Completely biodegradable composites of poly(propylene carbonate) and short,lignocellulose fiber Hildegardia populifolia

The composites of biodegradable poly(propylene carbonate) (PPC) reinforced with short Hildegardia populifolia natural fiber were prepared by melt mixing followed by compression molding. The mechanical properties, thermal properties, and morphologies of the composites were studied via static and dynamic mechanical measurements, thermogravimetric analysis, and scanning electron microscopy (SEM) techniques, respectively. Static tensile tests showed that the stiffness and tensile strength of the composites increased with an increasing fiber content. However, the elongation at break and the energy to break decreased dramatically with the addition of short fiber. The relationship between the experimental results and the compatibility or interaction between the PPC matrix and fiber was correlated. SEM observations indicated good interfacial contact between the short fiber and PPC matrix. Thermogravimetric analysis revealed that the introduction of short Hildegardia populifolia fiber led to a slightly improved thermooxidative stability of PPC. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 666–675, 2004     

The synthesis,characterization, and weathering behavior of polycarbonates derived from bis(P-hydroxyphenyl) dimethylsilane (BPSI)

Polycarbonates and copolycarbonates based on BPSi and BPA were easily made using the standard interfacial technique. Molecular weight and NMR data indicate that up to 4 mol % of the BPSi decomposes during polymerization via a base-catalyzed rearrangement of BPSi to arylsiloxanes. Oxygen index studies show an increased flame resistance with increasing BPSi monomer content. DSC measurements show a decrease in glass transition with BPSi monomer concentration while TGA shows an increase in char residue with BPSi monomer content. In addition, TGA indicates no change in either thermal or thermooxidative stability with the relative BPSi/BPA concentrations. Outdoor weathering of BPSi PC and BPA PC films indicates that BPSi PC is ca. 5 times more weathering resistant than BPA PC. This latter result can be attributed to a combination of BPSi PC's lower UV absorptivity, higher water repellency, and lower likelihood for side chain photooxidation. © 1993 John Wiley & Sons, Inc.     

Alternating copolymerization of carbon dioxide and epoxide by manganese porphyrin: The first example of polycarbonate synthesis from 1-atm carbon dioxide

The first successful example of the formation of polycarbonate from 1-atm carbon dioxide and epoxide was demonstrated by the alternating copolymerization of carbon dioxide and epoxide with manganese porphyrin as a catalyst. The copolymerization of carbon dioxide and cyclohexene oxide with (porphinato)manganese acetate proceeded under the 1-atm pressure of carbon dioxide to give a copolymer with an alternating sequence. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3549–3555, 2003     

Synthesis and characterization of poly(ethylene oxide‐co‐ethylene carbonate) macromonomers and their use in the preparation of crosslinked polymer electrolytes

Methacrylate‐functionalized poly(ethylene oxide‐co‐ethylene carbonate) macromonomers were prepared in two steps by the anionic ring‐opening polymerization of ethylene carbonate at 180 °C, with potassium methoxide as the initiator, followed by the reaction of the terminal hydroxyl groups of the polymers with methacryloyl chloride. The molecular weight of the polymer went through a maximum after approximately 45 min of polymerization, and the content of ethylene carbonate units in the polymer decreased with the reaction time. A polymer having a number‐average molecular weight of 2650 g mol^?1 and an ethylene carbonate content of 28 mol % was selected and used to prepare a macromonomer, which was subsequently polymerized by UV irradiation in the presence of different concentrations of lithium bis(trifluoromethanesulfonyl)imide salt. The resulting self‐supportive crosslinked polymer electrolyte membranes reached ionic conductivities of 6.3 × 10^?6 S cm^?1 at 20 °C. The coordination of the lithium ions by both the ether and carbonate oxygens in the polymer structure was indicated by Fourier transform infrared spectroscopy. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2195–2205, 2006     

Synthesis and characterization of multiblock copolymers composed of poly(5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one) outer blocks and poly(L‐lactide) inner blocks

Ethylene glycol (EG) initiated, hydroxyl‐telechelic poly(L ‐lactide) (PLLA) was employed as a macroinitiator in the presence of a stannous octoate catalyst in the ring‐opening polymerization of 5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one (MBC) with the goal of creating A–B–A‐type block copolymers having polycarbonate outer blocks and a polyester center block. Because of transesterification reactions involving the PLLA block, multiblock copolymers of the A–(B–A)_n–B–A type were actually obtained, where A is poly(5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one), B is PLLA, and n is greater than 0. ¹H and ¹³C NMR spectroscopy of the product copolymers yielded evidence of the multiblock structure and provided the lactide sequence length. For a PLLA macroinitiator with a number‐average molecular weight of 2500 g/mol, the product block copolymer had an n value of 0.8 and an average lactide sequence length (consecutive C₆H₈O₄ units uninterrupted by either an EG or MBC unit) of 6.1. For a PLLA macroinitiator with a number‐average molecular weight of 14,400 g/mol, n was 18, and the average lactide sequence length was 5.0. Additional evidence of the block copolymer architecture was revealed through the retention of PLLA crystallinity as measured by differential scanning calorimetry and wide‐angle X‐ray diffraction. Multiblock copolymers with PLLA crystallinity could be achieved only with isolated PLLA macroinitiators; sequential addition of MBC to high‐conversion L ‐lactide polymerizations resulted in excessive randomization, presumably because of residual L ‐lactide monomer. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6817–6835, 2006     

Effect of glass bead packing on the fibrillation of liquid‐crystalline polymer in polycarbonate

Polycarbonate (PC) was melt blended with small amount of liquid‐crystalline polymer (LCP) and various contents of glass beads (GB) having different diameters. The rheological measurements indicated that the GB addition increased the viscosity ratio and seemed unfavorable to the LCP fibrillation. However, the morphological observation showed that the LCP fibrillation was promoted by the GB addition and varied with the GB packing. With the increased GB packing by increasing the GB content and/or decreasing the GB diameter, LCP deformed from spheres and ellipsoids into stretched ellipsoids at lower shear rates and into long fibrils at higher shear rates. Although higher content of smaller GB jammed into the larger LCP droplets and inhibited the LCP fibrillation, very long LCP fibrils formed at higher shear rates at a high enough packing of GB. The relationship between GB packing and LCP fibrillation revealed two kinds of hydrodynamic effects of GB promoting the LCP fibrillation: at lower GB packing, the shear flow was enhanced by the high local shear between GB, in quantity; and for a high enough GB packing, the shear flow was changed, in quality, into elongational flow, which was more effective for the LCP fibrillation. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1020–1030, 2006     

Enzymatic Synthesis and Polymerization of Cyclic Trimethylene Carbonate Monomer with/without Methyl Substituent

The direct enzymatic synthesis of a cyclic trimethylene carbonate (1,3‐dioxane‐2‐one) monomer with/without a methyl substituent was carried out using dimethyl or diethyl carbonate and 1,3‐diol with the objective of producing aliphatic poly(trimethylene carbonate), a typical biodegradable synthetic plastic. The lipase‐catalyzed condensation of dimethyl or diethyl carbonate with aliphatic 1,3‐diols using immobilized Candida antarctica lipase (lipase CA) in an organic solvent at 70 °C afforded the corresponding methyl‐substituted and unsubstituted cyclic trimethylene carbonates. The cyclic trimethylene carbonates obtained by the reaction of dimethyl or diethyl carbonates with 1,3‐propanediol and 2‐methyl‐1,3‐propanediol were polymerized by lipase to produce the corresponding polycarbonates.

Total TMC yield as a function of the reaction time.     

Highly Enantioselective Catalytic System for Asymmetric Copolymerization of Carbon Dioxide and Cyclohexene Oxide

A new ligand can be easily prepared, and its intramolecular dinuclear zinc complexes act as a high performance catalyst for the asymmetric alternating copolymerization of cyclohexene oxide and CO₂ under very mild conditions (1 atm CO₂, room temperature), affording completely alternating polycarbonates with up to 93.8 % enantiomeric excess (ee) and 98 % yield. A high M_n value of 28 600 and a relatively narrow polydispersity (M_w/M_n ratio) of 1.43 were also achieved.     

Multinuclear cobalt–salen complexes with phenylene linker for epoxide polymerizations

Di‐ and trinuclear cobalt (Co)–salen complexes with a benzene ring as a rigid linker were explored for epoxide polymerizations. The dinuclear Co–salen complex with a 1,2‐phenylene linker showed higher catalytic activity than the dinuclear Co–salen complex with a 1,3‐phenylene linker and the trinuclear Co–salen complex with a 1,3,5‐benzenetriyl linker for the copolymerization of propylene oxide (PO) with carbon dioxide. A combination of the absolute configuration of the two Co–salen moieties was found to affect its catalytic activity. The optimized dinuclear Co–salen complex with a heterochiral combination demonstrated highest activity and maintained its catalytic activity under a low catalyst concentration. The heterochiral dinuclear Co–salen complex also showed high activity for the copolymerization of PO with cyclic anhydride. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55, 2150–2159     

Synthesis and radical polymerization of styrene‐based monomer having a five‐membered cyclic carbonate structure

A styrene‐based monomer having a five‐membered cyclic carbonate structure, 4‐vinylbenzyl 2,5‐dioxoran‐3‐ylmethyl ether (VBCE), was prepared by lithium bromide‐catalyzed addition of carbon dioxide to 4‐vinylbenxyl glycidyl ether (VBGE). Radical polymerization of the obtained VBCE was carried out using 2,2′‐azobisisobutyronitrile as an initiator. PolyVBCE with number‐averaged molecular weight higher than 13,800 was obtained by a solution polymerization in N,N‐dimethylformamide, N,N‐dimethylacetamide, dimethyl sulfoxide, and methyl ethyl ketone. The glass transition temperature and 5 wt % decomposition temperature of the polyVBCE were determined to be 52 and 305 °C by differential scanning calorimetry and thermal gravimetry analysis, respectively. It was confirmed that a polymer consisting of the same VBCE repeating unit can be also obtained via chemical modification of polyVBGE, that is, a lithium‐bromide‐catalyzed addition of carbon dioxide to a polyVBGE prepared from a radical polymerization of VBGE. Further copolymerization of VBCE with styrene gave the corresponding copolymer in a high yield. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012