发动机机油滤清器虑层强度分析及优化

针对机油滤清器工作工况下进出口压差、机油滤层强度及导流桩高度等问题, 通过试验测试与仿真相结合, 对滤清器初步设计进行了评估及优化, 以确保滤清器在工作工况下进出口压降及滤层强度能满足要求. 首先进行滤层性能试验, 得到滤层的惯性阻力系数和黏性阻力系数; 再通过滤层多孔介质CFD分析, 对滤清器进出口压降进行分析计算. 结果表明: 在-18℃、25℃和70℃的工况下, 进出口压降都小于10kPa, 满足相关要求. 针对滤层的最大主应力超过其抗拉强度的问题, 通过CAE仿真分析, 优化滤层与导流桩间隙, 将滤层最大主应力由110.1MPa降至36.99MPa, 小于其抗拉强度42.8MPa.     

移动加热器法生长碲锌镉晶体的组分输运与界面形貌研究

移动加热器法(THM)生长碲锌镉晶体时,界面稳定性对晶体生长的质量有很大影响。本文基于多物理场有限元仿真软件Comsol建立了THM生长碲锌镉晶体的数值模拟模型,讨论了Te边界层与组分过冷区之间的关系,对不同生长阶段的物理场、Te边界层与组分过冷区进行仿真研究,最后讨论了微重力对物理场分布的影响,并对比了微重力与正常重力下的生长界面形貌。模拟结果表明,Te边界层与组分过冷区的分布趋势是一致的,在不同生长阶段,流场中次生涡旋的位置会发生移动,从而导致生长界面的形貌随着生长的进行发生变化,同时微重力条件下形成的生长界面形貌最有利于单晶生长。因此,在晶体生长的中前期,对次生涡旋位置的控制和对组分过冷的削弱,是THM生长高质量晶体的有效方案。     

Viscoelastic properties of ultrathin polycarbonate films by liquid dewetting

A liquid dewetting method for the determination of the viscoelastic properties of ultrathin polymer films has been extended to study thickness effects on the properties of ultrathin polycarbonate (PC) films. PC films with film thicknesses ranging from 4 to 299 nm were placed on glycerol at temperatures from below the macroscopic glass transition temperature (T_g) to above it with the dewetting responses being monitored. It is found that the isothermal creep results for films of the same thickness, but dewetted at different temperatures can be superposed into one master curve, which is consistent with the fact of PC being a thermorheologically simple material. Furthermore, the results show that the T_g of PC thin films is thickness dependent, but the dependence is weaker than the results for freely standing films and similar to literature data for PC films supported on rigid substrates. It was also found that the rubbery plateau region for the PC films stiffens dramatically, but still less than what has been observed for freely standing polycarbonate films. The rubbery stiffening is discussed in terms of a recently reported model that relates macroscopic segmental dynamics with the stiffening. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1559–1566     

3D‐morphology reconstruction of nanoscale phase‐separation in polymer memory blends

In many organic electronic devices functionality is achieved by blending two or more materials, typically polymers or molecules, with distinctly different optical or electrical properties in a single film. The local scale morphology of such blends is vital for the device performance. Here, a simple approach to study the full 3D morphology of phase‐separated blends, taking advantage of the possibility to selectively dissolve the different components is introduced. This method is applied in combination with AFM to investigate a blend of a semiconducting and ferroelectric polymer typically used as active layer in organic ferroelectric resistive switches. It is found that the blend consists of a ferroelectric matrix with three types of embedded semiconductor domains and a thin wetting layer at the bottom electrode. Statistical analysis of the obtained images excludes the presence of a fourth type of domains. The criteria for the applicability of the presented technique are discussed. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1231–1237     

Precise Synthesis and Thin Film Self-Assembly of PLLA-b-PS Bottlebrush Block Copolymers

The ability of bottlebrush block copolymers (BBCPs) to self-assemble into ordered large periodic structures could greatly expand the scope of photonic and membrane technologies. In this paper, we describe a two-step synthesis of poly(l-lactide)-b-polystyrene (PLLA-b-PS) BBCPs and their rapid thin-film self-assembly. PLLA chains were grown from exo-5-norbornene-2-methanol via ring-opening polymerization (ROP) of l-lactide to produce norbornene-terminated PLLA. Norbonene-terminated PS was prepared using anionic polymerization followed by a termination reaction with exo-5-norbornene-2-carbonyl chloride. PLLA-b-PS BBCPs were prepared from these two norbornenyl macromonomers by a one-pot sequential ring opening metathesis polymerization (ROMP). PLLA-b-PS BBCPs thin-films exhibited cylindrical and lamellar morphologies depending on the relative block volume fractions, with domain sizes of 46–58 nm and periodicities of 70–102 nm. Additionally, nanoporous templates were produced by the selective etching of PLLA blocks from ordered structures. The findings described in this work provide further insight into the controlled synthesis of BBCPs leading to various possible morphologies for applications requiring large periodicities. Moreover, the rapid thin film patterning strategy demonstrated (>5 min) highlights the advantages of using PLLA-b-PS BBCP materials beyond their linear BCP analogues in terms of both dimensions achievable and reduced processing time.     

Role of FTFSI Anion Asymmetry on Physical Properties of AFTFSI (A=Li,Na and K) Based Electrolytes and Consequences on Supercapacitor Application

This study compares the physicochemical properties of six electrolytes comprising of three salts: LiFTFSI, NaFTFSI and KFTFSI in two solvent mixtures, the binary (3EC/7EMC) and the ternary (EC/PC/3DMC). The transport properties (conductivity, viscosity) as a function of temperature and concentration were modeled using the extended Jones-Dole-Kaminsky equation, the Arrhenius model, and the Eyring theory of transition state for activated complexes. Results are discussed in terms of ionicity, solvation shell, and cross-interactions between electrolyte components. The application of the six formulated electrolytes in symmetrical activated carbon (AC)//AC supercapacitors (SCs) was characterized by cyclic voltammetry (CV), galvanostatic cycling with potential limitation (GCPL), electrochemical impedance spectroscopy (EIS) and accelerated aging. Results revealed that the geometrical flexibility of the FTFSI anion allows it to access and diffuse easily in AC whereas its counter ions (Li⁺, Na⁺ or K⁺) can remain trapped in porosity. However, this drawback was partially resolved by mixing LiFTFSI and KFTFSI salts in the electrolyte.     

Metamorphic InAs(Sb)/InGaAs/InAlAs nanoheterostructures grown on GaAs for efficient mid-IR emitters

High-efficiency semiconductor lasers and light-emitting diodes operating in the 3–5?μm mid-infrared (mid-IR) spectral range are currently of great demand for a wide variety of applications, in particular, gas sensing, noninvasive medical tests, IR spectroscopy etc. III-V compounds with a lattice constant of about 6.1?Å are traditionally used for this spectral range. The attractive idea to fabricate such emitters on GaAs substrates by using In(Ga,Al)As compounds is restricted by either the minimum operating wavelength of ～8?μm in case of pseudomorphic AlGaAs-based quantum cascade lasers or requires utilization of thick metamorphic In_xAl_1-xAs buffer layers (MBLs) playing a key role in reducing the density of threading dislocations (TDs) in an active region, which otherwise result in a strong decay of the quantum efficiency of such mid-IR emitters. In this review we present the results of careful investigations of employing the convex-graded In_xAl_1-xAs MBLs for fabrication by molecular beam epitaxy on GaAs (001) substrates of In(Ga,Al)As heterostructures with a combined type-II/type-I InSb/InAs/InGaAs quantum well (QW) for efficient mid-IR emitters (3–3.6?μm). The issues of strain relaxation, elastic stress balance, efficiency of radiative and non-radiative recombination at T?=?10–300?K are discussed in relation to molecular beam epitaxy (MBE) growth conditions and designs of the structures. A wide complex of techniques including in-situ reflection high-energy electron diffraction, atomic force microscopy (AFM), scanning and transmission electron microscopies, X-ray diffractometry, reciprocal space mapping, selective area electron diffraction, as well as photoluminescence (PL) and Fourier-transformed infrared spectroscopy was used to study in detail structural and optical properties of the metamorphic QW structures. Optimization of the growth conditions (the substrate temperature, the As₄/III ratio) and elastic strain profiles governed by variation of an inverse step in the In content profile between the MBL and the InAlAs virtual substrate results in decrease in the TD density (down to 3?×?10⁷ cm^?2), increase of the thickness of the low-TD-density near-surface MBL region to 250–300?nm, the extremely low surface roughness with the RMS value of 1.6–2.4?nm, measured by AFM, as well as rather high 3.5?μm-PL intensity at temperatures up to 300?K in such structures. The obtained results indicate that the metamorphic InSb/In(Ga,Al)As QW heterostructures of proper design, grown under the optimum MBE conditions, are very promising for fabricating the efficient mid-IR emitters on a GaAs platform.     

Highly Luminescent Red Phosphorescent OLED with Interfacial Layers for Hole Transport and Electron Injection

Four kinds of red phosphorescent organic light-emitting devices were fabricated and compared to investigate the effect of interfacial layers for hole transport and electron injection. 1 nm-thick LiF in the device A and C and 1 nm-thick Cs₂CO₃ in the device B and D were deposited as an electron injection layer between the anode and the electron transport layer, and 5 nm-thick layer of dipyrazion[2,3-f:2′,2′-h]quinoxaline-2,3,6,7,10,11-hexacarbonitrile[HATCN] was inserted as a hole transport interfacial layer between the hole injection layer and the hole transport layer only in the device C and D. Under a luminance of 1000 cd/m², the power efficiencies were 7.6 lm/W and 8.5 lm/W in the device A and B, and 8.6 lm/W and 13.4 lm/W in the device C and D. The quantum efficiency of the device D was 15.8% under 1000 cd/m² which was somewhat lower than those of the device A and C, but a little higher than that of the device B. The luminance of the device D was much higher than those of the other devices at a given votage. The luminance of the device D at 7 V was 23,710 cd/m², which was 13.0, 3.4, and 4.0 times higher than those of the device A, B, and C at the same voltage, respectively.     

The visible and ultraviolet organic light-emitting diodes with germanium dioxide as facile solution-processed anode buffer layer

Germanium dioxide (GeO₂) aqueous solutions are facilely prepared and the corresponding anode buffer layers (ABLs) with solution process are demonstrated. Atomic force microscopy, X-ray photoelectron spectroscopy and ultraviolet photoelectron spectroscopy measurements show that solution-processed GeO₂ behaves superior film morphology and enhanced work function. Using GeO₂ as ABL of organic light-emitting diodes (OLEDs), the visible device with tris(8-hydroxy-quinolinato)aluminium as emitter gives maximum luminous efficiency of 6.5 cd/A and power efficiency of 3.5 lm/W, the ultraviolet device with 3-(4-biphenyl)-4-phenyl-5-tert-butylphenyl-1,2,4-triazole as emitter exhibits short-wavelength emission with peak of 376 nm, full-width at half-maximum of 42 nm, maximum radiance of 3.36 mW/cm² and external quantum efficiency of 1.5%. The performances are almost comparable to the counterparts with poly (3,4-ethylenedioxythiophene):poly (styrenesulfonate) as ABL. The current, impedance, phase and capacitance as a function of voltage characteristics elucidate that the GeO₂ ABL formed from appropriate concentration of GeO₂ aqueous solution favors hole injection enhancement and accordingly promoting device performance.     

Facile non‐lithographic route to highly aligned silica nanopatterns using unidirectionally aligned polystyrene‐block‐polydimethylsiloxane films

Thin films (monolayer and bilayer) of cylinder forming polystyrene‐block‐polydimethylsiloxane (PS‐b‐PDMS) were shear aligned by the swelling and deswelling of a crosslinked PDMS pad that was physically adhered to the film during solvent vapor annealing. The nanostructures formed by self‐assembly were exposed to ultraviolet‐ozone to partially oxidize the PDMS, followed by calcination in air at 500 °C. In this process, the PS segments were fully decomposed, while the PDMS yielded silica nanostructures. The highly aligned PDMS cylinders were thus deposited as silica nanolines on the silicon substrate. Using a bilayer film, the center‐to‐center distance of these features were effectively halved from 38 to 19 nm. Similarly, by sequential shear‐alignment of two distinct layers, a rhombic array of silica nanolines was fabricated. This methodology provides a facile route to fabricating complex topographically patterned nanostructures. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1058–1064