Poly(vinyl chloride)-paste/clay nanocomposites: Investigation of thermal and morphological characteristics

The paper concentrates on poly(vinyl chloride) - PVC - from the point of nanocomposite characterisation through thermal degradation of samples, evolution of the changes caused by elevating temperature using TGA, FTIR and Congo Red methods combined with morphological characterisation by XRD and TEM analyses. A novel method of PVC-paste/nanocomposite preparation while processing was used. During preparation, PVC plasticizer was mixed with clay, both natural and organophilic, and the suspension was then compounded with the other components. Two factors were followed: effect of shearing alone, and in combination with temperature. As is presented, the type of nano-filler and its chemical modifier have obvious influence on final properties either thermal or morphological. Presented contribution follows previous part of investigation and brings further information from PVC-paste/nanocomposite field.     

基于超分子结构共掺杂纳米复合薄膜的制备与荧光特性

为改善功能分了的特性,提出一种基于金属纳米粒子-偶氮染料复合物共掺杂超分子结构功能材料的设计新方法.并依照此方法制备出复合材料,观测了其显微结构,测量了其紫外-可见光吸收,研究了该超分子结构复合体系的荧光特性.实验发现,由于金属银纳米粒子的掺杂,使得超分子结构复合体系中功能分子甲基橙在溶液态体系的荧光强度增强近5倍,而在两种不同结构(共混结构和包覆结构)的薄膜态超分子结构体系中,其荧光强度分别被猝灭15%和20%.研究结果表明,复合膜中采用超分子结构完全能够改善功能分子的特性.     

Role of montmorillonite in flame retardancy of ethylene-vinyl acetate copolymer

The effects of non-treated (MMT), organophilic (OMM), and olefin/silicone polymer intercalated (IMM) montmorillonites on the thermal stability of ethylene-vinyl acetate copolymer (EVA) and on the flammability of magnesium hydroxide filled EVA were studied. The influence of various treatments on the delamination of montmorillonites in EVA was detected by rheological measurements and by Raman microscopy. The latter was a unique method for rapid detection of the dispersion also in highly filled EVA. Enhancement of thermo-oxidative stability of EVA and flame-retarded EVA could be observed by thermal analysis in the presence of variously treated montmorillonites. The flame-retardant efficiency of magnesium hydroxide was improved by simultaneous application of MMT and IMM. The increased performance of magnesium hydroxide was explained by the rheological effect of the IMM, catalytic effect of MMT and chemical interactions of montmorillonites with the metal hydroxide.     

PREPARATION OF POLYSULFONAMIDE/TiO2 NANOCOMPOSITES BY SOL-GEL

Polysulfonamide (PSA) was synthesized at room temperature, the polymerization based on terephthaloyl chloride and 3,3 '-diaminodiphenylsulfone in the common solvent N,N -Dimethyl-acetamide (DMAc). Polysulfonamide/titanium oxide nanocomposites were prepared by sol-gel method. Tetrabutyl titanate(TBT) was added into the polysulfonamide solution, at the same time ,some water was mixed to make the TBT hydrolyze. In the process, hydrochloric acid was used to catalyze the reaction. The polysulfonamide chemistry structure was characterized by FT-IR spectrum. Atomic force microscopy (AFM) was employed to observe the microstructure of the composite film. The thermal property was investigated by TGA.The results show that we have succeeded to synthesize the polysulfonamide, TiO2particles were well distributed in the composite film and average size was about 20 nm on average, the heat-resistance of nanocomposite was batter than the pure polysulfonamide.     

Preparation and rheological characterization of poly(n-butyl methacrylate)/montmorillonite composites

Intercalated nanocomposites constituted of poly(butyl methacrylate) (PBMA) as the matrix and an organically modified montmorillonite as the nanosize filler were prepared and rheologically characterized in detail. The rheological behavior of the composites showed dependence on both temperature and clay content. For composites of low clay contents, the steady shear viscosity showed a Newtonian plateau in the low shear rate region at low temperatures and the plateau was replaced by a shear-thinning curve when the temperature was raised. For composites of higher clay contents, strong shear-thinning behavior were observed at all shear rates and all temperatures. The viscoelastic data of the composites showed unusual terminal behavior of a decreasing terminal slope at low frequencies with increasing temperature and clay loading. X-ray diffraction spectra showed that annealing process at higher temperatures shifted the Bragg reflection peaks to a lower angle and broadened the peaks, which provided the evidence for the existence of a temperature-induced solid-like structure that was responsible for the shear thinning and the unusual terminal viscoelastic behavior.     

PREPARATION OF POLY（METHYL METHACRYLATE）/LAYERED DOUBLE HYDROXIDES NANOCOMPOSITES via in situ SOLUTION POLYMERIZATION

An exfoliated layered double hydroxides/poly(methyl methacrylate)(LDHs/PMMA)nanocomposite was prepared by in situ solution polymerization of methyl methacrylate(MMA)in the presence of 4-vinylbenzenesulfonate intercalated LDHs(MgAl-VBS LDHs).MgAl-VBS LDHs was prepared by the ion exchange method,and the structure and composition of the MgA1-VBS LDHs were determined by X-ray diffraction(XRD),infrared spectroscopy and elemental analysis.XRD and transmission electron microscopy(TEM)were employed to examine the structure of LDHs/PMMA nanocomposite.It was indicated that the LDHs layers were well exfoliated and dispersed in the PMMA matrix.The grafting of PMMA onto LDHs was confirmed by the extraction result and the weight fraction of grafted PMMA increased as the weight fraction of LDHs in the nanocomposites increased.     

Sugar-anionic clay composite materials: intercalation of pentoses in layered double hydroxide

The intercalation of non-ionized guest pentoses (ribose and 2-deoxyribose) into the Mg-Al and Zn-Al layered double hydroxides (LDHs) was carried out at 298 K by the calcination-rehydration reaction using the Mg-Al and Zn-Al oxide precursors calcined at 773 K. The resulting solid products reconstructed the LDH structure with incorporating pentoses, and the maximum amount of ribose intercalated by the Mg-Al oxide precursor was approximately 20 times that by the Zn-Al oxide precursor. The ribose/Mg-Al LDH was observed to have the expanded LDH structure with a broad (003) spacing of 0.85 nm. As the thickness of the LDH hydroxide basal layer is 0.48 nm, the interlayer distance of the ribose/Mg-Al LDH is 0.37 nm. This value corresponds to molecular size of ribose in thickness (0.36 nm), supporting that ribose is horizontally oriented in the interlayer space of LDH. The maximum amount of ribose intercalated by the Mg-Al oxide precursor was approximately 5 times that of 2-deoxyribose. Ribose is substituted only by the hydroxyl group at C-2 position for 2-deoxyribose. Therefore, the number of hydroxyl group of sugar is essentially important for the intercalation of sugar molecule into the LDH, suggesting that the intercalation behavior of sugar for the LDH was greatly influenced by hydrogen bond between hydroxyl group of the intercalated pentose and the LDH hydroxide basal layers.     

增容剂对聚丙烯/粘土纳米复合材料热分解动力学的影响

采用三单体固相接枝聚丙烯作为增容剂制备了聚丙烯粘土纳米复合材料.通过XRD和TEM表征了其纳米结构.利用动态TGA方法研究了聚丙烯和纳米复合材料的热稳定性.分别采用Flynn Wall Ozawa和Kissinger法研究了聚丙烯及其纳米复合材料的热分解动力学.结果都表明,蒙脱土的加入明显提高了聚丙烯的起始热分解温度,纳米复合材料热失重10%时的温度比聚丙烯提高40K左右;纳米复合材料的热分解温度区间明显比聚丙烯的窄;纳米复合材料热分解表观活化能明显增大,与聚丙烯相比提高50%以上.     

Thermal degradation studies of alkyl-imidazolium salts and their application in nanocomposites

Increasing the thermal stability of organically-modified layered silicates is one of the key points in the successful technical application of polymer-layered silicate nanocomposites on the industrial scale. To circumvent the detrimental effect of the lower thermal stability of alkyl ammonium-treated montmorillonite, a series of alkyl-imidazolium molten salts were prepared and characterized by elemental analysis, thermogravimetry (TGA) and thermal desorption mass spectroscopy (TDMS). The effect of counter ion, alkyl chain length and structural isomerism on the thermal stability of the imidazolium salts was investigated. Alkyl-imidazolium-treated montmorillonite clays were prepared by ion exchange of the imidazolium salts with Na-montmorillonite. These organically-modified clays were characterized by X-ray diffraction (XRD), TDMS and thermogravimetry coupled with Fourier transform infrared spectroscopy (TGA-FTIR), and compared to the conventional quaternary alkyl ammonium montmorillonite. Results indicate that the counter ion has an effect on the thermal stability of the imidazolium salts, and that imidazolium salts with PF₆⁻, N(SO₂CF₃)₂⁻ and BF₄⁻ anions are thermally more stable than the halide salts. A relationship was observed between the chain length of the alkyl group and the thermo-oxidative stability; as the chain length increased from propyl, butyl, decyl, hexadecyl, octadecyl to eicosyl, the stability decreased. The results also show that the imidazolium-treated montmorillonite has greater thermal stability compared to the imidazolium halide. Analysis of the decomposition products by FTIR provides an insight about the decomposition products which are water, carbon dioxide and hydrocarbons.     

苯并噁嗪中间体/蛭石插层纳米复合物热固化行为的研究

通过对双酚A型苯并嗪中间体 (BOZ A) 蛭石插层纳米复合物固化过程的分析表明长链烷基铵阳离子对BOZ A的热开环聚合反应没有表现出催化作用 ,也不影响纳米复合物的结构形态 .不同蛭石含量的插层纳米复合物 ,在形成不同纳米分散状态的纳米复合物的过程中 ,蛭石晶片对BOZ A的热开环聚合具有明显不同的阻碍作用 ,蛭石含量为 3%的插层纳米复合物 16 0℃的凝胶化时间较纯树脂延长约 7min ,活化能升高约8kJ mol,固化反应热焓降低约 14J g ,使得固化物的固化程度较纯树脂降低约 7%～ 10 % ,阻碍作用最大 ,其它含量的次之