Hybrid cyclotriphosphazene–polysiloxane–nano-SiO2 composites with improved mechanical properties

Starting from the functional cyclotriphosphazene, polysiloxane and nano-SiO₂ precursors, three new hybrid nanocomposites with reinforced mechanical properties were prepared. Young’s modulus values for all the composite samples are similar in the range of 7–11 MPa, stress at fracture increases with the nano-SiO₂ content increase in the material and reaches a maximum value of 36 MPa for the composite with 20% nano-SiO₂. The nanocomposites investigated are elastic and demonstrate the ability to be deformed without failure up to 54% strain.     

Hydrophobic Monomers Recognize Microenvironments in Hydrogel Microspheres during Free-Radical-Seeded Emulsion Polymerization

The three-dimensional structure of nanocomposite microgels was precisely determined by cryo-electron micrography. Several nanocomposite microgels that differ with respect to their nanocomposite structure, which were obtained from seeded emulsion polymerization in the presence of microgels, were used as model nanocomposite materials for cryo-electron micrography. The obtained three-dimensional segmentation images of these nanocomposite microgels provide important insights into the interactions between the hydrophobic monomers and the microgels, that is, hydrophobic styrene monomers recognize molecular-scale differences in polarity within the microgels during the emulsion polymerization. This result led to the formation of unprecedented multi-layered nanocomposite microgels, which promise substantial potential in colloidal applications.     

Electrocatalytic Oxidation of Ethanol on the Surface of Graphene Based Nanocomposites: An Introduction and Review to it in Recent Studies

This review gives an overview of the electrochemical investigations about the properties of various types of graphene composites in the ethanol oxidation. Various routes to provide appropriate graphene‐based materials required electrochemical techniques for investigation of different types of the materials as well as their performance and efficacy in ethanol oxidation are discussed in detail. Furthermore, it is demonstrated that the incorporation of suitable materials, e. g. noble metals (graphene‐supported binary and ternary metal nanoparticles), metal oxides, conductive polymer, etc, with graphene results in excellent electrocatalytic activity, superb durability and selectivity in ethanol oxidation. Immobilization of electrocatalytically active NPs on graphene supports using physical approaches is considered as an effective route to prepare direct ethanol fuel cell (DEFC) anode catalysts.     

Nanocomposite hydrogel consisting of Na‐montmorillonite with enhanced mechanical properties

A new kind of nanocomposite (NC) hydrogel with Na‐montmorillonite (MMT) is presented in this article. The NC hydrogels were synthesized by free radical copolymerization of acrylamide and (3‐acrylamidopropyl) trimethylammonium chloride (ATC) in the presence of MMT and N,N′‐methylene‐bis‐acrylamide used as chemical cross‐linker. Due to the cation‐exchange reaction between MMT and ATC (cationic monomer) during the synthesis of NC hydrogels, MMT platelets were considered chemical “plane” cross‐linkers, different from “point” cross‐linkers. With increasing amount of MMT, the crosslinking degree enhanced, causing a decrease of the swelling degree at equilibrium. Investigations of mechanical properties indicated that NC hydrogels exhibited enhanced strength and toughness, which resulted from chemical interaction between exfoliated MMT platelets and polymer chains in hydrogels. Dynamic shear measurements showed that both storage modulus and loss modulus increased with increasing MMT content. The idea described here provided a new route to prepare hydrogels with high mechanical properties by using alternative natural Na‐MMT. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1020–1026     

Sulfonic acid-functionalized Fe3O4-supported magnetized graphene oxide quantum dots: A novel organic-inorganic nanocomposite as an efficient and recyclable nanocatalyst for the synthesis of dihydropyrano[2,3-c]pyrazole and 4H-chromene derivatives

In this research, the main emphasis has been focused on the preparation of a novel Fe₃O₄-supported propane-1-sulfonic acid-grafted graphene oxide quantum dots (Fe₃O₄@GOQD-O-(propane-1-sulfonic acid)) that it was readily synthesized via a five-step procedure as a hitherto unreported magnetic nanocatalyst. This newly prepared Fe₃O₄@GOQD-O-(propane-1-sulfonic acid) nanocomposite was structurally well-established by different analytical techniques including Fourier transform infrared (FT-IR), X-ray diffraction (XRD), energy-dispersive X-ray (EDX), thermal gravimetric analysis (TGA), field emission gun-scanning electron microscope (FESEM), high-resolution transmission electron microscopy (HRTEM) and vibrating sample magnetometer (VSM) analyses. The high catalytic performance of this nanocomposite was exhibited in one-pot synthesis of dihydropyrano[2,3-c]pyrazole and 4H-chromene derivatives under mild conditions. Low reaction times, excellent yields of the products, benignity of the catalyst, easy reaction work-up and magnetic recyclability of the catalyst are the main advantages of the present protocol. Also, our research indicated that the Fe₃O₄@GOQD-O-(propane-1-sulfonic acid) could be reused up to five times without considerable loss of catalytic activity.     

Controlled Synthesis of Ni-Doped MoS2 Hybrid Electrode for Synergistically Enhanced Water-Splitting Process

The development of high-efficiency, low-cost, and earth-abundant electrocatalysts for overall water splitting remains a challenge. In this work, Ni-modified MoS₂ hybrid catalysts are grown on carbon cloth (Ni-Mo-S@CC) through a one-step hydrothermal treatment. The optimized Ni-Mo-S@CC catalyst shows excellent hydrogen evolution reaction (HER) activity with a low overpotential of 168 mV at a current density of 10 mA cm⁻² in 1.0 m KOH, which is lower than those of Ni-Mo-S@CC (1:1), Ni-Mo-S@CC (3:1), and pure MoS₂. Significantly, the Ni-Mo-S@CC hybrid catalyst also displays outstanding oxygen evolution reaction (OER) activity with a low overpotential of 320 mV at a current density of 10 mA cm⁻², and remarkable long-term stability for 30 h at a constant current density of 10 mA cm⁻². Experimental results and theoretical analysis based on density functional theory demonstrate that the excellent electrocatalytic performance can be attributed mainly to the remarkable conductivity, abundant active sites, and synergistic effect of the Ni-doped MoS₂. This work sheds light on a unique strategy for the design of high-performance and stable electrocatalysts for water-splitting electrolyzers.     

CoO–xCo(OH)2 supported silver nanoparticles: electrosynthesis in acetonitrile and catalytic activity

1. Download : Download high-res image (151KB)
2. Download : Download full-size image

     

Biologically and environmentally benign approach for PHB-silver nanocomposite synthesis and its characterization

PHB-silver nanocomposite (PHB-AgNc) was synthesized biologically by utilizing a dairy-industry by-product, cheese whey permeate as a substrate for Bacillus megaterium. The single-step synthesis of PHB-AgNc was further confirmed by UV–vis spectroscopy and GC-MS analysis. Further, the extracted PHB-Ag Nc was characterized by employing various techniques such as TEM, SEM, FTIR, NMR, Zeta Potential, and DLS analysis. Mechanical properties such as elongation at break, tensile strength, and Young's Modulus were found to be 1.305%, 35.42, and 1.058 N/mm², respectively. The nanocomposite was found to be stable, polydispersive, and hydrophobic. It exhibited a degradation temperature of 340 °C and portrayed significant antimicrobial resistance against common food pathogens such as E.coli and Pseudomonas spp. Batch fermentation study was carried out for a period of 96 h in a 14 L bioreactor. The highest biomass and nanocomposite yield obtained was 5.8 and 2.4 g/L, respectively. The highest product productivity concerning biomass was found to be 0.012 h⁻¹ at 12 h. The film's migration properties were tested for various food stimulants, and the values obtained were less than the overall migration limit established for food contact materials; hence, the film was found to be appropriate for food packaging applications.     

Ocimum basilicum seed mucilage reinforced with montmorillonite for preparation of bionanocomposite film for food packaging applications

Use of nanocomposites is a well-established approach in enhancing the mechanical and barrier properties of bionanocomposite film for food packaging applications. The seed mucilage of Ocimum basilicum was employed for the preparation of bionanocomposite films with montmorillonite (MMT) as nanofiller. The films were prepared by solvent-casting method at varied solution pH (1, 3, 5 and 9) and MMT loading (1%, 3%, 5%, 10%, 15% and 20%). The films were characterized for physical, mechanical and barrier properties in addition to microstructure and X-ray diffraction pattern. XRD analysis revealed the exfoliated dispersion of MMT at pH 9, confirming its effective interaction with the bionanocomposite film. Maximum film tensile strength was achieved at a lower MMT load of 5%. Water vapour permeability reduced with increase in MMT loading up to 5%, followed by an increase at higher MMT loadings. Film formed at pH 9 showed tensile strength of 17.3 ± 0.33 MPa and reduced water vapour permeability (WVP) of 0.21 g mm.m⁻².hr⁻¹.kPa⁻¹.