of nanoparticles suitable for biomedical applications, as the colloid does not contain excess dextran and does not coagulate.     

La1-xNdxSrCoO4催化剂的合成及其催化性能

采用聚丙烯胺溶胶-凝胶法制备了类钙钛矿La1-xNDxSrCoO4(x=0.1～0.9)复合氧化物催化剂,考察了其对CO和C3H8的催化氧化活性,并运用XRD、IR和TPR等手段对催化剂进行了表征.结果表明,所制备的样品均具有K2NiF4型结构,适量Nd2O3的加入增加了LaSrCoO4的催化活性,使LaSrCoO4催化剂粒度变小、晶格畸变率变大及与氧的结合能力减弱,从而有利于CO和C3H8氧化活性的提高.     

液晶显示器用导电粉的扫描电镜图像

液晶显示器用导电粉的形状、尺寸及偏差对于液晶显示屏的质量控制来说是非常重要的。论述了液晶显示器(LCD)用导电粉的作用和性能要求。给出了液晶显示器用导电粉的扫描电镜图像。该图像对观测导电粉的粒径分布、导电粉在导电点中的浓度和分析导电点缺陷、提高液晶显示器的产品质量具有一定的意义。     

不同溶剂体系中改性氢氧化镁的分散行为

研究了不同的表面改性剂对超细氢氧化镁的表面改性.并分别以水和乙醇为溶剂,研究了表面改性后氢氧化镁的分散行为.实验结果表明,以水为溶剂的体系,六偏磷酸钠分散性能最好,而以乙醇为溶剂,硅烷偶联剂KH-550分散性能最好,其用量为基体量的5%左右,可使制备的超细氢氧化镁粒径达到0.2 μm尺度以下.试验结果对进一步认识超细氢氧化镁的性质及其应用具有重要意义.     

电沉积制备金属超细Cu粉的研究

探讨了超细铜粉电沉积制备过程中阴极电流密度对粉体粒径的影响机制。结果表明:电流密度的改变对阴极过电位影响显著,电流密度从0.04A/cm2变化到0.1 A/cm2时,过电位从4.08V变化到9.96V;而过电位的变化直接引起粉体粒径的变化,粒径从大约50nm变化到700nm。分析表明,高电流密度可以获得较高的阴极过电位;在高的阴极过电位条件下,新核的生成速率高且稳定存在的晶核临界半径小,使得粉体粒径变细。     

退火温度对Fe基纳米晶粉芯磁致频移特性影响的研究

研究了充有不同温度退火Fe基纳米晶粉芯LC回路的磁致频移特性（MFS），发现充有不同温度退火Fe基纳米晶粉芯LC回路的磁致频移不同，充有经600℃退火Fe基纳米晶粉芯LC回路的磁致频移最灵敏。     

矿渣粉加固粉土的理论分析及路用性能研究

提出了矿渣粉加固粉土的相关理论。将矿渣粉在加固土中的作用归结为火山灰胶凝效应和微集料填充效应,而火山灰胶凝效应又可进一步归结为水化作用、激发作用和离子交换作用;认为微集料填充效应与矿渣粉细度极为相关;用框图归纳了矿渣粉加固土的两种作用效应。进行了矿渣粉、石灰粉加固土无侧限饱水抗压强度、水稳定性、冻稳定性、温度收缩和干燥收缩等路用性能试验,并进行比较。结果表明,矿渣粉加固土所测路用性能指标优于石灰粉加固土。为工程应用提供了试验依据。