The composites of barium ferrite coated on hollow ceramic microspheres were prepared using sol-gel technique. The crystal structure, morphology and microwave absorption properties of composite powders with different weight ratio of microspheres were studied with XRD, EDS, FESEM and vector network analyzer. The results show that the microwave absorption properties of composite powders are greatly improved. The maximum microwave loss of composite powders reaches 31 dB with an amount of 50 wt.% microspheres, and its density is only about 1.80 g/cm³. The effect of hollow ceramic microspheres on the microwave absorption property is also discussed.     

Preparation and microwave absorption properties of electroless Co-Ni-P coated strontium ferrite powder

A new type of Co-Ni-P coated strontium ferrite nanocomposite was prepared with electroless plating enhanced by ultrasonic wave at room temperature. The plating process was studied carefully. The morphology, crystal structure and microwave absorption properties of the Co-Ni-P coated powder were studied with field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), energy dispersive analysis of X-rays (EDX) and vector network analyzer. The results show that the strontium ferrite powder was successfully coated with Co-Ni-P alloy and possesses excellent microwave absorption properties. The maximum microwave loss of the composite powder reaches −44.12 dB. The bandwidth with the loss above −10 dB exceeds 13.8 GHz.     

复合型铁氧体全极化器

应用耦合波理论 ,对有两组NS/N′S′四磁极磁化铁氧体中极化传输进行了分析 .在X、S波段对多种椭圆极化进行了测试 ,还完成了 0°～ 180°范围内多种线极化波测试 .最后对全极化器应用作了简单介绍 .     

Mössbauer study of nanodimensional nickel ferrite – mechanochemical synthesis and catalytic properties

Iron–nickel spinel oxide NiFe₂O₄ nanoparticles have been prepared by the combination of chemical precipitation and subsequent mechanical milling. For comparison, their analogue obtained by thermal synthesis is also studied. Phase composition and structural properties of iron–nickel oxides are investigated by X-ray diffraction and Mössbauer spectroscopy. Their catalytic behavior in methanol decomposition to CO and methane is tested. An influence of the preparation method on the reduction and catalytic properties of iron–nickel samples is established.     

Effects of pH and citric acid contents on characteristics of ester-derived BaFe12O19 powder

The single domain size of BaFe₁₂O₁₉ powder with crystallite sizes less than 200 nm was produced using a citric acid precursor method. Fe³⁺ and Ba²⁺, in a molar ratio of 12, were chelated by COOH⁻ in an aqueous solution. After ethylene glycol additions, esterification, dehydration, and calcination led to the formation of ester-derived BaFe₁₂O₁₉ powder. High pH and/or high citric acid contents in the starting solution are required to complete chelate metallic ions in the solution and to form pure barium ferrite powder at 1073 K. Pure single magnetic domain BaFe₁₂O₁₉ particles of M(30 kOe)≈54 emu/g, M_r≈28 emu/g, and H_c≈3.7 kOe were produced using [citric acid]/[metallic ions]=1.5 and pH7.     

Effects of microstructure on the temperature dependence of relative initial permeability of NiCuZn ferrites

In the present work, ferrites with compositions of (Ni_0.27Zn_0.64Cu_x)Fe_1.98O₄ (x=0.1, 0.2) were prepared by conventional ceramic methods. The relationship between the microstructure and the temperature dependence of relative initial permeability was investigated. It was found that intergranular pores in the ferrites generate large demagnetizing fields, reducing the temperature dependence of the effective anisotropy field H_eff, and decreasing the temperature dependence of the relative initial permeability accordingly. However, intragranular pores pin the movement of domain walls. Compared with the permeability induced by domain wall motion, the permeability that resulted from the spin rotation is more sensitive to temperature. As a result, the relative initial permeability of ferrites becomes more sensitive to temperature with increasing micropores within grains.     

棒状钡铁氧体的反相微乳法制备

A rodlike barium ferrite precursor with an average size of 0.72～19.6 μm and aspect ratio of 2.6～8.3 has been successfully prepared in an inverse microemulsion consisting of isooctane, cetanyl trimethyl ammonium bromide (CTAB), n-C₄H₉OH and water with ammonia and ammonium oxalate as precipitants. On sintering at 780(C, the rodlike precursor particles could be transformed into rodlike particles of barium ferrite(BaFe₁₂O₁₉) with the average size and aspect ratio of 0.69～18.2 μm and 2.3～5.8, respectively. The effect of volume ratio of aqueous phase to oleic phase, the starting concentrations of metal ions and the starting concentration ratios of metal ions to precipitants were investigated.     

纳米Zn-Co铁氧体的固相合成及电磁损耗特性研究

采用NH₄HCO₃与FeCl₃·6H₂O，Zn(NO₃)₂·6H₂O，Co(NO₃)₂·6H₂O进行室温固相反应制得前驱物，经微波加热处理后，进而热分解分别制得复合氧化物ZnFe₂O₄、CoFe₂O₄和Co_0.5Zn_0.5Fe₂O₄。由激光粒度分析仪、XRD和SEM表征：获得了颗粒分布比较均一、平均粒度为65 nm左右、立方晶系尖晶石结构的纳米铁氧体粉体。经测试样品的相对介电常数和相对磁导率后，研究了它们的电磁损耗特性。结果表明：Co_0.5Zn_0.5Fe₂O₄在100～1 800 MHz内比另外两种铁氧体具有更好的电磁损耗特性。     

可溶性聚硅酸铝铁的制备及其在废水处理中的应用

以赤泥为原料,制备了高效无机高分子絮凝剂——聚硅酸铝铁(PSAF),并将该絮凝剂用于处理工业废水．研究絮凝剂的使用效果与投加量、投加方式、pH值、搅拌条件及水样本身性能间的关系．     

M?ssbauer studies of the phase composition and microstructure of the La1-xCaxFeO3-y system as related to the reactivity of surface and bulk oxygen

The phase composition and microstructure of samples of the La_1-xCa_xFeO_3-y system prepared via a ceramic route were characterized by M?ssbauer spectroscopy. In all cases, iron was found in the 3+ state. The ordering of anion vacancies in the samples with the composition in the range of 0.8 > x ≥ 0.4, which corresponds to a microheterogeneous solid solution, generates new distorted octahedral and fivefold/tetrahedral sites revealed by two typical sextets. The disordering of this solid solution and small (10-100 ?) sizes of domains with a perovskite, braunmillerite or Grenier phase structure caused the appearance of a superparamagnetic doublet, which grows with the Ca content up to x = 0.8 but disappears in the sample of pure braunmillerite. The appearance of Fe cations in a distorted coordination correlates with the increased activity of the samples with a microheterogeneous structure in the CO catalytic oxidation and with their reducibility by H₂. This revised version was published online in August 2006 with corrections to the Cover Date.